JPS6124040A - 光学式情報記録体 - Google Patents

光学式情報記録体

Info

Publication number
JPS6124040A
JPS6124040A JP14550484A JP14550484A JPS6124040A JP S6124040 A JPS6124040 A JP S6124040A JP 14550484 A JP14550484 A JP 14550484A JP 14550484 A JP14550484 A JP 14550484A JP S6124040 A JPS6124040 A JP S6124040A
Authority
JP
Japan
Prior art keywords
transparent
film
layer
thin film
synthetic resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP14550484A
Other languages
English (en)
Other versions
JPH0322657B2 (ja
Inventor
Kazu Yamanaka
山中　計
Yoshiyuki Fukumoto
福本　義行
Shigemasa Kawai
河合　重征
Michiyoshi Nishizaki
西崎　倫義
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sekisui Chemical Co Ltd
Original Assignee
Sekisui Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sekisui Chemical Co Ltd filed Critical Sekisui Chemical Co Ltd
Priority to JP14550484A priority Critical patent/JPS6124040A/ja
Publication of JPS6124040A publication Critical patent/JPS6124040A/ja
Publication of JPH0322657B2 publication Critical patent/JPH0322657B2/ja
Granted legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 （技術分野） 本発明はレーザー光の反射ま九は透過により信号の記録
・再生を行う光学式情報記録体に関する。
（従来技術） 従来、ビデオディスク、オーディオディスク、情報ファ
イルボックス等の光学式ディスクの基板用材料として線
、ポリメチルメタ調クリレート、ポリカーボネート等の
透明性に優れた合成樹脂が使われている。
しかしながら、ポリメチルメタクリレートは、成型加工
性と強度に優れているが、耐透湿性に劣シ、片面に記録
層が設けられ、該記録層上にアルミニウム等の反射膜が
設けられた光学式ディスクの記録層からの侵入は反射膜
によシ阻止されるが、記録層が設けられていない方の片
面から水分の侵入があるため、反 高湿下では、成形品に−→が生じ信号の読み堆シに誤差
が生じたシ、また、吸湿と乾燥との繰返しによシ、ポリ
メチルメタ膳クリレートと反射膜との間に剥離す生じる
という欠点がある。
この点を改善するため、例えば特開昭５８−３２２３８
号公報に記載の如く、透明樹脂基板の一面に、不透湿性
の記録媒体層または反射膜を、他面にＣａＦ＊、ＳｉＯ
ｘの不透湿膜を設けるととｋよシ、・ディスク周囲の温
度、湿度！形に対し安定化させることが提案されている
が、耐透湿性状十分でなく、前記欠点を解消するに至っ
ていない。
また、ポリカーボネートは、成形加工性が悪く、成形時
の歪が樹脂中に残シ、複屈折が生じ中すく、大形のディ
スクＫａ使用できないという欠点がある。
（Ｊ！明の目的） 本発明は、叙上の如き従来の欠点を解消し、透明性、成
形性に優れ、複屈折がなく、且つ耐透湿性に優れた光学
式情報記録体を提供ネることを目的としてなされたもの
である。
（発明の要旨） 本発明の要旨は、一面に記録層が設けられた透明な合成
樹脂基板の記録層が投砂られていない方の面に、透明防
湿フィルムｉ接着されてなる光学式情報記録体に存する
。
（発明の構成） 第１図に図示する如く、ポリメチルメタ−クリレート等
の透明な合成樹脂基板１の一面に信号トラック溝が形成
された如き、記録層指板ｌの記録層２が設けられていな
い方の面に、透明防湿フィルム５が接着されている。
透明防湿フィルム５は、ポリアクリルニトリル等の透明
合成樹脂フィルム５１の片面上にマグネシウム酸化物の
透明薄膜層５２が形成され、該透明薄膜層５２上に５ｉ
Ｏｚ　、　Ｂｔｕｓ　。
ＢａＯ、Ａｌ１　Ｏｘがモル比で、（Ｓ　１Ｏｔ）　：
　（Ｂ２Ｏ３）：　　（ＢａＯ＋ＡｔｔＯｓ）〜２〜４
　　：　　ｔ　〜ｚ　　：　　ｏ、ｓ〜！とされ九組成
物のアモルファス状透明薄膜層５３が形成されたものか
らなシ、合成樹脂板１の記録層５が設けられていない方
の面には、透明合成樹脂フィルム５１の透明薄膜層５２
及びアモルファス状透明薄膜層５３が形成されていない
方の面が接着されている。
尚、両層ｓｚ、ｓｓが形成された藺が接着されていて亀
よい。
透明金成樹脂フィルムとして杜、透明で且つ複屈折がな
くフィルムに形成できるものである必要があ〕、ポリア
クリｏ　＝　）リルからなるものが好適に使用されるが
、これに限定されることなく、同様の性能を有する材料
のものであればよい。
透明合成樹脂フィルム上に形成されるマグネシウム酸化
物の透明薄膜層線、真空蒸着やマグネシウムの反応蒸着
によシ形成される。
真空蒸着では、蒸着物質として酸化マグネシウムが採用
され、これを電子銃で加熱蒸着される。反応蒸着の方法
は、真空槽内に酸素ガスを導入しながら金属マグネシウ
ムを加熱蒸発させ、マグネシウム酸化物薄膜層を形成す
る。いずれの場合も、耐透湿性を向上させるためＫ　Ｈ
ｚ　Ｏなどのガスを導入しながら、マグネシウム酸化物
の透明薄膜層を形成することも可能である。
マグネシウム酸化物の透明薄膜層上に形成されるアモル
ファス状透明薄膜層はＳｉＯ２゜Ｂ鵞Ｏｓ　、　ＢａＯ
、ＡｔｔＯｓがモル比で（８１０り、；（Ｂｏｏｍ　）
　：　（ＢａＯ＋ＡｔｘＯｓ）　　＝　２〜４　：　ｓ
〜２：ａ３〜ｌとなされ九組成物からなる。
ＢａＯとＡｌｔｏｓ　ｆｌ、その一方が実質的に含まれ
なくてもよい。
アモルファス状透明薄膜層の上記の組成ＫＮａ＊０など
のアルカリ金属の酸化物が多量に入ると、その親水性の
丸めに耐透湿性状損われ、真空蒸着を行うに（組成が変
動しゃすい欠点が生じる。
また、アモルファス状透明薄膜層のそル比が、上記の範
囲を外れると、層ｊ離を起しゃすくなル、耐透湿性が悪
化し、（ＢａＯ＋ＡｚｚＯｓ）の量が小さくなると耐透
湿性が劣る傾向となる。
上記酸化組成物を酸化マグネシウムの透明薄膜層上に形
成する方法として最も好ましいのはスパッタリングであ
シ、スパッタリングのターゲットを上記の組成とするこ
とで＃を埋同じ組成のアモルファス状透明薄膜層を形成
することができる。また６、真空蒸着法、イオンブレー
ティング法によっても、上記組成のアモルファス状透明
薄膜層を形成することができる。真空蒸着の場合線、蒸
気圧の異なる混合物質をそのｔまの組成で薄膜層を形成
するの紘困難であるとされている。しかし、本発明者働
は上記組成物を予め電気炉で熔融しガラス化したものを
蒸発剤として使用し、電気鉄方式で蒸発させれば、略同
じ組成の蒸発膜が得られることを確認した。また、一般
に混合物を真空蒸着する時に用いられるフラッシュ蒸着
法によっても、上記の組成の蒸着膜を形成することがで
きる。
透明合成樹脂フィルム上に、酸化マグネシウムの透明薄
膜層と５１０ｔ、Ｂ＊αｓ、ＢａＯ，Ａｔｔｏｓ　カモ
Ａ比テ（５ｌ（ｈ）　：　（Ｂ宜Ｏｓ　）　：（ＢａＯ
＋ＡｌｔＯｓ）〜２〜４　：　ｔ　〜２　：０．３〜ｔ
とされた組成物からなるアモルファス状透明薄膜層が順
次形成されて透明防湿フィルムが形成されている。
透明合成樹脂基板の記録層が設けられていない方の面に
、透明防湿フィルムが接着されている。尚、透明防湿フ
ィルムの接着は１．酸化マグネシウムの透明薄膜層及び
アモルファス状透明薄膜層の両層が形成され丸面或いは
両層が形成されていない面のいずれを接着爾としてもよ
いが、酸化マグネシウム社水分と接触すると水酸化マグ
ネシウムに変化する苛能性があり、またアモルファス状
透明薄膜層は酎引っ掻き強度が強く、前記の両層が形成
されていない面を接着するのが好ましい。
叙上の構成において、酸化マグネシウムの透明薄膜状、
Ｘ線回折、ＲＨＥＥＤ（反射型高速電子線回折）、ＳＥ
Ｍ（走査電子顕微鏡）等の観察結果から、多結晶薄膜と
なっておル、水や酸素等線結晶の粒界を拡散して透過す
ると推定できるが、そこにアモルファス状透明薄膜層が
積層されているため、その粒界の通路が遮蔽されて、耐
透湿性、耐ガス透過性が格段改善されるものと推察され
る。
マグネシウム酸化物の透明薄膜層及びアモルファス状透
明薄膜層の厚みは、それぞれ！ｏｏＸ以上でなければ一
様な連続膜が形赦されにくい丸め、　Ｈ）ＯＡ以上必要
である。また両層の合計厚みが５ｏｏｏＸを越えると透
明性を損うことはないが、亀裂や剥離が生じやすくなる
ので好ましくない。
（発明の効果） 本発明光学式情報記録体は、叙上の如き構成とされてい
るので、透明合成樹脂基板の諸が生じること線始んどな
く、合成樹脂基板上に直接蒸着尋によシ透明防湿層を形
成するという低生産性手段を取ることなく、高性能の透
明防湿フィルムを別途生産性よく製造しておいて、これ
を透明合成樹脂基板上に接着するという簡便な手段によ
シ能率よく生産することができる。
（実施例） 以下に本発明の実施例を示す。
〈実施例１〉 厚み５０μｍの透明なポリアクリロニトリルフィルム上
に、真空槽内で真空度５Ｘ１０−’ＴＯＲＲＫ排気した
状態で、純度９９．９％の酸化マグネシウムを電子ビー
ム加熱方式によシ、成膜速度約ｉｏｏ　Ａ　／　ｆｌｅ
ｅで厚みｇｏｏｆのマグネシウム酸化物の透明薄膜層を
形成した。
マグネシウム酸化物の透明薄膜層上に％８１０ｇ　、　
Ｂｔｕｓ　、　ＢａＯ、Ａｔ＊Ｏｓがモル比で（Ｓｉｆ
ｔ）０．３３とした酸化物の混合物を電気炉で溶解しガ
ラス化したものを、真空度ｓ　ｘ　１ｏ−’ＴＯＲＩの
状態で、電子ビーム加熱方式により、成膜速度的１００
Ａ／ｓ＠ｅで厚み５００Ａのアモルファス状透明膜層を
形成した。
しかして、透明なポリアクリｏ二）リルの一方の面上に
、マグネシウム酸化物の透明薄膜層及びアモルファス状
透明薄膜層が順次形成された透明防湿フィルムを作成し
た。
この透明防湿フィルムを、前記両層が形成されていない
方の面を接着面とし、厚み２　ｍ　。
縦”１２０語、横１２０鵡の大きさの透明なポリメチル
メタ蟲クリレート基板の一面に、感光性接着剤（明星チ
ャーチル株式会社製の商品名［フォートボンドＪ）によ
シ接着し九′。
このポリメチルメタクリレート基板の透明防湿フィルム
が接着されていない方の面及び周囲にアルミニウムを１
ｓｏｏＸの厚みに蒸着し、その上に保護層をコートシ、
透明防湿フィルムが接着された面取外の部分からの水の
侵入を遮断した試料を作成した。　　゛ この試料の吸水後の反り、全光線透過率、゛量価、訃よ
び複屈折率を測定した。その結果を第１表に示す。
尚、各層の厚みは水晶発信式のモニターによシ計測し九
。アモルファス状透明薄膜層の組成は、Ｘ線マイクａア
ナライザーで分析したとζろ、当初の混合物の組成と略
同等であった。
定した。また、全光線透過率はＡ　Ｓ　ＴＭＤ　−１０
０３の方法によりｍ定した。また量化は、ＡＳＴＭＤ−
１ｏ　ｏ　ｓの方法にょシ測定した。
また、複屈折の有無性試料を２枚の偏光板の間ＫＨさみ
、可視光を透過して干渉稿を観察することによシ調べた
。
〈実施例２〉 実施例１に準じて、厚みｓｏｐｍの透明なポリアクリロ
ニトリルフィルムの一方の面上に１厚み５０Ｑ　Ｘのマ
グネシウム酸化物の透明薄膜層゛を形成し、その層上に
厚み１０００　Ａのアモルファス状透明薄膜層を形成し
た透明防湿フィルムを作成した以外拉実施例１と同様と
し九試料を作成し、この試料について実施例１と同様の
測定を行った。その結果な第１表に併せて示す。
〈実施例３〉 実施例ＩＫ準じて、厚＋５０μ電の透明膜ポリアクリロ
ニトリルフィルムの一方の面上に、厚み５００　Ａのマ
グネシウム酸化物の透明薄膜層を形成し、その層上に、
８１（ｈ　、　ＢａＯ易。
Ｂ　ａ　Ｏ、ＡｔｔＯｍが％に比で、（Ｓｌｏｔ）：（
ＢｖＯｓ　）　：　（Ｂａｄ）　：　（ＡｌｔＯｍ　）
＝　４　：　２　：０、７５　：　ｏ、２５とした酸化
物の混合物によシ１！施例１に準じて厚み５ｏｏＸのア
モルファス状透明薄膜層を形成し、それ以外線実施例五
と同様とした試料を作成し、この試料について実施例１
と同様の測定を行った。その結果を第１表に併せて示す
。
〈実施例４〉 厚みｇｏ　ｐｍの透明なポリアクリロニトリルフ３：１
：０．６７：α３３とした酸化物の混合物を電気炉で熔
解しガラス化し九本のを、真ｔ１度ｓｘ　１ｏ−ＩｓＴ
ＯＲＲＯ状１１１テ、電子ヒーＡ方式によシ、成膜速度
的１００Ｘ／　ｓ＠ｅで厚み５００又のアモルファス状
透明薄膜層を形成して、透明防湿フィルムを作成した以
外は実施例１と同様とした試料を作成し、この試料につ
いて、実施例１と同様の測定を行った。その結果を第１
表に併せて示す。
〈比較例！〉 厚み２３ｓ、縦１２０８．横１２０１１８の大きさのポ
リメチルメタアクリレート基板Ｏ向も処理していない試
料について、実施例１と同様の測定を行った。その結果
を第１表に併せて示す。
〈実施例２〉 厚み５０μｍの透明なアクリロニトリルフィルムを、一
面を接着面とし、厚みｚＩ＆、縦１２０鵡、横１２（Ｉ
ｓｓの透明なポリメチルメタアクリレート基板の一面に
、感光性接着剤（明星　　１チャーチル株式会社製の商
品名「フォートボンド」）によシ接着した。
このポリメチルメタアクリレート基板を実施例１と同様
に透明防湿フィルムが接着された画風外の部分からの水
の侵入を遮断した試料を作成し、実施ｌと同様の測定を
行った。
その結果を第１表に併せて示す。
第１！！ 第１表からも明らかな如く、実施例１〜４の場金杜、比
較例１．２の場合と比べて、反シが著しく小さく、且つ
全光線透過率、ｌ個、複屈折等は劣ることがない。
【図面の簡単な説明】
第１図は本発明の一例を示す断面図である。 符号の説明 ■・・・透明壕合成樹脂基板、　２・・・記録層、３・
・・反射膜、　４・・・保護層、　５・・・透明防湿フ
ィルム、　　５１・・・透明な合成樹脂フィルム、　　
５２・・・マグネシウム酸化物の透明薄膜層、　　５３
・・・アモルファス状透明薄膜層。

Claims (1)

  1. 【特許請求の範囲】 １、一面に記録層が設けられた透明な合成樹脂基板の、
    記録層が設けられていない方の面に、透明防湿フィルム
    が接着されてなる光学式情報記録体。 ２、合成樹脂基板がポリメチルメタクリレートである特
    許請求の範囲第１項記載の光学式情報記録体。 ３、透明防湿フィルムが透明合成樹脂フィルム上にマグ
    ネシウム酸化物の透明薄膜層が形成され、該透明薄膜層
    上にＳｉＯ＿２、Ｂ＿２Ｏ＿３、ＢａＯ、Ａｌ＿２Ｏ＿
    ３がモル比で、（ＳｉＯ＿２）：（Ｂ＿２Ｏ＿３）：（
    ＢａＯ＋Ａｌ＿２Ｏ＿３＝２〜４：１〜２：０．３〜１
    とされた組成物のアモルファス状透明薄膜層が形成され
    たものである特許請求の範囲第１項または第２項記載の
    光学式情報記録体。 ４、透明合成樹脂フィルムがポリアクリロニトリルから
    なるものである特許請求の範囲第３項記載の光学式情報
    記録体。
JP14550484A 1984-07-12 1984-07-12 光学式情報記録体 Granted JPS6124040A (ja)