JPS61217228A - 二層被覆金属板の製造方法 - Google Patents

二層被覆金属板の製造方法

Info

Publication number
JPS61217228A
JPS61217228A JP60060026A JP6002685A JPS61217228A JP S61217228 A JPS61217228 A JP S61217228A JP 60060026 A JP60060026 A JP 60060026A JP 6002685 A JP6002685 A JP 6002685A JP S61217228 A JPS61217228 A JP S61217228A
Authority
JP
Japan
Prior art keywords
mold
metal plate
coated
resin
metallic plate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP60060026A
Other languages
English (en)
Inventor
Junichi Yoshimoto
吉本　順一
Ryuichi Kitagawa
龍一 北川
Tadayuki Irisa
入佐　忠行
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Panasonic Electric Works Co Ltd
Original Assignee
Matsushita Electric Works Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Matsushita Electric Works Ltd filed Critical Matsushita Electric Works Ltd
Priority to JP60060026A priority Critical patent/JPS61217228A/ja
Publication of JPS61217228A publication Critical patent/JPS61217228A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 ［技術分野］ 本発明は防音遮音機能を有する二層被覆金属板の製造方
法に関する。
［背景技術」 従来にあっては、まず発泡材料に金属板をインサートし
た成形品を造り、この成形品に別工程あるいはオンライ
ンで表層材を被覆して二層被覆金属板を製造しているが
、この方法では複雑な形状の成形品を製造することがで
きなく、又押出インサート成形ては金型内で、発泡材料
を被覆し、発泡させた後、表層材を被覆する際に、発泡
材料により形成した発泡層が潰され、膜厚制御、発泡倍
率のコントロール、成形安定性を確保できなかった。又
金属板インサート成形品を塗装して二層被覆金属板を製
造したりもされているが、複雑な塗装設備が必要となる
だけでなく、溶剤タイプにあっては排気が問題となり、
又硬化時間を必要として生産性が低下してしまっていた
。
［発明の目的］ 本発明は上記事情に鑑みて為されたものであり、その目
的とするところは、複雑な形状の成形品を製造すること
ができ、しかも膜厚制御、発泡倍率のコントロール、成
形安定性を確保でき、更には生産性を向上させることが
できる二層被覆金属板の製造方法を提供することにある
。
［発明の開示コ 本発明の二層被覆金属板の製造方法は、金型１内に金属
板２を通して金型１内で金属板２に中芯発泡材料３を実
質的に無発泡状態て被覆すると共に中芯発泡月利３の上
から表層材４を被覆し、金型１を出た段階で金属板２に
被覆した中芯発泡月利３を発泡さぜ、この後サイジング
ダイ５を通して冷却させることを特徴とするものであり
、この構成により上記目的を達成できたもσ）である。
即ち金型］内で中芯発泡材料３を実質的に無発泡状態で
被覆するので、成形品に使用される樹脂量を一定にてき
、従って膜厚構成も一定にてきるものであり、しかもサ
イジングダイ５を通して冷却するので、発泡倍率を調整
することができると共に所定の発泡倍率に収束させるこ
とができ、成形安定性を確保できるものであり、又サイ
ジングダイ５により発泡倍率を調整するのて、金型１内
の温度、樹脂圧等を厳密に制御する必要がなく生産性を
向上させることかできるものである。
以下本発明を添ｆ＝１−の図面を参照して詳細に説明す
る。この実施例はいわゆる押出インザート成形について
のものである。押出成形用ダイである金型１には金属板
２を通ず通路６を形成しており、この通路６には金属板
２の進行方向で前後に通路６に連通ずる第１樹脂流路７
と第２樹脂流路８を形成している。押出機（図示１〜な
い）から第１樹脂流路７を通して発泡剤を含有し溶融し
た中芯発泡材料３を通路６に流し、第２樹脂流路８を通
して溶融した表層材４を通路６へと流すようにしている
。まず両面に接着剤を塗布した金属板２を金型１の入す
ロスリット９から通路６へ通ず。金属板２としては厚み
０．１（１〜０．１２ＩＩ１ｍの穴明は圧延５ｐｃ（第
４図）とか穴明けなしで、厚み０．１４ｍｍ、ピーリン
グ強度４．０ｋｇ／ｃｍ２以上の鋼板（第５図）を用い
る。
金型１内で金属板２に第１樹脂流路７を通して中芯発泡
材料３を実質的に無発泡状態で厚みが０．２ｍｍ程度と
なるように被覆する。中芯発泡材料３としては、例えば
硬質塩化ビニル樹脂に発泡剤を含有させたものであり、
この樹脂圧を金型１の出口スリット１０付近まで発泡ガ
ス圧以上に維持することにより無発泡状態に維持できる
。尚、ここていう実質的に無発泡状態とは発泡倍率が１
．８程度のものも含む概念である。この中芯発泡材料３
の被覆と同時に、第２樹脂流路８から表層材４を通路６
に流して金型１内てこの無発泡状態の中芯発泡材料３の
上から表層材４を被覆する。この表層材４としては、例
えば＾＾Ｓ樹脂を０．０５ｎｖ程度被覆する。このよう
にして金属板２に二層被覆して金型］の出口スリット１
０より外部に出す。この段階で金属板２に被覆した中芯
発泡材料３が発泡する。この後二層被覆した金属板２を
サイジングダイ５に通して完全に冷却し、最終寸法形状
にして最終製品として二層被覆金属板Ａを得る。従って
発泡倍率は金型１の出口スリット１０とサイジングダイ
５のサイジングスリット１１の相対的な関係で決まる。
例えば中芯発泡材料としてＰｖＣ樹脂を、表層材４とし
てＡＡＳ樹脂を採用し、金属板２としてｄ＝０．１４ｍ
＋ｎの穴明けなし鋼板を用い、厚Ｔ−１ｍｍ−Ｋ＝２．
３（倍）、ｔ＝０．０５ｍｍの成形品を得るためには金
型１の出１」スリット１０の厚Ｔｏ＝　０．５５９ｍｍ
であることが判る。
尚、本発明により製造した二層被覆金属板Ａは第６Ｌｉ
７Ｉに示ずように軒樋１３などとして実用に供される。
［発明の効果］ 本発明にあっては、金型内に金属板を通して金型内で金
属板に中芯発泡材料を無発泡状態で被覆すると共に中芯
発泡材料の上から表層材を被覆し、金型を出た段階で金
属板に被覆した中芯発泡材料を発泡させ、この後サイジ
ングダイを通して冷却させるものであって、金型内で中
芯発泡材料を無発泡状態で被覆するので、成形品に使用
される樹脂量を一定にでき、従って膜厚構成も一定にで
きるものであり、しかもサイジングダイを通して冷却す
るので、発泡倍率を調整することができると共に所定の
発泡倍率に収束させることができ、成形安定性を確保で
きるものであり、又サイジングダイにより発泡倍率を調
整するので、金型内の温度、樹脂圧等を厳密に制御する
必要がなく生産性を向上させることができるものである
。
【図面の簡単な説明】
第１図は本発明の一実施例をその方法を実施するための
装置と共に示す概略断面図、第２図は同上における金型
の出口スリットての二層金属板を示す断面図、第３図は
同上にお（Ｊるサイジングタイを出た最終製品状態ての
二層被覆金属板を示す断面図、第４図は穴明き鋼板を採
用した二層金属板を示す断面図、第５図は穴明きなし鋼
板を採用した場合の二層金属板を示す断面図、第６図は
同上の二層被覆金属板の使用例を示す斜視図であって、
１は金型、２は金属板、３は中芯発泡材料、４は表層材
、５はサイジングダイである。 代理人　弁理士　石　１）長　七 第１図 ′ｌ 第２図　　　　第３図

Claims (1)

    【特許請求の範囲】
  1. （１）金型内に金属板を通して金型内で金属板に中芯発
    泡材料を実質的に無発泡状態で被覆すると共に中芯発泡
    材料の上から表層材を被覆し、金型を出た段階で金属板
    に被覆した中芯発泡材料を発泡させ、この後サイジング
    ダイを通して冷却させることを特徴とする二層被覆金属
    板の製造方法。
JP60060026A 1985-03-25 1985-03-25 二層被覆金属板の製造方法 Pending JPS61217228A (ja)