JPS60242529A - 光学的情報記録媒体 - Google Patents

光学的情報記録媒体

Info

Publication number
JPS60242529A
JPS60242529A JP59096593A JP9659384A JPS60242529A JP S60242529 A JPS60242529 A JP S60242529A JP 59096593 A JP59096593 A JP 59096593A JP 9659384 A JP9659384 A JP 9659384A JP S60242529 A JPS60242529 A JP S60242529A
Authority
JP
Japan
Prior art keywords
film
recording medium
recording
thin film
optical information
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP59096593A
Other languages
English (en)
Inventor
Hiroki Suzuki
鈴木　央樹
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dai Nippon Printing Co Ltd
Original Assignee
Dai Nippon Printing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dai Nippon Printing Co Ltd filed Critical Dai Nippon Printing Co Ltd
Priority to JP59096593A priority Critical patent/JPS60242529A/ja
Publication of JPS60242529A publication Critical patent/JPS60242529A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 〔発明の技術分野〕 本発明は、記録層に低出力のエネルギービームを照射す
ることによって、記録層に大きな状態変化を生じせしめ
て多様な大きさの記録ビットを記録層形成できるヒート
モード記録法に適する光学的情報記録媒体に関する。
〔発明の技術的背景ならびにその問題点〕従来、レーザ
ー光線などの高密度エネルギービームを記録層が設けら
れた記辞媒体上にスポット状に集光照射させて、記録層
の一部を状態変化させて記録するようにしたいわゆるヒ
ートモード記録は知られている。このような記録媒体の
記録−としては、テルル、ビスマスなどの金属薄膜、ポ
リスチレン、ニトロセルロースなどの有機ｓｉ。
あるいはテルル低酸化物などの金属低酸化物の相転移を
利用したものなどが知られており、これらは「書いた後
、直読する」ことのできるいわゆるＤ　ＲＡＷ　（ｄｉ
ｒｅｃｔ　ｒｅａｄ　ａｆｔｅｒ　ｗｒｉｔｅ　）記録
媒体であり、高密度記録が可能で、追加書込みが可能で
あることから、現在、既に実用化されている光ディスク
のほかレーザーカードなと今後幅広い用途に使用される
ようになると考えられる。
従来から知られているヒートモード記録媒体のうち、テ
ルル、ビスマスなどの金属薄膜は、ビームスポットに対
する解像性に優れている反面、ビームスポットより比較
的大きな記録ビットを書込む場合には、駆動ミラーなど
を用いてビームを走査することが必要となり、この際ビ
ット内には金属が一部残存することがあり、このため記
録の読出し時にエラーが発生することがある。さらに円
形のピットを金属薄膜に書込む場合にはピットの外周部
に乱れが生ずるという問題点がある。−万有ｍ薄膜の場
合には円形のピットの書゛込みに適性を持つが、情報読
出し装置の焦点機構に対し、充分な反射率をもたらすこ
とが難しいという問題点があり、また金属低酸化物の相
転移を利用する記録媒体の場合には、エネルギービーム
によって生じる状態変化が微小で、情報の読出し装置の
高性能化が必要であるなどの問題点があった。
〔発明の目的ならびにその概要〕
本発明は、このような従来技術に伴なう問題点を解決し
ようとするものであって、低出力のエネルギービームを
記録層に照射することによって、記録媒体の記録層に大
きな状態変化を生じせしめて、記録ビットを形成し、こ
の際小面積から大面積までの多様な大きさのピットを形
成することの可能な光学的情報記゛録媒体・を提供する
ことを目的としている。
本発明に係る光学的情報記録媒体は（ａ）照射エネルギ
ービームの熱エネルギーによって蒸発または昇華する金
属酸化物薄膜と、（ｂ）エネルギービームの照射による
前記金属酸化物Ｓａの蒸発または昇華に伴う体積膨張作
用および照射エネルギービームの熱エネルギーの作用に
よって変形し、バブル状記録ビットを形成できる金属薄
膜とを、前記の順序で基板上に積層して形成されている
ことを特徴としている。
〔発明の詳細な説明〕
以下、本発明を図面に示す具体例についてより詳細に説
明する。
本発明に係る記録媒体１は、その断面図が図に示される
ように、基板２上に、照射エネルギービームの熱エネル
ギーによって蒸発または昇華する金属酸化物薄膜３と、
エネルギービームの照射による前記金属酸化物薄膜の蒸
発または昇華に伴なう体積膨張作用および照射エネルギ
ービームの熱エネルギーの作用によって変形し、バブル
状記録ビットを形成できる金属薄膜４とが、この順序で
積層されて形成されている。
金属酸化物簿膜３は、比較的低温度で蒸発または昇華す
るもの、たとえばＭ。０３、ＴｏＯ２、Ｓ　Ｏ、Ｉ　Ｏ
’、Ｓ　Ｏ、Ｒ，０７から選ｂ２５ｎ２３ｅ２ ばれた１種以上の金属酸化物から構成されておりこのう
ちＭｏ　０３　、Ｔｅ　０２が特に好ましい。金属酸化
物薄膜を基板上に謹けるには、真空蒸着法、スパッタリ
ング法、イオンブレーティング法などが適用できるが、
比較的簡便に再現性良く行なえるという観点から真空蒸
着法が好ましい。この金属酸化物の膜厚は、形成される
ピットの大きさや感度に影響を与えるが、１００〜２０
０ＯＡ、好ましくは２００〜５００Ａの範囲であること
が好ましい。
金属薄１１１４は、延展性を示す膜厚において充分な反
射率が得られるもの、たとえばＡＩ、Ｃｒ。
Ｍｎ、ｆ：ｅ、Ｃ，ＯｌＮ　ｉ、ｃｕ、ｚｎ、　Ｇｅ。
１；）、ｘｎ、ｓｎ、ｐｂ、Ｂ　ｔから選ばれた１種以
上の金属またはそれらの合金から構成されており、この
うちＡＩ、Ｃｕ、Ｓｎなどの金属が好ましい。上記の金
属は単独で用いても複合で用いてもよい。金属薄膜は、
記録された情報を続出す際に必要とされる反射率が得ら
れるような膜厚で前記金属酸化物簿ＷＡＳ上に設けられ
るが、その形成方法としては真空蒸着法、スパッタリン
グ法、イオンブレーティング法、電気メツキ法などが挙
げられるが、真空蒸着法が好ましい。またその膜厚は、
形成されるビットの大きさや感度に影響を与えるが、１
００〜２００ＯＡ好ましくは２００〜７００Ａの範囲で
あることが好ましい。
本発明に係る記録媒体は、金属薄膜をビーム反射層とし
、照射エネルギービームの熱エネルギーによって、基板
と金属薄膜との間にはさまれている金属酸化物を蒸発ま
たは昇華させ、その体積膨張作用および照射エネルギー
ビームの熱エネルギーの作用によって、前記の金属薄膜
をバブル状に変形せしめてビットを形成し、情報の記録
を行うものである。記録媒体は基板上に（ａ）金属酸化
物薄膜と（ｂ）金属薄膜とがこの順序で積層され形成さ
れる。
情報の記録は、基板側から記録層へエネルギービームを
照射させて行なわれ、情報の読出しは、記録媒体の金属
酸化物薄膜を蒸発または昇華させない程度の低エネルギ
ーのビームを同様に基板側から照射して、反射強度の変
化と位相変化とを関連づけて読取ることによって行なわ
れ゛る。このように照射されたエネルギービームは基板
を透過して記録層に達しているため、基板としては偏光
性や干渉性などのエネルギービームの伝達を妨害する因
子のない材料か、またはビーム伝達を妨害しないように
構成あるいは処理され１＝材料を用いることが望ましい
。このような性質を有する基板としては、ガラス、ポリ
メチルメタクリレート、ポリカーボネートのような材料
が好ましいが、前記の条件を満足するように構成されて
いるか処理されていればいかなる材料を用いてもよい。
なお本明細書において、エネルギービームとは、半導体
レーザー、アルゴンレーザー、ヘリウム−ネオンレーザ
−などのレーザービームに代表される高いエネルギーを
有しているビームを意味している。
〔発明の効果〕
本発明に係る光学的情報記録媒体における記録ビットは
、基板と金属薄膜との間にはさまれた金属酸化物が照射
エネルギービームの熱エネルギーによって蒸発または昇
華する際の体積膨張作用と照射エネルギービームの熱エ
ネルギーの作用による温度上昇とにより、金属薄膜がバ
ブル状に変形することにより形成されているため、金属
酸化物薄膜を低温で蒸発または昇華する金属酸化物で構
成するかあるいは延展性の良い金属を金属薄膜に用いる
ことにより、記録材料としての感度を高めることが可能
であり、またエネルギービームの出力あるいはエネルギ
ービームの照射時間を変化させることにより記録ピット
の直径を変化させることが可能である。用いる金属酸化
物、金属によっても異なるが、たとえば２μｍ径のスポ
ットにエネルギービームを集光して照射した場合で２〜
２０μｍ程度までビット径を変化させることができる。
また金属を変形せしめるのに固体から気体あるいは固体
から液体そして気体というような著しい体積膨張を生じ
る気化の過程を含む相変化を利用しているために、記録
時の金属酸化物薄膜の変化が著しく大きくかつ急峻であ
るので、金属低酸化物の相変化を利用した記録媒体のよ
うな微小変化を扱うものに比較して、状態変化を検出し
やすく、情報の読出し装置に要求される信号処理機能を
簡易化することができるという利点をも有している。
以下、実施例にもとづいて本発明を具体的に説明するが
、本発明はこれらの実施例に限定されるものではない。
実施例１ バッチ式真空蒸着装置内をｌＸｌ０−６Ｔｏｒｒの真空
度まで排気し、ルツボからＭ。０３を加熱蒸発させるこ
とにより、厚さ１．５ｍのポリメチルメタクリレート上
に、膜厚３００ＡのＭ。０３金属酸化物層を形成した。
次にこの上にＡＩを加熱蒸発させることにより、膜厚５
００ＡのＡ１金属層を形成して記録媒体を製造した。こ
の記録媒体の波長６３３０Ａにおける全反射率は４０％
であった。次にＨｅ−Ｎｅレーザー（波長６３３０Ａ）
を記録表面上３ｍＷのパワーでビーム径２μｍに集光し
てパルス巾１μｓｅｃで照射したところ、直径３μｍの
ビットが記録された。さらにＨｅ−Ｎｅレーザーを記録
面上６ｍＷのパワーでビーム径２μｍに集光してパルス
中１μｓｅｃで照射したところ直径１３ｕｍのピットが
記録された。
実施例２ バッチ式真空蒸着装置内を１ｘｌＯ”６Ｔｏｒｒの真空
度まで排気し、ルツボからＴ８０２を加熱蒸発させるこ
とにより、厚さ１．２Ｍ、直径１２ｃｍのＤＡＤ　（ｄ
ｉｇｉｔａｌ　ａｕｄｉｏ　ｄｉｓｃ）用ポリカーボネ
ート円盤に膜厚４００ＡのＴｏ０２金属酸化物層を形成
した。次にこの上にＣｕを加熱蒸発させることにより膜
厚５００Ａの金属層を形成して記録媒体を製造した。こ
の記録媒体の波長６３３０Ａにおける全反射率は３１％
であった。次にＨｅ−Ｊｌｅレーザー（波長６３３０Ａ
）を記録表面上３ｍＷのパワーでビーム径２μｍに集光
してパルス中１μｓｅｃで照射したところ直径５μｍの
ピットが記録された。さらにＨｅ−Ｊｌｅレーザを記録
表面上５ｍＷのパワーでビーム径２μｍに集光してパル
ス中１μｓｅｃで照射したところ、直径１５μｍのピッ
トが記録された。
【図面の簡単な説明】
図は本発明に係る記録媒体の断面図である。 ２・・・基板、３・・・金属酸化物薄膜、４・・・金属
薄膜出願人代理人　猪　股　清

Claims (3)

    【特許請求の範囲】
  1. （１）　基板上に、（ａ）照射エネルギービームの熱エ
    ネルギーによって蒸発または昇華する金属酸化物薄膜と
    、（ｂ）照射エネルギービームの照射による前記金属酸
    化物薄膜の蒸発または昇華に伴う体積１１＠作用および
    照射エネルギービームの熱エネルギーの作用により変形
    してバブル状記録ピットを形成できる金属薄膜とを、前
    記の順序で積層してなることを特徴とする光学的情報記
    録媒体。
  2. （２）　前記の金属酸化物薄膜がＭ。０３、Ｔ２Ｏ、Ｓ
    ｂ　Ｏ１Ｉ　Ｏ１ＳｏＯ２， ２２５ｎ２３ Ｒｏ２０□から選ばれた１種以上の酸化物により構成さ
    れている特許請求の範囲第１項記載の光学的情報記録媒
    体。
  3. （３）　前記の金属薄い膜がＡ　Ｉ　、Ｃｒ、Ｍｎ。 Ｆｅ１　Ｇｏ、Ｎ　ｉ、Ｃｕ、Ｚｎ、Ｇｅ、ＡＯｌ（ｎ
    、３ｎ、Ｐｂ、Ｂｉから選ばれた１種以上の金属または
    その合金である特許請求の範囲第１項記載の光学的情報
    記録媒体。
JP59096593A 1984-05-16 1984-05-16 光学的情報記録媒体 Pending JPS60242529A (ja)