JPS5964550A - 散光性安全ガラス - Google Patents

散光性安全ガラス

Info

Publication number
JPS5964550A
JPS5964550A JP57171305A JP17130582A JPS5964550A JP S5964550 A JPS5964550 A JP S5964550A JP 57171305 A JP57171305 A JP 57171305A JP 17130582 A JP17130582 A JP 17130582A JP S5964550 A JPS5964550 A JP S5964550A
Authority
JP
Japan
Prior art keywords
glass
safety glass
light
adhesive layer
light scattering
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP57171305A
Other languages
English (en)
Other versions
JPH0256295B2 (ja
Inventor
Yoshio Okada
義夫 岡田
Teruo Hori
照夫 堀
Masamitsu Nakabayashi
中林　正光
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SATOOSEN KK
Satosen Co Ltd
Takeda Pharmaceutical Co Ltd
Original Assignee
SATOOSEN KK
Satosen Co Ltd
Takeda Chemical Industries Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SATOOSEN KK, Satosen Co Ltd, Takeda Chemical Industries Ltd filed Critical SATOOSEN KK
Priority to JP57171305A priority Critical patent/JPS5964550A/ja
Priority to KR1019830004622A priority patent/KR900002555B1/ko
Publication of JPS5964550A publication Critical patent/JPS5964550A/ja
Publication of JPH0256295B2 publication Critical patent/JPH0256295B2/ja
Granted legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 本発明は、散光性安全ガラス、より詳しくは、光は透過
させるが背後にある人又は物体又は光源−は視認できな
い散光性安全ガラスに関する。
従来から、採光窓、浴室ドア、マンション等のベランダ
腰板、地下街や店舗等の天井の百光源用パネル等には、
各種のものが用いられているが、いずれも充分満足でき
るものではない。例えば、スリガラスや型板ガラスを用
いた場合、地震の場合或は人又は物体が衝突した場合破
損し易く、鋭角の破片が飛散又は落下し危険であるとい
う欠点がある。また、乳白アクリル板も用いられている
が、火災時に布置ガスを発生ずる、屋外で用いるとクラ
ック、着色等が発生し、耐ａｔ＋に劣る、経時的に反り
が生じる、汚れ易い等耐久性に劣る等の欠点がある。艷
に、板ガラスに、低融点ガラスる安全性が低いという欠
点がある。同様に、板ガラスに、エポキシ系、メラミン
系の有機乳白塗料を塗布したものもあるが、破損に対す
る安全性も低い、該塗膜の硬度が低いため表面に疵がつ
く、該塗膜が剥１イｔする等耐久性の面で欠点がある。
これらの欠点を解消すべく、第１図に示す如く、例工ば
ポリエステルに酸化チタンを分散させて乳白化した乳白
フィルム（１）を、透明接着層（２１、ｆ２）を介して
２枚の４反ガラス（３１、＋３＋に密着挾持させたもの
もある。これは、破損しにくい、反り、剥離等の耐久性
の点で問題がない等の利点はあるが、その反面、光の透
過性が充分ではなく、可視部の全透過率で８０％程度の
光透過性しか有しない。一方、光透過性を向上させるべ
く酸化チタンの配合量を少くすると、今度は背後にある
物又ζＡ人が透祁されてしまう等の欠点がある。しかも
、中間の乳白フィルム（１）を２枚の板ガラス（３］　
、　（３＋に密層挾持するための透明接着層ｆ２１　、
　＋２１が必須とされるため、その製造工程数が多いと
いう問題点をも有する０ 本発明者は、以上の如き現状に鍮ろ、採光窓、浴室ドア
、ベランダＪｉｆｆ板、面光源用パネル智の目的に適し
た利料を開発すべく鋭意０［究を重ねた。
その結果、特定の透明な熱可す件樹脂に、特定の透光性
乳白剤を均一分散させた接着層により、少くとも２枚の
板ガラスを密着させてなる積層状の散光性安全ガラスが
、前記従来の欠点を全て解消し得ることを見出し、本発
明を完成した。
本発明の散光性安全ガラスは、高強度を有し、震動や物
体もしくは人体の衝突による破損Ｉこ対し高い抵抗性を
示し、仮に破損しても破片が飛散せず、また衝突物体が
貫通しにくい安全性の高いものである。また、屋外での
長期使用によっても、耐候、耐久性の点で問題がなく、
万一の火災時にあっても燃焼し難く、有毒ガス発生のお
そわも少ない。更に、透光性が高いにも拘らず、背後に
ある人又は物体又は光源が、例えば１５ｃｍ程度離れる
ともはやこれらを透視して視認できなくなるという極め
て特異な性質を有するものである。
以下、木発明を添付図面について説明する。木発明の散
光性安全ガラスは、第２図に示す如く、２枚の板ガラス
（１０）　、　００１並びに特定の透光性乳白剤を均一
分散させた接着層■を基本的構成要素とするものである
。
一ヒ記板ガラス（１０）としては、普沖板ガラス、磨き
板ガラス、型板ガラス、金鋼又は線入り板ガラス、着色
板ガラス等各種のものが広く使用できる。板ガラス００
）は、片面が若干の凹凸を有したものであってもよく、
また２枚の板ガラスは同種のものでも異種のものであっ
てもよい。イ反ガラス（１０）の厚みとしては、特に制
限はなく、一般に市販されている２〜１．２　ｍｍ程度
の厚みのものであれは多くの用途に適合する。勿論、使
用目的に応じて該厚みが更に犬なるものを用いてもよい
し、また２枚の板ガラスのうち一方の板ガラスのノウみ
を畳ならせてもよい。更に、金銅入り又は線入り板ガラ
スを使用すると、木兄、明のｆ、’ｉ’／光性安全ガラ
スの防火性、難燃性、災の耐貫通性等が一段と向上し、
消防法でいう乙種防火扉としての性能を有する。
接Ｍ層切に使用する熱可嘔性れノ脂としては、合せガラ
ス用の接着機能を有する他に、血１侯性が、ｌ＜、シか
も後述する透光性乳白剤がノど９−に分散するものであ
ることを要する。かかる熱可咽性樹脂としては、σ−オ
レフィンービニルエステル共重合体及びその変性物、エ
チレン−アクリル酸共重合体、変性エチレン共重合体、
アクリル樹脂、ブロック共重合ゴム、ポリウレタン樹脂
、塩化ビニル樹脂、塩化ビニル−酢酸ビニル共重合体、
アイオノマー４：５ｔ　ＩＩ！ｔ　、塩討；化ポリエチ
レン、塩素化ポリプロピレン、ポリアミド樹脂、ポリニ
スデル樹脂、ポリ酢酸ビニル樹脂の変性体等が挙げられ
る。これらの樹脂の中で、特にα−オレフィン−ビニル
エステル共重合体及びその変性物が好ましい。該α−オ
レフィン−ビニルエステル共重合体において、α−オレ
フィンとしてはエチレン、プロビレｙ、ｌ−ブテン、■
−ペンテン等が使用でき、特にエチレンが好ましい。ビ
ニルエステルとしてはキ酸ビニル、酢酸ビニル、プロピ
オン酸ビニル、［１δ酸ビニル、安息香酸ビニル等が挙
げられ、特に酢酸ビニルが好ましい。該共重合体中のビ
ニルエステル合議は、５〜５０重耽％７保度のものが好
ましい。また、上記α−オレフィン−ビニルエステル共
重合体の変性物としては、該共重合体をケン化率（加水
分解率）５〜９５％、好ましくは４゜〜７０％になるよ
うにケン化して得られるケン化物、或は該ケン化物に、
アクリル酸、メタクリル酸、マレイン酸等で代表される
カルボキシル基含有不飽和化合物又は無水マレイン酸、
無水コハク酸、無水フタル酸等で代表される工１．″４
状酸無水物を、該共重合体に対して０．１〜１５重斗％
程度の割合で反応させることにより得られるカルボキシ
ル変性体等が掌げられる。これらのα−オレフィン−ビ
ニルエステル共用″合体及びその変性物のうちでも、メ
ルトインデックス（１９０’Ｃ，荷重２１６゜ｙ−ｃ−
測定）が、０．５〜５００　ｆ　／　１０分程度のもの
が好適である。
更に、本発明においては、上記樹脂中に、フェニルサリ
チレート、レゾルシノールモノベンゾエート、２−（２
′−ヒドロキシ−３′−七−ブチル−に−メチルフェニ
ル）−５−クロロ−ベンゾトリアゾール等で代表される
紫外線吸収剤や、２．６−ジーｔ−ブチル−ｐ−クレゾ
ール、テトラキス〔メチレン−８−Ｃ’８．５−ジ−ｔ
−ブチル−４−ヒドロキシフェニル）プロピオネートコ
メタン等で代表される１液化防止剤等の添加ｆｉｌｌを
配合してもよい。
上記熱可塑性樹脂に均一分散させるべき透光性乳白剤と
しては、無機化学ハンドブック（無機化学ハンドブック
編集安員会編、昭和４０年８月１５日発行、　　１０８
０ページ）の中で透明性白と定義されている無機顔料を
指し、本発明に用いるものはその中で特に微粉末乃至微
結晶状のものであることを要する。かかる乳白剤として
は、炭酸カルシウム、アルミナ、カオリンクレー、珪酸
カルシウム、酸化マグネシウム、水酸化マグネシウム、
水酸化アルミニウム、炭酸マグネシウム、メルク、長石
粉、マイカ、バ丹イト、炭酸バリウム等が使用でき、こ
れらのうちでも特に炭酸カルシウムが好ましい。
本発明においては、散光性安全ガラスの光の全透過率を
少くとも８５％程度とするが、直進透過皐は低く抑え、
背後の物体又は人又は光源が１５ａｍ　程度離れると込
視できなくなるように、上記乳白剤の粒径、配合量を適
宜選択する必要がある。
本発明の散光性安全ガラスの使用、ｌも”１所、使用目
的、光源の種類、強さ等にもよるが、一般にｌ　Ｈｚ乳
白剤は、その平均粒径を０．１〜５０μｍ程度、好まし
くは０．５〜３０μｍ程度とし、その貼可鍬件樹１１）
１に対する配合量を０．１〜３０重量％、好ましくは１
〜２０重景％重量れば通常良好な結果を得ることかでき
る。
特に、乳白剤として炭酸カルシウムを用いる場合、その
平均粒径を０．５〜５μｍ程度とし、その樹脂に対する
配合量を２〜１０重童％程度とするのが好ましいＯ 接着層■の厚みも、本発明散光性安全ガラスの使用場所
、使用目的、上記乳白剤の配合量等により変り得るが、
通常０．８〜１．　□　ｍｍ、程度、好ましくは０．８
５〜０．７ｍｍ程度とすればよい〇本発明の散光性安全
ガラスを製造するには、前記２枚の板ガラス（ＩＱｌ、
（ＩＩ及び接着層（２０）を、第２図に示す如く重ね合
せ、層間に気泡が残留しないように脱気して該接着層■
の融着温度まで加熱、圧着し、全体を密着一体化させれ
ばよい。
本発明の散光性安全ガラスは、特異な光の透過性（又は
分散性）、破損に対する抵抗性、防火乃至難燃性、耐候
、耐久性等の点において侵れており、採光窓、浴室ドア
、ベランダ腰板、面光源用パネル等に、屋内、屋外いず
れの場所においても有利に使用できるものである。また
、製造も容易に少ない工程数で行なえるという利点も有
する。
また、本発明においては、必要に応じて、板ガラス００
）を８枚以上の適当数用い、各板ガラス間に接着層■を
配した構造の多層積層安全ガラスとすることも勿論可能
である。
実施例１゜ エチレン−酢酸ビニル共重合体ケン化物のカルホキシル
変性体（メルトインデックス２０ｆ／ＬＯ’Ａ−１尚品
名「デュミランパウダーＣ−１５５０ＵＪ武［ロ系品工
業（１狼製）に、平均わ゛ｌ径約１７１ｍの炭酸カルシ
ウム微結晶を濃度３重量％で均一分散させ、これを厚さ
０．８６ｍｍのフィルムに成形する。該フィルムを厚さ
Ｂｍｍの２枚の普通板ガラス（１８２９ｍｍＸ９１４ｍ
ｍ）に挾持し、層間の気泡を脱気し、約１２０°Ｃに加
熱して接着圧１気圧で全体を密着一体化し１本発明の散
光性安全ガラスを得た。
ＪＩＳ　、Ｋ　　６７１４に準じ測定したところ、この
散光性安全ガラスは、光の全透過率が６０％と高いにも
拘らず、背後に１５　ｃｍ　ＨＨして置いた明るい物体
は透視できず、単に該物体が存在することが判る程度で
あった０尚、このものの畿（ｄＢは、９０％であった。
また、上記散光性ガラスについて、　ＪＩＳ　　Ｒ８２
０５による合せガラス板耐衝撃性試験及び耐熱性試験、
並びにＪＩＳ　Ｒ８２１２による自動車用合せガラス板
の耐光性試験を行なったところ、合格した。
実施例２゜ 炭酸カルシウム微結晶の配合量を５重量％とする以外は
実施例１と同様にして、本発明の散光性安全ガラスを得
る。
この散光性安全ガラスの光の全透過率は４５％であるが
、背後に１５ｃｍ離して設置した螢光灯光源が一本の光
源としては認められず、該散光性安全ガラス全体が面光
源として発光した。尚、このものの曇価は、９３％であ
った０ また、実施例１と同様にＪＩＳ　Ｒ８２０５及びＪＩＳ
　Ｒ８２１２にもとづく試験を行なったところ、合格し
た。
実施例３゜ 板ガラスの一方を厚さ６．７ｍｍの網入り板ガラスに代
える以外は実施例１と同様にして本発明の散光性安全ガ
ラスを得る。
光透過性については実施例１と同様であり、安全性試験
にも合格した。更に、ＪＩＳ　Ａ−ｉａｘｔ　力ｉ熱試
験で乙種防火戸屋外用２級Ｂ種ζこも合格した。
【図面の簡単な説明】
第１図は、従来の乳白安全ガラスの断面図を示す。第２
図は本分明の散光性安全ガラスの断面図である〇 （１）・・・乳白フィルム、　（２）・・・透明接着層
、（３）・・・板ガラス、　　　　＋１０）・・・板ガ
ラス、（支））・・・乳白剤を均一分散させた接着層Ｏ
（以　上） 一３コ 第　１　図 第２図 手続補正書輸発） 昭和５８年ｌＯ月！１　日 特許庁長官　　名杉和夫　　　殿 １、事件の表示 昭和５７年特　許　願第１７１３０５　　号２・　発明
（’）　名ｋ　　散光性安全ガラス３、補正をする者 事件との関係　特許出願人 （２９３）武田薬品工業株式会社 （ほか１名） ５、補正命令の日付　　　　　　　　　　　　　　　　
　　゛′−パ自　　　発 ６、補正により増加する発明の数 な　　　し 補　　正　　の　　内　　容 ｌ　明細書の記載を下記正誤表の通シに訂正する。 ２　明細書第１３頁第３行１Ｂ種にも合格した。」とあ
るを、次の通シに訂正する。 ［Ｂ種にも合格した。 実施例　４ 下記第１表に記載の粒径を有する透光性乳白剤を下記第
１表に記載の配合量で使用する以外は実施例１と同様に
して本発明の散光性安全ガラスを得た。 得られた散光性安全ガラスの光の全光線透過率及び曇価
は第１表に記載の通シであった。 第１表 また、これらの安全ガラスの背後に１５ｆｆ離して置い
た明るい物体は透視できず、単に該物体が存在すること
が判る程度であった。 更に、上記で得られた散光性安全カラスについてＪＩＳ
　　Ｒ３２０５による合せガラス板耐＃ｉ′撃性試験及
び耐熱性試験並びにＪＩＳ　　Ｒ３２１２による自動車
用合せガラス板の耐光性試験を行なったところ、いずれ
も合格した。」

Claims (1)

    【特許請求の範囲】
  1. ■　熱可塑性樹脂に透光性乳白剤を分散させた接着層に
    より、少くとも２枚の板ガラスを密着させてなる。Ｍ層
    状散光性安全ガラス。
JP57171305A 1982-09-30 1982-09-30 散光性安全ガラス Granted JPS5964550A (ja)