JPH10510007A - 高引張り強度を有するマンガン含有材料 - Google Patents
高引張り強度を有するマンガン含有材料Info
- Publication number
- JPH10510007A JPH10510007A JP8518662A JP51866296A JPH10510007A JP H10510007 A JPH10510007 A JP H10510007A JP 8518662 A JP8518662 A JP 8518662A JP 51866296 A JP51866296 A JP 51866296A JP H10510007 A JPH10510007 A JP H10510007A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- powder
- iron
- less
- sintering
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (1)
- 【特許請求の範囲】 1.粉末を圧縮して焼結することによって多孔部品を製造するための鉄基粉末 において,鉄に加えて、Mo 0.25〜2.0重量%と、Mn 1.2〜3. 5重量%と、Si 0.5〜1.75重量%と、C 0.2〜1.0重量%と、 Cu 0.25重量%未満を含む不純物の2重量%以下、好ましくは1重量%以 下とを含有する鉄基粉末。 2.請求の範囲第1項に記載の粉末において,Moの前記量が、0.5〜2. 0重量%であることを特徴とする粉末。 3.請求の範囲第1項または第2項に記載の粉末において,Mnの前記量が、 1.2〜3.0重量%であることを特徴とする鉄基粉末。 4.請求の範囲第1項から第3項までのいづれか1項に記載の粉末において, Siの前記量が、0.5〜1.50重量%であることを特徴とする鉄基粉末。 5.請求の範囲第1項から第4項までのいづれか1項に記載の粉末において, Cの前記量が、0.3〜0.9重量%であることを特徴とする鉄基粉末。 6.請求の範囲第1項から第5項までのいづれか1項に記載の粉末において, MnおよびSiが、フェロマンガン、フェロシリコンまたはシリコン−マンガン −鉄母合金の形態で添加されることを特徴とする粉末。 7.請求の範囲第6項に記載の粉末において,前記シリコン−マンガン−鉄母 合金のマンガン/シリコンの重量比が、1〜3の間で変動することを特徴とする 粉末。 8.請求の範囲第1項から第7項までのいづれか1項に記載の粉末において, Moが、FeおよびMoの予合金形態で添加されることを特徴とする粉末。 9.請求の範囲第1項から第8項までのいづれか1項に記載の粉末において, Cr<0.25 O<0.03 Cu<0.25 N<0.02 Ni<0.25 Be<0.01 Al<0.20 B<0.02 P<0.05 その他<0.5 S<0.05 の範囲内で不可避不純物を含むことを特徴とする粉末。 10.鉄に加えて、Mo 0.25〜2.0重量%と、Mn 1.2〜3.5重 量%と、Si 0.5〜1.75重量%と、C 0.15〜0.70重量%と、 Cu 0.25重量%未満を含む2重量%以下の不純物とを含有し粉末冶金的に 製造される多孔部品。 11.焼結多孔部品を粉末冶金的に製造する方法において,Mo 0.25〜2 .0重量%と、Mn 1.2〜3.5重量%と、Si 0.5〜1.75重量% と、C 0.2〜1.0重量%と、Cu 0.25重量%未満を含む2重量%以 下の不純物とを含む鉄基粉末を使用し,該粉末を所望の形状に圧縮し,該圧縮体 を1120℃を超える温度で焼結することを特徴とする方法。