JPH07310283A - 紡織繊維の処理方法 - Google Patents

紡織繊維の処理方法

Info

Publication number
JPH07310283A
JPH07310283A JP7094086A JP9408695A JPH07310283A JP H07310283 A JPH07310283 A JP H07310283A JP 7094086 A JP7094086 A JP 7094086A JP 9408695 A JP9408695 A JP 9408695A JP H07310283 A JPH07310283 A JP H07310283A
Authority
JP
Japan
Prior art keywords
fiber
group
textile
formula
treated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP7094086A
Other languages
English (en)
Inventor
Dieter Reinehr
ライネール ディーター
Werner Kaufmann
カウフマン ヴェルナー
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Novartis AG
Original Assignee
Ciba Geigy AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ciba Geigy AG filed Critical Ciba Geigy AG
Publication of JPH07310283A publication Critical patent/JPH07310283A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】 （修正有） 【目的】紡織繊維と反応可能な紫外線吸収剤を、該繊維
を基準にして０．１乃至３．０重量％使用して、繊維を
処理して、該繊維のＳＰＦを向上させる方法を提供す
る。 【構成】上記紫外線吸収剤は式ＡＢを有する。Ａは下記
の式（１）、（２）、（３）または（４）のいずれかで
あり；

Description

【発明の詳細な説明】
【０００１】本発明は、紡織繊維を処理する方法、特に
１個またはそれ以上の繊維反応性基を含有する紫外線吸
収剤を用いて紡織繊維を処理する方法、ならびにその方
法によって処理された紡織繊維から製造された繊維製品
に関する。
【０００２】従来、太陽光中の紫外線成分に曝される人
間の皮膚を紫外線成分による傷害から保護するために
は、紫外線吸収剤を含有する製剤を皮膚に直接塗布する
方法がとられてきた。世界の、たとえばオーストリアお
よびアメリカのような日光の強い気候の地域において
は、いわゆるオゾン層破壊の結果に対する心配と相まっ
て、日光の過度の被曝による潜在的危険についての意識
が大いに高まっている。無防備に過度に太陽に曝される
ことにより起こる皮膚傷害のきわめて悲惨な例は、皮膚
の黒色腫あるいは皮膚ガンの発生である。太陽光に対す
る皮膚の保護レベルを高めるために、皮膚の直接的保護
の他に取るべき追加的手段が現在種々研究されている。
たとえば、皮膚を衣類で覆って、太陽光線に直接曝され
ないようにして皮膚を保護することが考えられている。
【０００３】ほとんどの天然および合成繊維材料は、少
なくとも部分的に太陽光中の紫外線成分を透過する。し
たがって、単に衣類をつけているいるだけでは、その下
の皮膚を、紫外線による傷害から十分に保護することに
はならない。濃く染色した染料を含有するおよび／また
は緻密に織られた組織を有する衣類は、その下の皮膚を
ある程度保護するであろうが、そのような衣類は、着用
者の個人的快適さの点からみて、日光の強い高温な気候
においては実用的とはいえない。したがって、未染色ま
たは淡く染色された軽い夏物を含めて、衣類の下の皮膚
を紫外線から保護できるようにする必要がある。
【０００４】このような軽い夏物衣料は通常２００ｇ／
m2以下の密度であり、その衣料をつくっている繊維の種
類にもよるが、その日光防護率（ＳＰＦ＝sun protecti
on factor)の評価は１０乃至２０である。日焼け防止手
段（日焼け止めクリームまたは布）のＳＰＦ評価値は、
当該日焼け防止手段を身につけている平均的な人が平均
的日光被爆条件下において日焼け症にかかるまでの時間
の倍数であると定義できる。たとえば、普通の人が標準
的露光条件のもとにおいては通常３０分後には日焼け症
にかかる（保護時間は３０分）とすると、ＳＰＦ評価が
５である日焼け防止手段はその保護時間を、３０分から
２時間３０分にまで延長できるということである。たと
えば平均的な色白の肌をもつ人の場合に日中の一番熱い
時で、平均日焼け罹患時間が最短、わずか１５分間であ
るような特に日差しの強い気候の所に住む人達にとって
は、少なくとも２０のＳＰＦ評価を持つことが軽装衣料
に対して要望される。ＷＯ９４／４５１５特許明細書に
は、紫外線吸収剤を準備し、その紫外線吸収剤を密度が
２００ｇ／m2以下の布に付与し、しかして紫外線吸収剤
を布に染着させて、特に布の３重量％以下の紫外線吸収
剤の付与によって、紫外線吸収剤と布との組み合わせに
対して２０以上のＳＰＦ評価を達成する方法が記載され
ている。
【０００５】誠に驚くべきことながら、今回、紡織繊維
と反応することのできる基を含有する特定の紫外線吸収
剤を用いて紡織繊維を処理するとその繊維紫外線吸収剤
処理から製造された布に対して卓越したＳＰＦ評価が与
えられることが見いだされた。したがって、本発明は紡
織繊維のＳＰＦを向上させる方法を提供するものであ
り、本発明の方法は、紡織繊維を、該繊維を基準にして
０．１乃至３．０重量％の、紡織繊維と反応可能な基を
１個またはそれ以上含有し、かつ式 ＡＢ ［式中、Ａは下記式（１），（２），（３）または
（４）であり
【化５】 Ｂは紡織繊維と反応可能な基である］を有する紫外線吸
収剤を使用して処理することを特徴とする。
【０００６】好ましい繊維反応性基Ｂの例は、ハロトリ
アジニルアミノ基、ハロピリミジニルアミノ基および脂
肪族反応性基である。特に、下記式（５）または（６）
を有するハロトリアジニルアミノ基
【化６】 下記式（７）または（８）を有するハロピリミジニルア
ミノ基
【化７】 ならびに、特に下記のいずれかの式を有する脂肪族反応
性基である。
【化８】
【０００７】式（１）乃至（４）の中のフェニル基およ
び／またはナフチル基は、ハロゲン好ましくは塩素、Ｓ
Ｏ3 Ｍ（ここにおいて、Ｍは水素またはアルカリ金属、
特にナトリウムである）、アルキル（好ましくはＣ1-Ｃ
4 アルキル）、アルコキシ（好ましくはＣ1-Ｃ4 アルコ
キシ）、ベンジルからなる群より選択された１個、２個
または３個の置換基によって置換されることができる。
【０００８】式ＡＢの化合物は、その製造方法と共にＷ
Ｏ９４／４５１５号特許明細書において一般的に記載さ
れている。しかしながら、このＷＯ９４／４５１５号特
許明細書が教示している方法は、本発明の方法とは完全
にかけ離れている。すなわち、その特許明細書（例え
ば、８頁）には、上記式（１）乃至（４）の基Ａのｏ−
ヒドロキシ基を含有していない類似体から誘導された化
合物を使用することが特に推奨されている。式（１）乃
至（４）の基Ａ中におけるｏ−ヒドロキシ基の存在は、
化合物ＡＢが紫外線を有効に吸収することを保証するた
めに決定的に重要である。
【０００９】本発明の方法によって処理される紡織繊維
は、天然または合成繊維、またはそれらの混合物であり
うる。天然繊維の例は木綿、ビスコース、亜麻(flax)、
レーヨンまたはリネン、好ましくは木綿の如き植物繊
維、ならびにウール、モヘヤー、カシミヤ、アンゴラお
よびシルク、好ましくはウールの如き動物繊維を含む。
合成繊維材料はポリエステル、ポリアミドまたはポリア
クリロニトリル繊維などを含む。好ましくは、本発明の
方法によって処理される紡織繊維は、２００g/m2より少
ない密度を有しており、そして前もって濃色に染色され
ていない。
【００１０】本発明の方法において使用される紫外線吸
収剤ＡＢのいくつかは、水に難溶性であり、分散された
状態で施用される必要があるかもしれない。この目的の
ためには、それら紫外線吸収剤を、都合よくは石英ボー
ルとインペラーとを使用して、適当な分散剤と共に１乃
至２ミクロンの粒径になるまで摩砕すればよい。
【００１１】かかる水に難溶性の紫外線吸収剤用の分散
剤としては、下記のものがあげられる： （ア）アルキレンオキシド付加物の酸エステルまたはそ
の塩、たとえばエチレンオキシドの４乃至４０モルとフ
ェノールの１モルとの重付加物の酸エステルまたはその
塩、または４−ノニルフェノールの１モル、またはジノ
ニルフェノールの１モル、または特に前もってフェノー
ルの１モルにスチレンの１乃至３モルを付加して製造さ
れた化合物１モルとエチレンオキシドの６乃至３０モル
との付加物のリン酸エステル； （イ）ポリエチレンスルホナート； （ウ）脂肪酸タウリド； （エ）アルキル化ジフェニルオキシド−モノ−または−
ジ−スルホナ−ト； （オ）ポリカルボン酸エステルのスルホナート； （カ）脂肪アミン、脂肪アミド、脂肪酸または脂肪アル
コール（いずれも８乃至２２個の炭素原子を有する）
に、あるいは三価乃至六価のＣ3-Ｃ6 アルカノールに、
エチレンオキシドおよび／またはプロピレンオキシドの
１乃至６０モル、好ましくは２乃至３０モルを付加した
付加生成物を有機ジカルボン酸または無機多塩基酸で酸
エステルに変換したもの； （キ）リグニンスルホナート；および特に、 （ク）ホルムアルデヒド縮合物、たとえばリグニンスル
ホナートおよび／またはフェノールとホルムアルデヒド
との縮合生成物；ホルムアルデヒドと芳香族スルホン酸
との縮合物、たとえばジトリルエーテルスルホナートと
ホルムアルデヒドとの縮合生成物；ナフタレンスルホン
酸および／またはナフトール−またはナフチルアミンス
ルホン酸とホルムアルデヒドとの縮合生成物；フェノー
ルスルホン酸および／またはスルホン化ジヒドロキシジ
フェニルスルホンおよびフェノールまたはクレゾールと
ホルムアルデヒドおよび／または尿素との縮合生成物；
またはジフェニルオキシド−ジスルホン酸誘導体とホル
ムアルデヒドとの縮合生成物。
【００１２】本発明の方法においては、紫外線吸収剤の
他に少量の１種またはそれ以上の助剤を使用することも
できる。助剤の例をあげれば、乳化剤、香料、着色用染
料、乳白剤、蛍光増白剤、殺菌剤、非イオン界面活性
剤、繊維ケヤー成分特に繊維柔軟剤、よごれ解離または
よごれ忌避成分または防水剤、ゲル化防止剤たとえばア
ルカリ金属の亜硝酸塩または硝酸塩、特に硝酸ナトリウ
ム、および腐食防止剤たとえばケイ酸ナトリウムなどで
ある。これら任意添加物の量は、被処理繊維に対して１
重量％を超過すべきではない。
【００１３】本発明の方法は、皮膚に保護を与えるほ
か、さらに本発明によって処理された繊維製品の使用寿
命を延長する。この効果は、たとえば、その引き裂き強
度および／またはその耐光堅牢性を保つことによる。本
発明は、また本発明の方法によって処理された繊維から
製造された繊維布ならびに処理された布から製造された
衣料品を提供する。本発明の方法によって処理された繊
維布およびかかる布から製造された繊維製品および衣料
品は、未処理かつ未染色の布のＳＰＦの評価が１０乃至
２０であるのに対して、一般的に２０またはそれ以上の
ＳＰＦ評価ランクを有する。以下、本発明をさらに実施
例によって説明する。
【００１４】実施例１ ２−アミノ−フェノール−４−スルホン酸と塩化シアヌ
ールとの常用のカップリングによって得られた２、４−
ジクロロ−ｓ−トリアジン−６−イル−２−アミノ−フ
ェノール−４−スルホン酸ナトリウム塩を、吸尽法によ
って木綿に施用した。すなわち、綿１００％の布（密度
１４５ｇ／m2）の試料５ｇを、実験室用染色機を使用し
て浴比４０：１，５０℃において３０分間、下記成分を
含有する水性調合物を用いて処理した。 ＮａＣｌ ５０g/l ２、４−ジクロロ−ｓ−トリアジン−６−イル−ｐ−アミノ−ｏ−ヒドロキシ −フェニル−スルホン酸ナトリウム塩 綿布の２重量％ この後、Na2CO3５g/l を、５０℃において３０分間にわ
たって添加した。その後、処理された綿布を温水と冷水
とでよくすすぎ洗いし、乾燥した。日光保護率ＳＰＦ
を、ウルブリヒトボウル（ulbricht bowl）を具備した
二重格子分光光度計を使用して,その試料布片を透過し
た紫外線を測定することによって測定した。ＳＰＦの計
算は、B.L.DiffeyとJ.RobsonｎとによってJ.Soc.Cosm.C
hem. 40(1989),pp 130-131に記載されている方法によっ
て実施した。本実施例において処理された綿布は、２５
以上のＳＰＦ評価を有していた。２、４−ジクロロ−ｓ
−トリアジン−６−イル−２−アミノ−フェノール−４
−スルホン酸ナトリウム塩の代わりに下記式のいずれか
の化合物を使用した場合にも同様な結果を得た。
【化９】
【００１５】実施例２ 綿１００％の試料布片（密度１０９ｇ／m2）５ｇを、下
記成分を含有する水性浴を用いてパジング（絞り率８０
％）し、綿布基質上に活性成分を１重量％の濃度で与え
た： 炭酸水素ナトリウム ４g/l 尿素 ５０g/l 下記式の化合物 １２．５g/l
【化１０】 上記式の化合物は水に不溶性であるので、５％（w/w)水
性分散物として添加した。この水性分散物は、該化合物
５％とPluronic F 108１％とを脱イオン水中においてガ
ラスビーズの存在下において摩砕することによって得ら
れた。パジングはアルカリ性pH価において実施した。処
理された試料布片を８０℃において２分間乾燥し、次に
１２０℃において１０分間サーモフィックスした。この
ようにして処理された綿布は、２５以上のＳＰＦ評価を
有していた。
【００１６】実施例３ 綿１００％の試料布片（密度１０９ｇ／m2）５ｇを、下
記成分を含有する水性浴を用いてパジング（絞り率８０
％）し、綿布基質上に活性成分を１重量％の濃度で与え
た： ソーダ １０g/l 尿素 １００g/l 硫酸ナトリウム １０g/l アルギン酸ナトリウム １g/l 下記式の化合物 １２．５ｇ／ｌ
【化１１】 上記式の化合物は水に不溶性であるので、５％（ｗ／
ｗ）水性分散物として添加した。この水性分散物は、該
化合物５％とPluronic F 108１％とを脱イオン水中にお
いてガラスビーズの存在下において摩砕することによっ
て得られた。パジングはアルカリ性pH価において実施し
た。処理された試料布片を８０℃において２分間乾燥
し、次に１２０℃において１０分間サーモフィックスし
た。このようにして処理された綿布は、２５以上のＳＰ
Ｆ評価を有していた。
【００１７】実施例４ ウール１００％の試料布片（密度１２５ｇ／m2）５ｇ
を、下記成分を含有する水性浴を用いてパジング（絞り
率８０％）し、ウール基質上に活性成分を１重量％の濃
度で与えた： ４０％酢酸 ２g/l 下記式の化合物 １２．５g/l
【化１２】 上記式の化合物は水に不溶性であるので、５％（w/w)水
性分散物として添加した。この水性分散物は、該化合物
５％とPluronic F 108１％とを脱イオン水中において、
ガラスビーズの存在下において摩砕することによって得
られた。パジングは酸性pH価（酢酸を用いてpH４乃至
４．５に調整）において実施した。処理された試料布片
を８０℃において２分間乾燥し、次に１２０℃において
１０分間サーモフィックスした。このようにして処理さ
れたウール試料片は、５０以上のＳＰＦ評価を有してい
た。
【００１８】実施例５ 漂白木綿クレトンの複数の試料片を、下記成分を含有す
る水性浴を用いてパジング（絞り率８０％）し、木綿基
質上に活性成分を１重量％の濃度で与えた： ４０％酢酸 ２g/l 下記式の化合物 １２．５g/l
【化１３】 上記式の化合物は水に不溶性であるので、５％（w/w)水
性分散物として添加した。この水性分散物は、該化合物
５％とPluronic F 108１％とを脱イオン水中においてガ
ラスビーズの存在下において摩砕することによって得ら
れた。パジングはアルカリ性pH価（ソーダを加えてpH１
０乃至１１に調整）において実施した。処理された試料
綿布を８０℃において２分間乾燥し、続いて１７０℃に
おいて１０分間サーモフィックスした。このようにして
処理された試料綿布は、２５以上のＳＰＦ評価を有して
いた。

Claims (17)

    【特許請求の範囲】
  1. 【請求項１】 紡織繊維の日光防護率（ＳＰＦ=sun pro
    tection factor) を向上させる方法において、紡織繊維
    を、該紡織繊維を基準にして０．１乃至３．０重量％
    の、紡織繊維と反応可能な基を１個またはそれ以上含有
    し、かつ式 ＡＢ ［式中、Ａは下記式（１），（２），（３）または
    （４） 【化１】 の基であり、そしてＢは紡織繊維と反応可能な基であ
    る］を有する紫外線吸収剤を使用して処理することを特
    徴とする方法。
  2. 【請求項２】 Ｂがハロトリアジニルアミノ基、ハロピ
    リミジニルアミノ基または脂肪族繊維反応性基である請
    求項１記載の方法。
  3. 【請求項３】 ハロトリアジニルアミノ基が下記式
    （５）または（６）を有する請求項２記載の方法。 【化２】
  4. 【請求項４】 ハロピリミジニルアミノ基が下記式
    （７）または（８）を有する請求項２記載の方法。 【化３】
  5. 【請求項５】 脂肪族繊維反応性基が下記のいずれかの
    式を有する請求項２記載の方法。 【化４】
  6. 【請求項６】 式（１）乃至（４）の中のフェニル基お
    よび／またはナフチル基が、ハロゲン、ＳＯ3 Ｍ（ここ
    において、Ｍは水素またはアルカリ金属である）、アル
    キル、アルコキシ、ベンジルからなる群より選ばれた１
    個、２個または３個の置換基によって置換されている請
    求項１乃至５のいずれかに記載の方法。
  7. 【請求項７】 ハロゲンが塩素であり、そしてＭが水素
    またはナトリウムである請求項６記載の方法。
  8. 【請求項８】 被処理紡織繊維が天然または合成繊維、
    またはそれらの混合物である請求項１乃至７のいずれか
    に記載の方法。
  9. 【請求項９】 天然繊維が植物繊維または動物繊維であ
    る請求項８記載の方法。
  10. 【請求項１０】 植物繊維が木綿、ビスコース、亜麻(f
    lax)、レーヨンまたはリネンであり、そして動物繊維が
    ウール、モヘヤー、カシミヤ、アンゴラまたはシルクで
    ある請求項９記載の方法。
  11. 【請求項１１】 合成繊維がポリエステル、ポリアミド
    またはポリアクリロニトリル繊維である請求項８記載の
    方法。
  12. 【請求項１２】 被処理紡織繊維が２００g/m2より少な
    い密度を有しており、そして前もって濃色に染色されて
    いない請求項１乃至１１のいずれかに記載の方法。
  13. 【請求項１３】 紫外線吸収剤が水に難溶性であり、分
    散された状態において施用される請求項１乃至１２のい
    ずれかに記載の方法。
  14. 【請求項１４】 紫外線吸収剤のほかに、少量の１種ま
    たはそれ以上の助剤が使用される請求項１乃至１３のい
    ずれかに記載の方法。
  15. 【請求項１５】 助剤が乳化剤、香料、着色用染料、乳
    白剤、蛍光増白剤、殺菌剤、非イオン界面活性剤、繊維
    ケヤー成分、ゲル化防止剤または腐食防止剤である請求
    項１４記載の方法。
  16. 【請求項１６】 前記請求項のいずれかに記載の方法に
    よって処理された繊維から製造された繊維布。
  17. 【請求項１７】 ２０またはそれ以上のＳＰＦ評価ラン
    クを有する請求項１６記載の繊維布。
JP7094086A 1994-04-20 1995-04-20 紡織繊維の処理方法 Pending JPH07310283A (ja)