JPH066394B2 - 光情報記録媒体 - Google Patents
光情報記録媒体Info
- Publication number
- JPH066394B2 JPH066394B2 JP59108443A JP10844384A JPH066394B2 JP H066394 B2 JPH066394 B2 JP H066394B2 JP 59108443 A JP59108443 A JP 59108443A JP 10844384 A JP10844384 A JP 10844384A JP H066394 B2 JPH066394 B2 JP H066394B2
- Authority
- JP
- Japan
- Prior art keywords
- recording medium
- recording
- optical information
- information recording
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 〔技術分野〕 本発明は特定の化合物を含む記録層を有する光情報記録
媒体に関する。さらに詳しくは、レーザビームにより直
接記録し反射光の変化によって情報再生を行なう方法に
用いられる光情報記録媒体に関する。
媒体に関する。さらに詳しくは、レーザビームにより直
接記録し反射光の変化によって情報再生を行なう方法に
用いられる光情報記録媒体に関する。
従来、回転しているディスク状の情報記録媒体にレーザ
光を照射して情報の記録再生を行なう情報記録再生装置
が知られている。そしてこの種の情報記録装置に用いら
れる情報記録媒体の記録層としては低融点金属または低
融点金属と誘導体を用いるものなどが提案されている。
しかし、これらは保存性が悪い、分解能が低い、記録密
度が低い、コスト高になるなどの欠点を有する。そこ
で、最近になって比較的長波長の光で物性変化し得る有
機薄膜を記録層に用いることが提案されているが、一般
に長波長側に吸収特性をもつ有機化合物は熱および光に
対して安定性が低いなどの問題点があることから必ずし
も記録特性上満足できる記録層が開発されていないのが
現状である。
光を照射して情報の記録再生を行なう情報記録再生装置
が知られている。そしてこの種の情報記録装置に用いら
れる情報記録媒体の記録層としては低融点金属または低
融点金属と誘導体を用いるものなどが提案されている。
しかし、これらは保存性が悪い、分解能が低い、記録密
度が低い、コスト高になるなどの欠点を有する。そこ
で、最近になって比較的長波長の光で物性変化し得る有
機薄膜を記録層に用いることが提案されているが、一般
に長波長側に吸収特性をもつ有機化合物は熱および光に
対して安定性が低いなどの問題点があることから必ずし
も記録特性上満足できる記録層が開発されていないのが
現状である。
本発明は上記現状に鑑みてなされたものであって、その
目的は半導体レーザなどの長波長光による記録再生が可
能で保存性にすぐれかつ再生劣化が少く記録密度の高い
光情報記録媒体を提供することである。
目的は半導体レーザなどの長波長光による記録再生が可
能で保存性にすぐれかつ再生劣化が少く記録密度の高い
光情報記録媒体を提供することである。
本発明者は上記目的を達成するために鋭意研究を行った
結果、下記一般式で示される化合物自体が安定な記録材
料として有用であることを見出し本発明の完成に至っ
た。
結果、下記一般式で示される化合物自体が安定な記録材
料として有用であることを見出し本発明の完成に至っ
た。
すなわち、本発明は下記一般式で示される化合物を含む
記録層を有する光情報記録媒体を提供することにある。
記録層を有する光情報記録媒体を提供することにある。
一般式 ただし、R1ないしR3は同じかまたは異なっていてもよく
そしてそれぞれは水素、ハロゲン、ヒドロキシ基、カル
ボキシル基あるいは置換もしくは未置換のアルキル、ア
ルコキシ、アリール、アシル、アシルオキシまたアルケ
ニル基を表わしそしてＭはNi、Co、Cu、Mn、PdまたはPtを表
わす。
そしてそれぞれは水素、ハロゲン、ヒドロキシ基、カル
ボキシル基あるいは置換もしくは未置換のアルキル、ア
ルコキシ、アリール、アシル、アシルオキシまたアルケ
ニル基を表わしそしてＭはNi、Co、Cu、Mn、PdまたはPtを表
わす。
本発明の上記化合物の具体例を以下の表に示すが、本発
明はこれらのみに限定されるものではない。
明はこれらのみに限定されるものではない。
本発明の光情報記録媒体は基本的には基板と記録層とか
ら構成されるものであるが、必要に応じてさらに下引
層、保護層などを設けることもできる。また、記録層同
士を内側にして２枚の記録媒体を対向させたいわゆるエ
アーサンドイッチ構造にすることも可能である。
ら構成されるものであるが、必要に応じてさらに下引
層、保護層などを設けることもできる。また、記録層同
士を内側にして２枚の記録媒体を対向させたいわゆるエ
アーサンドイッチ構造にすることも可能である。
本発明における記録層はレーザ光の照射により何らかの
光学的変化を生じさせその変化により情報を記録できる
ものであって、この記録層中には上記一般式の化合物が
含有されている必要がある。また、記録層の形成にあた
っては上記一般式の化合物を１種または２種以上の組合
せで用いてもよい。さらに、本発明の上記化合物は他の
染料例えばフタロシアニン系染料、テトラヒドロコリン
系染料、ジオキサジン系染料、トリフェノチアジン系染
料、フェナンスレン系染料、シアニン（メロシアニン）
系染料、アントラキノン（インダンスレン）系染料、キ
サンテン系染料、トリフェニルメタン系染料、クロコニ
ウム系染料、ピリリウム系染料、アズレン系染料などま
たは金属、金属化合物例えばIn、Sn、Te、Bi、Ａ、Se、TeO
2、SnO、As、Cdなどと混合分散あるいは積層の形態で用い
ることもできる。また、本発明の上記化合物は高分子材
料例えばアイオノマー樹脂、ポリアミド系樹脂、ビニル
系樹脂、天然高分子、シリコーン、液状ゴムなどの種々
の材料もしくはシランカップリング剤などの中に混合分
散して用いてもよいしあるいは特性改良の目的で安定剤
（例えば、遷移金属錯体）、分散剤、難燃剤、滑剤、帯
電防止剤、界面活性剤、可塑剤などと一緒に用いること
もできる。
光学的変化を生じさせその変化により情報を記録できる
ものであって、この記録層中には上記一般式の化合物が
含有されている必要がある。また、記録層の形成にあた
っては上記一般式の化合物を１種または２種以上の組合
せで用いてもよい。さらに、本発明の上記化合物は他の
染料例えばフタロシアニン系染料、テトラヒドロコリン
系染料、ジオキサジン系染料、トリフェノチアジン系染
料、フェナンスレン系染料、シアニン（メロシアニン）
系染料、アントラキノン（インダンスレン）系染料、キ
サンテン系染料、トリフェニルメタン系染料、クロコニ
ウム系染料、ピリリウム系染料、アズレン系染料などま
たは金属、金属化合物例えばIn、Sn、Te、Bi、Ａ、Se、TeO
2、SnO、As、Cdなどと混合分散あるいは積層の形態で用い
ることもできる。また、本発明の上記化合物は高分子材
料例えばアイオノマー樹脂、ポリアミド系樹脂、ビニル
系樹脂、天然高分子、シリコーン、液状ゴムなどの種々
の材料もしくはシランカップリング剤などの中に混合分
散して用いてもよいしあるいは特性改良の目的で安定剤
（例えば、遷移金属錯体）、分散剤、難燃剤、滑剤、帯
電防止剤、界面活性剤、可塑剤などと一緒に用いること
もできる。
次に、図面について本発明による光情報記録媒体の構成
を説明する。
を説明する。
第１図に示すように、本発明の光情報記録媒体は基本的
には基板１上に上記一般式の化合物を含む記録層２を設
けたものである。また、記録層は光反射層と光吸収層と
を任意の順序で組合せた２層構成とすることもできる。
には基板１上に上記一般式の化合物を含む記録層２を設
けたものである。また、記録層は光反射層と光吸収層と
を任意の順序で組合せた２層構成とすることもできる。
記録層の形成は蒸着、スパッタリング、CVDまたは溶液
塗布などの通常の手段によって行うことができる。塗布
法を用いる場合には有機溶媒に溶解してスプレー、ロー
ラーコーティング、デイッピングおよびスピンニングな
どの慣用のコーティング法によって行なわれる。有機溶
媒としては一般には、メタノール、エタノール、イソプ
ロパノールなどのアルコール類、アセトン、メチルエチ
ルケトン、シクロヘキサノンなどのケトン類、N,N−ジ
メチルホルムアミド、N,N−ジメチルアセトアミドなど
のアミド類、ジメチルスルホキシドなどのスルホキシド
類、テトラヒドロフラン、ジオキサン、エチレングリコ
ールモノメチルエーテルなどのエーテル類、酢酸メチ
ル、酢酸エチルなどのエステル類、クロロホルム、塩化
メチレン、ジクロルエタン、四塩化炭素、トリクロルエ
タンなどの脂肪族ハロゲン化炭化水素類あるいはベンゼ
ン、トルエン、キシレン、リグロイン、モノクロルベン
ゼン、ジクロルベンゼンなどの芳香族類などを用いるこ
とができる。記録層の膜厚は100Å〜10μｍ好ましくは2
00Å〜２μｍが適当である。
塗布などの通常の手段によって行うことができる。塗布
法を用いる場合には有機溶媒に溶解してスプレー、ロー
ラーコーティング、デイッピングおよびスピンニングな
どの慣用のコーティング法によって行なわれる。有機溶
媒としては一般には、メタノール、エタノール、イソプ
ロパノールなどのアルコール類、アセトン、メチルエチ
ルケトン、シクロヘキサノンなどのケトン類、N,N−ジ
メチルホルムアミド、N,N−ジメチルアセトアミドなど
のアミド類、ジメチルスルホキシドなどのスルホキシド
類、テトラヒドロフラン、ジオキサン、エチレングリコ
ールモノメチルエーテルなどのエーテル類、酢酸メチ
ル、酢酸エチルなどのエステル類、クロロホルム、塩化
メチレン、ジクロルエタン、四塩化炭素、トリクロルエ
タンなどの脂肪族ハロゲン化炭化水素類あるいはベンゼ
ン、トルエン、キシレン、リグロイン、モノクロルベン
ゼン、ジクロルベンゼンなどの芳香族類などを用いるこ
とができる。記録層の膜厚は100Å〜10μｍ好ましくは2
00Å〜２μｍが適当である。
基板１は基板側から書込み記録を行なう場合は使用レー
ザ光に対して透明でなければならず、また記録層側から
行なう場合は透明である必要はない。基板としてはガラ
ス、ポリエステル、ポリアミド、ポリオレフィン、ポリ
カーボネート、エポキシ、ポリイミド、ポリメチルメタ
クリレートなどのプラスチック、金属、セラミックスが
通常使用されるがその他記録媒体に使用されるものなら
どれでもよい。
ザ光に対して透明でなければならず、また記録層側から
行なう場合は透明である必要はない。基板としてはガラ
ス、ポリエステル、ポリアミド、ポリオレフィン、ポリ
カーボネート、エポキシ、ポリイミド、ポリメチルメタ
クリレートなどのプラスチック、金属、セラミックスが
通常使用されるがその他記録媒体に使用されるものなら
どれでもよい。
また、第２図ないし第４図に示すように第１図の構成の
ものにさらに下引層３および／または保護層４を設けた
構成とすることもできる。この際、下引層および／また
は保護層中には本発明の上記一般式で表わされる化合物
が含有されていてもよい。
ものにさらに下引層３および／または保護層４を設けた
構成とすることもできる。この際、下引層および／また
は保護層中には本発明の上記一般式で表わされる化合物
が含有されていてもよい。
下引層３は(a)接着性の向上、(b)水またはガラスなどの
バリヤー、(c)記録層の保存安定性の向上、(d)反射率の
向上、(e)溶剤からの基板の保護および(f)プレグルーブ
の形成などを目的として使用される。(a)の目的に対し
ては前記高分子材料およびシランカップリング剤などの
種々の物質を用いることができ、(b)、(c)の目的に対し
ては上記高分子材料以外に無機化合物例えばSiO2、MgF2、
SiO、TiO2、ZnO、TiN、SiNなど、金属または半金属例えばZ
n、Cu、S、Ni、Cr、Ge、Se、Cd、Ag、Ａなどを用いることがで
きる。(d)の目的に対しては金属例えばＡ、Agなどま
たは金属光沢を有する有機薄膜例えばメタン染料、キサ
ンテン系染料などを用いることができそして(e)、(f)の
目的に対しては紫外線硬化樹脂、熱硬化性樹脂、熱可塑
性樹脂などを用いることができる。下引層の膜厚は0.1
〜３０μｍ好ましくは0.2〜１０μｍが適当である。ま
た、保護層４はキズ、ホコリ、汚れなどからの保護およ
び記録層の化学的安定性の向上を目的として設けられ、
その材料としては下引き層と同じ材料を使用することが
できる。保護層の膜厚は0.1μｍ以上好ましくは５０μ
ｍ以上が適当である。
バリヤー、(c)記録層の保存安定性の向上、(d)反射率の
向上、(e)溶剤からの基板の保護および(f)プレグルーブ
の形成などを目的として使用される。(a)の目的に対し
ては前記高分子材料およびシランカップリング剤などの
種々の物質を用いることができ、(b)、(c)の目的に対し
ては上記高分子材料以外に無機化合物例えばSiO2、MgF2、
SiO、TiO2、ZnO、TiN、SiNなど、金属または半金属例えばZ
n、Cu、S、Ni、Cr、Ge、Se、Cd、Ag、Ａなどを用いることがで
きる。(d)の目的に対しては金属例えばＡ、Agなどま
たは金属光沢を有する有機薄膜例えばメタン染料、キサ
ンテン系染料などを用いることができそして(e)、(f)の
目的に対しては紫外線硬化樹脂、熱硬化性樹脂、熱可塑
性樹脂などを用いることができる。下引層の膜厚は0.1
〜３０μｍ好ましくは0.2〜１０μｍが適当である。ま
た、保護層４はキズ、ホコリ、汚れなどからの保護およ
び記録層の化学的安定性の向上を目的として設けられ、
その材料としては下引き層と同じ材料を使用することが
できる。保護層の膜厚は0.1μｍ以上好ましくは５０μ
ｍ以上が適当である。
さらに、本発明による光情報記録媒体の構成としては、
第１図ないし第４図に示した同一構成の２枚の記録媒体
（場合によりその１枚の基板のみとして）を用い記録層
２を内側に配置して密封したいわゆるエアーサンドイッ
チ構造にしてもよいし、保護層４を介して接着したいわ
ゆる密着サンドイッチ構造（貼り合せ構造）にしてもよ
い。
第１図ないし第４図に示した同一構成の２枚の記録媒体
（場合によりその１枚の基板のみとして）を用い記録層
２を内側に配置して密封したいわゆるエアーサンドイッ
チ構造にしてもよいし、保護層４を介して接着したいわ
ゆる密着サンドイッチ構造（貼り合せ構造）にしてもよ
い。
なお、レーザ光源として波長750〜850nmの半導体レーザ
を用いると装置の小型化が可能となる。
を用いると装置の小型化が可能となる。
以下に実施例を掲げて本発明をさらに説明するが、本発
明はこれに限定されるものではない。
明はこれに限定されるものではない。
実施例１ 厚さ1.2mmのポリメチルメタクリレート（以下「PMMA」
と略記）基板上に前記化合物Ａのテトラヒドロフラン溶
液を回転塗布して厚さ0.1μｍの記録層を形成し記録媒
体を作製した。
と略記）基板上に前記化合物Ａのテトラヒドロフラン溶
液を回転塗布して厚さ0.1μｍの記録層を形成し記録媒
体を作製した。
実施例２ 実施例１において前記化合物例Ｄを用いて記録層を形成
した以外は実施例１と同様にして記録媒体を作製した。
した以外は実施例１と同様にして記録媒体を作製した。
実施例３ 実施例１で形成した記録層の上にさらに厚さ100Åの銀
蒸着膜を設けて記録媒体を作製した。
蒸着膜を設けて記録媒体を作製した。
実施例４ 厚さ1.2mmのPMMA基板上に前記化合物例Ｂと下記一般式
(I)の化合物とを１：１の重量比で混合した1,2−ジクロ
ルエタン溶液を回転塗布して厚さ0.1μｍの記録層を形
成し記録媒体を作製した。
(I)の化合物とを１：１の重量比で混合した1,2−ジクロ
ルエタン溶液を回転塗布して厚さ0.1μｍの記録層を形
成し記録媒体を作製した。
実施例５ 厚さ1.2mmのPMMA基板上に前記化合物例Ｃと下記一般式
(II)の化合物とを７：３の重量比で混合した1,2−ジク
ロルエタン溶液を回転塗布して厚さ0.1μｍの記録層を
設けさらにその上に下記一般(III)の化合物を厚さ0.05
μｍで真空蒸着して記録媒体を作製した。
(II)の化合物とを７：３の重量比で混合した1,2−ジク
ロルエタン溶液を回転塗布して厚さ0.1μｍの記録層を
設けさらにその上に下記一般(III)の化合物を厚さ0.05
μｍで真空蒸着して記録媒体を作製した。
実施例６ 厚さ1.2mmのPMMA基板上に厚さ１５０ÅのTe蒸着膜を設
けさらにその上に前記化合物例Ｆの1,2−ジクロルエタ
ン溶液を回転塗布し厚さ0.1μｍの記録層を形成し記録
媒体を作製した。
けさらにその上に前記化合物例Ｆの1,2−ジクロルエタ
ン溶液を回転塗布し厚さ0.1μｍの記録層を形成し記録
媒体を作製した。
上記実施例で作製した記録媒体に波長790nmの半導体レ
ーザ光を用いて基板側より書込みパワー2.25mW、記録周
波数0.5MHz、線速1.5m/secで情報を書込み再生し、その
スペクトル解析（スキャニングフイルター、バンド幅30
KHz）を行なってC/Nを測定した。次に、同じ記録媒体に
54000ルックスのタングステン光を５０時間照射した後
のC/Nを測定した。その結果を以下の表にまとめて示
す。
ーザ光を用いて基板側より書込みパワー2.25mW、記録周
波数0.5MHz、線速1.5m/secで情報を書込み再生し、その
スペクトル解析（スキャニングフイルター、バンド幅30
KHz）を行なってC/Nを測定した。次に、同じ記録媒体に
54000ルックスのタングステン光を５０時間照射した後
のC/Nを測定した。その結果を以下の表にまとめて示
す。
〔効果〕 上述のようにして構成された本発明の光情報記録媒体は
以下の効果を奏することができる。
以下の効果を奏することができる。
１．長波長レーザ（半導体レーザ）を用いても高感度に
記録できる。
記録できる。
２．良好な形状でピットを形成することが出来、高いC/
Nが得られる。
Nが得られる。
３．熱および光に対する安定性が高く、保存性に優れ、
再生劣化の少い記録体が得られる。
再生劣化の少い記録体が得られる。
【図面の簡単な説明】 第１図ないし第４図は本発明の光情報記録媒体の構成を
示す断面図である。 １…基板、２…記録層、３…下引き層、４…保護層。
示す断面図である。 １…基板、２…記録層、３…下引き層、４…保護層。
───────────────────────────────────────────────────── フロントページの続き (72)発明者 大庭 秀章 東京都大田区中馬込１丁目３番６号 株式 会社リコー内 (72)発明者 上田 裕 東京都大田区中馬込１丁目３番６号 株式 会社リコー内
Claims (1)
- 【請求項１】一般式 （式中、R1ないしR3は同じかまたは異なっていてもよく
そしてそれぞれは水素、ハロゲン、ヒドロキシ基、カル
ボキシル基あるいは置換もしくは未置換のアルキル、ア
ルコキシ、アリール、アシル、アシルオキシまたはアル
ケニル基を表わしそしてＭはNi、Co、Cu、Mn、PdまたはPtを
表わす）の化合物を包む記録層を有することを特徴とす
る、光情報記録媒体。