JPH06328871A - 熱転写受容シート - Google Patents

熱転写受容シート

Info

Publication number
JPH06328871A
JPH06328871A JP13992893A JP13992893A JPH06328871A JP H06328871 A JPH06328871 A JP H06328871A JP 13992893 A JP13992893 A JP 13992893A JP 13992893 A JP13992893 A JP 13992893A JP H06328871 A JPH06328871 A JP H06328871A
Authority
JP
Japan
Prior art keywords
coating layer
accepting sheet
resin
sheet
heat transfer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP13992893A
Other languages
English (en)
Inventor
Shigeo Hayashi
滋雄 林
Koji Narita
光司 成田
Yukio Kusaka
幸雄 日下
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
New Oji Paper Co Ltd
Original Assignee
New Oji Paper Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by New Oji Paper Co Ltd filed Critical New Oji Paper Co Ltd
Priority to JP13992893A priority Critical patent/JPH06328871A/ja
Priority to US08/243,829 priority patent/US5407894A/en
Priority to EP19940303566 priority patent/EP0625428B1/en
Priority to DE1994603557 priority patent/DE69403557T2/de
Publication of JPH06328871A publication Critical patent/JPH06328871A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】 【目的】 染料熱転写プリンターに使用されたときに、
熱可塑性樹脂をラミネートした基材を用いた場合の濃度
ムラの欠点を解消し、プリント画像が鮮明な熱転写受容
シートを提供する。 【構成】 セルロースパルプを主成分とする原紙上に、
曲げ弾性率が７０００Kg／cm2 以下である樹脂被覆層
と、熱転写画像形成染料を受容、染着する画像受容層を
有する。

Description

【発明の詳細な説明】
【０００１】
【産業上の利用分野】本発明は、染料熱転写画像受容シ
ートに関するものである。更に詳しくは本発明は、染料
熱転写プリンターに使用されたとき、濃度むらのない鮮
明な画像が得られる熱転写受容シートに関する。
【０００２】
【従来の技術】近年、熱転写方式の高画質のカラーハー
ドコピー、特に染料熱転写型プリンターの開発が急速に
進んでいる。染料熱転写型プリンターでは、３色（イエ
ロー、マゼンタ、シアン）の昇華性染料層を、サーマル
ヘッドの加熱エネルギーを連続的に制御して加熱し、そ
れぞれの色の染料の転写量を変化させ、濃度階調のフル
カラー画像を可能にしている。
【０００３】このような染料熱転写プリンターにより、
高画質のプリントを高速で受容シート上に形成するため
には、受容シートの基材として、ポリオレフィンなどの
熱可塑性樹脂を主成分とし、空隙を有する二軸延伸フィ
ルムを用いることが知られている。染料熱転写受容シー
ト（以下、受容シートと略す）では、この基材上に、熱
可塑性樹脂を主成分とする画像受容層（以下、受容層と
略す）を有している。これらの基材を用いた受容シート
は、厚さが均一で、柔軟性があり、セルロース繊維から
なる紙等に比べ熱伝導度が小さいなどの利点があり、従
って均一で濃度の高いプリントが得られるという長所が
ある。
【０００４】しかし、このような二軸延伸フィルムを画
像の再現性を要求される受容シートの基材として用いた
場合、延伸時の残留応力がプリント時の熱で戻り、延伸
方向に熱収縮し、その結果、受容シートにカールやシワ
が発生し、これが、プリンター中を走行する受容シート
の紙詰まりなどのトラブルの原因となっていた。上記カ
ール、またはシワ発生という欠点を改善するために、比
較的熱収縮性の小さい芯材や弾性率の大きい芯材の両面
に延伸フィルムを積層貼合したラミネートシートを基材
として用いることが知られている。
【０００５】しかし、このような基材は熱収縮率の異な
るシートを積層しているため、熱などによる収縮率差が
原因となるカールが発生した。また、表裏に積層してい
る延伸フィルムの収縮率差を同じにしても、プリント時
に熱は表方向にのみかかるので、受容シート表面、裏面
では温度が異なり、このため表裏に収縮率に差がでてカ
ールを起こしていた。さらに表裏に延伸フィルムを積層
しているためコストが大幅に上がってしまった。
【０００６】上記のような熱変形性のある延伸フィルム
を基材として用いることなく、画像の濃度むらを解消す
るために、高平滑な紙の表面に５〜３５μｍ、５〜２５
ｇ／m2のポリオレフィン樹脂をラミネートした基材を用
いることが提案されている（特開平2ー106397号公報、2ー
307786号公報）。ラミネート量により画像品質はある程
度改善できるが、濃度むらを改善するにはいたっていな
い。また、米国特許第4774224 号明細書にはラミネート
した基材の中心線表面粗さを7.5 μインチ以下にするこ
とより、濃度むら、光沢むらを向上させることが提案さ
れているが充分ではない。
【０００７】
【発明が解決しようとする課題】本発明は、紙上に熱可
塑性樹脂層を設けた基材を使用した場合の濃度むらを解
消した染料熱転写画像受容シートを提供しょうとするも
のである。
【０００８】
【課題を解決するための手段】本発明者らは上記の課題
を鋭意研究した結果、受容シートに使用する樹脂被覆層
の曲げ弾性率を特定値以下にすれば、濃度むらが発生し
ないことを見出し、課題の解決に成功した。本発明の熱
転写受容シートはセルロースパルプを主成分として含む
原紙と、前記原紙の少なくとも一方の面に形成され、か
つ、熱可塑性樹脂を主成分として含む樹脂被覆層と、前
記樹脂被覆層上に形成され、かつ、熱転写画像形成染料
を受容、染着する画像受容層とを有し、前記樹脂被覆層
のＪＩＳ Ｋ ７２０３に規定した曲げ弾性率が７００
０Kg／cm2 以下であることを特徴とするものである。
【０００９】紙上にポリオレフィン樹脂をラミネートし
た基材を用いた受容シートは、濃度むらや、白抜けと呼
ばれる転写不良部が発生することは良く知られていた。
これらの欠点は、ラミネート表面や紙表面の凹凸に起因
すると言われている。本発明の熱転写受容シートの画質
が優れる理由は明確でないが以下のように推定される。
プリント時に受容シートはサーマルヘッドとプラテンロ
ーラーに挟まれ、圧力を受けながらプリントされる。受
容シートの表面が平滑であれば、サーマルヘッドと受容
シートの密着性が向上し、濃度むらのない均一な画像が
得られる。しかし、受容シートの弾性率が高いと、わず
かな凹凸でも凸部が変形されず、凹部とサーマルヘッド
の密着性が悪くなり濃度むらが生じる。その反面、多少
の凹凸が受容シート表面に存在しても、受容シートの弾
性率が小さければ、受容シート表面凸部が変形し、プリ
ント時にはサーマルヘッドとの密着性が向上し、濃度む
らを生じないと考えられる。
【００１０】本発明の樹脂被覆層に用いられる熱可塑性
樹脂としては低密度ポリエチレン、高密度ポリエチレ
ン、ポリプロピレン、ポリブテン、ポリペンテン等のホ
モポリマー、またはエチレンーポリプロピレン共重合体
等のオレフィンの２つ以上からなる共重合体、およびこ
れらの混合物が使用できる。
【００１１】さらに本発明の樹脂被覆層中にはステアリ
ン酸アミド、ステアリン酸亜鉛等の金属塩、リン系化合
物等の酸化防止剤、酸化チタン、コバルトブルー、群青
等の顔料や染料を添加してもよい。重要なことは、これ
らの樹脂被覆層の曲げ弾性率を７０００Kg／cm2 以下に
することである。本発明における樹脂被覆層は溶融押し
出しラミネーターにより形成されるが、得られる被覆層
の表面平均度や、原紙との接着性が良好であることが好
ましい。本発明の樹脂被覆層の塗布量は10〜40 g／m2が
好ましい。 10g／m2よりも少ない場合は濃度むらが発生
しやすく、40 g／m2以上ではプリント濃度が低下するこ
ともある。
【００１２】本発明に使用されるセルロースパルプは特
に限定はされないが、例えば、広葉樹や針葉樹の化学パ
ルプや機械パルプ等の木材パルプ、古紙パルプ、麻や綿
等の非木材天然パルプ、ポリエチレンやポリプロピレン
等を原料とした合成パルプ等を挙げることができ、これ
らを組み合わせて使用する。特に、広葉樹の化学パルプ
が好ましい。上記のパルプの他に、アクリル繊維やレー
ヨン繊維、フェノール繊維、ポリアミド繊維、ポリエス
テル繊維等の有機繊維、ガラス繊維や炭素繊維、アルミ
ナ繊維等の無機繊維等、各種の繊維を混抄してもよい。
パルプを抄紙する工程で、各種のアニオン性、ノニオン
性、カチオン性あるいは、両性の歩留向上剤、紙力増強
剤、サイズ剤が適宜選択して使用される。抄紙性の観点
より、パルプを５０重量％以上配合したシートの方が好
ましい。
【００１３】本発明の受容層に使用できる受容層樹脂と
しては、熱可塑性飽和ポリエステル樹脂、塩化ビニルー
酢酸ビニル共重合体、塩化ビニループロピオン酸ビニル
共重合体などの塩ビ系樹脂が好ましいが、その他ポリカ
ーボネート樹脂、ポリビニルアセタール樹脂、ポリアミ
ド樹脂、エポキシ樹脂などを用いても良い。本発明の受
容層には置換フェノール、テルペンなどの低分子有機化
合物を酸化防止、紫外線吸収、増感の目的でブレンドす
ることが可能である。また、塗料の色度、不透明度の向
上に用いられる白色顔料、受容層の色調を調整する蛍光
染料や、ブルー、バイオレットなどの染料も必要に応じ
て添加可能である。上記の白色顔料、紫外線吸収剤など
の添加剤は受容層の主成分である受容層樹脂と混合して
塗工するのが便利であるが、別の層として受容層の上、
又は下に塗工しても良い。
【００１４】更に、熱によるインクシートと、受容層と
の印画時の耐熱融着を高めるために離型剤を使用するこ
とが出来る。このような離型剤としてパラフィン、ポリ
エチレンワックスなどのワックス類、金属石鹸、シリコ
ーンオイル、シリコーン系樹脂、フッ素系界面活性剤、
フッ素系樹脂などを添加することが可能であり、添加量
は１５重量％以下が好ましい。
【００１５】樹脂被覆層と受容層間の接着性を改善する
ために中間層を設けてもよい。各種の親水性樹脂、疎水
性樹脂が使用可能であり、例えばポリビニルアルコー
ル、ポリビニルピロリドン等のビニルポリマーおよびそ
の誘導体、ポリアクリルアミド、ポリジメチルアクリル
アミド、ポリアクリル酸またはその塩、ポリアクリル酸
エステル等のアクリル基を含むポリマー、ポリメタクリ
ル酸、ポリメタクリル酸エステル等のメタクリル基を含
むポリマー、澱粉、アルギン酸ソーダ、ポリエチレンイ
ミン、カルボキシメチルセルロース等が挙げられる。
【００１６】受容シートのプリンター内での走行時に静
電気が発生し、走行トラブルとなることを防ぐために、
シートの少なくともいずれかの面に帯電防止剤を、画像
受容層内に添加、又はバックコートなどの方法で含有で
きる。帯電防止剤としてはカチオン系親水性高分子が良
く用いられる。
【００１７】
【実施例】本発明を下記実施例によって更に詳細に説明
する。勿論、本発明はこれらによって限定されるもので
はない。尚、実施例中の「部」はすべて「重量部」であ
る。実施例１ 上質紙の表裏側に、表１に示すようなポリオレフィンを
それぞれ２０ｇ／m2になるようにラミネートした。最後
に表面をコロナ処理をした後、下記組成の画像受容層塗
料組成物をワイヤーバーを用いて塗布、乾燥、固形分塗
布量が６ｇ／m2の受容層を設け受容シートを得た。
【００１８】画像受容層塗料組成物 成 分 重 量 ポリエステル樹脂（商標：バイロン200 、東洋紡製） １００部 シリコンオイル （商標：KF393 、信越シリコン製） ３部 イソシアネート （商標：タケネートD-110N、武田薬品製） ５部 トルエン ３００部
【００１９】得られた受容シートをカラーバー信号発生
器（商標：C13A2 、シバゾク製）によりステップパター
ンを染料熱転写プリンター（商標：AGー EP60、松下電器
製）でプリントした。表１にプリント濃度むら、未転写
部の官能評価結果を示す。尚、官能評価は以下のように
行った。
【００２０】２段階評価 ○： 濃度むら、未転写部がない ×： 濃度むら、未転写部がある比較例１ 実施例１と同じく第１表に記載した条件で受容シートを
作製し、評価を行った。評価結果を第１表に示す。
【００２１】
【表１】
【００２２】
【発明の効果】本発明の熱転写受容シートは、曲げ弾性
率が7000Kg／cm2 以下の樹脂被覆層を原紙上に設けるこ
とにより、濃度むらのない鮮明な画像が得られるもので
ある。

Claims (1)

    【特許請求の範囲】
  1. 【請求項１】 セルロースパルプを主成分として含む原
    紙と、前記原紙の少なくとも一方の面に形成され、か
    つ、熱可塑性樹脂を主成分として含む樹脂被覆層と、前
    記樹脂被覆層上に形成され、かつ、熱転写画像形成染料
    を受容、染着する画像受容層とを有する熱転写受容シー
    トにおいて、前記樹脂被覆層のＪＩＳＫ ７２０３に規
    定した曲げ弾性率が７０００Kg／cm2 以下であることを
    特徴とする染料熱転写受容シート。
JP13992893A 1993-05-20 1993-05-20 熱転写受容シート Pending JPH06328871A (ja)