JPH05229B2 - - Google Patents
Info
- Publication number
- JPH05229B2 JPH05229B2 JP59020181A JP2018184A JPH05229B2 JP H05229 B2 JPH05229 B2 JP H05229B2 JP 59020181 A JP59020181 A JP 59020181A JP 2018184 A JP2018184 A JP 2018184A JP H05229 B2 JPH05229 B2 JP H05229B2
- Authority
- JP
- Japan
- Prior art keywords
- recording
- thin film
- recording medium
- composition
- tix
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】
(イ) 産業上の利用分野
本発明は光学的な記録媒体に関するものであり
レーザ光等の光及び熱エネルギーを用いて情報を
高密度に記録し、且つ再生可能な記録媒体に関す
る。
レーザ光等の光及び熱エネルギーを用いて情報を
高密度に記録し、且つ再生可能な記録媒体に関す
る。
(ロ) 従来技術
レーザ光等のエネルギービームを照射して、基
板上の金属等の薄膜を溶隔あるいは蒸発させ、ピ
ツトを形成する方式の記録材料としては感度が高
く、基板上の記録層の膜厚が均一であり化学、物
理的にも安定で長期にわたつて記録再生ができな
ければならない。
板上の金属等の薄膜を溶隔あるいは蒸発させ、ピ
ツトを形成する方式の記録材料としては感度が高
く、基板上の記録層の膜厚が均一であり化学、物
理的にも安定で長期にわたつて記録再生ができな
ければならない。
例えば、日経エレクトロニクス1982年１月４日
号第86頁以下、「画像フアイルに使われ出した光
デイスク・メモリ」なる記事等に開示されている
如く、現在この方式の記録材料としてはテルル
（Te）が一般的に用いられている。Teは熱伝導
率が低く、光吸収係数が大きく、低融点であるの
で感度の良い記録膜が得られるが、空気中の水分
によつて容易に酸化され、光学的に透明な二酸化
テルル（TeO2）に変化するため信号が再生でき
なくなり、長期間の情報の記録は非常に難しい。
すなわち記録寿命が短いという欠点を有してい
る。
号第86頁以下、「画像フアイルに使われ出した光
デイスク・メモリ」なる記事等に開示されている
如く、現在この方式の記録材料としてはテルル
（Te）が一般的に用いられている。Teは熱伝導
率が低く、光吸収係数が大きく、低融点であるの
で感度の良い記録膜が得られるが、空気中の水分
によつて容易に酸化され、光学的に透明な二酸化
テルル（TeO2）に変化するため信号が再生でき
なくなり、長期間の情報の記録は非常に難しい。
すなわち記録寿命が短いという欠点を有してい
る。
又前掲の記事中には、チタニウム（Ti）単体
を薄膜材料として使用する例（第98頁第１３図
ｂ）も挙げられている。しかし乍らTi単体は感
度が劣るだけでなく大面積に亘つて均一な組成の
ものを低コストで得ることが困難であるという欠
点を否めない。
を薄膜材料として使用する例（第98頁第１３図
ｂ）も挙げられている。しかし乍らTi単体は感
度が劣るだけでなく大面積に亘つて均一な組成の
ものを低コストで得ることが困難であるという欠
点を否めない。
(ハ) 目的
本発明は、上記欠点を改善し、長期間にわたつ
て情報の記録、再生ができる記録媒体を提供する
ことを目的とする。
て情報の記録、再生ができる記録媒体を提供する
ことを目的とする。
(ニ) 構成
本発明は、基板上にテルル（Te）とチタン
（Ti）からなるTe100−ｘ・Tix（３≦ｘ≦15）の
組成の組成をもつ非晶質薄膜を形成したものであ
る。
（Ti）からなるTe100−ｘ・Tix（３≦ｘ≦15）の
組成の組成をもつ非晶質薄膜を形成したものであ
る。
(ホ) 実施例
第１図は本発明の光学記録媒体の要部断面斜視
図を示すものである。この記録媒体は基本的に記
録薄膜１を内面に形成した透明基盤２と、保護基
盤３及び両者を一定の間隔を空けて一体に固定す
るスペーサ４，５で構成される。矢印は記録、再
生用のレーザ光の方向を示す。
図を示すものである。この記録媒体は基本的に記
録薄膜１を内面に形成した透明基盤２と、保護基
盤３及び両者を一定の間隔を空けて一体に固定す
るスペーサ４，５で構成される。矢印は記録、再
生用のレーザ光の方向を示す。
前記透明基盤２は、ガラス、ポリメチルメタク
リレート樹脂、ポリカーボネート樹脂、ポリメチ
ールテレフタレート樹脂或はアクリル樹脂等の如
く蒸着或はスパツタリング金属等の付着性が良く
透明度の秀れた素材で成型される。
リレート樹脂、ポリカーボネート樹脂、ポリメチ
ールテレフタレート樹脂或はアクリル樹脂等の如
く蒸着或はスパツタリング金属等の付着性が良く
透明度の秀れた素材で成型される。
前記記録薄膜としては、上述の長寿命化を計る
という課題の他、記録再生用のLD（半導体レーザ
ダイオード）の出力、Ｓ／Ｎ（Ｃ／Ｎ）、感度、信
頼性等の観点から、種々の実験により、テルル
（Te）とチタニウム（Ti）を主成分とし、Te
（100−ｘ）・Tix〔ｘはモル％（但し３≦ｘ≦15）〕
なる組成の非晶質薄膜を採用した。
という課題の他、記録再生用のLD（半導体レーザ
ダイオード）の出力、Ｓ／Ｎ（Ｃ／Ｎ）、感度、信
頼性等の観点から、種々の実験により、テルル
（Te）とチタニウム（Ti）を主成分とし、Te
（100−ｘ）・Tix〔ｘはモル％（但し３≦ｘ≦15）〕
なる組成の非晶質薄膜を採用した。
この非晶質薄膜は蒸着若しくはスパツタリング
法によつて前記透明基盤２上に300〜500Åの膜厚
に形成される。
法によつて前記透明基盤２上に300〜500Åの膜厚
に形成される。
Tiの含有量対Ｃ／Ｎ（dB）の関係を、デイスク
半径60cm、回転数700rpm、記録周波数2MHzの条
件で実験した結果を表わす第２図を参照すれば、
少くとも０≦ｘ≦15の範囲でＣ／Ｎ dB≧45の
Ｃ／Ｎが確保出来ることが確認される。また、デ
イスク半径対LD出力（デイスク面上）の特性を
Tiの含有量をパラメータとして測定した結果を
示した第３図を参照すれば、大径デイスクにおい
ても０≦ｘ≦20の範囲で読出出力の影響を受け
ず、なお且つLDの出力上限の範囲で十分な録再
特性を確保し得ることが判る。
半径60cm、回転数700rpm、記録周波数2MHzの条
件で実験した結果を表わす第２図を参照すれば、
少くとも０≦ｘ≦15の範囲でＣ／Ｎ dB≧45の
Ｃ／Ｎが確保出来ることが確認される。また、デ
イスク半径対LD出力（デイスク面上）の特性を
Tiの含有量をパラメータとして測定した結果を
示した第３図を参照すれば、大径デイスクにおい
ても０≦ｘ≦20の範囲で読出出力の影響を受け
ず、なお且つLDの出力上限の範囲で十分な録再
特性を確保し得ることが判る。
次にTe（100−ｘ）・Tixの組成比と記録寿命と
の関係を確認するために、透明基盤２としてアク
リル樹脂製の円盤を用い、その内面にTe（100−
ｘ）・Tixの組成（但しｘ＝０，２，４，７，
15・）の記録薄膜を300Åの膜厚に形成した記録
媒体のサンプルを用意し、温度60℃、湿度90％の
雰囲気中に放置して加速試験を行つた。その結果
を第４図に表わす。
の関係を確認するために、透明基盤２としてアク
リル樹脂製の円盤を用い、その内面にTe（100−
ｘ）・Tixの組成（但しｘ＝０，２，４，７，
15・）の記録薄膜を300Åの膜厚に形成した記録
媒体のサンプルを用意し、温度60℃、湿度90％の
雰囲気中に放置して加速試験を行つた。その結果
を第４図に表わす。
この加速試験の結果に依れば、従来のTe単体
の記録膜が試験開始後相対的な透過率が試験開始
後１日で20％，１週間後に200％以上にも上昇し
たのに比べて本発明のTe100−ｘ・Tixの組成の
記録媒体の場合少くとも３≦ｘの範囲で記録安定
性が大巾に向上し記録寿命が著しく向上すること
が判る。特にｘ＝７即ち、Te93Ti7の場合には１
ケ月経過後にも相対透過率は殆んど変化しない。
従つてTiの含有量ｘモル％を３≦ｘ≦15に選定
し、Te（100−ｘ）・Tixの組成の記録薄膜によつ
て記録媒体を形成すれば本発明の目的に沿う記録
媒体を実現し得ることが判る。
の記録膜が試験開始後相対的な透過率が試験開始
後１日で20％，１週間後に200％以上にも上昇し
たのに比べて本発明のTe100−ｘ・Tixの組成の
記録媒体の場合少くとも３≦ｘの範囲で記録安定
性が大巾に向上し記録寿命が著しく向上すること
が判る。特にｘ＝７即ち、Te93Ti7の場合には１
ケ月経過後にも相対透過率は殆んど変化しない。
従つてTiの含有量ｘモル％を３≦ｘ≦15に選定
し、Te（100−ｘ）・Tixの組成の記録薄膜によつ
て記録媒体を形成すれば本発明の目的に沿う記録
媒体を実現し得ることが判る。
(ヘ) 発明の効果
本発明に依れば、長記録寿命で感度がよく低コ
ストの光学式記録媒体が実現出来る。
ストの光学式記録媒体が実現出来る。
図面はいずれも本発明に係り、第１図は要部断
面斜視図、第２図はTiの含有量とＣ／Ｎの関係
を表わす図、第３図はデイスク半径とLD出力と
の関係をTe−Ti素材の組成をパラメータとして
表わす図、第４図は相対的透過率の加速試験の結
果を示す図である。 １……記録薄膜、２……透明基盤、３……保護
基盤、４，５……スペーサ。
面斜視図、第２図はTiの含有量とＣ／Ｎの関係
を表わす図、第３図はデイスク半径とLD出力と
の関係をTe−Ti素材の組成をパラメータとして
表わす図、第４図は相対的透過率の加速試験の結
果を示す図である。 １……記録薄膜、２……透明基盤、３……保護
基盤、４，５……スペーサ。
Claims (1)
- 【特許請求の範囲】 １ エネルギービームの照射によつて情報を記録
する方式の光学記録媒体において、基板上で
Te100-x・Tix〔但しｘはモル％，３≦×≦15〕な
る組成をもつ非晶質薄膜を形成したことを特徴と
する光学記録媒体。