JPH04331751A - セメント用減水剤 - Google Patents
セメント用減水剤Info
- Publication number
- JPH04331751A JPH04331751A JP13044691A JP13044691A JPH04331751A JP H04331751 A JPH04331751 A JP H04331751A JP 13044691 A JP13044691 A JP 13044691A JP 13044691 A JP13044691 A JP 13044691A JP H04331751 A JPH04331751 A JP H04331751A
- Authority
- JP
- Japan
- Prior art keywords
- cement
- water
- parts
- time
- salt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【0001】
【産業上の利用分野】本発明はセメントペースト、モル
タル、コンクリートなどセメント組成物に関するもので
あり、特に流動性の経時的低下が少なく、また減水性が
高く、施工性、作業性の改善されたセメント用減水剤に
関する。
タル、コンクリートなどセメント組成物に関するもので
あり、特に流動性の経時的低下が少なく、また減水性が
高く、施工性、作業性の改善されたセメント用減水剤に
関する。
【0002】
【従来の技術と発明が解決しようとする課題】セメント
ペースト、モルタル、コンクリート等は、土木、建築等
に大量に使用されている。そして、その作業性の改善、
強度や耐久性の向上、ひび割れ性の減少等諸物性の向上
を目的として、ナフタレンスルホン酸ホルマリン縮合物
を主成分とする減水剤が従来より主として用いられてき
た。
ペースト、モルタル、コンクリート等は、土木、建築等
に大量に使用されている。そして、その作業性の改善、
強度や耐久性の向上、ひび割れ性の減少等諸物性の向上
を目的として、ナフタレンスルホン酸ホルマリン縮合物
を主成分とする減水剤が従来より主として用いられてき
た。
【0003】一方近年の都市部等での交通事情の悪化は
、セメント組成物の運搬に長時間を必要としてきており
、流動性の経時的低下が極めて少ないセメント用減水剤
への要求が特に高まってきた。しかしながらこの要求に
対し、現今までナフタレンスルホン酸ホルマリン縮合物
の他、種々のセメント用減水剤が公知ではあるが、この
流動性の経時的低下が極めて少なく、しかも減水性が高
く、また強度や耐久性に重大な影響を与えるセメント組
成物中の空気量の経時的安定性がよいという点において
は不十分であった。
、セメント組成物の運搬に長時間を必要としてきており
、流動性の経時的低下が極めて少ないセメント用減水剤
への要求が特に高まってきた。しかしながらこの要求に
対し、現今までナフタレンスルホン酸ホルマリン縮合物
の他、種々のセメント用減水剤が公知ではあるが、この
流動性の経時的低下が極めて少なく、しかも減水性が高
く、また強度や耐久性に重大な影響を与えるセメント組
成物中の空気量の経時的安定性がよいという点において
は不十分であった。
【0004】
【課題を解決するための手段】そこで本発明者等は、特
に流動性の経時的低下が少なく、また減水効果が大きく
、またセメント組成物中の空気量の経時的安定性のよい
セメント用減水剤を目標に研究を重ねた結果、本発明に
到達したものである。
に流動性の経時的低下が少なく、また減水効果が大きく
、またセメント組成物中の空気量の経時的安定性のよい
セメント用減水剤を目標に研究を重ねた結果、本発明に
到達したものである。
【0005】即ち一般式(I)
[式中Xは
のいずれかを示す(但し、nは1から5の整数、R1
、R3 は夫々独立して水素、またはアルキル基、R2
、R4 は夫々独立してアルキル基を示す)]で示さ
れる化合物またはその塩と、アルデヒド類、及びアミノ
酸またはその塩とを水性条件下、任意の順序で反応させ
て得られる縮合生成物を分散剤として含有することを特
徴とするセメント用減水剤を提供するものである。
、R3 は夫々独立して水素、またはアルキル基、R2
、R4 は夫々独立してアルキル基を示す)]で示さ
れる化合物またはその塩と、アルデヒド類、及びアミノ
酸またはその塩とを水性条件下、任意の順序で反応させ
て得られる縮合生成物を分散剤として含有することを特
徴とするセメント用減水剤を提供するものである。
【0006】本発明に用いる一般式(I)で示される化
合物としては2,2−ビス(4−ヒドロキシフェニル)
プロパン、4,4´−ジヒドロキシジフェニルメタン、
4,4´−ジヒドロキシジフェニルスルホン、4,4´
−ジヒドロキシビフェニル、4,4´−ジヒドロキシジ
フェニルエーテル、4,4´−エチリデン−ビスフェノ
ール、4,4−ビス(4−ヒドロキシフェニル)吉草酸
、4,4−ビス(4−ヒドロキシフェニル)酪酸、及び
それらの異性体が好んで用いられ、またこれらを組み合
わせて用いることもできる。
合物としては2,2−ビス(4−ヒドロキシフェニル)
プロパン、4,4´−ジヒドロキシジフェニルメタン、
4,4´−ジヒドロキシジフェニルスルホン、4,4´
−ジヒドロキシビフェニル、4,4´−ジヒドロキシジ
フェニルエーテル、4,4´−エチリデン−ビスフェノ
ール、4,4−ビス(4−ヒドロキシフェニル)吉草酸
、4,4−ビス(4−ヒドロキシフェニル)酪酸、及び
それらの異性体が好んで用いられ、またこれらを組み合
わせて用いることもできる。
【0007】またアミノ酸としては、グルタミン酸、グ
リシン、イミノ二酢酸、アラニン、アスパラギン酸、セ
リン、アミノ酪酸、グルタチオン、アミノカプロン酸、
バリン、フェニルアラニン、メチオニン、ロイシン等が
あげられる。
リシン、イミノ二酢酸、アラニン、アスパラギン酸、セ
リン、アミノ酪酸、グルタチオン、アミノカプロン酸、
バリン、フェニルアラニン、メチオニン、ロイシン等が
あげられる。
【0008】アルデヒド類としては、ホルムアルデヒド
、パラホルムアルデヒド、ヘキサメチレンテトラミン等
のホルムアルデヒド重合及び縮合物、アセトアルデヒド
等が有用であり、特に好ましくは、ホルムアルデヒド及
びその誘導体である。
、パラホルムアルデヒド、ヘキサメチレンテトラミン等
のホルムアルデヒド重合及び縮合物、アセトアルデヒド
等が有用であり、特に好ましくは、ホルムアルデヒド及
びその誘導体である。
【0009】本発明の縮合物は、一般式(I)の化合物
またはその塩30ないし70重量部、アミノ酸またはそ
の塩10ないし60重量部、及びアルデヒド類10ない
し50重量部を水性条件下、常圧ないし加圧下に、反応
することにより得ることができる。また通常反応温度は
30ないし 130℃、反応時間は1ないし50時間で
行う。
またはその塩30ないし70重量部、アミノ酸またはそ
の塩10ないし60重量部、及びアルデヒド類10ない
し50重量部を水性条件下、常圧ないし加圧下に、反応
することにより得ることができる。また通常反応温度は
30ないし 130℃、反応時間は1ないし50時間で
行う。
【0010】本発明のセメント用減水剤は以下の効果を
有する。 ・流動性の経時的低下が極めて少ない。 ・空気量の経時的安定性がよい。 ・減水効果が大きい。
有する。 ・流動性の経時的低下が極めて少ない。 ・空気量の経時的安定性がよい。 ・減水効果が大きい。
【0011】なお、本発明のセメント用減水剤は、セメ
ント重量の0.01%ないし 2.0%、好ましくは
0.1%ないし 0.6%の割合で使用される。配合量
が少なすぎると期待した効果は得られず、多すぎるとセ
メントが過度に分散し、分離現象を起こし好ましくない
。
ント重量の0.01%ないし 2.0%、好ましくは
0.1%ないし 0.6%の割合で使用される。配合量
が少なすぎると期待した効果は得られず、多すぎるとセ
メントが過度に分散し、分離現象を起こし好ましくない
。
【0012】セメントは、普通ポルトランドセメント、
早強セメント、超早強セメント、高炉セメント、中庸熱
セメント、フライアッシュセメント、耐硫酸塩セメント
などが用いられる。また他のセメント用添加剤、例えば
減水剤、空気連行剤、凝結遅延剤、防水剤、膨脹剤、シ
リカヒューム、石粉等と併用することもできる。
早強セメント、超早強セメント、高炉セメント、中庸熱
セメント、フライアッシュセメント、耐硫酸塩セメント
などが用いられる。また他のセメント用添加剤、例えば
減水剤、空気連行剤、凝結遅延剤、防水剤、膨脹剤、シ
リカヒューム、石粉等と併用することもできる。
【0013】
【実施例】以下、実施例によって本発明を詳細に説明す
るが、実施例中の部は重量部を示している。 合成例(1) 4,4´−ジヒドロキシジフェニルメタン40.0部と
L−グルタミン酸ナトリウム37.4部、及び47%水
酸化ナトリウム水溶液17.0部を水 182.6部に
加える。この固液に温度90℃にて37%ホルマリン4
0.5部を 0.5時間で滴下する。その後、温度80
℃で3時間反応させて縮合物の水溶液を得た。
るが、実施例中の部は重量部を示している。 合成例(1) 4,4´−ジヒドロキシジフェニルメタン40.0部と
L−グルタミン酸ナトリウム37.4部、及び47%水
酸化ナトリウム水溶液17.0部を水 182.6部に
加える。この固液に温度90℃にて37%ホルマリン4
0.5部を 0.5時間で滴下する。その後、温度80
℃で3時間反応させて縮合物の水溶液を得た。
【0014】合成例(2)
2,2−ビス(4−ヒドロキシフェニル)プロパン38
.1部とL−グルタミン酸ナトリウム31.2部、及び
47%水酸化ナトリウム水溶液14.2部を水 180
.2部に加える。この固液に温度90℃にて37%ホル
マリン33.8部を 0.5時間で滴下する。その後、
温度80℃で4時間反応させて縮合物の水溶液を得た。
.1部とL−グルタミン酸ナトリウム31.2部、及び
47%水酸化ナトリウム水溶液14.2部を水 180
.2部に加える。この固液に温度90℃にて37%ホル
マリン33.8部を 0.5時間で滴下する。その後、
温度80℃で4時間反応させて縮合物の水溶液を得た。
【0015】合成例(3)
4,4´−ジヒドロキシジフェニルスルホン50.1部
とL−グルタミン酸ナトリウム37.4部、及び47%
水酸化ナトリウム水溶液22.1部を水 207.8部
に加える。この固液に温度90℃にて37%ホルマリン
40.5部を 0.5時間で滴下する。その後、温度
100℃で12時間反応させて縮合物の水溶液を得た。
とL−グルタミン酸ナトリウム37.4部、及び47%
水酸化ナトリウム水溶液22.1部を水 207.8部
に加える。この固液に温度90℃にて37%ホルマリン
40.5部を 0.5時間で滴下する。その後、温度
100℃で12時間反応させて縮合物の水溶液を得た。
【0016】合成例(4)
2,2−ビス(4−ヒドロキシフェニル)プロパン45
.6部とL−グリシン15.0部、及び47%水酸化ナ
トリウム水溶液17.1部を水 188.4部に加える
。この固液に温度90℃にて37%ホルマリン40.5
部を 0.5時間で滴下する。その後、温度70℃で3
時間反応させて縮合物の水溶液を得た。
.6部とL−グリシン15.0部、及び47%水酸化ナ
トリウム水溶液17.1部を水 188.4部に加える
。この固液に温度90℃にて37%ホルマリン40.5
部を 0.5時間で滴下する。その後、温度70℃で3
時間反応させて縮合物の水溶液を得た。
【0017】合成例(5)
2,2−ビス(4−ヒドロキシフェニル)プロパン45
.6部とイミノ二酢酸26.6部、及び47%水酸化ナ
トリウム水溶液34.2部を水 205.1部に加える
。この固液に温度90℃にて37%ホルマリン40.5
部を 0.5時間で滴下する。その後、温度80℃で4
時間反応させて縮合物の水溶液を得た。
.6部とイミノ二酢酸26.6部、及び47%水酸化ナ
トリウム水溶液34.2部を水 205.1部に加える
。この固液に温度90℃にて37%ホルマリン40.5
部を 0.5時間で滴下する。その後、温度80℃で4
時間反応させて縮合物の水溶液を得た。
【0018】(コンクリート試験)上記本発明の各減水
剤を添加したコンクリートのコンシステンシーを、比較
例としてナフタレンスルホン酸ホルマリン縮合物(花王
(株)製 マイティー150)のコンシステンシーと
比較し、コンクリートのスランプロス(流動性の経時変
化)を比較した。なおコンクリートの配合を表1に示す
。そして、コンクリートは、セメント、骨材、及び減水
剤を含む水を 100リットル可搬傾胴式ミキサーにて
90秒混練し、直後、60、 120分後にスランプを
測定した。 コンクリートのスランプ、及び空気量はJISに準拠し
て行った。
剤を添加したコンクリートのコンシステンシーを、比較
例としてナフタレンスルホン酸ホルマリン縮合物(花王
(株)製 マイティー150)のコンシステンシーと
比較し、コンクリートのスランプロス(流動性の経時変
化)を比較した。なおコンクリートの配合を表1に示す
。そして、コンクリートは、セメント、骨材、及び減水
剤を含む水を 100リットル可搬傾胴式ミキサーにて
90秒混練し、直後、60、 120分後にスランプを
測定した。 コンクリートのスランプ、及び空気量はJISに準拠し
て行った。
【0019】
【表1】
【0020】測定結果を表2に示す。
【0021】
【表2】
【0022】本発明の減水剤は、比較例の減水剤より少
ない添加率で目標スランプを得ることができ、これは分
散性(減水性)に優れていることを示している。またス
ランプの経時変化から、本発明の減水剤は、流動性の経
時的低下が極めて少ないことを示している。さらに空気
量の経時変化もほとんどなく、安定性がよいことを示し
ている。これらの結果より本発明の減水剤が優れた効果
を有するのは明らかである。
ない添加率で目標スランプを得ることができ、これは分
散性(減水性)に優れていることを示している。またス
ランプの経時変化から、本発明の減水剤は、流動性の経
時的低下が極めて少ないことを示している。さらに空気
量の経時変化もほとんどなく、安定性がよいことを示し
ている。これらの結果より本発明の減水剤が優れた効果
を有するのは明らかである。
Claims (2)
- 【請求項1】一般式(I) [式中Xは のいずれかを示す(但し、nは1から5の整数、R1
、R3 は夫々独立して水素、またはアルキル基、R2
、R4 は夫々独立してアルキル基を示す)]で示さ
れる化合物またはその塩と、アルデヒド類、及びアミノ
酸またはその塩とを水性条件下、任意の順序で反応させ
て得られる縮合生成物を分散剤として含有することを特
徴とするセメント用減水剤。 - 【請求項2】 一般式(I)で示される化合物が2、
2−ビス(4−ヒドロキシフェニル)プロパンであり、
アミノ酸またはその塩がグルタミン酸ナトリウムである
請求項1記載のセメント用減水剤。