JPH04142982A - 光記録媒体 - Google Patents

光記録媒体

Info

Publication number
JPH04142982A
JPH04142982A JP2267281A JP26728190A JPH04142982A JP H04142982 A JPH04142982 A JP H04142982A JP 2267281 A JP2267281 A JP 2267281A JP 26728190 A JP26728190 A JP 26728190A JP H04142982 A JPH04142982 A JP H04142982A
Authority
JP
Japan
Prior art keywords
light
layer
substrate
recording medium
optical recording
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2267281A
Other languages
English (en)
Other versions
JP3026357B2 (ja
Inventor
Shuichi Yanagisawa
柳沢　秀一
Tatsuro Sakai
達郎 酒井
Takashi Chuma
隆 中馬
Yasushi Araki
荒木　泰志
Fumio Matsui
文雄 松井
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Pioneer Corp
Original Assignee
Pioneer Electronic Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Pioneer Electronic Corp filed Critical Pioneer Electronic Corp
Priority to JP02267281A priority Critical patent/JP3026357B2/ja
Priority to US07/690,487 priority patent/US5328802A/en
Publication of JPH04142982A publication Critical patent/JPH04142982A/ja
Application granted granted Critical
Publication of JP3026357B2 publication Critical patent/JP3026357B2/ja
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 〔産業上の利用分野〕 本発明は、書込み可能な光記録媒体、特に光透過性の基
板の上に光吸収層と光反射層を有する光記録媒体に関す
る。
〔従来の技術〕
従来、いわゆる書込み可能な光記録媒体の記録膜には例
えば、シアニン系、フタロシアニン系などの有機色素が
用いられていることは一般に良く知られている。
そして、このような光記録媒体の書込み方法としては、
記録膜の微小面積にレーザビームを集光させ、それを熱
エネルギーに変換し、記録膜の性状を変えて（ピット形
成）行っている。この記録膜の性状変化を円滑に行うた
めに、媒体の構成は基板上に記録膜を設層したものを２
枚用意し、記録膜を対向して配置したいわゆるエアーサ
ンドイッチ構造とされることが一般的である。
このようなタイプの光記録媒体に用いられる書込み用の
レーザビームは、透明基板側から照射され、記録膜の中
に光読取り可能なピットを形成する。記録されたデータ
を再生するための読取り用のレーザビームは、書込み用
のそれに比べ弱い出力であり、ピットが形成された部分
と、そうでない部分のコントラストは電気信号として読
み取られる。
一方、上記媒体とは異なり予めすでにデータが記録され
ているいわゆるＲ　ＯＭ　（ｒｅａｄ　ｏｎｌｙｍｅｍ
ｏｓ）タイプの媒体も存在し、音声記録と情報処理の分
野で広く実用化されている。そして、このものには上記
のごとく書込み可能な記録膜が存在しない。すなわち、
再生されるべくデータに相当するプレピット、プリグル
ープはすでにプラスチック基板の上にプレス成形によっ
て形成され、この上にＡｕ、Ａｇ、Ｃｕ、Ａ１等の金属
からなる反射層が形成され、さらにこの上に保護層が形
成されている。このＲＯＭタイプの典型的な媒体は、い
わゆるＣＤと呼ばれるコンパクトディスクである。この
ＣＤの記録と読み取りの信号の仕様は規格化されており
、この規格に準じて、ＣＤの再生装置がコンパクトディ
スクプレーヤー（ＣＤプレーヤー）として広く使われて
いる。
ところで、前記書込み可能な光記録媒体は、レーザビー
ムを用いる点においてはＣＤと同様であり、また、媒体
の形態もディスク形状をなしている点においてはＣＤと
同様である。それゆえ、ＣＤ仕様の規格に適合し、ＣＤ
プレーヤーにそのまま使える書込み可能な媒体の開発が
強く要望されている。
〔発明が解決しようとする課題〕
しかしながら、上記した有機色素を用いたものは光劣化
に対する耐久性が十分とは言えず、さらには、高温高湿
等の過酷環境下における耐久性も十分とは言えず、これ
らの点の改善が強く要望されている。
本発明はこのような実情のもと創案されたものであり、
その目的はＣＤ規格に合うように高い反射率がとれ、十
分な変調度を有することはもとより、光劣化に対する耐
久性および高温高湿等の過酷環境下における耐久性に優
れた光記録媒体を提供することにある。
〔課題を解決するための手段〕
上記課題を解決するため本発明の光記録媒体は、光透過
性基板の上に光吸収層を有し、該光吸収層の上に光反射
層を有する光記録媒体において、前記光吸収層は、下記
構造式 下記一般式 で表されるクエンチャ（式中Ｒ１Ｒ２、Ｒ３、Ｒ４はそ
れぞれ水素または置換基を表わす）を含有するように構
成した。
本発明の光記録媒体の一部を切り欠いた概略斜視図が第
１図に示される。
本発明の光記録媒体１は、光透過性基板１１の上に光吸
収層１２が設層され、この光吸収層１２の上に光反射層
１３が設層され、この光反射層１３の上に保護層１４が
設層される。
光透過性基板１１は、生産性向上の観点から、いわゆる
射出成形樹脂基板を用いることが好ましく、このものは
、例えば、ポリカーボネート樹脂（Ｐ　Ｃ）　　ポリメ
タクリル酸メチル樹脂（ＰＭＭＡ）等の透明材料から形
成される。このような基板１１の厚さは１．０〜１．５
ｍｍ程度とされる。
このような基板１１の上には、光吸収層１２か成膜され
、この光吸収層１２には下記構造式で表されるシアニン
系色素が含有される。
さらに、本発明の光吸収層１２には下記一般式［Ｉ］で
示されるクエンチャが含有される。
一般式［Ｉ］ れぞれ、水素またはこれに代わる置換基を表わす。
置換基としては、 ＣＨ３０−，０ＣＨ２０−、ＣＨ３ＣＯ０−（ｎ　　Ｃ
３Ｈ７）　２　Ｎ （Ｃ２Ｈ５）　２　Ｎ　　、　　ＣＡ 等が挙げられる。
このようなりエンチャの具体例としては、例えば、以下
の構造式［Ｑ−１，］〜［Ｑ−４］のものが挙げられる
。
［Ｑ−１コ ［Ｑ ２］ ［Ｑ−３］ ［Ｑ ４］ これらのクエンチャの中でも、 上記構造式 ［ ％式％ 前記シアニン系色素の 光劣化を防止する点て特に好ま しい。
このような クエンチャは、色素の光劣化を防止し、特に読出し光に
よる脱色（再生劣化）を防止するために用いられる。こ
のようなりエンチャは、前記色素１モルに対して、０．
０１〜１０モル程度含有される。
このようなりエンチャはおよび前記シアニン系色素を含
有する光吸収層１２は、例えばスピンコード法等の常用
手段により塗設される。塗設される光吸収層の厚さは２
０〜２０００　ｎｍ程度である。なお、塗布に用いる溶
媒としては、公知の種々のものが用いられ、例えば、ジ
アセトンアルコール、エチルセロソルブ、メチルセロソ
ルブ、イソホロン、メタノール、テトラフルオロプロパ
ツール、ジクロロエタン等が挙げられる。
このような光吸収層１２の上には、光反射層１３が設け
られる。光反射層１３はＡｕ、Ａｇ。
Ｃｕ、Ａ１等の金属から構成され、このものは真空蒸着
、スパッタリング、イオンブレーティング等の各種蒸着
メツキ法で成膜される。このような光反射層１３の厚さ
は、０．０２〜２．０μｍ程度とされる。
このような光反射層１３の上には、通常、光吸収層１２
と光反射層１３を保護するために保護層１４が設層され
る。保護層１４は、一般に、紫外線硬化性樹脂をスピン
コードして塗設した後、紫外線を照射し、塗膜を硬化さ
せて形成する。その他、エポキシ樹脂、アクリル樹脂、
シリコーン樹脂、ウレタン樹脂等が保護層１４の材質と
して用いられる。このような保護層１４の厚さは、通常
、０．１〜１００μｍ程度である。
なお、前記基板１１と光吸収層１２との間には、基板１
１を溶媒から保護するための中間層を設けても良い。ま
た、光吸収層１２と、光反射層１３の間には、光吸収や
光反射効率を上げるために中間層を設けてもよい。
〔作用〕
本発明の光記録媒体には、一般に回転下において、記録
光がパルス状に照射される。
この時、光吸収層１２の一部が融解、除去されピットが
形成される。
このように形成されたピットは、やはり媒体の回転下、
読み出し光の反射光の差を検出することによって行われ
る。
〔実施例〕
以下、具体的実施例を示して本発明をさらに詳細に説明
する。
光吸収層に含有される色素としては、前記シアニン系色
素を用い、クエンチャとしては前記［Ｑ−１］を用い、
これらをそれぞれエチルセロソルブの溶媒に溶解させ、
このものを直径１２０ｍｍ。
厚さ１．２ｍｍのポリカーボネート基板上に１１００ｎ
の厚さに塗設した。なお、色素とクエンチャとの混合比
は色素７モルに対してクエンチャ１モルとした。このよ
うにして本発明の光記録媒体サンプルを作製した。
色　　素 ［Ｄ−１］ クエンチャ ［０−１］ 上記条件で作製した本発明の媒体サンプルの光安定特性
を以下の方法で評価した。
評価方法 キセノンランプ光（波長５００〜８５０ｎｍ：エネルギ
３２ＫＷ／ｍ）を基板側から照射し、照射前後での透過
率の変化を分光光度計で経時的に測定した。照射光によ
り色素が劣化すると色素の光吸収が減少し、透過率が増
加する。透過率の経時変化のグラフを第３図に示した。
第３図のグラフによれば、特にＣＤプレヤーの再生レー
ザ波長である７８０ｎｍ近辺では、照射前後で透過率の
変化は無いと言え、本発明の色素の光劣化の防止には本
発明のクエンチャが極めて良好な結果を示すことがわか
る。
次いで、高温高湿下および高温低湿下での耐環境特性を
評価するために以下の実験を行った。
光吸収層に含有される色素としては、上記本発明に用い
られる色素を用い、クエンチャとしては前記［Ｑ−１］
を用い、これらをそれぞれエチルセロソルブの溶媒に溶
解させ、このものを直径１２０■、厚さ１．２ｍｍのポ
リカーボネート基板上に１１００ｎの厚さに塗設した。
なお、色素とクエンチャとの混合比は色素５モルに対し
てクエンチャ１モルとした。なお、基板は予め、スパイ
ラルグループ（グループピッチ１．６μｍ１溝幅０．６
μｍ１溝深さ６００人）が射出成形によって形成されて
いるものを用いた。光吸収層の上にさらにＡｕからなる
光反射層を真空蒸着法で１０００人厚さに設層した。さ
らに、この光吸収層の上にフォトポリマーの保護膜を設
層し、本発明の光記録媒体サンプルを作製した。なお、
市販されている他社製品を比較サンプルとした。これら
のサンプルに下記条件でＥ’ＦＭ信号を記録し、加速環
境に投入した。
電気特性測定条件（記録再生時） 波長・７７８ｎｍ　　線速・１゜ ライトパワー　６．ＯｍＷ リードパワー：０．５ｍＷ 加速環境 ７０°Ｃ１９０％ＲＨ ７０℃、ＤＲＹ ４　ｍ　／　ｓ の２条件 環境加速前後の再生信号の変化を次頁の表１に示す。
表中、各電位等は第５図に示されるように定義される。
すなわち、■　は鏡面部電位、■、はうンド部電位、■
２グループ部電位、Ｉ　ｔｏｐは記録信号のうち、ＩＩ
Ｔ（１９６ＫＨ２）振幅の最も明るい部分の電位を表し
、ＩＩＩＴは記録信号のうちＩＩＴ　（１９６ＫＨｚ）
振幅、Ｉ３Ｔは記録信号のうち３Ｔ　（７２０ＫＨ２）
振幅を表す。
さらに、投入時間を延長した場合における記録部の１．
１．　Ｔ振幅の経時変化が第４図に示される。
〔発明の効果〕
上記の結果より本発明の効果は明らかである。
すなわち、本発明の光記録媒体は光吸収層に所定のシア
ニン系の色素とクエンチャを含有しているので、ＣＤ規
格に合うように高い反射率がとれ、十分な変調度を有す
る書込み可能な光記録媒体であることはもとより、光劣
化に対する耐久性に優れ、しかも高温高湿等の過酷環境
下における耐久性にも極めて優れた効果を奏する。
【図面の簡単な説明】
第１図は本発明の光記録媒体の一部を切り欠いた概略斜
視図、第２図は第１図の切欠部の部分拡大断面図、第３
図は光吸収層の透過率の経時変化を示すグラフ、第４図
は記録部のＩＩＴ振幅の経時劣化を示すグラフ、第５図
はＣＤ規格における各電位を定義する図である。 １・・・光記録媒体、１１・・・光透過性基板、１２・
・・光吸収層、１３・・・光反射層、１４・・・保護層
。

Claims (1)

  1. 【特許請求の範囲】 光透過性基板の上に光吸収層を有し、該光吸収層の上に
    光反射層を有する光記録媒体において、 前記光吸収層は、下記構造式 ▲数式、化学式、表等があります▼ で表されるシアニン系色素と、 下記一般式 ▲数式、化学式、表等があります▼ で表されるクエンチャ（式中Ｒ＿１、Ｒ＿２、Ｒ＿３、
    Ｒ＿４はそれぞれ水素または置換基を表わす）を含有す
    ることを特徴とする光記録媒体。
JP02267281A 1990-10-04 1990-10-04 光記録媒体 Expired - Lifetime JP3026357B2 (ja)