JPH07137448A - 光記録媒体およびその製造方法 - Google Patents

光記録媒体およびその製造方法

Info

Publication number
JPH07137448A
JPH07137448A JP28534893A JP28534893A JPH07137448A JP H07137448 A JPH07137448 A JP H07137448A JP 28534893 A JP28534893 A JP 28534893A JP 28534893 A JP28534893 A JP 28534893A JP H07137448 A JPH07137448 A JP H07137448A
Authority
JP
Japan
Prior art keywords
film
recording medium
optical recording
recording film
recording
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP28534893A
Other languages
English (en)
Inventor
Shingo Iwasaki
新吾 岩崎
Hiroshi Tsuji
大志 辻
Takashi Chuma
隆 中馬
Satoru Tanaka
覚 田中
Shuichi Yanagisawa
秀一 柳沢
Fumio Matsui
文雄 松井
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Pioneer Corp
Original Assignee
Pioneer Electronic Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Pioneer Electronic Corp filed Critical Pioneer Electronic Corp
Priority to JP28534893A priority Critical patent/JPH07137448A/ja
Priority to US08/336,669 priority patent/US5478623A/en
Publication of JPH07137448A publication Critical patent/JPH07137448A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】 【目的】 湿度による劣化のばらつきが小さくて耐湿性
に優れ、安定した性能を発揮する光記録媒体およびその
製造方法を提供する。 【構成】 基板１１上に、記録膜１２、光反射膜１３お
よび保護膜１４を基板１１側からこの順に形成するとと
もに、記録膜１２をｐＨ６．０以上の2,2,3,3 −テトラ
フルオロ−１−プロパノール（ＴＦＰ）を用いた有機色
素により形成する。

Description

【発明の詳細な説明】
【０００１】
【産業上の利用分野】本発明は、光記録媒体およびその
製造方法に関し、特に色素膜からなる記録膜を備えた光
記録媒体およびその製造方法に関する。
【０００２】
【従来の技術】従来、いわゆる書込み可能な追記型の光
記録媒体の記録膜には、例えばシアニン系、フタロシア
ニン系などの有機色素が用いられていることは一般に良
く知られている。
【０００３】そして、このような追記型の光記録媒体の
書込み方法としては、記録膜の微小面積にレーザビーム
を集光させ、それを熱エネルギーに変換し、記録膜の性
状を変えて（ピット形成）行なっている。この記録膜の
性状変化を円滑に行なうために、媒体の構成は基板上に
記録膜を設層したものを２枚用意し、記録膜を対向させ
て配置したいわゆるエアーサンドイッチ構造とされるこ
とが一般的である。
【０００４】このようなタイプの追記型光記録媒体に用
いられる書込み用のレーザビームは、透明基板側から照
射され、記録膜の中に光読取り可能なピットを形成す
る。記録されたデータを再生するための読取り用のレー
ザビームの出力は、書込み用のそれに比べて弱い出力を
用いており、ピットが形成された部分と、そうでない部
分のコントラストは電気信号として読み取られる。
【０００５】一方、前記追記型光記録媒体とは異なり、
予めすでにデータが記録されているいわゆるＲＯＭ（re
ad only memory）タイプの媒体も存在し、音声記録と情
報処理の分野で広く実用化されている。しかし、このも
のには上記のごとく書込み可能な記録膜が存在しない。
すなわち、再生されるべきデータに相当するプリピット
はすでにプラスチック基板の上に射出成形によって形成
され、この上にＡｕ、Ａｇ、Ｃｕ、Ａｌ等の金属からな
る反射層が形成され、さらにこの上に保護層が形成され
ている。このＲＯＭタイプの典型的な媒体は、いわゆる
ＣＤと呼ばれるコンパクトディスクである。このＣＤの
記録と読み取りの信号の仕様は規格化されており、この
規格に準じて、ＣＤの再生装置がコンパクトディスクプ
レーヤー（ＣＤプレーヤー）として広く使われている。
【０００６】ところで、前記書込み可能な追記型光記録
媒体は、レーザビームを用いる点においてはＣＤと同様
であり、また、媒体の形態もディスク形状をなしている
点においてはＣＤと同様である。それゆえ、ＣＤ仕様の
規格に適合し、ＣＤプレーヤーにそのまま使える書込み
可能な光記録媒体の開発が活発に行われている。
【０００７】具体的には、光透過性の基板と、この基板
の上に形成された有機色素を含有する記録膜と、この記
録膜の上に形成された光反射膜と、この光反射膜の上に
形成された保護膜とを備える構成とした追記型光録媒体
についての種々の検討がなされている。
【０００８】そして、このような光記録媒体の記録膜を
形成する色素材料の溶媒には、たとえばジアセトンアル
コール、エチルセロソルブ、メチルセロソルブ、イソホ
ロン、メタノール、テトラフルオロプロパノールなどが
適宜に選択され、使用されている。
【０００９】
【発明が解決しようとする課題】ところで、前記の光記
録媒体の使用態様としては例えば車載ＣＤプレーヤーに
よる再生が考えられるため、耐環境性に優れていること
が要求される。
【００１０】そこで、本発明者が光記録媒体に要求され
る耐環境性について鋭意検討を重ねた結果、色素材料の
溶媒に特定の溶媒を用いて形成した記録膜を有する光記
録媒体は特に耐湿性が優れ、安定した性能を発揮するこ
とを見出すに至った。
【００１１】本発明は、かかる事情に基づいてなされた
ものであり、本発明の目的は特に湿度による劣化のばら
つきが小さくて耐湿性に優れた光記録媒体およびそのよ
うな利点を有する光記録媒体を効率良く得るための製造
方法を提供することにある。
【００１２】
【課題を解決するための手段】上記の目的を達成するた
めの本発明の構成は、光透過性基板と、この光透過性基
板の上に形成された記録膜と、この記録膜の上に形成さ
れた光反射膜と、この光反射膜の上に形成された保護膜
とを備える光記録媒体において、前記記録膜が溶媒にｐ
Ｈ６．０以上の2,2,3,3 −テトラフルオロ−１−プロパ
ノール（ＴＦＰ）を用いた有機色素により形成されてい
ることを特徴とする光記録媒体であり、光透過性基板上
に有機色素からなる記録膜を形成する記録膜形成工程
と、該記録膜形成工程で形成された記録膜上に光反射膜
を形成する光反射膜形成工程と、該光反射膜形成工程で
形成された光反射膜上に保護膜を形成する保護膜形成工
程とを有する光記録媒体の製造方法において、前記記録
膜形成工程で使用する有機色素の溶媒にｐＨ６．０以上
の2,2,3,3 −テトラフルオロ−１−プロパノール（ＴＦ
Ｐ）を用いることを特徴とする光記録媒体の製造方法で
ある。
【００１３】
【実施例】次に本発明の実施例を示し、本発明の光記録
媒体およびその製造方法について併せて説明する。
【００１４】図１は書き込み可能であって、かつＣＤ規
格に適合するような光記録媒体の一例を示す部分断面図
である。この図に示されるように、本発明の光記録媒体
１は、グルーブ１０が形成された光透過性の基板１１の
上に記録膜１２が設けられ、この記録膜１２の上に光反
射膜１３が設けられ、さらに光反射膜１３の上に保護膜
１４が設けられたものである。
【００１５】光透過性の基板１１は、ディスク形状をな
し、基板１１の片側平面には、トラッキング用のグルー
ブ１０が、同心円状にまたはスパイラル状に形成されて
いる。このようなグルーブ１０を有する基板１１は、生
産性向上の観点から、いわゆる一体的に形成された射出
成形樹脂基板を用いることが好ましく、このものは、例
えば、ポリカーボネート樹脂（ＰＣ）、ポリメタクリル
酸メチル樹脂（ＰＭＭＡ）等の透明材料から形成され
る。また、一体的に形成された射出成形樹脂基板に限ら
ず、いわゆる２Ｐ（photo-polymer ）法で形成した基板
であってもよい。このような基板１１の厚さは１．０〜
１．５mm程度とされる。
【００１６】この基板１１の上には、記録膜１２が形成
される。記録膜１２の中には、有機色素が含有される。
ここで、有機色素としては、フタロシアニン色素、シア
ニン色素が挙げられる。これらのなかでも、好ましいの
は次式［Ｉ］で表わされるフタロシアニン色素である。
【００１７】
【化１】 上記式［Ｉ］において、ＭｅはＳｉ原子、Ａｌ原子およ
びＧａ原子のいずれかを表し、Ｐｃはフタロシアニン環
を表す。また、ｍは１または２であり、ｎは１〜５のい
ずれかの整数を表す。
【００１８】このような色素を主成分として含有する記
録膜１２は、例えば、スピンコート法等の常用手段によ
り塗設される。有機色素の塗布に用いる溶媒には、ｐＨ
６．０以上、好ましくはｐＨ６．４以上である２，２，
３，３−テトラフルオロ−１−プロパノール（ＴＦＰ）
が用いられる。このような２，２，３，３−テトラフル
オロ−１−プロパノール（ＴＦＰ）は、２００〜２５０
ｎｍ付近に吸収をもたないものである。
【００１９】ここで、溶媒に用いられる２，２，３，３
−テトラフルオロ−１−プロパノール（ＴＦＰ）のｐＨ
が６．０未満であると、そのような溶媒を用いて形成さ
れた記録膜を有する光記録媒体は湿度による劣化のばら
つきが大きくなり、安定した性能が発揮されないことが
ある。
【００２０】このような記録膜１２の膜厚は、通常、１
００Å〜１００００Å程度であり、好ましくは５００Å
〜５０００Å程度である。このような記録膜１２の上に
は、光反射膜１３が設けられる。光反射膜１３はＡｕ、
Ａｌ、Ａｇ、Ｃｕ等の金属から構成され、このものは真
空蒸着、スパッタリング、イオンプレーティング等で成
膜される。この光反射膜１３の厚さは、０．０２〜２．
０μｍ程度とされる。
【００２１】光反射膜１３の上には、記録膜１２と光反
射膜１３とを保護するために保護膜１４が設層される。
保護膜１４は、一般に、紫外線硬化性樹脂をスピンコー
ト法により塗設した後、紫外線を照射し、塗膜を硬化さ
せて形成する。その他、エポキシ樹脂、アクリル樹脂、
シリコーン樹脂、ウレタン樹脂等が保護膜１４の形成材
料に用いられる。
【００２２】このような保護膜１４の厚さは、通常、
２．５μｍ以上、好ましくは３．０μｍ以上である。な
お、保護膜１４の形成材料が紫外線硬化樹脂である場
合、保護膜１４の厚さが過大になると、紫外線照射によ
る硬化が効率良く行われなくなるので、紫外線照射によ
る硬化を効率良く行なうためには保護膜１４の厚さは５
０μｍ以下とするのが好ましい。
【００２３】なお、基板１１における記録膜１２の形成
方向とは反対方向の面の上には有機材料からなる反射率
調整用のトップコート膜を設けても良く、また、基板１
１と記録膜１２との間には、基板１１を溶媒から保護す
るための中間層を設けても良い。
【００２４】以上のようにして形成される本発明の光記
録媒体には、一般に回転下において、記録光が記録膜に
パルス状に照射される。このとき記録膜の一部が融解、
昇華してピットが形成される。
【００２５】このように形成されたピットは、やはり媒
体の回転下、読出し光の反射光の差を検出することによ
って行われる。 （実験例）以下、実験例を示して本発明をさらに詳細に
説明する。実験例１ 記録膜に含有されるフタロシアニン色素として、下記式
で特定されるフタロシアニンを用い、これをｐＨ６．６
の２，２，３，３−テトラフルオロ−１−プロパノール
中に溶解し、スピンコート法により直径１２０ｍｍ、厚
さ１．２ｍｍのポリカーボネート（ＰＣ）基板１１上に
塗布し、膜厚１０００Åの記録膜１２を形成した。
【００２６】
【化２】 なお、上記式においてＰｃはフタロシアニン環を表わ
す。この記録膜１２の上に、Ａｕからなる光反射膜１３
を、１０００Åの厚さに抵抗加熱型真空蒸着法で成膜
し、この光反射膜１３の上にさらに紫外線硬化型アクリ
レート樹脂からなる保護膜１４を厚さ３μｍに形成して
本発明の光記録媒体（サンプル１）を作成した。
【００２７】一方、上記サンプル１の作成において、ｐ
Ｈ６．６の２，２，３，３−テトラフルオロ−１−プロ
パノールに代えてｐＨ４．４の２，２，３，３−テトラ
フルオロ−１−プロパノールを用いたほかは、上記サン
プル１の作成と同様にして光記録媒体（比較サンプル
１）を作成した。
【００２８】これらのサンプル１および比較サンプル１
について、４５℃−９０％ＲＨの加速試験を行なってＴ
ＦＰのｐＨの違いによる１０８ｎｓ単一周波の劣化につ
いてＲtop 信号、ＲＦamp 信号、キャリアレベルおよび
Ｃ／Ｎ比の各項目の評価を行なった。
【００２９】結果を図２〜図５に示す。実験例２ ｐＨ４．４のＴＦＰおよびｐＨ６．６のＴＦＰのそれぞ
れについて、水（Ｈ2Ｏ）で３６倍に希釈したものにつ
いて下記の条件で分光特性を調べた。
【００３０】結果を図６に示す。 スキャンスピード：３００（７５０）ｎｍ／ｍｉｎ スリット（可視）：２．００ｎｍ スリット（近赤外）：自動制御 ホトマル電圧：自動制御 ＰｂＳ感度：２結果の検討 図２〜図５より、本発明品であるサンプル１は比較サン
プル１に比べていずれの項目においても劣化が少ないこ
とがわかる。
【００３１】また、図６より、ｐＨが４．４であるＴＦ
Ｐは、２００〜２５０ｎｍ付近に吸収をもち、分光特性
が安定しないのに対し、ｐＨが６．６であるＴＦＰは、
２００〜２５０ｎｍ付近に吸収をもたず、分光特性が安
定していることがわかる。
【００３２】これらより、有機色素の溶媒にｐＨ６．０
以上のＴＦＰを用いてなる本発明の光記録媒体は、湿度
による劣化が少なくて耐湿性に優れていることが確認さ
れた。
【００３３】
【発明の効果】本発明は以上のように構成したので、本
発明によれば、特に湿度による劣化が少なくて安定した
性能を発揮するという利点を有する光記録媒体およびそ
のような利点を有する光記録媒体を効率良く得ることの
できる製造方法を提供することができる。
【図面の簡単な説明】
【図１】本発明の光記録媒体の一例を示す部分拡大断面
図である。
【図２】実験例１におけるＲtop 信号と経過時間との関
係を示すグラフである。
【図３】実験例１におけるＲamp 信号と経過時間との関
係を示すグラフである。
【図４】実験例１におけるキャリアレベルと経過時間と
の関係を示すグラフである。
【図５】実験例１におけるＣ／Ｎ比と経過時間との関係
を示すグラフである。
【図６】ｐＨ４．４のＴＦＰおよびｐＨ６．６のＴＦＰ
のそれぞれについて分光特性を示す特性図である。
【符号の説明】
１…光記録媒体 １０…グルーブ １１…基板 １２…記録膜 １３…光反射膜 １４…保護膜
フロントページの続き (72)発明者 田中 覚 埼玉県鶴ケ島市富士見６丁目１番１号 パ イオニア株式会社総合研究所内 (72)発明者 柳沢 秀一 埼玉県鶴ケ島市富士見６丁目１番１号 パ イオニア株式会社総合研究所内 (72)発明者 松井 文雄 埼玉県鶴ケ島市富士見６丁目１番１号 パ イオニア株式会社総合研究所内

Claims (2)

    【特許請求の範囲】
  1. 【請求項１】 光透過性基板と、この光透過性基板の上
    に形成された記録膜と、この記録膜の上に形成された光
    反射膜と、この光反射膜の上に形成された保護膜とを備
    える光記録媒体において、前記記録膜が溶媒にｐＨ６．
    ０以上の2,2,3,3 −テトラフルオロ−１−プロパノール
    （ＴＦＰ）を用いた有機色素により形成されていること
    を特徴とする光記録媒体。
  2. 【請求項２】 光透過性基板上に有機色素からなる記録
    膜を形成する記録膜形成工程と、該記録膜形成工程で形
    成された記録膜上に光反射膜を形成する光反射膜形成工
    程と、該光反射膜形成工程で形成された光反射膜上に保
    護膜を形成する保護膜形成工程とを有する光記録媒体の
    製造方法において、前記記録膜形成工程で使用する有機
    色素の溶媒にｐＨ６．０以上の2,2,3,3 −テトラフルオ
    ロ−１−プロパノール（ＴＦＰ）を用いることを特徴と
    する光記録媒体の製造方法。
JP28534893A 1993-11-15 1993-11-15 光記録媒体およびその製造方法 Pending JPH07137448A (ja)