JPH041276A - 隠蔽性塗料 - Google Patents
隠蔽性塗料Info
- Publication number
- JPH041276A JPH041276A JP2102322A JP10232290A JPH041276A JP H041276 A JPH041276 A JP H041276A JP 2102322 A JP2102322 A JP 2102322A JP 10232290 A JP10232290 A JP 10232290A JP H041276 A JPH041276 A JP H041276A
- Authority
- JP
- Japan
- Prior art keywords
- emulsion
- resin emulsion
- synthetic resin
- foaming
- concealing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は、隠蔽性塗料及びカバーシートに関し、更に詳
しくは、郵便はがき等の紙片の表面の少なくとも一部分
を見ることができないように隠蔽することが可能なカバ
ーシート、及びこのカバーシート等に用いる隠蔽性塗料
に関する。
しくは、郵便はがき等の紙片の表面の少なくとも一部分
を見ることができないように隠蔽することが可能なカバ
ーシート、及びこのカバーシート等に用いる隠蔽性塗料
に関する。
〔従来の技術及び発明が解決しようとする課題〕近年、
銀行の預金残高の通知等の秘密事項を記載した郵便物に
おいて、秘密事項の記載欄を郵送中は隠しておき、正規
の受は取り人が簡単にその内容をみることができるよう
に、簡単に剥離可能なカバーシートを用いた郵便はがき
が開発されている(実開平1−67075号、実公昭5
4−3789号、特開昭64−36490号、特開昭6
436491号、特開昭64−77592号公報等)。
銀行の預金残高の通知等の秘密事項を記載した郵便物に
おいて、秘密事項の記載欄を郵送中は隠しておき、正規
の受は取り人が簡単にその内容をみることができるよう
に、簡単に剥離可能なカバーシートを用いた郵便はがき
が開発されている(実開平1−67075号、実公昭5
4−3789号、特開昭64−36490号、特開昭6
436491号、特開昭64−77592号公報等)。
カバーシートに用いる隠蔽性のあるシートとしては、従
来不透明顔料含有塗液をコートしたコート紙などの不透
明な洋紙類が用いられてきたが、隠蔽性は不十分であっ
た。隠蔽性を上げる試みとしては不透明顔料の添加量を
増す、隠蔽性のある着色剤を用いる、あるいはアルミ箔
の積層等があるが、それぞれ性能不十分、裏うつりかす
る、コストアップ等の問題があり、より効果的な隠蔽塗
料の開発が望まれていた。
来不透明顔料含有塗液をコートしたコート紙などの不透
明な洋紙類が用いられてきたが、隠蔽性は不十分であっ
た。隠蔽性を上げる試みとしては不透明顔料の添加量を
増す、隠蔽性のある着色剤を用いる、あるいはアルミ箔
の積層等があるが、それぞれ性能不十分、裏うつりかす
る、コストアップ等の問題があり、より効果的な隠蔽塗
料の開発が望まれていた。
本発明者らは、上記課題を解決すべく鋭意研究の結果、
合成樹脂エマルションを含む組成物を機械的に発泡させ
て得られるムース状の発泡体からなる塗料を塗布するこ
とにより飛躍的に隠蔽力が向上することを見出し本発明
を完成するに到った。
合成樹脂エマルションを含む組成物を機械的に発泡させ
て得られるムース状の発泡体からなる塗料を塗布するこ
とにより飛躍的に隠蔽力が向上することを見出し本発明
を完成するに到った。
即ち、本発明は、合成樹脂エマルションを含む組成物を
機械的に発泡させて得られる発泡体からなることを特徴
とする隠蔽性塗料、及びこの隠蔽性塗料からなる隠蔽層
を有することを特徴とするカバーシートを提供するもの
である。
機械的に発泡させて得られる発泡体からなることを特徴
とする隠蔽性塗料、及びこの隠蔽性塗料からなる隠蔽層
を有することを特徴とするカバーシートを提供するもの
である。
以下、本発明の隠蔽性塗料について詳細に記す。
本発明で使用される合成樹脂エマルションとしてはポリ
ビニル系エマルション、ポリウレタン系エマルション、
ポリエステル系エマルション等、いずれであっても良い
が、中でもポリビニル系エマルションが製造が容易であ
り好ましい。このポリビニル系エマルションは乳化重合
法を始めとする公知のいずれの重合法を用いたものでも
良いが、発泡剤無添加でも容易に機械発泡でき、さらに
生成発泡体の泡の粒径が小さく、隠蔽力が高く、かつ、
泡安定性が良好なことから、特開昭62−241901
号公報に示される転相法を用いて製造される粒径50〜
300人の自己分散型樹脂エマルションを用いるのが最
も好ましい。
ビニル系エマルション、ポリウレタン系エマルション、
ポリエステル系エマルション等、いずれであっても良い
が、中でもポリビニル系エマルションが製造が容易であ
り好ましい。このポリビニル系エマルションは乳化重合
法を始めとする公知のいずれの重合法を用いたものでも
良いが、発泡剤無添加でも容易に機械発泡でき、さらに
生成発泡体の泡の粒径が小さく、隠蔽力が高く、かつ、
泡安定性が良好なことから、特開昭62−241901
号公報に示される転相法を用いて製造される粒径50〜
300人の自己分散型樹脂エマルションを用いるのが最
も好ましい。
ここで転相法とは、塩生成基又はポリアルキレンオキサ
イド基を有する重合可能な二重結合を有する単量体0.
5〜60重量%と、それと共重合し得る重合可能な二重
結合を有する単量体99.5〜40重量%とを、アルコ
ール系及び/又はケトン系溶剤中で溶液重合を行い均質
な共重合体を得、次にこの共重合体に、必要に応じ中和
剤を加え塩生成基をイオン化し、続いて水を加えた後ア
ルコール系及び/又はケトン系溶剤を留去し水相へ転相
する方法のことをいう。
イド基を有する重合可能な二重結合を有する単量体0.
5〜60重量%と、それと共重合し得る重合可能な二重
結合を有する単量体99.5〜40重量%とを、アルコ
ール系及び/又はケトン系溶剤中で溶液重合を行い均質
な共重合体を得、次にこの共重合体に、必要に応じ中和
剤を加え塩生成基をイオン化し、続いて水を加えた後ア
ルコール系及び/又はケトン系溶剤を留去し水相へ転相
する方法のことをいう。
この様にして得られた粒子径50〜300人の超微粒子
のエマルションは透明乃至半透明のコロイド分散体で、
レーザー光照射でチンダル現象が認められる。
のエマルションは透明乃至半透明のコロイド分散体で、
レーザー光照射でチンダル現象が認められる。
樹脂エマルションの粒径が50人未満のものは親水基を
多く含み乾燥性が劣る。また300人を越えたものでは
発泡時、微細な泡が出来にくいため好ましくない。
多く含み乾燥性が劣る。また300人を越えたものでは
発泡時、微細な泡が出来にくいため好ましくない。
上記の転相法に用いられる塩生成基又はポリアルキレン
オキサイド基を有し重合可能な二重結合を有する単量体
としては、アニオン性単量体、カチオン性単量体、両性
単量体、ノニオン性単量体等がある。更に詳しくはアニ
オン性単量体としては、アクリル酸、メタクリル酸、イ
タコン酸、マレイン酸等の不飽和カルボン酸モノマー、
スチレンスルホン酸、2−アクリルアミド−2−メチル
プロパンスルホン酸等の不飽和スルホン酸モノマー及び
その塩、ビニルホスホン酸、ビニルホスフェート、アシ
ンドホスホキシエチル(メタ)アクリレート等の不飽和
リン酸モノマーがあり、カチオン性単量体としては、不
飽和3級アミン含有モノマー等があり、ノニオン性単量
体としては、不飽和カルボン酸七ツマ−とポリオキシア
ルキレングリコール又は低級アルコールのポリオキシア
ルキレンオキシド付加物とのエステル類、あるいはアリ
ルグリシジルエーテル又は不飽和カルボン酸七ツマ−の
グリシジルエーテルとポリオキシアルキレングリコール
又は低級アルコールのポリオキシアルキレンオキシド付
加物との反応物等があり、両性単量体としては、N −
(3−スルホプロピル)−N−メタクリル酸イソブチル
−N、N−ジメチルアンモニウムベタイン2.N −(
3−スルホプロピル)−N−メタクロリルアミドプロピ
ルーN、 N−ジメチルアンモニウムベタイン、1−(
3−スルホプロピル)−2−ビニルピリジニウムベタイ
ン等がある。
オキサイド基を有し重合可能な二重結合を有する単量体
としては、アニオン性単量体、カチオン性単量体、両性
単量体、ノニオン性単量体等がある。更に詳しくはアニ
オン性単量体としては、アクリル酸、メタクリル酸、イ
タコン酸、マレイン酸等の不飽和カルボン酸モノマー、
スチレンスルホン酸、2−アクリルアミド−2−メチル
プロパンスルホン酸等の不飽和スルホン酸モノマー及び
その塩、ビニルホスホン酸、ビニルホスフェート、アシ
ンドホスホキシエチル(メタ)アクリレート等の不飽和
リン酸モノマーがあり、カチオン性単量体としては、不
飽和3級アミン含有モノマー等があり、ノニオン性単量
体としては、不飽和カルボン酸七ツマ−とポリオキシア
ルキレングリコール又は低級アルコールのポリオキシア
ルキレンオキシド付加物とのエステル類、あるいはアリ
ルグリシジルエーテル又は不飽和カルボン酸七ツマ−の
グリシジルエーテルとポリオキシアルキレングリコール
又は低級アルコールのポリオキシアルキレンオキシド付
加物との反応物等があり、両性単量体としては、N −
(3−スルホプロピル)−N−メタクリル酸イソブチル
−N、N−ジメチルアンモニウムベタイン2.N −(
3−スルホプロピル)−N−メタクロリルアミドプロピ
ルーN、 N−ジメチルアンモニウムベタイン、1−(
3−スルホプロピル)−2−ビニルピリジニウムベタイ
ン等がある。
また上記の転相法に用いられる塩生成基又はポリオキシ
アルキレン基を有する重合可能な二重結合を有する単量
体と共重合しうる単量体としては、アクリル酸メチル、
アクリル酸エチル、アクリル酸n−ブチル、アクリル酸
2−エチルヘキシル、アクリル酸ドデシル、メタクリル
酸メチル、メタクリル酸イソブチル等の(メタ)アクリ
ル酸エステル類、スチレン、ビニルトルエンなどのスチ
レン系モノマー、アクリル酸ヒドロキシエチル、アクリ
ル酸ヒドロキシプロピルなどのヒドロキシ基含有モノマ
ー、N−メチロール(メタ)アクリルアミド、N−ブト
キシメチル(メタ)アクリルアミドなどのN−置換(メ
タ)アクリル糸上ツマ−、アクリル酸グリシジル、メタ
クリル酸グリシジルなどのエポキシ基含有モノマー、並
びにアクリロニトリルなどの1種又は2種以上から選択
することができる。
アルキレン基を有する重合可能な二重結合を有する単量
体と共重合しうる単量体としては、アクリル酸メチル、
アクリル酸エチル、アクリル酸n−ブチル、アクリル酸
2−エチルヘキシル、アクリル酸ドデシル、メタクリル
酸メチル、メタクリル酸イソブチル等の(メタ)アクリ
ル酸エステル類、スチレン、ビニルトルエンなどのスチ
レン系モノマー、アクリル酸ヒドロキシエチル、アクリ
ル酸ヒドロキシプロピルなどのヒドロキシ基含有モノマ
ー、N−メチロール(メタ)アクリルアミド、N−ブト
キシメチル(メタ)アクリルアミドなどのN−置換(メ
タ)アクリル糸上ツマ−、アクリル酸グリシジル、メタ
クリル酸グリシジルなどのエポキシ基含有モノマー、並
びにアクリロニトリルなどの1種又は2種以上から選択
することができる。
本発明に用いられる合成樹脂エマルションの固形分濃度
は20〜30重量%が好ましい。
は20〜30重量%が好ましい。
本発明の合成樹脂エマルションを含む組成物中には上記
の合成樹脂エマルション以外に、本発明の目的を損わな
い範囲で必要に応じて、水性塗料組成物のバインダーと
して使用される樹脂エマルション、水溶性樹脂、ヒドロ
キシエチルセルロース、ポリビニルアルコール、でん粉
等の被膜形成性ポリマー、カオリン、クレータルク、酸
化チタン、炭酸カルシウム等の不透明顔料、起泡助剤、
粘度調整剤、整泡剤、架橋剤、分散剤、さらには着色剤
、充填剤、老化防止剤、防カビ剤、難燃剤等を配合する
ことができる。
の合成樹脂エマルション以外に、本発明の目的を損わな
い範囲で必要に応じて、水性塗料組成物のバインダーと
して使用される樹脂エマルション、水溶性樹脂、ヒドロ
キシエチルセルロース、ポリビニルアルコール、でん粉
等の被膜形成性ポリマー、カオリン、クレータルク、酸
化チタン、炭酸カルシウム等の不透明顔料、起泡助剤、
粘度調整剤、整泡剤、架橋剤、分散剤、さらには着色剤
、充填剤、老化防止剤、防カビ剤、難燃剤等を配合する
ことができる。
このようにして得られる合成樹脂エマルションを含む組
成物を、公知の方法により機械的に発泡させ、均一で微
細な気泡を有する発泡体とする。なお、この発泡に機械
的撹拌を用いるのが一般的であるが、その発泡機の種類
は特に限定されない。気泡の混入量及び大きさについて
は気体のエマルションへの送入量、エマルションの粘度
、撹拌速度等によって調製され、発泡倍率は一般に1.
5〜10倍が好ましい。
成物を、公知の方法により機械的に発泡させ、均一で微
細な気泡を有する発泡体とする。なお、この発泡に機械
的撹拌を用いるのが一般的であるが、その発泡機の種類
は特に限定されない。気泡の混入量及び大きさについて
は気体のエマルションへの送入量、エマルションの粘度
、撹拌速度等によって調製され、発泡倍率は一般に1.
5〜10倍が好ましい。
このようにして発泡させた発泡体からなる隠蔽性塗料を
カバーシート用紙上に塗布、流延あるいは吹きつけた後
乾燥することによって水が除去され、均一で微細な気泡
を有する本発明のカバーシートが得られる。乾燥温度は
通常60〜160°C1好ましくは100〜140″C
であり、エマルションが熱硬化性ポリマーの場合は、さ
らに必要な熱処理を行えばよい。
カバーシート用紙上に塗布、流延あるいは吹きつけた後
乾燥することによって水が除去され、均一で微細な気泡
を有する本発明のカバーシートが得られる。乾燥温度は
通常60〜160°C1好ましくは100〜140″C
であり、エマルションが熱硬化性ポリマーの場合は、さ
らに必要な熱処理を行えばよい。
又、樹脂のガラス転移温度(Tg)が低く、加熱時に減
粘して破泡するような場合は、エマルション温度が上昇
するとゲル化性能を示す、曇点が0〜100°Cで、分
子量が1000以上のオルガノポリシロキサン−ポリオ
キシアルキレン共重合体、フェノール又はアルキルフェ
ノールのホルマリン縮金物のポリオキシアルキレン付加
物等のいわゆる感熱ゲル化剤を用いれば有効な場合もあ
る。
粘して破泡するような場合は、エマルション温度が上昇
するとゲル化性能を示す、曇点が0〜100°Cで、分
子量が1000以上のオルガノポリシロキサン−ポリオ
キシアルキレン共重合体、フェノール又はアルキルフェ
ノールのホルマリン縮金物のポリオキシアルキレン付加
物等のいわゆる感熱ゲル化剤を用いれば有効な場合もあ
る。
〔実施例]
本発明を以下の実施例で詳細に説明するが、本発明はこ
れら実施例になんら限定されるものではない。
れら実施例になんら限定されるものではない。
尚、以下の実施例で用いた本発明に係わる転相法による
自己分散型樹脂エマルション及び乳化重合法によるビニ
ル樹脂エマルションの構成モノマー組成及び平均粒子径
を次の表1に示す。
自己分散型樹脂エマルション及び乳化重合法によるビニ
ル樹脂エマルションの構成モノマー組成及び平均粒子径
を次の表1に示す。
表 1
注) t−BMA ;イソブチルメタクリレート聞^
;メチルメタクリレート 2−EEIA ; 2−エチルへキシルアクリレート
St−スチレン n−BA ;n−ブチルアクリレートAA iア
クリル酸 ガAA iメタクリル酸 転相法により合成したエマルション1〜3は中和剤とし
てトリエチルアミンを使用し、又、乳化重合法で合成し
たエマルション4は乳化剤としてアルキルベンゼンスル
ホン酸ソーダを使用した。
;メチルメタクリレート 2−EEIA ; 2−エチルへキシルアクリレート
St−スチレン n−BA ;n−ブチルアクリレートAA iア
クリル酸 ガAA iメタクリル酸 転相法により合成したエマルション1〜3は中和剤とし
てトリエチルアミンを使用し、又、乳化重合法で合成し
たエマルション4は乳化剤としてアルキルベンゼンスル
ホン酸ソーダを使用した。
実施例1〜4
表2に示したエマルション組成物をステンレスビーカー
に入れ、T、に、オートホモミキサー(特殊機化工業型
)を用い3500 rpmで1分間撹拌して発泡体を得
、これを文字が印刷されたコート紙上にバーコーターを
用いて厚さ100μで塗布し、熱風乾燥機(150“C
110分)で乾燥した。
に入れ、T、に、オートホモミキサー(特殊機化工業型
)を用い3500 rpmで1分間撹拌して発泡体を得
、これを文字が印刷されたコート紙上にバーコーターを
用いて厚さ100μで塗布し、熱風乾燥機(150“C
110分)で乾燥した。
次でポリエチレンフィルム(30μ)を感圧接着剤を用
いて貼り合わせてカバーシートを得た。
いて貼り合わせてカバーシートを得た。
このカバーシートについて隠蔽性を肉眼で観察し、下記
基準で評価した。
基準で評価した。
結果を表2に示す。
〈隠蔽性評価基準〉
◎:文字が見えない
○:わずかに文字が見える
△:かなり文字が見える
×:隠蔽性なし
比較例1〜2
エマルション組成物を発泡せずに塗布する以外は実施例
1と同様にしてカバーシートを得、同様に隠蔽性を評価
した。
1と同様にしてカバーシートを得、同様に隠蔽性を評価
した。
結果を表2に示す。
注)
*1:ラストラ90(フリーボード社製)*2 : W
−1o (石屋産業■製)傘3:ポイズ530(花王■
製) 本4ニステアリン酸アンモニウム
−1o (石屋産業■製)傘3:ポイズ530(花王■
製) 本4ニステアリン酸アンモニウム
Claims (1)
- 【特許請求の範囲】 1、合成樹脂エマルションを含む組成物を機械的に発泡
させて得られる発泡体からなることを特徴とする隠蔽性
塗料。 2、合成樹脂エマルションが平均粒子径50〜300オ
ングストロームの自己分散型樹脂エマルションである請
求項1記載の隠蔽性塗料。 3、請求項1又は2記載の隠蔽性塗料からなる隠蔽層を
有することを特徴とするカバーシート。