JPH02300388A - 壁紙 - Google Patents
壁紙Info
- Publication number
- JPH02300388A JPH02300388A JP11878089A JP11878089A JPH02300388A JP H02300388 A JPH02300388 A JP H02300388A JP 11878089 A JP11878089 A JP 11878089A JP 11878089 A JP11878089 A JP 11878089A JP H02300388 A JPH02300388 A JP H02300388A
- Authority
- JP
- Japan
- Prior art keywords
- fluorine
- polymer
- acrylic polymer
- contained
- copolymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
〔産業上の利用分野〕
本発明は、壁紙に関するものである。
[従来の技術]
従来壁紙には、耐久性、防汚性を向上せしめる目的で、
アクリル樹脂など比較的耐候性の優れた被覆材で保護コ
ートしたものが多く利用されている。 [発明の解決しようとする課題〕 従来、防汚性の優れた壁紙としてアクリル樹脂をコーテ
ィングしたものがあったが、耐久性が乏しく、長期間の
使用に充分耐え得るものではなかうた。 本発明は、上記従来技術の問題点を解消する、即ち、耐
候性に優れかつ防汚性が長期に保たれ、保護コートの密
着性の優れた壁紙を提供することを目的とするものであ
る。
アクリル樹脂など比較的耐候性の優れた被覆材で保護コ
ートしたものが多く利用されている。 [発明の解決しようとする課題〕 従来、防汚性の優れた壁紙としてアクリル樹脂をコーテ
ィングしたものがあったが、耐久性が乏しく、長期間の
使用に充分耐え得るものではなかうた。 本発明は、上記従来技術の問題点を解消する、即ち、耐
候性に優れかつ防汚性が長期に保たれ、保護コートの密
着性の優れた壁紙を提供することを目的とするものであ
る。
本発明は、前述の課題を解決するためになされたもので
あり7、熱可塑性樹脂シート上に、架橋部位を有する含
フッ素共重合体(a)および(a)と相溶するアクリル
系重合体(b)を主成分とする塗料の被膜を形成してな
る壁紙を提供するものである。 本発明の壁紙の基材としての熱可塑性樹脂としては、塩
化ビニル樹脂、ポリエチレン樹脂、ポリエステル樹脂な
どが例示される。中でも、塩゛化ビニル樹脂、特に軟質
塩化ビニル樹脂が最も一般に用いられている。かかる塩
化ビニル樹脂としては、塩化ビニルの単独重合体のほか
に、塩化ビニルと酢酸ビニル、エチレン、プロピレン、
アクリル酸エステル、メタクリル酸エステルなどの単量
体の少なくとも一種の40f!′量%以下、好ましくは
30重量%以下の量との共重合体、及びこれら単独重合
体または共重合体に対して相溶性のある重合体、例えば
、エチレン−酢酸ビニル共重合体、塩化ビニル−酢酸ビ
ニル共重合体などがブレンドされていてもよい。 また、塩化ビニル樹脂には適当量の可塑剤が配合され、
軟質塩化ビニル樹脂として使用されることが多い、可塑
剤の配合量としては、塩化ビニル樹脂100重量部当た
り、30〜70重量部程の範囲が好ましく採用される。 また、可塑剤としては、フタル酸ジブチル、フタル酸ジ
オクチル、アジピン酸ジイソデシル、リン酸トリクレジ
ル、エポキシ化大豆油、エポキシ化アマニ油などが例示
される。また、塩化ビニル樹脂には、滑剤、酸化防止剤
、帯電防止剤、熱安定剤、着色剤、難燃剤などの通常の
添加物が添加されていてもよい。 さらに、塩化ビニル樹脂には防曇を目的として界面活性
剤が添加されていてもよい。かかる界面活性剤としては
ノニオン系界面活性剤が好ましく採用される。 本発明において、上記熱可塑性樹脂シート上に被膜を形
成する塗料としては、架橋部位を有する含フッ素共重合
体(a)及び(a)と相溶するアクリル系重合体(b)
を主成分とするものが採用される。 ここで、架橋部位を有する含フッ素共重合体(a)とし
ては、フルオロオレフィン単位に基づくフッ素含有量が
10重量%以上である溶剤可溶性含フッ素共重合体が好
ましく採用される。 上記の(a)の含フッ素共重合体はフルオロオレフィン
単位に基づ(フッ素含有量が10重量%以上、好ましく
は10〜70重量%、さらに好ましくは15〜50重量
%であって、未硬化の状態でテトラヒドロフラン中で測
定される固有粘度が0、O1〜4.0dl/ gのもの
が用いられる。而して、フッ素含有量が10重量%より
少ないと目的とする耐候性の向上効果は低下する。また
、固有粘度は上記の範囲において塗料としての塗装性が
良好となり、しかも形成される被膜の物性も優れたもの
となる。かかる含フッ素系重合体としては、フルオロオ
レフィンおよびフルオロオレフィンと共重合可能な共単
量体として、エチレン性不飽和化合物との共重合体が好
ましく採用される。 かかるフルオロオレフィンとしてはテトラフルオロエチ
レン、クロロトリフルオロエチレン、トリフルオロエチ
レン、フッ化ビニリデン、ヘキサフルオロプロピレン、
ペンタフルオロプロピレンなどが例示される。これらの
うち、特にテトラフルオロエチレン、クロロトリフルオ
ロエチレン、フッ化ビニリデン、ヘキサフルオロプロピ
レンが好ましく採用される。また、フルオロオレフィン
と共重合可能な単量体としてのエチレン性不飽和化合物
としては、オレフィン類、ビニルエーテル類、ビニルエ
ステル類、アリルエーテル類、アリルエステル類、アク
リロイル基含有の化合物、メタアクリロイル基含有の化
合物などが例示される。 これらのうち、特にフルオロオレフィン類との共重合性
に優れるオレフィン類、ビニルエーテル類、ビニルエス
テル類、アリルエーテル類の炭素数1−10程度の直鎖
状、分岐状あるいは脂環状のアルキル基を有するものが
好ましい。 含フッ素共重合体(a)において、フルオロオレフィン
に基づく、単位は30〜70モル%含有するのが好まし
く、30モル%以下であると耐候性の向上効果は充分で
なく、70モル%を越えると溶剤に対する溶解性が低下
する傾向があり、塗料としての塗布作業に支障を生ずる
供とがある。 また、共重合体において、フル才ロオレフィンおよびエ
チレン性不飽和化合物は、それぞれ単独であってもよい
し、二種以上が併用されたものであってもよい。 本発明の塗料の主要構成成分における(a)の含フッ素
共重合体において架橋部位を有するものは、他の成分、
硬化剤、あるいは共重合体間で反応して三次元網状構造
を形成し、被膜の耐溶剤性、耐酸、耐アルカリ性が向上
するという好ましい結果を与えるので架橋部位を有する
ものが好適に採用される。 而して、架橋部位としては、水酸基、カルボン酸基、酸
アミド基、アミノ基、メルカプト基などの活性水素含有
基や、エポキシ基、炭素−炭素不飽和基、臭素、ヨウ素
などの活性ハロゲン基などが挙げられる。これらのうち
、活性水素含有基は通常硬化剤として使用されるインシ
アネート系硬化剤、アミノブラスト系硬化剤などとの反
応性に優れるという点において好ましく、特に水酸基が
好適である。 かかる架橋部位の共重合体への導入方法は、例えばヒド
ロキシアルキルビニルエーテル、ヒドロキシアルキルア
リールエーテル、ヒドロキシアリールビニルエーテル、
ヒドロキシアルキルアリルエーテル、ヒドロキシアルキ
ルビニルエステル、グリシジルビニルエーテル、アクリ
ル酸、メタクリル酸、アリールビニールエーテル、ジア
ミノエチルビニルエーテルなどの架橋反応部位を有する
単量体を共重合せしめる、あるいは含フッ素共重合体に
酸無水物、イソシアナート、アルキル(メタ)アクリレ
ートなどを反応させて付加せしめる方法などが採用され
る。また、共重合体の一部を分解せしめる方法として、
加水分解可能なエステル基を有する単量体を共重合せし
めた後、共重合体を加水分解することにより共重合体中
にカルボン酸または水酸基を生成せしめる方法も採用さ
れる。さらに、水酸基含有共重合体にコハク酸なとの二
価カルボン酸無水物を反応させてカルボン酸基を導入す
る方法も採用される。 本発明の塗料の主要構成成分である前記含フッ素共重合
体(a)と相溶するアクリル系重合体(b)は、アクリ
ル酸またはメタクリル酸の炭素数1〜12のアルコール
エステルであって、分子量500〜go、 oooのア
クリル系重合体である。かかるアクリル系重合体として
は、メチルアクリレート、メチルメタクリレート、エチ
ルアクリレート、エチルメタクリレート、プロピルアク
リレート、プロピルメタクリレート、n−ブチルメタク
リレート、1so−ブチルメタクリレート、tert−
ブチルメタクリレート、n−ブチルアクリレートおよび
tert−ブチルアクリレートアクリロニトリル、メタ
アクリロニトリルなどが例示される。また、好ましくは
、これら単量体の2種以上よりなる共重合体、あるいは
上記例示以外のアクリル酸のアルコールエステル、スチ
レン、マレイン酸、ビニルエステル類(酢酸ビニルなど
)、ビニルシランなどとの共重合体が使用される。さら
に好ましくは、アクリル系重合体において、架橋部位を
有する重合体は含フッ素共重合体の架橋部位との反応に
よって架橋され、塗料の被膜は三次元網状構造となり、
優゛れた特性を示す。 ここで、(b)のアクリル系重合体において架橋部位と
しては、水酸基、グリシジル基、アミド基、シラノール
基などであるのが好適であり、例えば水酸基の導入は、
2−ヒドロキシエチルアクリレート、2−ヒドロキシエ
チルメタクリレート、2−ヒドロキシプロピルアクリレ
ート、2−ヒドロキシメタクリレート、3−ヒドロキシ
プロピルアクリレート、3−ヒドロキシプロピルメタク
リレート、2−ヒドロキシブチルアクリレート、2−ヒ
ドロキシブチルメタクリレート、3−ヒドロキシブチル
アクリレート、3−ヒドロキシブチルメタクリレート、
4−ヒドロキシブチルアクリレート、4−ヒドロキシブ
チルメタクリレート、3−クロロ−2−ヒドロキシプロ
ピルアクリレート、3−クロロ−2−ヒドロキシプロピ
ルメタクリレートなど、またグリシジル基の導入はグリ
シジルアクリレート、グリシジルメタクリレート、 (
β−メチル)グリシジルアクリレート、(β−メチ′ル
)グリシジルメタクリレートなど、さらにアミド基の導
入はアクリルアミド、メタクリルアミド、ジメチルアク
リルアミド、ジメチルメタクリルアミド、N −ter
t−ブチルアクリルアミド、N −tert−ブチルメ
タクリルアミド、N−オクチルアクリルアミド、N−オ
クチルメタクリルアミド、ジアセトンアクリルアミド、
ジアセトンメタクリルアミドなど、またシラノール基の
導入はビニルシランなどの単量体と前記のアクリル系重
合体あるいは共重合体を与える共単量体とを共重合させ
ることによって行なわれる。 また、シラノール基は、水酸基含有アクリル系重合体に
イソシアネートシランまたはシラン系カップリング剤な
どを付加する方法でも導入することができる。 ここで、(b)のアクリル系重合体は、架橋部位を有す
る重合体と架橋部位を有さない重合体との混合物であっ
てもよく、架橋部位を有さない重合体とは、上記例示の
水酸基、グリシジル基、アミド基などを有する単量体と
の共重合体を含むものではない、而して架橋部位を有さ
ないアクリル系重合体の割合は、好ましくは架橋部位を
有するアクリル系重合体に対し50重量%までである。 さらに、塗料の主要構成成分である(a)および(b)
に対し硬化剤を配合することは勿論可能であり、(a)
の含フッ素共重合体および(b)のアクリル系重合体と
相溶し、それらを硬化せしめるものが用いられる。かか
る硬化剤としては、ポリイソシアナート系、例えばヘキ
サメチレンジイソシアナート、インホロンジイソシアナ
ートなどの無黄変ジイソシアナート類ならびにその付加
物、イソシアネート基をフェノールなどのブロック化剤
でブロックしたブロックイソシアネートなどが好適なも
のとして採用し得る。また、メラミン系、金属アルコキ
シド系、尿素樹脂系、多塩基酸系、エポキシ系、シラノ
ール系など種々の硬化剤も使用可能である。ここで、含
フッ素共重合体(a)の架橋部位が水酸基である場合、
ポリイソシアナート系、金属アルコキシド系が好適であ
る。またメラミン系硬化剤としては特にメタノール、エ
タノール、プロパツール、ブタノールなどの低級アルコ
ールの1種または2種以上により部分的にエーテル化さ
れたメラミンは好適なものとして採用される。かかる硬
化剤は架橋部位を有する共重合体あるいは重合体の三次
網目構造の形成に極めて有用な作用を与える。 硬化剤とともに硬化を促進させる目的から、触媒が併用
されてもよく、かかる硬化助剤として例えばイソシアネ
ート系硬化剤にジブチルチンラウレートが、またメラミ
ン系硬化剤にパラトルエンスルホン酸系などの触媒が含
フッ素共重合体100重量部に対し0.001〜2重量
部の割合で用いられる。 本発明の塗料における主要構成成分のそれぞれの割合は
、(a)の含フッ素共重合体30〜90重量%、(b)
のアクリル系重合体lθ〜70重量%・であるのが好適
である。含フッ素共重合体が少ないと、フッ素含有量が
減少し、目的とする耐候性の向上効果が達成されず、一
方アクリル系重合体が少ないと、基材への接着性が低下
する。 而して、含フッ素共重合体およびアクリル系重合体それ
ぞれは上記の割合の範囲内において1種に限定されるこ
となく2IIi以上を併用してもよいことは勿論である
0次に硬化剤は含フッ素共重合体とアクリル系重合体の
合計量に対し0〜20重量%の割合で用いられる。 塗料には、主要構成成分の他に、含フッ素共重合体およ
びアクリル系重合体の合計量に対し0.5〜3%の紫外
線吸収剤が含まれることによって耐候性をさらに向上さ
せることが可能である。かかる紫外線吸収剤としては、
従来公知ないし周知の2−ヒドロキシベンゾフェノン、
2.4−ヒドロキシベンゾフェノン、2−ヒドロキシド
4−n−オクトキシベンゾフェノン、2−ヒドロキシ−
4−(1−メチル−2−ヒドロキシ)エトキシベンゾフ
ェノン、2−ヒドロキシー4−(2−ヒドロキシ−3−
メタクリロキシ)プロポキシベンゾフェノンなどのベン
ゾフェノン系あるいは2− (2’ −ヒドロキシ−5
゛−メチルフェニル)ベンゾトリアゾール、2− (2
’−ヒドロキシ−3゛、5°−ジ−t−ブチルフェニル
)ベンゾトリアゾールなどのベンゾトリアゾール系のも
のが単独または併用して用いられる。 さらに、かかる塗料にはフルオロアルキル基を有するア
クリル系重合体(c)を添加し、プラスチックシートの
撥水性などを向上せしめてもよい、かかるフルオロアル
キル基を有するアクリル系重合体(c)としては、前記
含フッ素共重合体(a)またはアクリル系重合体(b)
と同様の架橋部位を有するものを採用すると、撥水性な
どが長期にわたって保持されるため好ましい。 また、かかるフルオロアルキル基を有するアクリル系重
合体(c)の添加量は、含フッ素共重合体(a)および
アクリル系重合体(b)の合計100重量部当たりo、
i〜30重量部程度の範囲で採用することが好ましい。 その他、特性の向上を目的として、塗料には、例えば消
泡剤、帯電防止剤、顔料、分散安定剤、粘度調節剤、レ
ベリング剤、ゲル化防止剤などの添加剤を配合すること
もできる。顔料の配合は被膜の陰蔽性という効果を有す
る。 また、必要な折り曲げ密着性などを得る目的でブライマ
ーを使用することももちろん可能である。 本発明の塗料は前記の如き、含フッ素共重合体(a)お
よびアクリル系重合体(b)などの主要構成成分さらに
必要に応じ硬化剤、紫外線吸収剤、フルオロアルキル基
を有するアクリル系重合体(c)その他の添加剤を有機
溶媒に溶解せしめることによって得られるが、用いられ
る溶媒としては例えばトルエン、キシレンなどの芳香族
炭化水素類、プロパツール、ブタノールなどのアルコー
ル類、酢酸エチル、酢酸ブチルなどのエステル類、メチ
ルエチルケトン、メチルイソブチルケトンなどのケトン
類、エチルセロソルブの如きグリコールエーテル類、さ
らに市販の各種ジンナール類なと、種々の一般有機溶媒
である。塗料成分の濃度としては1〜60重量%、好ま
しくは5〜50重量%に調製されてなるのが被膜を形成
する作業性において好適である。 塗料の調製に際しては、例えばボールミル。 ペイントシェーカー、サンドミル、ジェットミル、三本
ロール、ニーダ−などの通常の塗料化に用いられる種々
の機器を用いることによって行なわれ、特に限定されな
い、この際に、前記例示の如き添加剤を添加することが
できる。 本発明において、熱可塑性樹脂シートに塗料の被膜を形
成する方法は、成形体上に塗料をへヶ塗り、スプレー吹
付、フローコータなどにより塗布する、あるいは塗料中
にシートを浸漬することによって塗布し、溶媒を揮散さ
せるに充分な乾燥を行ない、次に加熱あるいは室温で放
置せしめて被膜とする。この際の加熱処理は。 成形体の変形しない温度以下とし、例えば60℃にて1
0分間の処理で充分である。 形成される塗料被膜の厚さは2〜1100uにおいて充
分なる効果が認められる。被膜の厚さの調製は、塗料の
成分濃度と塗布条件によって決定されるが、多層被膜に
形成されても何ら問題ない、成形体の形状も何ら限定さ
れない。 [実施例] 実施例1〜11.比較例1〜3 第1表に示す組成よりなる塗料No、1−13を調整し
た。壁紙の表面に塗料No、1=13をグラビアコータ
ーにより形成される被膜の膜厚が5μmになるように調
整して塗布し、室温にて乾燥後60℃にて10分間加熱
することによって硬化被膜を形成した。 このようにして被膜を形成したシートについて、次の評
価試験を行なった結果を第2表に示した。 接触角:水及びn−へキサデンカンの接触角を測定した
。 密着性:被膜の密着性をASTM−3359の方法に従
い ■初期、■温水浸漬後(60℃×30日)、■サンシャ
インウェザーメーター1000時間処理後のそれぞれで
測定し残った マス目数で評価する。 耐候性:サンシャインウェザ−メータ1000時間処理
前後においてカラー測定機(ス ガ試験機社製= 5M−3)で測定し、その黄変劣化を
処理前後の差(ΔE)とし て求める。 第1表中、含フッ素共重合体の F−Aは、 TFE / HBVE/ n−RYE =
48.1/12.5/39.4(重量%)の割合で共
重合であり、テトラヒドロフラン中30℃で測定される
固有粘度([η]という)が0.15 (di/g)で
ある共重合体、(以下、同じ) F−8は、CTFE/ I(BVE/ CHVE/ E
VE = 56.415.7/12.4/25.5.
[η] =0.21/di/g 。 F−Cは、HFP / HBVE/ n−BYE =
66、7/8.0/25.3゜[η] =0.08/d
i/g 。 F−Dは、TFE / C8mCOOCH=CH1/C
H1=CHCH10CHICH,0H=53.7/23
.1/23.2. [η] =0.18dl/g。 F−Eは、CTFE/EVE /HBVE/ヘオバ9
= 39.4717.2/9.5/33.9. [η
] = 0.40dl/g。 F−Fは、TFE / EVE / HBVE/ C)
lt”cHOcHtcFscFtH=57.0/22.
4/10.8/9.8. [η] =+ O,1Od
l/g。 (TFEはテトラフルオロエチレン、HBVEはω−ヒ
ドロキシブチルビニルエーテル、n−BYEはn−ブチ
ルビニルエーテル、CTFEはクロロトリフルオロエチ
レン、CHVEはシクロヘキシルビニルエーテル、EV
Eはエチルビニルエーテル、 HFPはへキサフルオロ
プロピレン、ベオバ9はシェル化学社製、炭素数9の分
岐上のアルキル基を有するビニルエーテルである。) ト1は、1so−ブチルメタクリレート/n−ブチルア
クリレート/2−ヒドロキシエチルメタクリレート=7
/2/l(モル比)の割合で共重合した共重合体(以下
同じ)。 M−2は、メチルアクリレート/n−ブチルアクリレー
ト/グリシジルアクリレート=8/l/1 。 M−3は、n−ブチルメタクリレート/Lso−ブチル
メタクリレート/アクリロニトリル/2−ヒドロキシエ
チルメタクリレート= 1/7/1/10ト4は、メチ
ルメタクリレート/n−ブチルメタクリレート=515
゜ を表わす。 フルオロアルキル基含有アクリル重合体はCH*=CH
C00CHxCHt (CFt) I oF/1so−
ブチルメタクリレート/n−ブチルアクリレート/2−
ヒドロキエチルメタクリレート= 20/60/10/
10重量%の共重合体。 イソシアネート硬化剤は、コロネートEH(日本ポリウ
レタン社製)。 紫外線吸収剤は、バイオソーブ130 (共同薬品製
)である。 第2表 比較例2は、塗料の被膜が形成されていない壁紙である
。 実施例12 実施例1において、乾燥条件を120℃、1分間とする
他は同様にして行なったところ、はぼ実施例1と同様の
効果が得られた。 【発明の効果コ 本発明の壁紙は、特定の塗料の被膜が良好な密着性を保
持して、形成されているために、耐久性、防染性にきわ
めて優れたものである。
あり7、熱可塑性樹脂シート上に、架橋部位を有する含
フッ素共重合体(a)および(a)と相溶するアクリル
系重合体(b)を主成分とする塗料の被膜を形成してな
る壁紙を提供するものである。 本発明の壁紙の基材としての熱可塑性樹脂としては、塩
化ビニル樹脂、ポリエチレン樹脂、ポリエステル樹脂な
どが例示される。中でも、塩゛化ビニル樹脂、特に軟質
塩化ビニル樹脂が最も一般に用いられている。かかる塩
化ビニル樹脂としては、塩化ビニルの単独重合体のほか
に、塩化ビニルと酢酸ビニル、エチレン、プロピレン、
アクリル酸エステル、メタクリル酸エステルなどの単量
体の少なくとも一種の40f!′量%以下、好ましくは
30重量%以下の量との共重合体、及びこれら単独重合
体または共重合体に対して相溶性のある重合体、例えば
、エチレン−酢酸ビニル共重合体、塩化ビニル−酢酸ビ
ニル共重合体などがブレンドされていてもよい。 また、塩化ビニル樹脂には適当量の可塑剤が配合され、
軟質塩化ビニル樹脂として使用されることが多い、可塑
剤の配合量としては、塩化ビニル樹脂100重量部当た
り、30〜70重量部程の範囲が好ましく採用される。 また、可塑剤としては、フタル酸ジブチル、フタル酸ジ
オクチル、アジピン酸ジイソデシル、リン酸トリクレジ
ル、エポキシ化大豆油、エポキシ化アマニ油などが例示
される。また、塩化ビニル樹脂には、滑剤、酸化防止剤
、帯電防止剤、熱安定剤、着色剤、難燃剤などの通常の
添加物が添加されていてもよい。 さらに、塩化ビニル樹脂には防曇を目的として界面活性
剤が添加されていてもよい。かかる界面活性剤としては
ノニオン系界面活性剤が好ましく採用される。 本発明において、上記熱可塑性樹脂シート上に被膜を形
成する塗料としては、架橋部位を有する含フッ素共重合
体(a)及び(a)と相溶するアクリル系重合体(b)
を主成分とするものが採用される。 ここで、架橋部位を有する含フッ素共重合体(a)とし
ては、フルオロオレフィン単位に基づくフッ素含有量が
10重量%以上である溶剤可溶性含フッ素共重合体が好
ましく採用される。 上記の(a)の含フッ素共重合体はフルオロオレフィン
単位に基づ(フッ素含有量が10重量%以上、好ましく
は10〜70重量%、さらに好ましくは15〜50重量
%であって、未硬化の状態でテトラヒドロフラン中で測
定される固有粘度が0、O1〜4.0dl/ gのもの
が用いられる。而して、フッ素含有量が10重量%より
少ないと目的とする耐候性の向上効果は低下する。また
、固有粘度は上記の範囲において塗料としての塗装性が
良好となり、しかも形成される被膜の物性も優れたもの
となる。かかる含フッ素系重合体としては、フルオロオ
レフィンおよびフルオロオレフィンと共重合可能な共単
量体として、エチレン性不飽和化合物との共重合体が好
ましく採用される。 かかるフルオロオレフィンとしてはテトラフルオロエチ
レン、クロロトリフルオロエチレン、トリフルオロエチ
レン、フッ化ビニリデン、ヘキサフルオロプロピレン、
ペンタフルオロプロピレンなどが例示される。これらの
うち、特にテトラフルオロエチレン、クロロトリフルオ
ロエチレン、フッ化ビニリデン、ヘキサフルオロプロピ
レンが好ましく採用される。また、フルオロオレフィン
と共重合可能な単量体としてのエチレン性不飽和化合物
としては、オレフィン類、ビニルエーテル類、ビニルエ
ステル類、アリルエーテル類、アリルエステル類、アク
リロイル基含有の化合物、メタアクリロイル基含有の化
合物などが例示される。 これらのうち、特にフルオロオレフィン類との共重合性
に優れるオレフィン類、ビニルエーテル類、ビニルエス
テル類、アリルエーテル類の炭素数1−10程度の直鎖
状、分岐状あるいは脂環状のアルキル基を有するものが
好ましい。 含フッ素共重合体(a)において、フルオロオレフィン
に基づく、単位は30〜70モル%含有するのが好まし
く、30モル%以下であると耐候性の向上効果は充分で
なく、70モル%を越えると溶剤に対する溶解性が低下
する傾向があり、塗料としての塗布作業に支障を生ずる
供とがある。 また、共重合体において、フル才ロオレフィンおよびエ
チレン性不飽和化合物は、それぞれ単独であってもよい
し、二種以上が併用されたものであってもよい。 本発明の塗料の主要構成成分における(a)の含フッ素
共重合体において架橋部位を有するものは、他の成分、
硬化剤、あるいは共重合体間で反応して三次元網状構造
を形成し、被膜の耐溶剤性、耐酸、耐アルカリ性が向上
するという好ましい結果を与えるので架橋部位を有する
ものが好適に採用される。 而して、架橋部位としては、水酸基、カルボン酸基、酸
アミド基、アミノ基、メルカプト基などの活性水素含有
基や、エポキシ基、炭素−炭素不飽和基、臭素、ヨウ素
などの活性ハロゲン基などが挙げられる。これらのうち
、活性水素含有基は通常硬化剤として使用されるインシ
アネート系硬化剤、アミノブラスト系硬化剤などとの反
応性に優れるという点において好ましく、特に水酸基が
好適である。 かかる架橋部位の共重合体への導入方法は、例えばヒド
ロキシアルキルビニルエーテル、ヒドロキシアルキルア
リールエーテル、ヒドロキシアリールビニルエーテル、
ヒドロキシアルキルアリルエーテル、ヒドロキシアルキ
ルビニルエステル、グリシジルビニルエーテル、アクリ
ル酸、メタクリル酸、アリールビニールエーテル、ジア
ミノエチルビニルエーテルなどの架橋反応部位を有する
単量体を共重合せしめる、あるいは含フッ素共重合体に
酸無水物、イソシアナート、アルキル(メタ)アクリレ
ートなどを反応させて付加せしめる方法などが採用され
る。また、共重合体の一部を分解せしめる方法として、
加水分解可能なエステル基を有する単量体を共重合せし
めた後、共重合体を加水分解することにより共重合体中
にカルボン酸または水酸基を生成せしめる方法も採用さ
れる。さらに、水酸基含有共重合体にコハク酸なとの二
価カルボン酸無水物を反応させてカルボン酸基を導入す
る方法も採用される。 本発明の塗料の主要構成成分である前記含フッ素共重合
体(a)と相溶するアクリル系重合体(b)は、アクリ
ル酸またはメタクリル酸の炭素数1〜12のアルコール
エステルであって、分子量500〜go、 oooのア
クリル系重合体である。かかるアクリル系重合体として
は、メチルアクリレート、メチルメタクリレート、エチ
ルアクリレート、エチルメタクリレート、プロピルアク
リレート、プロピルメタクリレート、n−ブチルメタク
リレート、1so−ブチルメタクリレート、tert−
ブチルメタクリレート、n−ブチルアクリレートおよび
tert−ブチルアクリレートアクリロニトリル、メタ
アクリロニトリルなどが例示される。また、好ましくは
、これら単量体の2種以上よりなる共重合体、あるいは
上記例示以外のアクリル酸のアルコールエステル、スチ
レン、マレイン酸、ビニルエステル類(酢酸ビニルなど
)、ビニルシランなどとの共重合体が使用される。さら
に好ましくは、アクリル系重合体において、架橋部位を
有する重合体は含フッ素共重合体の架橋部位との反応に
よって架橋され、塗料の被膜は三次元網状構造となり、
優゛れた特性を示す。 ここで、(b)のアクリル系重合体において架橋部位と
しては、水酸基、グリシジル基、アミド基、シラノール
基などであるのが好適であり、例えば水酸基の導入は、
2−ヒドロキシエチルアクリレート、2−ヒドロキシエ
チルメタクリレート、2−ヒドロキシプロピルアクリレ
ート、2−ヒドロキシメタクリレート、3−ヒドロキシ
プロピルアクリレート、3−ヒドロキシプロピルメタク
リレート、2−ヒドロキシブチルアクリレート、2−ヒ
ドロキシブチルメタクリレート、3−ヒドロキシブチル
アクリレート、3−ヒドロキシブチルメタクリレート、
4−ヒドロキシブチルアクリレート、4−ヒドロキシブ
チルメタクリレート、3−クロロ−2−ヒドロキシプロ
ピルアクリレート、3−クロロ−2−ヒドロキシプロピ
ルメタクリレートなど、またグリシジル基の導入はグリ
シジルアクリレート、グリシジルメタクリレート、 (
β−メチル)グリシジルアクリレート、(β−メチ′ル
)グリシジルメタクリレートなど、さらにアミド基の導
入はアクリルアミド、メタクリルアミド、ジメチルアク
リルアミド、ジメチルメタクリルアミド、N −ter
t−ブチルアクリルアミド、N −tert−ブチルメ
タクリルアミド、N−オクチルアクリルアミド、N−オ
クチルメタクリルアミド、ジアセトンアクリルアミド、
ジアセトンメタクリルアミドなど、またシラノール基の
導入はビニルシランなどの単量体と前記のアクリル系重
合体あるいは共重合体を与える共単量体とを共重合させ
ることによって行なわれる。 また、シラノール基は、水酸基含有アクリル系重合体に
イソシアネートシランまたはシラン系カップリング剤な
どを付加する方法でも導入することができる。 ここで、(b)のアクリル系重合体は、架橋部位を有す
る重合体と架橋部位を有さない重合体との混合物であっ
てもよく、架橋部位を有さない重合体とは、上記例示の
水酸基、グリシジル基、アミド基などを有する単量体と
の共重合体を含むものではない、而して架橋部位を有さ
ないアクリル系重合体の割合は、好ましくは架橋部位を
有するアクリル系重合体に対し50重量%までである。 さらに、塗料の主要構成成分である(a)および(b)
に対し硬化剤を配合することは勿論可能であり、(a)
の含フッ素共重合体および(b)のアクリル系重合体と
相溶し、それらを硬化せしめるものが用いられる。かか
る硬化剤としては、ポリイソシアナート系、例えばヘキ
サメチレンジイソシアナート、インホロンジイソシアナ
ートなどの無黄変ジイソシアナート類ならびにその付加
物、イソシアネート基をフェノールなどのブロック化剤
でブロックしたブロックイソシアネートなどが好適なも
のとして採用し得る。また、メラミン系、金属アルコキ
シド系、尿素樹脂系、多塩基酸系、エポキシ系、シラノ
ール系など種々の硬化剤も使用可能である。ここで、含
フッ素共重合体(a)の架橋部位が水酸基である場合、
ポリイソシアナート系、金属アルコキシド系が好適であ
る。またメラミン系硬化剤としては特にメタノール、エ
タノール、プロパツール、ブタノールなどの低級アルコ
ールの1種または2種以上により部分的にエーテル化さ
れたメラミンは好適なものとして採用される。かかる硬
化剤は架橋部位を有する共重合体あるいは重合体の三次
網目構造の形成に極めて有用な作用を与える。 硬化剤とともに硬化を促進させる目的から、触媒が併用
されてもよく、かかる硬化助剤として例えばイソシアネ
ート系硬化剤にジブチルチンラウレートが、またメラミ
ン系硬化剤にパラトルエンスルホン酸系などの触媒が含
フッ素共重合体100重量部に対し0.001〜2重量
部の割合で用いられる。 本発明の塗料における主要構成成分のそれぞれの割合は
、(a)の含フッ素共重合体30〜90重量%、(b)
のアクリル系重合体lθ〜70重量%・であるのが好適
である。含フッ素共重合体が少ないと、フッ素含有量が
減少し、目的とする耐候性の向上効果が達成されず、一
方アクリル系重合体が少ないと、基材への接着性が低下
する。 而して、含フッ素共重合体およびアクリル系重合体それ
ぞれは上記の割合の範囲内において1種に限定されるこ
となく2IIi以上を併用してもよいことは勿論である
0次に硬化剤は含フッ素共重合体とアクリル系重合体の
合計量に対し0〜20重量%の割合で用いられる。 塗料には、主要構成成分の他に、含フッ素共重合体およ
びアクリル系重合体の合計量に対し0.5〜3%の紫外
線吸収剤が含まれることによって耐候性をさらに向上さ
せることが可能である。かかる紫外線吸収剤としては、
従来公知ないし周知の2−ヒドロキシベンゾフェノン、
2.4−ヒドロキシベンゾフェノン、2−ヒドロキシド
4−n−オクトキシベンゾフェノン、2−ヒドロキシ−
4−(1−メチル−2−ヒドロキシ)エトキシベンゾフ
ェノン、2−ヒドロキシー4−(2−ヒドロキシ−3−
メタクリロキシ)プロポキシベンゾフェノンなどのベン
ゾフェノン系あるいは2− (2’ −ヒドロキシ−5
゛−メチルフェニル)ベンゾトリアゾール、2− (2
’−ヒドロキシ−3゛、5°−ジ−t−ブチルフェニル
)ベンゾトリアゾールなどのベンゾトリアゾール系のも
のが単独または併用して用いられる。 さらに、かかる塗料にはフルオロアルキル基を有するア
クリル系重合体(c)を添加し、プラスチックシートの
撥水性などを向上せしめてもよい、かかるフルオロアル
キル基を有するアクリル系重合体(c)としては、前記
含フッ素共重合体(a)またはアクリル系重合体(b)
と同様の架橋部位を有するものを採用すると、撥水性な
どが長期にわたって保持されるため好ましい。 また、かかるフルオロアルキル基を有するアクリル系重
合体(c)の添加量は、含フッ素共重合体(a)および
アクリル系重合体(b)の合計100重量部当たりo、
i〜30重量部程度の範囲で採用することが好ましい。 その他、特性の向上を目的として、塗料には、例えば消
泡剤、帯電防止剤、顔料、分散安定剤、粘度調節剤、レ
ベリング剤、ゲル化防止剤などの添加剤を配合すること
もできる。顔料の配合は被膜の陰蔽性という効果を有す
る。 また、必要な折り曲げ密着性などを得る目的でブライマ
ーを使用することももちろん可能である。 本発明の塗料は前記の如き、含フッ素共重合体(a)お
よびアクリル系重合体(b)などの主要構成成分さらに
必要に応じ硬化剤、紫外線吸収剤、フルオロアルキル基
を有するアクリル系重合体(c)その他の添加剤を有機
溶媒に溶解せしめることによって得られるが、用いられ
る溶媒としては例えばトルエン、キシレンなどの芳香族
炭化水素類、プロパツール、ブタノールなどのアルコー
ル類、酢酸エチル、酢酸ブチルなどのエステル類、メチ
ルエチルケトン、メチルイソブチルケトンなどのケトン
類、エチルセロソルブの如きグリコールエーテル類、さ
らに市販の各種ジンナール類なと、種々の一般有機溶媒
である。塗料成分の濃度としては1〜60重量%、好ま
しくは5〜50重量%に調製されてなるのが被膜を形成
する作業性において好適である。 塗料の調製に際しては、例えばボールミル。 ペイントシェーカー、サンドミル、ジェットミル、三本
ロール、ニーダ−などの通常の塗料化に用いられる種々
の機器を用いることによって行なわれ、特に限定されな
い、この際に、前記例示の如き添加剤を添加することが
できる。 本発明において、熱可塑性樹脂シートに塗料の被膜を形
成する方法は、成形体上に塗料をへヶ塗り、スプレー吹
付、フローコータなどにより塗布する、あるいは塗料中
にシートを浸漬することによって塗布し、溶媒を揮散さ
せるに充分な乾燥を行ない、次に加熱あるいは室温で放
置せしめて被膜とする。この際の加熱処理は。 成形体の変形しない温度以下とし、例えば60℃にて1
0分間の処理で充分である。 形成される塗料被膜の厚さは2〜1100uにおいて充
分なる効果が認められる。被膜の厚さの調製は、塗料の
成分濃度と塗布条件によって決定されるが、多層被膜に
形成されても何ら問題ない、成形体の形状も何ら限定さ
れない。 [実施例] 実施例1〜11.比較例1〜3 第1表に示す組成よりなる塗料No、1−13を調整し
た。壁紙の表面に塗料No、1=13をグラビアコータ
ーにより形成される被膜の膜厚が5μmになるように調
整して塗布し、室温にて乾燥後60℃にて10分間加熱
することによって硬化被膜を形成した。 このようにして被膜を形成したシートについて、次の評
価試験を行なった結果を第2表に示した。 接触角:水及びn−へキサデンカンの接触角を測定した
。 密着性:被膜の密着性をASTM−3359の方法に従
い ■初期、■温水浸漬後(60℃×30日)、■サンシャ
インウェザーメーター1000時間処理後のそれぞれで
測定し残った マス目数で評価する。 耐候性:サンシャインウェザ−メータ1000時間処理
前後においてカラー測定機(ス ガ試験機社製= 5M−3)で測定し、その黄変劣化を
処理前後の差(ΔE)とし て求める。 第1表中、含フッ素共重合体の F−Aは、 TFE / HBVE/ n−RYE =
48.1/12.5/39.4(重量%)の割合で共
重合であり、テトラヒドロフラン中30℃で測定される
固有粘度([η]という)が0.15 (di/g)で
ある共重合体、(以下、同じ) F−8は、CTFE/ I(BVE/ CHVE/ E
VE = 56.415.7/12.4/25.5.
[η] =0.21/di/g 。 F−Cは、HFP / HBVE/ n−BYE =
66、7/8.0/25.3゜[η] =0.08/d
i/g 。 F−Dは、TFE / C8mCOOCH=CH1/C
H1=CHCH10CHICH,0H=53.7/23
.1/23.2. [η] =0.18dl/g。 F−Eは、CTFE/EVE /HBVE/ヘオバ9
= 39.4717.2/9.5/33.9. [η
] = 0.40dl/g。 F−Fは、TFE / EVE / HBVE/ C)
lt”cHOcHtcFscFtH=57.0/22.
4/10.8/9.8. [η] =+ O,1Od
l/g。 (TFEはテトラフルオロエチレン、HBVEはω−ヒ
ドロキシブチルビニルエーテル、n−BYEはn−ブチ
ルビニルエーテル、CTFEはクロロトリフルオロエチ
レン、CHVEはシクロヘキシルビニルエーテル、EV
Eはエチルビニルエーテル、 HFPはへキサフルオロ
プロピレン、ベオバ9はシェル化学社製、炭素数9の分
岐上のアルキル基を有するビニルエーテルである。) ト1は、1so−ブチルメタクリレート/n−ブチルア
クリレート/2−ヒドロキシエチルメタクリレート=7
/2/l(モル比)の割合で共重合した共重合体(以下
同じ)。 M−2は、メチルアクリレート/n−ブチルアクリレー
ト/グリシジルアクリレート=8/l/1 。 M−3は、n−ブチルメタクリレート/Lso−ブチル
メタクリレート/アクリロニトリル/2−ヒドロキシエ
チルメタクリレート= 1/7/1/10ト4は、メチ
ルメタクリレート/n−ブチルメタクリレート=515
゜ を表わす。 フルオロアルキル基含有アクリル重合体はCH*=CH
C00CHxCHt (CFt) I oF/1so−
ブチルメタクリレート/n−ブチルアクリレート/2−
ヒドロキエチルメタクリレート= 20/60/10/
10重量%の共重合体。 イソシアネート硬化剤は、コロネートEH(日本ポリウ
レタン社製)。 紫外線吸収剤は、バイオソーブ130 (共同薬品製
)である。 第2表 比較例2は、塗料の被膜が形成されていない壁紙である
。 実施例12 実施例1において、乾燥条件を120℃、1分間とする
他は同様にして行なったところ、はぼ実施例1と同様の
効果が得られた。 【発明の効果コ 本発明の壁紙は、特定の塗料の被膜が良好な密着性を保
持して、形成されているために、耐久性、防染性にきわ
めて優れたものである。
Claims (1)
- 【特許請求の範囲】 1、熱可塑性樹脂シート上に、架橋部位を有する含フッ
素共重合体(a)および(a)と相溶するアクリル系重
合体(b)を主成分とする塗料の被膜を形成してなる壁
紙。 2、塗料がさらにフルオロアルキル基を有するアクリル
系重合体(c)を有する請求項1の壁紙。 3、アクリル系重合体(b)が架橋部位を有する請求項
1の壁紙。 4、塗料がさらに硬化剤を含む請求項1の壁紙。