JPH02202527A - 静電気防止剤 - Google Patents
静電気防止剤Info
- Publication number
- JPH02202527A JPH02202527A JP2355489A JP2355489A JPH02202527A JP H02202527 A JPH02202527 A JP H02202527A JP 2355489 A JP2355489 A JP 2355489A JP 2355489 A JP2355489 A JP 2355489A JP H02202527 A JPH02202527 A JP H02202527A
- Authority
- JP
- Japan
- Prior art keywords
- antistatic agent
- organopolysiloxane
- metal
- metal compound
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
本発明は合成樹脂用帯電防止剤に関する。
従来の技術
合成樹脂用静電防止剤としては種々の化合物が開発され
実用化されてきた。その代表的例は界面活性剤であり、
これが内添または、表面処理用として用いられてきた。
実用化されてきた。その代表的例は界面活性剤であり、
これが内添または、表面処理用として用いられてきた。
界面活性剤はその疎水性基を合成樹脂側に親水性基を外
表面に向けて配向するため、合成樹脂表面に吸水性の導
電性膜を形成して、発生した静電気を逃すことにより帯
電防止作用を発現する。
表面に向けて配向するため、合成樹脂表面に吸水性の導
電性膜を形成して、発生した静電気を逃すことにより帯
電防止作用を発現する。
しかしながら、界面活性剤は合成樹脂表面に吸水性の層
を形成するため、その表面にべとつきを生じ、ブロッキ
ングや滑り難さの原因となり易い。
を形成するため、その表面にべとつきを生じ、ブロッキ
ングや滑り難さの原因となり易い。
従って、合成樹脂繊維等の処理のごとく、帯電性と同時
に平滑性を必要とする用途にあっては、さらに平滑性付
与のI;め、無機粉末等を内添もしくは表面付与する必
要があった。しかしながら無機粉末を併用し得る用途は
極めて限られている。平滑性を付与するための別の方法
としてはシリコーン油(ジメチルポリシロキサン等)等
の平滑剤を併用する方法であるが通常のシリコーン油は
静電気発生能が非常に大きいからこれをベースとする処
理剤に対しては従来の界面活性剤では、十分な静電気防
止作用が達成されない場合が多々経験されている。
に平滑性を必要とする用途にあっては、さらに平滑性付
与のI;め、無機粉末等を内添もしくは表面付与する必
要があった。しかしながら無機粉末を併用し得る用途は
極めて限られている。平滑性を付与するための別の方法
としてはシリコーン油(ジメチルポリシロキサン等)等
の平滑剤を併用する方法であるが通常のシリコーン油は
静電気発生能が非常に大きいからこれをベースとする処
理剤に対しては従来の界面活性剤では、十分な静電気防
止作用が達成されない場合が多々経験されている。
一方、オルガノポリシロキサン金属化合物自体は公知で
あり、多くはオルガノポリシロキサン組成物の熱安定性
を改良する目的で用いられている。
あり、多くはオルガノポリシロキサン組成物の熱安定性
を改良する目的で用いられている。
この様な例は例えば特公昭51−24377号公報、特
公昭36−6189号公報および特公昭43−1630
4号公報等に記載されているが、いずれもオルガノポリ
シロキサン金属化合物の静電気防止能について言及して
いない。
公昭36−6189号公報および特公昭43−1630
4号公報等に記載されているが、いずれもオルガノポリ
シロキサン金属化合物の静電気防止能について言及して
いない。
発明が解決しようとする課題
本発明は合成樹脂に用いて優れた静電気防止能を有し、
かつ平滑性に対しても悪影響を有さす、加えてシリコー
ン油等とも均一に混合し、かつ静電気防止能を発現し得
る静電気防止剤を提供することを目的とする。
かつ平滑性に対しても悪影響を有さす、加えてシリコー
ン油等とも均一に混合し、かつ静電気防止能を発現し得
る静電気防止剤を提供することを目的とする。
課題を解決するための手段
本発明はオルガノポリシロキサン金属化合物を主成分と
する合成樹脂用静電気防止剤およびこれに更に金属石け
んを配合した静電気防止剤を提供する。
する合成樹脂用静電気防止剤およびこれに更に金属石け
んを配合した静電気防止剤を提供する。
本発明に用いられるオルガノポリシロキサン金体であっ
て末端ヒドロキシ基の少なくとも一個が金属と結合また
は配位したものである。これらの化合物は前述のごとき
公告公報に記載された公知の化合物である。最も一般的
なすルガノポリシロキサン金属化合物は一般式: で表わされる。式中、R,、R,およびR1は同一また
は異なってもよい炭化水素基である。本発明にとって好
ましい炭化水素基は側鎖を有することもある飽和または
不飽和のアルキル基;フェニル基Wのアリール基;ベン
ジル基等のアラルキル基;シクロヘキシル基等のシクロ
アルキル基等が例示されるがメチル基、エチル基等の低
級アルキル基、特にメチル基を主とする化合物が好まし
い。
て末端ヒドロキシ基の少なくとも一個が金属と結合また
は配位したものである。これらの化合物は前述のごとき
公告公報に記載された公知の化合物である。最も一般的
なすルガノポリシロキサン金属化合物は一般式: で表わされる。式中、R,、R,およびR1は同一また
は異なってもよい炭化水素基である。本発明にとって好
ましい炭化水素基は側鎖を有することもある飽和または
不飽和のアルキル基;フェニル基Wのアリール基;ベン
ジル基等のアラルキル基;シクロヘキシル基等のシクロ
アルキル基等が例示されるがメチル基、エチル基等の低
級アルキル基、特にメチル基を主とする化合物が好まし
い。
Mは金属原子、好ましくは2〜4価の金属原子、例えば
鉄、チタン、セリウム、ジルコニウム、モリブデン、コ
バルト等であり、特にセリウムにおいて好結果が得られ
る。金属原子は分子中にO01〜5!i量%、特に0.
2〜3重量%含まれるのが好ましい。
鉄、チタン、セリウム、ジルコニウム、モリブデン、コ
バルト等であり、特にセリウムにおいて好結果が得られ
る。金属原子は分子中にO01〜5!i量%、特に0.
2〜3重量%含まれるのが好ましい。
式中、nはオルガノポリシロキサンの重合度を示し、好
ましくは2〜lO1より好ましくは3〜5の数である。
ましくは2〜lO1より好ましくは3〜5の数である。
mは、金属原子の価数であり、好ましくは2〜4である
。オルガノポリシロキサン金属化合物の粘度は使用態様
によって異なるが内添用では50〜300cs/20℃
;表面処理用では1O−100cs/20℃が好ましい
。
。オルガノポリシロキサン金属化合物の粘度は使用態様
によって異なるが内添用では50〜300cs/20℃
;表面処理用では1O−100cs/20℃が好ましい
。
本発明合成樹脂用静電気防止剤はさらに金属石けん、特
に長鎖脂肪酸の金属石けんを含んでいてもよい。この処
方は特に外部表面処理用として有用である。
に長鎖脂肪酸の金属石けんを含んでいてもよい。この処
方は特に外部表面処理用として有用である。
長鎖脂肪酸としては、ラウリン酸、ミリスチン酸、パル
ミチン酸、ステアリン酸、パルミトレイン酸、オレイン
酸、エイコ酸、エルカa%lJ/−ル酸、リルン酸、リ
シノール酸、アビエチン酸等の他、側鎖を有するもので
あってもよい。
ミチン酸、ステアリン酸、パルミトレイン酸、オレイン
酸、エイコ酸、エルカa%lJ/−ル酸、リルン酸、リ
シノール酸、アビエチン酸等の他、側鎖を有するもので
あってもよい。
金属石けんを形成する金属原子は、2価以上の金属原子
、例えばカルシウム、マグネシウム、アルミニウム、亜
鉛等が好ましい。もちろんこれらに限定されるものでは
ない。これらの金属石けんは、合成樹脂の平滑性に寄与
し、静電気の発生を抑制する。
、例えばカルシウム、マグネシウム、アルミニウム、亜
鉛等が好ましい。もちろんこれらに限定されるものでは
ない。これらの金属石けんは、合成樹脂の平滑性に寄与
し、静電気の発生を抑制する。
金属石けんの配合量はオルガノポリシロキサン金属化合
物100重量部当り好ましく゛は20重量部以下、より
好ましくは10重量部以下である。
物100重量部当り好ましく゛は20重量部以下、より
好ましくは10重量部以下である。
本発明静電気防止剤は更に他の成分、例えば従来静電気
防止剤として用いられていた各種界面活性剤や平滑性を
付与するために用いられてきた鉱物油、シリコーン油等
、エポキシ変性シリコーン油等を配合してもよい。さら
にこれを溶剤型外部表面処理剤として用いるときは、上
記成分を溶解するための有機溶剤、例えば脂肪酸炭化水
素系、芳香族炭化水素系、アルコール系、ケトン系、エ
ーテル系、エステル系等の各種溶剤の単独または混合溶
剤を用いてよく、あるいは、上記化合物を乳化型または
可溶化型外部表面処理に用いるときは、乳化または可溶
化用の界面活性剤および必要ならば溶剤を併用してもよ
い。
防止剤として用いられていた各種界面活性剤や平滑性を
付与するために用いられてきた鉱物油、シリコーン油等
、エポキシ変性シリコーン油等を配合してもよい。さら
にこれを溶剤型外部表面処理剤として用いるときは、上
記成分を溶解するための有機溶剤、例えば脂肪酸炭化水
素系、芳香族炭化水素系、アルコール系、ケトン系、エ
ーテル系、エステル系等の各種溶剤の単独または混合溶
剤を用いてよく、あるいは、上記化合物を乳化型または
可溶化型外部表面処理に用いるときは、乳化または可溶
化用の界面活性剤および必要ならば溶剤を併用してもよ
い。
本発明静電気防止剤は、内部添加用としであるいは外部
表面処理用として用いてもよい。
表面処理用として用いてもよい。
内添用として用いるときは、防止剤中のオルガノポリシ
ロキサン金属化合物含量は30〜100重量%が適当で
ある。これをオルガノポリシロキサン金属化合物の合成
樹脂に対する配合量が好ましくは1〜20重量%、より
好ましくは1−10重量%となるように用いる。
ロキサン金属化合物含量は30〜100重量%が適当で
ある。これをオルガノポリシロキサン金属化合物の合成
樹脂に対する配合量が好ましくは1〜20重量%、より
好ましくは1−10重量%となるように用いる。
表面処理用として用いるときは静電気防止剤中のオルガ
ノポリシロキサン金属化合物含量は5〜50重量%程度
が適当であり、表面付着量は、オルガノポリシロキサン
金属化合物含量として対合成樹脂表面積当りO,l=1
g/+1”程度が適当であ本発明静電気防止剤は、例え
ばポリエステル、ポリアミド、ポリウレタン、ポリアセ
タール、ポリカーボネート、ポリエチレン、ポリゾロピ
レン、ポリ塩化ビニル等の合成樹脂に混練し、これを、
スレート、パイプ、波板、繊維、フィルム、シート等各
種成形材料に成形する。或は予め成形したものに付着さ
せて使用する。
ノポリシロキサン金属化合物含量は5〜50重量%程度
が適当であり、表面付着量は、オルガノポリシロキサン
金属化合物含量として対合成樹脂表面積当りO,l=1
g/+1”程度が適当であ本発明静電気防止剤は、例え
ばポリエステル、ポリアミド、ポリウレタン、ポリアセ
タール、ポリカーボネート、ポリエチレン、ポリゾロピ
レン、ポリ塩化ビニル等の合成樹脂に混練し、これを、
スレート、パイプ、波板、繊維、フィルム、シート等各
種成形材料に成形する。或は予め成形したものに付着さ
せて使用する。
以下、実施例をあげて説明する。
実施例1
市販の塩化ビニル樹脂粉末(電気化学部、一般用)10
0部に対し、可塑剤(大へ化学製、ジオクチルフタレー
))20部及びシリコーンセリウム化合物(セリウム含
i1.7重量%、粘度100cs)t。
0部に対し、可塑剤(大へ化学製、ジオクチルフタレー
))20部及びシリコーンセリウム化合物(セリウム含
i1.7重量%、粘度100cs)t。
部をロール混練した後、細断しペレット状にする。
これをプレス成型し、表面抵抗測定試料とした。
比較例として、シリコーンセリウム化合物を用いないで
ロール混練し、プレス成型した試料を調製した。両者の
表面抵抗を表=1に示す。
ロール混練し、プレス成型した試料を調製した。両者の
表面抵抗を表=1に示す。
表1
表面抵抗二表面伝導度計にて測定
48時間調湿後(20°C×65%RH)実施例2(繊
維用処理剤) 市販のポリウレタン弾性繊維(140de)をノルマル
ヘキサンを溶剤として超音波洗浄により脱脂し、ノーオ
イル糸とする。このノーオイル糸を表2に示す処理剤で
処理し、静電特性を測定した。
維用処理剤) 市販のポリウレタン弾性繊維(140de)をノルマル
ヘキサンを溶剤として超音波洗浄により脱脂し、ノーオ
イル糸とする。このノーオイル糸を表2に示す処理剤で
処理し、静電特性を測定した。
(以下、余白)
表中表示
鉱物油:流動パラフィングレード、40〜80秒ジメチ
ルシリコーン:lO〜50cs 水溶性シリコーン:ポリエーテル変性シリコーン粘度5
00〜3000cs 可溶化剤ニジオクチルフタレート等のエステル類金属5
最ニステアリン酸AL。
ルシリコーン:lO〜50cs 水溶性シリコーン:ポリエーテル変性シリコーン粘度5
00〜3000cs 可溶化剤ニジオクチルフタレート等のエステル類金属5
最ニステアリン酸AL。
本発明品A:セリウム含量1.7重量%、粘度:1Oc
s20℃ 本発明量B:セリウム含!1.7重量%、粘度: 10
0cs20℃ 評価法 表面抵抗 *対プラスティック 直径50mm、厚さ5mmに圧縮成型した試料を20°
C×65%RHで48時間調湿後、表面伝導度計を使用
して測定した。
s20℃ 本発明量B:セリウム含!1.7重量%、粘度: 10
0cs20℃ 評価法 表面抵抗 *対プラスティック 直径50mm、厚さ5mmに圧縮成型した試料を20°
C×65%RHで48時間調湿後、表面伝導度計を使用
して測定した。
*対繊維
給油糸59を20°C×65%RHで48時間調湿後繊
維表面伝導度計で測定した。
維表面伝導度計で測定した。
土茎朋
給油糸で九編地を作製し、オネストメーターにセットす
る試料台を11000rpで回転させながら、試料に4
秒間10000ボルトの電圧をかけ、初期電圧を停止後
、試料に誘起された電圧が半減するまでの時間を測定し
た。
る試料台を11000rpで回転させながら、試料に4
秒間10000ボルトの電圧をかけ、初期電圧を停止後
、試料に誘起された電圧が半減するまでの時間を測定し
た。
この時間(半減期)が短いほど、導電性が優れているこ
とを示す。
とを示す。
実施例の様に、本発明成分はプラスチック等の内部添加
においても、又繊維剋理剤として表面塗布した場合でも
、静電気防止効果に優れる事が認められる。
においても、又繊維剋理剤として表面塗布した場合でも
、静電気防止効果に優れる事が認められる。
発明の効果
本発明によると従来の界面活性剤にみられるブロッキン
グや滑り難さの問題が解消し、かつシリコーン油等とも
配合可能な静電気防止剤を得ることができる。
グや滑り難さの問題が解消し、かつシリコーン油等とも
配合可能な静電気防止剤を得ることができる。
特許出願人松本油脂製薬株式会社
Claims (1)
- 【特許請求の範囲】 1、オルガノポリシロキサン金属化合物を主成分とする
合成樹脂用静電気防止剤。 2、オルガノポリシロキサン金属化合物が一般式: ▲数式、化学式、表等があります▼[ I ] [式中、R_1、R_2およびR_3は同一または異な
ってもよい炭化水素基、MはFe、Ti、Zr、Ceお
よびMoから選ばれる金属、nは2〜10の数およびm
はMの価数を示す]で表わされる化合物である請求項1
に記載の静電気防止剤。 3、オルガノポリシロキサン金属化合物および金属石け
んを主成分とする合成樹脂静電気防止剤。