JP7466729B2 - 電子グレードガラス繊維組成物、そのガラス繊維及び電子グレードガラス繊維布 - Google Patents
電子グレードガラス繊維組成物、そのガラス繊維及び電子グレードガラス繊維布 Download PDFInfo
- Publication number
- JP7466729B2 JP7466729B2 JP2023039633A JP2023039633A JP7466729B2 JP 7466729 B2 JP7466729 B2 JP 7466729B2 JP 2023039633 A JP2023039633 A JP 2023039633A JP 2023039633 A JP2023039633 A JP 2023039633A JP 7466729 B2 JP7466729 B2 JP 7466729B2
- Authority
- JP
- Japan
- Prior art keywords
- weight
- glass fiber
- range
- electronic grade
- grade glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
SiO2 54.2~60重量%、Al2O3 11~17.5重量%、B2O3 0.7~4.5重量%、CaO 18~23.8重量%、MgO 1~5.5重量%、RO=CaO+MgO ≦24.8重量%、R2O=Na2O+K2O+Li2O <1重量%、TiO2 0.05~0.8重量%、Fe2O3 0.05~0.7重量%、F2 0.01~1.2重量%を含み、
重量百分率比C1=SiO2/(RO+R2O)の範囲は2.20以上であり、且つ上記成分の全含有量は98.5重量%以上である電子グレードガラス繊維組成物を提供する。
重量百分率比C1=SiO2/(RO+R2O)の範囲は2.20以上であり、且つ上記成分の全含有量は98.5重量%以上である。
SiO2 54.2~60重量%、Al2O3 11~17.5重量%、B2O3 0.7~4.5重量%、CaO 18~23.8重量%、MgO 1~5.5重量%、RO=CaO+MgO ≦24.8重量%、R2O=Na2O+K2O+Li2O <1重量%、TiO2 0.05~0.8重量%、Fe2O3 0.05~0.7重量%、F2 0.01~1.2重量%を含み、
重量百分率比C1=SiO2/(RO+R2O)の範囲は2.20以上であり、重量百分率比C2=(SiO2+Al2O3-B2O3)/(RO+R2O)の範囲は2.73以上であり、重量百分率比C3=(SiO2+Al2O3)/(RO+R2O+B2O3)の範囲は2.50以上であり、且つ上記成分の全含有量は98.5重量%以上である。
SiO2 55~59.5重量%、Al2O3 11.5~16.5重量%、B2O3 0.7~4.5重量%、CaO 18~23.3重量%、MgO 1~4.5重量%、RO=CaO+MgO ≦24.4重量%、R2O=Na2O+K2O+Li2O <1重量%、RO+R2O 20.5~25重量%、TiO2 0.05~0.8重量%、Fe2O3 0.05~0.7重量%、F2 0.05~1.2重量%を含み、
重量百分率比C1=SiO2/(RO+R2O)の範囲は2.20以上であり、重量百分率比C2=(SiO2+Al2O3-B2O3)/(RO+R2O)の範囲は2.73以上であり、且つ上記成分の全含有量は98.5重量%以上である。
SiO2 55~59.5重量%、Al2O3 12~15.9重量%、B2O3 1~3.5重量%、CaO 18~23.3重量%、MgO 1.1~4重量%、RO=CaO+MgO ≦24.4重量%、R2O=Na2O+K2O+Li2O ≦0.8重量%、RO+R2O 20.5~25重量%、TiO2 0.05~0.8重量%、Fe2O3 0.05~0.7重量%、F2 0.05~1.2重量%を含み、
重量百分率比C1=SiO2/(RO+R2O)の範囲は2.24~2.75であり、重量百分率比C2=(SiO2+Al2O3-B2O3)/(RO+R2O)の範囲は2.75~3.35であり、重量百分率比C3=(SiO2+Al2O3)/(RO+R2O+B2O3)の範囲は2.50以上であり、且つ上記成分の全含有量は98.5重量%以上である。
SiO2 54.2~60重量%、Al2O3 11~17.5重量%、B2O3 0.7~4.5重量%、CaO 18~23.8重量%、MgO 1~5.5重量%、RO=CaO+MgO ≦24.8重量%、R2O=Na2O+K2O+Li2O <1重量%、TiO2 0.05~0.8重量%、Fe2O3 0.05~0.7重量%、F2 0.01~1.2重量%を含み、
重量百分率比C1=SiO2/(RO+R2O)の範囲は2.20以上であり、且つ上記成分の全含有量は98.5重量%以上である。
本発明に係る電子グレードガラス繊維組成物は、成分として、
SiO2 54.2~60重量%、Al2O3 11~17.5重量%、B2O3 0.7~4.5重量%、CaO 18~23.8重量%、MgO 1~5.5重量%、RO=CaO+MgO ≦24.8重量%、R2O=Na2O+K2O+Li2O <1重量%、RO+R2O ≦25.2重量%、TiO2 0.05~0.8重量%、Fe2O3 0.05~0.7重量%、F2 0.01~1.2重量%を含み、
重量百分率比C1=SiO2/(RO+R2O)の範囲は2.20以上であり、重量百分率比C2=(SiO2+Al2O3-B2O3)/(RO+R2O)の範囲は2.73以上であり、且つ上記成分の全含有量は98.5重量%以上である。
本発明に係る電子グレードガラス繊維組成物は、成分として、
SiO2 54.2~60重量%、Al2O3 11~17.5重量%、B2O3 0.7~4.5重量%、CaO 18~23.8重量%、MgO 1~5.5重量%、RO=CaO+MgO ≦24.8重量%、R2O=Na2O+K2O+Li2O ≦0.8重量%、TiO2 0.05~0.8重量%、Fe2O3 0.05~0.7重量%、F2 0.01~1.2重量%を含み、
重量百分率比C1=SiO2/(RO+R2O)の範囲は2.20以上であり、重量百分率比C2=(SiO2+Al2O3-B2O3)/(RO+R2O)の範囲は2.73以上であり、重量百分率比C3=(SiO2+Al2O3)/(RO+R2O+B2O3)の範囲は2.50以上であり、且つ上記成分の全含有量は98.5重量%以上である。
本発明に係る電子グレードガラス繊維組成物は、成分として、
SiO2 54.2~60重量%、Al2O3 11~17.5重量%、B2O3 0.7~4.5重量%、CaO 18~23.3重量%、MgO 1~5.5重量%、RO=CaO+MgO ≦24.4重量%、R2O=Na2O+K2O+Li2O <1重量%、RO+R2O ≦25.2重量%、TiO2 0.05~0.8重量%、Fe2O3 0.05~0.7重量%、F2 0.01~1.2重量%を含み、
重量百分率比C1=SiO2/(RO+R2O)の範囲は2.20以上であり、重量百分率比C2=(SiO2+Al2O3-B2O3)/(RO+R2O)の範囲は2.73以上であり、且つ上記成分の全含有量は98.5重量%以上である。
本発明に係る電子グレードガラス繊維組成物は、成分として、
SiO2 54.2~60重量%、Al2O3 11~17.5重量%、B2O3 0.7~4.5重量%、CaO 18~23.3重量%、MgO 1~5.5重量%、RO=CaO+MgO ≦24.4重量%、R2O=Na2O+K2O+Li2O <1重量%、RO+R2O 20.5~25重量%、TiO2 0.05~0.8重量%、Fe2O3 0.05~0.7重量%、F2 0.05~1.2重量%を含み、
重量百分率比C1=SiO2/(RO+R2O)の範囲は2.20以上であり、重量百分率比C2=(SiO2+Al2O3-B2O3)/(RO+R2O)の範囲は2.73以上であり、重量百分率比C3=(SiO2+Al2O3)/(RO+R2O+B2O3)の範囲は2.50以上であり、且つ上記成分の全含有量は98.5重量%以上である。
本発明に係る電子グレードガラス繊維組成物は、成分として、
SiO2 54.2~60重量%、Al2O3 11~17.5重量%、B2O3 0.7~4.5重量%、CaO 18~23.8重量%、MgO 1~5.5重量%、RO=CaO+MgO ≦24.8重量%、R2O=Na2O+K2O+Li2O <1重量%、TiO2 0.05~0.8重量%、Fe2O3 0.05~0.7重量%、F2 0.01~1.2重量%を含み、
重量百分率比C1=SiO2/(RO+R2O)の範囲は2.24~2.75であり、重量百分率比C2=(SiO2+Al2O3-B2O3)/(RO+R2O)の範囲は2.73以上であり、且つ上記成分の全含有量は98.5重量%以上である。
本発明に係る電子グレードガラス繊維組成物は、成分として、
SiO2 54.2~60重量%、Al2O3 11~17.5重量%、B2O3 0.7~4.5重量%、CaO 18~23.8重量%、MgO 1~5.5重量%、RO=CaO+MgO ≦24.8重量%、R2O=Na2O+K2O+Li2O <1重量%、TiO2 0.05~0.8重量%、Fe2O3 0.05~0.7重量%、F2 0.01~1.2重量%を含み、
重量百分率比C1=SiO2/(RO+R2O)の範囲は2.24~2.75であり、重量百分率比C2=(SiO2+Al2O3-B2O3)/(RO+R2O)の範囲は2.75~3.35以上であり、且つ上記成分の全含有量は98.5重量%以上である。
本発明に係る電子グレードガラス繊維組成物は、成分として、
SiO2 55~59.5重量%、Al2O3 11.5~16.5重量%、B2O3 0.7~4.5重量%、CaO 18~23.3重量%、MgO 1~4.5重量%、RO=CaO+MgO ≦24.4重量%、R2O=Na2O+K2O+Li2O <1重量%、RO+R2O 20.5~25重量%、TiO2 0.05~0.8重量%、Fe2O3 0.05~0.7重量%、F2 0.01~1.2重量%を含み、
重量百分率比C1=SiO2/(RO+R2O)の範囲は2.20以上であり、重量百分率比C2=(SiO2+Al2O3-B2O3)/(RO+R2O)の範囲は2.75~3.35であり、且つ上記成分の全含有量は98.5重量%以上である。
本発明に係る電子グレードガラス繊維組成物は、成分として、
SiO2 55~59.5重量%、Al2O3 11.5~16.5重量%、B2O3 0.7~4重量%、CaO 18~23.3重量%、MgO 1~4.5重量%、RO=CaO+MgO ≦24.4重量%、R2O=Na2O+K2O+Li2O ≦0.8重量%、TiO2 0.05~0.8重量%、Fe2O3 0.05~0.7重量%、F2 0.05~1.2重量%を含み、
重量百分率比C1=SiO2/(RO+R2O)の範囲は2.24~2.75であり、重量百分率比C2=(SiO2+Al2O3-B2O3)/(RO+R2O)の範囲は2.73以上であり、且つ上記成分の全含有量は98.5重量%以上である。
本発明に係る電子グレードガラス繊維組成物は、成分として、
SiO2 55~59.5重量%、Al2O3 12~15.9重量%、B2O3 1~3.5重量%、CaO 18~22.8重量%、MgO 1~4.5重量%、RO=CaO+MgO 20~24.4重量%、R2O=Na2O+K2O+Li2O ≦0.8重量%、RO+R2O 20.5~25重量%、TiO2 0.05~0.8重量%、Fe2O3 0.05~0.7重量%、F2 0.05~1.2重量%を含み、
重量百分率比C1=SiO2/(RO+R2O)の範囲は2.24~2.75であり、重量百分率比C2=(SiO2+Al2O3-B2O3)/(RO+R2O)の範囲は2.75~3.35であり、重量百分率比C3=(SiO2+Al2O3)/(RO+R2O+B2O3)の範囲は2.50以上であり、且つ上記成分の全含有量は98.5重量%以上である。
(1)成形温度は、粘度が103ポイズであるときのガラス溶融物の温度に相当する。
(2)液相線温度は、ガラス溶融物を冷却したときに結晶核が形成され始める温度、すなわちガラスの結晶化の上限温度に相当する。
(3)△T値は、成形温度と液相線温度の差であり、線引き成形の温度範囲を示す。
(4)引張強度は、ガラス繊維が引張条件下で耐えられる最高力を特徴付け、ASTM D2343に準じて浸漬糸の引張強度をテストする。
(5)誘電率
誘電率の測定方法は以下のとおりである。原料を均一に混合し、白金るつぼに入れ、高温電気炉にて1550±30℃で6時間保温し、清澄でよく均質化された高温溶融ガラスを得て、溶融ガラスを予熱したステンレス鋼型に注いでガラスブロックを作り、ガラスブロックをマッフル炉に入れてアニーリングし、アニーリングしたガラスブロックを切断して研磨し、厚さ約1.5mm、長さ約30mmの長方形ガラス板を得て、前記ガラス板に銀電極をコーティングした後、誘電率を測定する。誘電率が小さいほど、ガラス媒体の分極能力が小さく、電気絶縁材料としての安定性が良好である。
(6)気泡数
気泡数の測定方法はほぼ以下のとおりである。専用型を使用して各実施例の配合材料を同じ形状のサンプルにプレスし、高温顕微鏡のサンプルプラットフォームに配置してから、設定された空間温度である1500℃までプログラム昇温し、保温せずにガラスサンプルを室温まで炉冷し、次に、光学顕微鏡で各ガラスサンプルの気泡数を微視的に観察する。ここで、気泡数は、顕微鏡のイメージング範囲を基準とする。
(7)耐水性
減量率で特徴付けられ、その測定方法としては、粒径40~80メッシュのガラス粉末を95℃の水に24時間放置し、定期的に撹拌し、ガラス粉末の減量率を測定する。減量率が小さいほど、ガラスの耐水性は良好である。
(8)耐酸性
減量率で特徴付けられ、その測定方法としては、粒径40~80メッシュのガラス粉末を23℃の10%HCL溶液にて48時間放置し定期的に撹拌し、ガラス粉末の減量率を測定する。減量率が小さいほど、ガラスの耐酸性は良好である。
(9)原料のコスト係数
従来のEガラス繊維組成物B1を基準として、原料のコスト係数を1.0に設定し、その他の組成部については、この基準で計算する。原料のコスト係数が小さいほど、組成物の原料のコスト係数は低い。
本発明による電子グレードガラス繊維組成物は、ガラスの誘電特性を改善し、ガラス繊維の機械的特性、耐水性及び耐酸性を向上させ、原料のコストを大幅に削減させ、原料の揮発を大幅に減少させ、耐火材料に対する侵食を低減させることができるだけでなく、大規模なタンクキルン化生産に適している。従来のガラス繊維組成物と比較して、本発明のガラス繊維組成物は、製品のコストパフォーマンス、原料コスト、誘電率、引張強度、液相線温度、成形範囲、耐水性及び耐酸性の点で実質的な進歩を遂げている。したがって、本発明は、産業上の利用可能性が良好である。
Claims (19)
- 電子グレードガラス繊維組成物であって、成分として、
SiO2 54.2~59.5重量%、
Al2O3 11~17.5重量%、
B2O3 0.7~4.5重量%、
CaO 18~23.8重量%、
MgO 1~5.5重量%、
RO=CaO+MgO≦24.4重量%、
R2O=Na2O+K2O+Li2O<1重量%、
Na2O+K2O 0.1~0.65重量%、
TiO2 0.05~0.8重量%、
Fe2O3 0.05~0.7重量%、
F2 0.01~1.2重量%を含み、
重量百分率比C1=SiO2/(RO+R2O)の範囲は2.20以上であり、且つ
上記成分の全含有量は99.5重量%以上であり、
ZnOを含まないことを特徴とする電子グレードガラス繊維組成物。 - 重量百分率比C2=(SiO2+Al2O3-B2O3)/(RO+R2O)の範囲は2.73以上である、ことを特徴とする請求項1に記載の電子グレードガラス繊維組成物。
- 重量百分率比C3=(SiO2+Al2O3)/(RO+R2O+B2O3)の範囲は、2.50以上である、ことを特徴とする請求項1に記載の電子グレードガラス繊維組成物。
- 重量百分率比C4=B2O3/R2Oの範囲は1以上である、ことを特徴とする請求項1に記載の電子グレードガラス繊維組成物。
- 成分として、SiO2 54.2~59.5重量%、
Al2O3 11~17.5重量%、
B2O3 0.7~4.5重量%、
CaO 18~23.8重量%、
MgO 1~5.5重量%、
RO=CaO+MgO ≦24.4重量%、
R2O=Na2O+K2O+Li2O <1重量%、
Na2O+K2O 0.1~0.65重量%、
RO+R2O ≦25.2重量%、
TiO2 0.05~0.8重量%、
Fe2O3 0.05~0.7重量%、
F2 0.01~1.2重量%を含み、
重量百分率比C1=SiO2/(RO+R2O)の範囲は2.20以上であり、且つ
上記成分の全含有量は99.5重量%以上である、ことを特徴とする請求項1に記載の電子グレードガラス繊維組成物。 - 前記ROの含有量の範囲は20~24.4重量%である、ことを特徴とする請求項1に記載の電子グレードガラス繊維組成物。
- 前記RO+R2Oの含有量の範囲は20.5~25重量%である、ことを特徴とする請求項1に記載の電子グレードガラス繊維組成物。
- 前記R2Oの含有量の範囲は0.8重量%以下である、ことを特徴とする請求項1に記載の電子グレードガラス繊維組成物。
- 前記F2の含有量の範囲は0.05~1.2重量%である、ことを特徴とする請求項1に記載の電子グレードガラス繊維組成物。
- 重量百分率比K2O/Na2Oの範囲は0.5よりも大きい、ことを特徴とする請求項1に記載の電子グレードガラス繊維組成物。
- 前記Al2O3+MgOの含有量の範囲は13~19.1重量%である、ことを特徴とする請求項1に記載の電子グレードガラス繊維組成物。
- 成分として、SiO2 54.2~59.5重量%、
Al2O3 11~17.5重量%、
B2O3 0.7~4.5重量%、
CaO 18~23.8重量%、
MgO 1~5.5重量%、
RO=CaO+MgO ≦24.4重量%、
R2O=Na2O+K2O+Li2O <1重量%、
Na2O+K2O 0.1~0.65重量%、
TiO2 0.05~0.8重量%、
Fe2O3 0.05~0.7重量%、
F2 0.01~1.2重量%を含み、
重量百分率比C1=SiO2/(RO+R2O)の範囲は2.20以上であり、
重量百分率比C2=(SiO2+Al2O3-B2O3)/(RO+R2O)の範囲は2.73以上であり、
重量百分率比C3=(SiO2+Al2O3)/(RO+R2O+B2O3)の範囲は2.50以上であり、且つ
上記成分の全含有量は99.5重量%以上である、ことを特徴とする請求項1に記載の電子グレードガラス繊維組成物。 - 成分として、SiO2 55~59.5重量%、
Al2O3 11.5~16.5重量%、
B2O3 0.7~4.5重量%、
CaO 18~23.3重量%、
MgO 1~4.5重量%、
RO=CaO+MgO ≦24.4重量%、
R2O=Na2O+K2O+Li2O <1重量%、
Na2O+K2O 0.1~0.65重量%、
RO+R2O 20.5~25重量%、
TiO2 0.05~0.8重量%、
Fe2O3 0.05~0.7重量%、
F2 0.05~1.2重量%を含み、
重量百分率比C1=SiO2/(RO+R2O)の範囲は2.20以上であり、
重量百分率比C2=(SiO2+Al2O3-B2O3)/(RO+R2O)の範囲は2.73以上であり、且つ
上記成分の全含有量は99.5重量%以上である、ことを特徴とする請求項1に記載の電子グレードガラス繊維組成物。 - 成分として、SiO2 55~59.5重量%、
Al2O3 12~15.9重量%、
B2O3 1~3.5重量%、
CaO 18~23.3重量%、
MgO 1.1~4重量%、
RO=CaO+MgO≦24.4重量%、
R2O=Na2O+K2O+Li2O≦0.8重量%、
Na2O+K2O 0.1~0.65重量%、
RO+R2O 20.5~25重量%、
TiO2 0.05~0.8重量%、
Fe2O3 0.05~0.7重量%、
F2 0.05~1.2重量%を含み、
重量百分率比C1=SiO2/(RO+R2O)の範囲は2.24~2.75であり、
重量百分率比C2=(SiO2+Al2O3-B2O3)/(RO+R2O)の範囲は2.75~3.35であり、
重量百分率比C3=(SiO2+Al2O3)/(RO+R2O+B2O3)の範囲は2.50以上である、且つ
上記成分の全含有量は99.5重量%以上である、ことを特徴とする請求項1に記載の電子グレードガラス繊維組成物。 - 総含有量が0.5重量%未満のSO3、SrO、CeO2、La2O3、Y2O3、ZrO2のうちの1種又は複数種をさらに含む、ことを特徴とする請求項1に記載の電子グレードガラス繊維組成物。
- 電子グレードガラス繊維であって、
請求項1~15のいずれか1項に記載の電子グレードガラス繊維組成物で製造される、ことを特徴とする電子グレードガラス繊維。 - 室温で周波数が1MHzであるときの誘電率の範囲は6.0~7.0である、ことを特徴とする請求項16に記載の電子グレードガラス繊維。
- 電子グレードガラス繊維布であって、
請求項16に記載の電子グレードガラス繊維を含有する、ことを特徴とする電子グレードガラス繊維布。 - プリント回路基板の基材として用いられることを特徴とする請求項18に記載の電子グレードガラス繊維布。