JP7463684B2 - 液体組成物セット、収容容器セット、硬化物形成装置、硬化物形成方法、及び液体組成物 - Google Patents
液体組成物セット、収容容器セット、硬化物形成装置、硬化物形成方法、及び液体組成物 Download PDFInfo
- Publication number
- JP7463684B2 JP7463684B2 JP2019182665A JP2019182665A JP7463684B2 JP 7463684 B2 JP7463684 B2 JP 7463684B2 JP 2019182665 A JP2019182665 A JP 2019182665A JP 2019182665 A JP2019182665 A JP 2019182665A JP 7463684 B2 JP7463684 B2 JP 7463684B2
- Authority
- JP
- Japan
- Prior art keywords
- liquid composition
- compound
- group
- general formula
- electron
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
また、加熱することで硬化する液体組成物を用いる場合、加熱に多大なエネルギーが必要となるため好ましくない。
本実施形態の液体組成物セットは、一般式(1)で表される化合物及び酸性物質を含有する第一の液体組成物と、ビニル基又はアクリロイル基を有する化合物を含有する第二の液体組成物と、を有し、必要に応じてその他組成物を有していてもよい。
液体組成物セットは、第一の液体組成物及び第二の液体組成物が接触すると硬化し、硬化物を形成する。ここで、硬化するとは、第一の液体組成物及び第二の液体組成物が接触することで重合物を生じることであるが、固形化する場合に限られず、増粘する場合や、固形化物と増粘物が混在する状態になる場合なども含まれる。また、硬化物とは、第一の液体組成物及び第二の液体組成物が接触することで生じる重合物であるが、固体に限られず、増粘物や、固体と増粘物の混在物なども含まれる。
また、第一の液体組成物及び第二の液体組成物が接触することで硬化物を形成可能である場合とは、第一の液体組成物及び第二の液体組成物の接触のみに基づいて硬化物を形成可能である場合をいう。言い換えると、活性エネルギー線の照射および加熱等の外部エネルギーの付与が行われなくても硬化物が形成可能である場合をいう。なお、硬化物が、第一の液体組成物と第二の液体組成物の接触のみに基づいて形成可能なのであれば、硬化時に追加的に外部エネルギーの付与が行われてもよいが、外部エネルギーの付与が行われないことが好ましい。なお、本願でいう活性エネルギー線とは、紫外線、電子線、α線、β線、γ線、X線等を表す。
第一の液体組成物は、一般式(1)で表される化合物及び酸性物質を含有する液体組成物であり、必要に応じてその他物質を含有してもよい。
一般式(1)で表される化合物は、重合性化合物であり下記のように表される。一般式(1)で表される化合物は、第一の液体組成物及び第二の液体組成物が接触することで、後述する第二の液体組成物に含有される化合物と重合反応を生じて硬化物を形成する。また、一般式(1)で表される化合物を用いることで硬化性を向上させることができる。
酸性物質とは、水に溶解又は分散させた際に、当該水溶液又は分散液が酸性を示す物質であり、有機酸や無機酸を用いることができる。また、遊離酸に限らず、上記条件で酸性を示す物質であれば酸無水物、酸塩化物、及び固体酸も用いることができる。
酸性物質は、第一の液体組成物中における一般式(1)で表される化合物の硬化を抑制する。一般式(1)で表される化合物には空気に触れるだけで急速に硬化反応が進むものが含まれ、例えば、シアノアクリレート化合物等は瞬間接着剤の主成分としても広く知られている。より具体的には、一般式(1)で表される化合物は、空気中の水等と接触することによりアニオン重合を開始するので、酸性物質により本重合を抑制する。これにより、第一の液体組成物が一般式(1)で表される化合物を含有していたとしても、第一の液体組成物単体では長期間硬化せず、液体状態を維持することができ、本実施形態の液体組成物セットの取扱性が向上し、用途の幅が広がる。例えば、第一の液体組成物が付与された直後に硬化物を形成することが抑制されるため、硬化物が形成されるまでの間に十分に第一の液体組成物が濡れ広がることができ、表面性や膜厚などの観点で均一性に優れた硬化物を得ることができる。また、インクジェット方式などで第一の液体組成物を付与する際に、硬化物により吐出孔が詰まることや装置内の流路が詰まることを抑制することができる。更に、第一の液体組成物の長期間における保存安定性が向上する。
また、酸性物質は、一般式(1)で表される化合物と混合した際に硬化物を形成しない範囲で重合性官能基を有していてもよい。一般式(1)で表される化合物と混合しても硬化物を形成しない重合性官能基としては、例えば、メタクリロイル基等が挙げられる。なお、重合性官能基を有する酸性物質としては、一般式(1)で表される化合物の一例として列挙したメチレンマロン酸、シアノアクリル酸等であってもよい。
第一の液体組成物は、空気と接触した場合であっても長期間安定して粘度上昇や硬化が抑制され、ほぼ一定の液体状態を維持できる。これにより、インクジェット方式などで第一の液体組成物を付与する際に、硬化物により吐出孔が詰まることや装置内の流路が詰まることを抑制することができる。更に、第一の液体組成物の長期間における保存安定性が向上する。
このような長期間安定した第一の液体組成物の状態を表す物性の一例としては、例えば、粘度変化率を挙げることができる。第一の液体組成物の粘度変化率は、5.0%以下であることが好ましく、3.0%以下であることがより好ましく、1.0%以下であることが更に好ましい。粘度変化率は、第一の液体組成物を容積110mLの容器(アズワン社製褐色ガラススクリュー管瓶No.8)に50mL入れ、容器中の第一の液体組成物が温度25℃かつ湿度50%RHの空気に接触している状態で密閉し、温度25℃の環境下で1日(24時間)静置したとき、下記式に基づいて算出される物性である。なお、粘度は、温度25℃において市販の粘度計を用いて測定することができ、例えば、東機産業社製E型粘度計TVE-22Lを用いることができる。また、粘度変化率の測定に用いる第一の液体組成物は、製造直後のものに限定されず、例えば、製造後に容器等に密閉されて市販されたもの等であってもよい。なお、市販されたものを用いて粘度変化率の測定を行う場合、開封直後に本測定を開始することが好ましい。
第二の液体組成物は、ビニル基又はアクリロイル基を有する化合物を含有する液体組成物であり、必要に応じてその他物質を含有してもよい。
ビニル基又はアクリロイル基を有する化合物は、第一の液体組成物及び第二の液体組成物が接触することで、上記一般式(1)で表される化合物と重合反応を生じて硬化物を形成する。より具体的には、酸性物質によりアニオン重合が抑制されている一般式(1)で表される化合物と、ビニル基又はアクリロイル基を有する化合物と、がラジカル重合を生じて硬化物を形成する。これにより、本実施形態の液体組成物セットは、活性エネルギー線の照射および加熱等の外部エネルギーの付与を必要とせずに硬化物を形成することができる。また、第一の液体組成物及び第二の液体組成物が重合開始剤を実質的に含有しなくても硬化物を形成することができる。重合開始剤とは、外部エネルギーを付与された場合にそれを吸収してラジカルまたはイオンを生成し、重合性化合物の重合を開始させるものである。重合開始剤は、硬化反応時だけでなく、反応後の硬化物における臭気の原因にもなる。また、重合開始剤は、その分解生成物が毒性を有している場合もある。そのため、本実施形態の液体組成物セットは、重合開始剤を実質的に含有しないことで、臭気や毒性等の課題を回避することができる。なお、本実施形態では、重合開始剤を実質的に含有しないことが好ましいが、重合開始剤を含んでいてもよい。なお、第一の液体組成物及び第二の液体組成物が重合開始剤を実質的に含有しないとは、第一の液体組成物及び第二の液体組成物において重合開始剤の含有量が検出限界以下であることが好ましく、含まれないことがより好ましい。
また、エチレングリコールアクリレート、ジエチレングリコールアクリレート、トリエチレングリコールアクリレート、ポリエチレングリコールアクリレート、プロピレングリコールアクリレート、ジプロピレングリコールアクリレート、トリプロピレングリコールアクリレート、ポリプロピレングリコールアクリレート、メトキシエチレングリコールアクリレート、メトキシジエチレングリコールアクリレート、メトキシトリエチレングリコールアクリレート、メトキシポリエチレングリコールアクリレート、メトキシプロピレングリコールアクリレート、メトキシジプロピレングリコールアクリレート、メトキシトリプロピレングリコールアクリレート、メトキシポリプロピレングリコールアクリレート、などのモノアクリレートに加え、ジオキサングリコールジアクリレート、トリシクロデカンジメタノールジアクリレート、ビスフェノールAジアクリレート、ビスフェノールFジアクリレート、ブタンジオールジアクリレート、ヘキサンジオールジアクリレート、オクタンジオールジアクリレート、ノナンジオールジアクリレート、デカンジオールジアクリレート、ドデカンジオールジアクリレート、ヘキサデカンジオールジアクリレート、ネオペンチルグリコールジアクリレート、イソシアヌレートジアクリレート、及びヒドロキシピバリン酸ネオペンチルグリコールジアクリレート等の化合物、これら化合物のエチレングリコール変性品及びこれら化合物のプロピレングリコール変性品等のアルキレングリコール変性品、これら化合物のカプロラクトン変性品なども挙げられる。
また、エチレングリコールジアクリレート、ジエチレングリコールジアクリレート、トリエチレングリコールジアクリレート、ポリエチレングリコールジアクリレート、プロピレングリコールジアクリレート、ジプロピレングリコールジアクリレート、トリプロピレングリコールジアクリレート、及びポリプロピレングリコールジアクリレート等のジアクリレートなども挙げられる。
また、イソシアヌレートトリアクリレート、トリメチロールプロパントリアクリレート、グリセリントリアクリレート、ペンタエリスリトールトリアクリレート、ペンタエリスリトールテトラアクリレート、ジトリメチロールプロパントリアクリレート、ジトリメチロールプロパンテトラアクリレート、ジペンタエリスリトールペンタアクリレート、及びジペンタエリスリトールヘキサアクリレート等の化合物、これら化合物のエチレングリコール変性品及びこれら化合物のプロピレングリコール変性品等のアルキレングリコール変性品、これら化合物のカプロラクトン変性品なども挙げられる。
以上のように、アクリル酸エステル化合物としては、モノアクリレート、ジアクリレート、多官能アクリレートを適宜使用することができる。また、ハイパーブランチ型アクリレート、デンドリマー型アクリレート、ポリエステル系アクリレート、ポリウレタン系アクリレート、エポキシ系アクリレート、ポリブタジエン系アクリレートなどのアクリレートオリゴマーも使用できる。
第一の液体組成物及び第二の液体組成物から選ばれる少なくともいずれか一方をインク等として用いる場合、必要に応じて、色材を含有させてもよい。色材としては、特に制限されず、無機顔料、有機顔料、染料などを用いることができる。
ブラック顔料としては、ファーネス法又はチャネル法で製造されたカーボンブラック等が使用できる。
イエロー顔料としては、Pig.Yellow系の顔料、例えばピグメントイエロー1、ピグメントイエロー2、ピグメントイエロー3、ピグメントイエロー12、ピグメントイエロー13、ピグメントイエロー14、ピグメントイエロー16、ピグメントイエロー17、ピグメントイエロー73、ピグメントイエロー74、ピグメントイエロー75、ピグメントイエロー83、ピグメントイエロー93、ピグメントイエロー95、ピグメントイエロー97、ピグメントイエロー98、ピグメントイエロー114、ピグメントイエロー120、ピグメントイエロー128、ピグメントイエロー129、ピグメントイエロー138、ピグメントイエロー150、ピグメントイエロー151、ピグメントイエロー154、ピグメントイエロー155、ピグメントイエロー180、ピグメントイエロー185等が使用できる。
マゼンタ顔料としては、Pig.Red系の顔料、例えばピグメントレッド5、ピグメントレッド7、ピグメントレッド12、ピグメントレッド48(Ca)、ピグメントレッド48(Mn)、ピグメントレッド57(Ca)、ピグメントレッド57:1、ピグメントレッド112、ピグメントレッド122、ピグメントレッド123、ピグメントレッド168、ピグメントレッド184、ピグメントレッド202、ピグメントバイオレット19等が使用できる。
シアン顔料としては、Pig.Blue系の顔料、例えばピグメントブルー1、ピグメントブルー2、ピグメントブルー3、ピグメントブルー15、ピグメントブルー15:3、ピグメントブルー15:4、ピグメントブルー16、ピグメントブルー22、ピグメントブルー60、バットブルー4、バットブルー60等が使用できる。
白色顔料、もしくは物性改質のための無色の充填剤としては、硫酸バリウム等のアルカリ土類金属の硫酸塩、炭酸カルシウム等のアルカリ土類金属の炭酸塩、微粉ケイ酸、合成ケイ酸塩等のシリカ類、ケイ酸カルシウム、アルミナ、アルミナ水和物、酸化チタン、酸化亜鉛、タルク、クレイ等が使用できる。
重合禁止剤としては、例えば、4-メトキシ-1-ナフトール、メチルハイドロキノン、ハイドロキノン、t-ブチルハイドロキノン、ジ-t-ブチルハイドロキノン、メトキノン、2,2′-ジヒドロキシ-3,3′-ジ(α-メチルシクロヘキシル)-5,5′-ジメチルジフェニルメタン、p-ベンゾキノン、ジ-t-ブチルジフェニルアミン、9,10-ジ-n-ブトキシシアントラセン、4,4′-〔1,10-ジオキソ-1,10-デカンジイルビス(オキシ)〕ビス〔2,2,6,6-テトラメチル〕-1-ピペリジニルオキシなどが挙げられる。なお、第一の液体組成物中には、アルカリであるイオン重合禁止剤を添加しないことが好ましい。
界面活性剤としては、例えば、ポリエーテル、アミノ基、カルボキシル基、水酸基等を有する高級脂肪酸エステル、側鎖又は末端にポリエーテル、アミノ基、カルボキシル基、水酸基等を有するポリジメチルシロキサン化合物、ポリエーテル、アミノ基、カルボキシル基、水酸基等を有するフルオロアルキル化合物などが挙げられる。
液体組成物セットの用途は、目的に応じて適宜選択することができ、例えば、成形用樹脂、塗料、接着剤、絶縁材、離型剤、コーティング材、シーリング材、各種レジスト、各種光学材料などが挙げられる。
さらに、液体組成物セットは、後述するようにインクセット、又はインクジェット用インクセットとして用いて2次元の文字や画像、各種基材への意匠塗膜を形成するだけでなく、3次元の立体像(立体造形物)を形成するための立体造形用材料セットとしても用いることもできる。この立体造形用材料セットは、積層造形法において用いる立体構成材料(モデル材)や支持部材(サポート材)として用いてもよい。
液体組成物セットは、第一の液体組成物及び第二の液体組成物から選ばれる少なくともいずれか一方をインクとして用いることでインクセットとすることができる。
液体組成物セットは、第一の液体組成物及び第二の液体組成物から選ばれる少なくともいずれか一方をインクジェット方式で吐出するインクとして用いることでインクジェット用インクセットとすることができる。
上記の第一の液体組成物を第一の収容容器に収容し上記の第二の液体組成物を第二の収容容器に収容してセットとすることで、収容容器セットを作製することができる。なお、第一の収容容器は第一の液体組成物が収容された状態の容器を意味し、第二の収容容器は第二の液体組成物が収容された状態の容器を意味する。これにより、各液体組成物の搬送や交換等の作業において、これらに直接触れる必要がなくなり、手指や着衣の汚れを防ぐことができる。また、各液体組成物へのごみ等の異物の混入を防止することができる。
図1に示すように、注入口242から液体組成物を収容袋241内に充填し、該収容袋中に残った空気を排気した後、該注入口242を融着により閉じる。使用時には、ゴム部材からなる排出口243に装置本体の針を刺して装置に液体組成物を供給する。収容袋241は、透気性のないアルミニウムラミネートフィルム等の包装部材により形成される。
硬化物形成装置は、第一の液体組成物を付与する第一の付与手段と、第二の液体組成物を付与する第二の付与手段と、を有し、必要に応じて、その他の手段を有してもよい。本装置は、第一の付与手段から付与された第一の液体組成物と第二の付与手段から付与された第二の液体組成物とを接触させて硬化物を形成させる。このとき、先に付与された第一の液体組成物に対して第二の液体組成物を接触させて硬化物を形成する場合、先に付与された第二の液体組成物に対して第一の液体組成物を接触させて硬化物を形成する場合、及び第一の液体組成物及び第二の液体組成物を同時に付与することで接触させて硬化物を形成する場合のいずれであってもよい。また、本装置は、硬化物を形成するときに外部エネルギーを付与する手段を有さないことが好ましい。
図3に示す硬化物形成装置は、収納している基材を送り出す送出手段1、送り出された基材を搬送する経路である搬送経路2、基材に対して第一の液体組成物を吐出する第一の吐出手段および第二の液体組成物を吐出する第二の吐出手段が一体化した手段である吐出手段3、基材を収納するために巻き取る巻取手段6を有する。
(実施例1~51、比較例1~3)
下記表1~3に示す処方の材料を混合攪拌した後、1μmメンブレンフィルターでろ過し、第一の液体組成物を作製した。同様に、下記表1~3に示す処方の材料を混合攪拌した後、1μmメンブレンフィルターでろ過し、第二の液体組成物を作製した。その後、下記表1~3に示す通り、第一の液体組成物と第二の液体組成物を組み合わせて実施例1~51、比較例1~3の液体組成物セットを作製した。
なお、表1~3に示す各数値の単位は「質量%」である。
また、表1~3における各材料の記号は以下の化合物又は物質を表す。
~第一の液体組成物~
・A:メチレンマロネート化合物
・B:シアノアクリレート化合物
・C:シアン化ビニリデン
・D:ニトロエチレン
・E:酸性物質
~第二の液体組成物~
・F:ビニル基を有する化合物(ビニルエーテル化合物)
・F’:ビニル基とアクリロイル基を有する化合物
・G:ビニル基を有する化合物(スチレン化合物)
・H:アクリロイル基を有する化合物(アクリル酸エステル化合物)
・I:アクリロイル基を有する化合物(アクリルアミド化合物)
・J:ビニル基を有する化合物(N-ビニル化合物)
~第一の液体組成物中の一般式(1)で表される化合物~
・A1:メチレンマロン酸ジエチル(X=-COOEt、Y=-COOEt、シグマアルドリッチ社製)
・B1:シアノアクリル酸エチル(X=-CN、Y=-COOEt、田岡化学工業株式会社製)
・B2:シアノアクリル酸イソブチル(X=-CN、Y=-COO(iso-Bu)、東亞合成株式会社製)
・B3:シアノアクリル酸エトキシエチル(X=-CN、Y=-COOC2H4-O-Et、東亞合成株式会社製)
・C1:シアン化ビニリデン(X=-CN、Y=-CN、Zhengzhou JACS Chem Co,Ltd.社製)
・D1:ニトロエチレン(X=-H、Y=-NO2、Santa Cruz Biotechnology,Inc.社製)
~第一の液体組成物中の酸性物質~
・E1:酢酸(東京化成工業株式会社製)
・E2:乳酸(東京化成工業株式会社製)
・E3:リン酸メタクリロイルオキシエチル(共栄社化学株式会社製、ライトエステルP-2M)
・E4:カプロラクトン変性リン酸メタクリロイルオキシエチル(日本化薬株式会社製、KAYAMER PM-21)
~第二の液体組成物中のビニル基又はアクリロイル基を有する化合物~
・F1:トリエチレングリコールジビニルエーテル(東京化成工業株式会社製)
・F’2:2-(2-ビニロキシエトキシ)エチルアクリレート(株式会社日本触媒製)
・G1:スチレン(東京化成工業株式会社製)
・G2:4-メチルスチレン(東京化成工業株式会社製)
・H1:フェノキシエチルアクリレート(東京化成工業株式会社製)
・H2:ジペンタエリスリトールヘキサアクリレート(日本化薬株式会社製 KAYARAD DPHA)
・I1:4-アクリロイルモルホリン(東京化成工業株式会社製)
・I2:N-(2-ヒドロキシエチル)アクリルアミド(東京化成工業株式会社製)
・J1:N-ビニルカプロラクタム(東京化成工業株式会社製)
・J2:N-ビニルピロリドン(株式会社日本触媒製)
プラスチック基材(ポリエチレンテレフタレートフィルム、東洋紡製、商品名:エステルフィルムE5100、厚さ100ミクロン)に対し、第一の液体組成物をワイヤーバーで塗工した。第一の液体組成物の塗布量は、1平方メートル当たり1×101グラムとなるようにした。次に、第一の液体組成物の塗工面の一部に対し、第二の液体組成物をマイクロシリンジで滴下した。第二の液体組成物の滴下量は、1平方メートル当たり1×101グラムとなるようにした。その後、1分後、10分後、60分後の時点で、両液体組成物の混和部を指触して下記評価基準に基づいて硬化性および取扱性を評価した。なお、本評価は、温度23℃以上25℃以下にて行った。
(評価基準)
A:指に何も付着しないない程度に硬化している
B:硬化しているが指にわずかに液体組成物が付着する
C:液状であり硬化が不十分
F:ワイヤーバーで塗工する前から増粘、硬化が始まり、均一な塗膜形成が困難
プラスチック基材(ポリエチレンテレフタレートフィルム、東洋紡製、商品名:エステルフィルムE5100、厚さ100ミクロン)に対し、第一の液体組成物をワイヤーバーで塗工した。第一の液体組成物の塗布量は、1平方メートル当たり1×101グラムとなるようにした。次に、第一の液体組成物の塗工面の一部に対し、循環型ヘッド(MH5421MF、リコー社製)を搭載したインクジェット吐出装置を用いて第二の液体組成物(図1に示すアルミ製パウチ袋に気泡が入らないように密封されており、更に図2に示すようなプラスチック製カートリッジに収納されている)をベタ状(3cm×3cm)に吐出した。第二の液体組成物の吐出量は、1平方メートル当たり1×101グラムとなるようにした。その後、1分後、10分後、60分後の時点で、両液体組成物の混和部を指触して下記評価基準に基づいて硬化性および取扱性を評価した。なお、本評価は、温度23℃以上25℃以下にて行い、循環型ヘッドの温調機能は使用しなかった。
(評価基準)
A:指に何も付着しないない程度に硬化している
B:硬化しているが指にわずかに液体組成物が付着する
C:液状であり硬化が不十分
F:ワイヤーバーで塗工する前から増粘、硬化が始まり、均一な塗膜形成が困難
プラスチック基材(ポリエチレンテレフタレートフィルム、東洋紡製、商品名:エステルフィルムE5100、厚さ100ミクロン)に対し、循環型ヘッド(MH5421MF、リコー社製)を搭載したインクジェット吐出装置を用いて第一の液体組成物(図1に示すアルミ製パウチ袋に気泡が入らないように密封されており、更に図2に示すようなプラスチック製カートリッジに収納されている)をベタ状(5cm×5cm)に吐出した。第一の液体組成物の吐出量は、1平方メートル当たり1×101グラムとなるようにした。次に、第一の液体組成物の吐出面の一部に対し、循環型ヘッド(MH5421MF、リコー社製)を搭載したインクジェット吐出装置を用いて第二の液体組成物(図1に示すアルミ製パウチ袋に気泡が入らないように密封されており、更に図2に示すようなプラスチック製カートリッジに収納されている)をベタ状(3cm×3cm)に吐出した。第二の液体組成物の吐出量は、1平方メートル当たり1×101グラムとなるようにした。その後、1分後、10分後、60分後の時点で、両液体組成物の混和部を指触して下記評価基準に基づいて硬化性および取扱性(吐出性)を評価した。本評価は、温度23℃以上25℃以下にて行い、循環型ヘッドの温調機能は使用しなかった。
(評価基準)
A:指に何も付着しないない程度に硬化している
B:硬化しているが指にわずかに液体組成物が付着する
C:液状であり硬化が不十分
F:第一の液体組成物を収容するカートリッジから吐出ヘッドまでの経路であるチューブ内にて硬化物が形成されて吐出困難である
第一の液体組成物を容積110mLの容器(アズワン社製褐色ガラススクリュー管瓶No.8)に50mL入れ、容器中の第一の液体組成物が温度25℃かつ湿度50%RHの空気に接触している状態で密閉し、温度25℃の環境下で1日(24時間)、7日(168時間)、30日(720時間)静置したとき、下記式に基づいて粘度変化率を算出した。次に、下記評価基準に基づいて保存性を評価した。なお、粘度は、温度25℃において東機産業社製E型粘度計TVE-22Lを用いることで測定した。
A:粘度変化率が5.0%以下である
B:粘度変化率が5.0%より大きい
C:粘度計の測定限界を超えて粘度増加した又は瓶内の少なくとも一部で硬化が目視で確認できる
F:第一の液体組成物を容器に入れる際に、容器壁面に飛散して付着した液滴が直ちに硬化する
2 搬送経路
3 吐出手段
6 巻取手段
200 収容容器
241 収容袋
242 注入口
243 排出口
244 カートリッジケース
Claims (29)
- 前記第一の液体組成物及び前記第二の液体組成物が接触すると硬化する請求項1から6のいずれか一項に記載の液体組成物セット。
- 前記一般式(1)で表される化合物は、シアノアクリレート化合物である請求項1から7のいずれか一項に記載の液体組成物セット。
- 前記第二の液体組成物は、ビニルエーテル化合物、N-ビニル化合物、アクリル酸エステル化合物、及びアクリルアミド化合物から選ばれる少なくとも1つを含有する請求項1から8のいずれか一項に記載の液体組成物セット。
- 前記第一の液体組成物及び前記第二の液体組成物は、重合開始剤を実質的に含有しない請求項1から10のいずれか一項に記載の液体組成物セット。
- 下記一般式(1)で表される化合物及び酸性物質を含有する第一の液体組成物を収容した第一の収容容器と、ビニル基又はアクリロイル基を有する化合物を含有する第二の液体組成物を収容した第二の収容容器と、を有する収容容器セットであって、
前記第一の液体組成物は、インクジェット方式で吐出される液体組成物であり、
前記酸性物質は、塩酸、硝酸、硫酸、二酸化硫黄、スルトン化合物、カルボン酸化合物、スルホン酸化合物、及びリン酸化合物から選ばれる少なくとも1つである収容容器セット。
- 下記一般式(1)で表される化合物及び酸性物質を含有する第一の液体組成物を収容した第一の収容容器と、ビニル基又はアクリロイル基を有する化合物を含有する第二の液体組成物を収容した第二の収容容器と、を有する収容容器セットであって、
前記第二の液体組成物は、インクジェット方式で吐出される液体組成物であり、
前記酸性物質は、塩酸、硝酸、硫酸、二酸化硫黄、スルトン化合物、カルボン酸化合物、スルホン酸化合物、及びリン酸化合物から選ばれる少なくとも1つである収容容器セット。
- 下記一般式(1)で表される化合物及び酸性物質を含有する第一の液体組成物を付与する第一の付与手段と、ビニル基又はアクリロイル基を有する化合物を含有する第二の液体組成物を付与する第二の付与手段と、を有する硬化物形成装置であって、
前記第一の付与手段は、インクジェット方式で吐出する付与手段であり、
前記酸性物質は、塩酸、硝酸、硫酸、二酸化硫黄、スルトン化合物、カルボン酸化合物、スルホン酸化合物、及びリン酸化合物から選ばれる少なくとも1つである硬化物形成装置。
- 下記一般式(1)で表される化合物及び酸性物質を含有する第一の液体組成物を付与する第一の付与手段と、ビニル基又はアクリロイル基を有する化合物を含有する第二の液体組成物を付与する第二の付与手段と、を有する硬化物形成装置であって、
前記第二の付与手段は、インクジェット方式で吐出する付与手段であり、
前記酸性物質は、塩酸、硝酸、硫酸、二酸化硫黄、スルトン化合物、カルボン酸化合物、スルホン酸化合物、及びリン酸化合物から選ばれる少なくとも1つである硬化物形成装置。
- 下記一般式(1)で表される化合物及び酸性物質を含有する第一の液体組成物を付与する第一の付与工程と、ビニル基又はアクリロイル基を有する化合物を含有する第二の液体組成物を付与する第二の付与工程と、を有する硬化物形成方法であって、
前記第一の付与工程は、インクジェット方式で吐出する付与工程であり、
前記酸性物質は、塩酸、硝酸、硫酸、二酸化硫黄、スルトン化合物、カルボン酸化合物、スルホン酸化合物、及びリン酸化合物から選ばれる少なくとも1つである硬化物形成方法。
- 下記一般式(1)で表される化合物及び酸性物質を含有する第一の液体組成物を付与する第一の付与工程と、ビニル基又はアクリロイル基を有する化合物を含有する第二の液体組成物を付与する第二の付与工程と、を有する硬化物形成方法であって、
前記第二の付与工程は、インクジェット方式で吐出する付与工程であり、
前記酸性物質は、塩酸、硝酸、硫酸、二酸化硫黄、スルトン化合物、カルボン酸化合物、スルホン酸化合物、及びリン酸化合物から選ばれる少なくとも1つである硬化物形成方法。