JP7397605B2 - 偏光板の製造方法 - Google Patents
偏光板の製造方法 Download PDFInfo
- Publication number
- JP7397605B2 JP7397605B2 JP2019166289A JP2019166289A JP7397605B2 JP 7397605 B2 JP7397605 B2 JP 7397605B2 JP 2019166289 A JP2019166289 A JP 2019166289A JP 2019166289 A JP2019166289 A JP 2019166289A JP 7397605 B2 JP7397605 B2 JP 7397605B2
- Authority
- JP
- Japan
- Prior art keywords
- polarizing plate
- polarizer
- optical film
- boric acid
- region
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
厚み15μm以下の偏光子の少なくとも片側に光学フィルムを貼合して第1積層体を作製する第1積層工程と、
前記第1積層体を、温度35℃以上において相対湿度75%RH以上の気相中に保持する加湿処理工程と
を含む、偏光板の製造方法。
[2] 前記第1積層体を成形加工する成形工程を前記加湿処理工程前にさらに含む、[1]に記載の偏光板の製造方法。
[3] 前記成形工程において、前記第1積層体に異形部を形成する、[2]に記載の偏光板の製造方法。
[4] 前記第1積層体を切削加工する切削工程を前記加湿処理工程前にさらに含む、[2]または[3]に記載の偏光板の製造方法。
[5] 前記切削工程において、前記第1積層体の平面視において、光学フィルムの端部の位置と偏光子の端部の位置とが同一となるように前記第1積層体を切削加工する、[4]に記載の偏光板の製造方法。
[6] ホウ酸とヨウ素とを含有する樹脂フィルムを含み、厚みが15μm以下である偏光子であって、
前記偏光子の端部を含む領域において、該領域以外の領域におけるホウ酸の濃度より低い濃度でホウ酸を含有する領域を有し、
前記偏光子の端部を含む領域においてヨウ素抜けが生じていない、偏光子。
[7] [6]に記載の偏光子と、前記偏光子の少なくとも片側に貼合された光学フィルムとを有する、偏光板。
[8] 前記偏光板の平面視における端部において、前記偏光子の端部の位置と前記光学フィルムの端部の位置とが同一である、[7]に記載の偏光板。
[9] [8]に記載の偏光板を備えた画像表示装置。
[10] カメラホールを有する、[9]に記載の画像表示装置。
本発明の一実施態様に係る偏光板の製造方法は、厚み15μm以下の偏光子の少なくとも片側に光学フィルムを貼合して第1積層体を作製する第1積層工程と、第1積層体を、温度35℃以上において相対湿度75%RH以上の気相中に保持する加湿処理工程とを含む。
第1積層工程では、偏光子と光学フィルムとを重ねて互いに貼合することにより第1積層体を作製する。偏光子および光学フィルムは長尺な帯状であってよい。偏光子を、一対の光学フィルムの間に配置されるように重ねる場合、図2に示されるように、第1積層体10において、偏光子7は一対の第1光学フィルム5および第2光学フィルム9の間に位置する。光学フィルムは、接着剤からなる接着層を介して偏光子に貼合することができる。
偏光子は、例えば一軸延伸されたポリビニルアルコール系樹脂フィルムにヨウ素が吸着配向され、ポリビニルアルコール分子鎖同士がホウ酸で架橋された偏光子であってよい。偏光子は、吸収軸に平行な振動面をもつ直線偏光を吸収し、吸収軸に直交する(透過軸と平行な)振動面をもつ直線偏光を透過する性質を有する吸収型の偏光子であることができる。
光学フィルムは、透光性を有する熱可塑性樹脂であってよい。光学フィルムは、光学的に透明な熱可塑性樹脂であってもよい。光学フィルムを構成する樹脂は、例えば、鎖状ポリオレフィン系樹脂、環状オレフィンポリマー系樹脂(COP系樹脂)、セルロースエステル系樹脂、ポリエステル系樹脂、ポリカーボネート系樹脂、(メタ)アクリル系樹脂、ポリスチレン系樹脂、またはこれらの混合物若しくは共重合体であってよい。
第1積層体を温度35℃以上において相対湿度75%RH以上の気相中に保持することにより加湿処理を行う。加湿処理によれば、第1積層体の端部を含む領域において、この領域以外の領域におけるホウ酸の濃度より低い濃度でホウ酸を含有する領域(以下、ホウ酸低含有領域ともいう)が形成されるにもかかわらずヨウ素抜けが生じず、ホウ酸低含有領域においても直線偏光能が発揮されるようになる。本発明の製造方法により製造された偏光板は、ヒートショック試験においてもクラックが生じず、端部を含む領域においても直線偏光能を発揮することができる。
ヨウ素抜けが生じている領域(以下、略してヨウ素抜け領域ともいう)は、偏光顕微鏡を用いてクロスニコル状態で光が透過する領域として目視で観察される領域である。ヨウ素には、例えばヨウ素分子(I2)、ポリヨウ素錯体(I3 -、I5 -)、ヨウ素イオン(I-)が含まれる。
本明細書において、平面視とは、偏光板の厚み方向から見ることを意味する。
ホウ酸低含有領域は、偏光板の平面視における端部から15μm以下の全領域と、偏光板の平面視における端部から内側方向において15μm超200μm未満の全領域とに連続的に形成されていてよい。言い換えれば、ホウ酸低含有領域は、偏光板の平面視における端部および端部から200μm未満の間の全領域にわたって形成されてよい。ホウ酸低含有領域が、偏光板の平面視における端部および端部から200μm未満の間の全領域にわたって形成される場合、ホウ酸低含有領域とそれ以外の領域との境界が端部および端部から200μm未満の間の領域に存在することができる。
ホウ酸低含有領域は、好ましくは偏光板の平面視における端部および端部から100μm以下の間の全領域にわたって形成され、より好ましくは偏光板の平面視における端部および端部から50μm以下の間の全領域にわたって形成され、さらに好ましくは偏光板の平面視における端部および端部から20μm以下の間の全領域にわたって形成される。
ホウ酸低含有領域が形成された領域とそれ以外の領域との境界は、例えば後述の実施例の欄において説明する飛行時間型二次イオン質量分析法(TOF-SIMS)において得られる端部からの距離に対するホウ酸濃度プロファイルから求めることができる。例えば、ホウ酸濃度プロファイルにおいてホウ酸イオン強度が一定である領域が読み取れる場合には、その領域のホウ酸イオン強度の平均値を求め、端部から、ホウ酸イオン強度が上記平均値となる位置までをホウ酸低濃度部位とすることができる。上記ホウ酸イオン強度が一定である領域がホウ酸濃度プロファイルにおいて読み取りにくい場合には、ホウ酸濃度プロファイルにおいて、ホウ酸イオン強度が最大となる点から内側に30μmの範囲におけるホウ酸イオン強度の平均値を求め、端部から、ホウ酸イオン強度が上記平均値となる位置までをホウ酸低濃度部位とすることができる。
偏光板の製造方法は、加湿処理工程前に、第1積層体を成形加工する成形工程をさらに含むことができる。成形工程において、第1積層体を、切断および/または打ち抜き加工により所定の形状に成形加工することができる。切断および/または打ち抜き加工は、刃物を用いたり、レーザー光を照射したりすることにより行うことができる。レーザー光は、CO2レーザーであってよい。
偏光板の製造方法は、加湿処理工程前に、エンドミルを第1積層体または後述の第2積層体の外周に接触させて、エンドミルを積層体の外周に沿って移動させる切削工程をさらに含むことができる。図2に示されるように、切削工程前の第1積層体10の外周全域において、偏光子7および第1光学フィルム5および第2光学フィルム9の端部の位置は揃っていてよい。
本発明の別の実施態様に係る偏光子は、ホウ酸とヨウ素とを含有する樹脂フィルムを含み、厚みが15μm以下である偏光子である。偏光子は、例えば一軸延伸されたポリビニルアルコール系樹脂フィルムにヨウ素が吸着配向され、ポリビニルアルコール分子鎖同士がホウ酸で架橋された偏光子であってよい。偏光子は、吸収軸に平行な振動面をもつ直線偏光を吸収し、吸収軸に直交する(透過軸と平行な)振動面をもつ直線偏光を透過する性質を有する吸収型の偏光子であることができる。
偏光子のホウ酸低含有領域は、偏光子の平面視における端部から15μm以下の全領域と、偏光子の平面視における端部から内側方向において15μm超200μm未満の全領域とに連続的に形成されていてよい。言い換えれば、偏光子のホウ酸低含有領域は、偏光子の平面視における端部および端部から200μm未満の間の全領域にわたって形成されてよい。偏光子のホウ酸低含有領域が、偏光子の平面視における端部および端部から200μm未満の間の全領域にわたって形成される場合、偏光子のホウ酸低含有領域とそれ以外の領域との境界が端部および端部から200μm未満の間の領域に存在することができる。
偏光子のホウ酸低含有領域は、好ましくは偏光子の平面視における端部および端部から100μm以下の間の全領域にわたって形成され、より好ましくは偏光子の平面視における端部および端部から50μm以下の間の全領域にわたって形成され、さらに好ましくは偏光子の平面視における端部および端部から20μm以下の間の全領域にわたって形成される。
ホウ酸低含有部位が形成された領域とそれ以外の領域との境界は、上述の偏光板の製造方法において述べた方法により決定することができる。
本発明のさらに別の実施態様にかかる偏光板は、上述の偏光子と、偏光子の少なくとも片側に貼合された光学フィルムとを有する。光学フィルムの例示および好ましい範囲は、上述の偏光板の製造方法において説明した例示および好ましい範囲が適用される。
例えば、偏光板は、第1光学フィルムおよび第2光学フィルムからなる一対の光学フィルムに加えて、樹脂を含む別の光学フィルムを更に備えてよい。つまり、偏光板は、3枚以上の光学フィルムを備えていてよい。例えば、図10に示されるように、偏光板が、第1光学フィルム3および第2光学フィルム4と、第1光学フィルム3および第2光学フィルム4の間に位置する偏光子2と、第1光学フィルム3に重なる第3光学フィルム15を備えてよい。第3光学フィルム15は、上述の接着層を介して第1光学フィルム3に重ねられてよい。第3光学フィルム15に含まれる樹脂は、第1光学フィルム3および第2光学フィルム4其々に含まれる樹脂として列挙された上記の樹脂のうち少なくともいずれかであってよい。第3光学フィルム15の組成は、第1光学フィルム3の組成と同じであってよい。第3光学フィルム15の組成は、第1光学フィルム3の組成と異なってもよい。第3光学フィルム15の組成は、第2光学フィルム4の組成と同じであってよい。第3光学フィルム15の組成は、第2光学フィルム4の組成と異なってもよい。第3光学フィルム15の厚みは、例えば、5μm以上200μm以下であってよい。第3光学フィルム15は、画像表示装置の製造過程において、偏光板から剥離され、除去されてよい。つまり、第3光学フィルム15は、仮の光学フィルムであってよい。
偏光板は画像表示装置に用いることができる。画像表示装置としては、例えば液晶表示装置、有機EL表示装置等が挙げられる。偏光板は、画像表示装置の視認側に配置される偏光板に用いられてもよいし、画像表示装置のバックライト側に配置される偏光板に用いられてもよいし、視認側およびバックライト側の双方の偏光板に用いられてもよい。偏光板は、色抜け箇所が目立ちにくいことから、画像表示装置の視認側に用いられた場合であっても、デザイン性が損なわれにくい。そのため、画像表示装置は、カメラホールを有する画像表示装置、例えばスマートフォンや携帯電話等のモバイル機器、およびパーソナルコンピュータ等に用いられる画像表示装置として好適である。
実施例および比較例で得られた偏光板を、粘着剤層を用いてコーニングガラスに貼合した。このガラス貼合サンプルを冷熱衝撃試験機に入れ、「-40℃の槽で30分間保持した後、瞬時に85℃の槽に移して30分間保持する」操作を1サイクルとし、これを100サイクル繰り返すヒートショック試験を実施した。光学顕微鏡を用いて、クラックの有無を確認した。
飛行時間型二次イオン質量分析法(TOF-SIMS)によりホウ酸イオン(BO3 3-)の濃度の分布を求めた。図11に示すように、偏光板110の光学フィルム5(厚み52μm)側に貼合したプロテクトフィルムを剥離し、光学フィルム9(厚み21μm)側の粘着剤層の上に貼合したセパレートフィルムを剥離し、凹状部のコーナーを含む端部領域1箇所を100μm幅で偏光板の内側に向けて1mm(1000μm)長さに切出し、測定サンプル200とした。測定サンプル200は、光学フィルム201(厚み52μm)、接着層202(厚み1μm)、偏光子203(厚み8μm)、接着層204(厚み1μm)、光学フィルム205(厚み21μm)、粘着剤層206(厚み20μm)をこの順に有した。イオンビームは、測定サンプル200の長さ方向(1000μm)側面における測定領域207を走査しながら照射して、この側面におけるホウ酸イオンのシグナル強度の2次元分布を得、得られた2次元分布から偏光子側面に相当する部分を切出し、測定サンプル200の長さ方向に対してシグナル強度の積算値をプロットして、長さ方向に対するホウ酸濃度のプロファイルを得た。飛行時間型二次イオン質量分析法(TOF-SIMS)の条件を下記に示す。
なおホウ酸濃度の測定は偏光板状態で行ったが、得られたホウ酸濃度は偏光子のホウ酸濃度と見なすことができる。
装置名:製品名:PHI TRIFT V nano TOF(アルバック・ファイ株式会社)
照射した一次イオン:Au3 +
一次イオン加速電圧:30kV
イオンビームの空間分解能:1μm×1μm
測定領域の面積:200μm×200μm
得られたホウ酸濃度プロファイルから、端部からの距離が30μm以上60μm以下の範囲におけるホウ酸イオン強度の平均値を求め、端部から、ホウ酸イオン強度が上記平均値となる位置までをホウ酸低濃度部位とし、偏光板端部からのホウ酸低濃度部位が形成されている領域の長さ(ホウ酸低濃度部位の長さ)を測定した。
偏光板の塩基処理を行った部分について光学顕微鏡透過光により観察を行い、光学顕微鏡像をパーソナルコンピューターに取り込み、以下のように、偏光板端部からのヨウ素低濃度部位が形成されている領域の長さ(ヨウ素低濃度部位の長さ)を測定した。
パーソナルコンピューター上に取込んだ光学顕微鏡画像において、目視ではヨウ素低濃度部位は明るく見え、内側領域は暗く見える。光学顕微鏡画像に画像処理を施して、ヨウ素低濃度部の明るさが180~220となり、内側領域の明るさが100~140となるように、256階調の白黒画像(明るさ255が白で0が黒)に変換し、明るさが180以上となる領域(白)をヨウ素低濃度部位としてヨウ素低濃度部位が存在するか確認した。
厚み20μmのポリビニルアルコールフィルム(平均重合度約2,400、ケン化度99.9モル%以上)を、乾式延伸により約4.9倍に一軸延伸し、さらに緊張状態を保ったまま、60℃の純水に1分間浸漬した後、ヨウ素/ヨウ化カリウム/水の重量比が0.05/5/100の水溶液に28℃で60秒間浸漬した。その後、ヨウ化カリウム/ホウ酸/水の重量比が8.5/8.5/100の水溶液に72℃で300秒間浸漬した。引き続き26℃の純水で20秒間洗浄した後、65℃で乾燥し、ポリビニルアルコールフィルムにヨウ素が吸着配向している厚み8μmの偏光子を得た。
厚み30μmのポリビニルアルコールフィルムを用いて、乾式延伸により約5.0倍に一軸延伸し、厚み12μmの偏光子を得たこと以外は、厚み8μmの偏光子と同様にして厚み12μmの偏光子を得た。
厚み75μmのポリビニルアルコールフィルムを用いて、乾式延伸により約4倍に一軸延伸し、厚み28μmの偏光子を得た以外は、厚み8μmの偏光子と同様にして厚み28μmの偏光子を得た。
COP:厚み23μmのシクロオレフィン系樹脂フィルム(日本ゼオン株式会社製)。
TAC:厚み20μmのトリアセチルセルロースフィルム(コニカミノルタ株式会社製)。
水100部に対して、カルボキシル基変性ポリビニルアルコール(株式会社クラレ製のKL-318)3部を溶解し、その水溶液に、水溶性エポキシ化合物であるポリアミドエポキシ系添加剤(住化ケムテックス株式会社製のスミレーズレジン(登録商標)650(30)、固形分濃度30%の水溶液〕1.5部を添加して、水系接着剤とした。
8μm偏光子の両面に、水系接着剤を介して、コロナ放電処理を施した光学フィルム(COPフィルム)を貼合した。一方の光学フィルムの偏光子とは反対側の面に粘着剤を塗布して粘着剤層を形成し、その上にセパレートフィルムを貼合した。このセパレートフィルムは、粘着剤層から剥離可能であった。粘着剤層を設けた光学フィルムとは別の光学フィルムの偏光子とは反対側にプロテクトフィルムを貼合した。このプロテクトフィルムは光学フィルムから剥離可能であった。こうして得られた偏光板を5.5cm角にチップカットし、打抜き刃を用いて直径6mmの貫通孔を設ける異形加工を行った。
加湿処理の条件を表1に示す条件に変えたこと以外は実施例1と同様にして実施例2の偏光板を作製した。結果を表1に示す。また、図12に偏光板の端部からの距離に対するホウ酸濃度の測定結果を示す。さらに、図13にヨウ素抜け観察結果を示す。
加湿処理の条件を表1に示す条件に変えたこと以外は実施例1と同様にして実施例3の偏光板を作製した。結果を表1に示す。
加湿処理の条件を表1に示す条件に変えたこと以外は実施例1と同様にして比較例1の偏光板を作製した。結果を表1に示す。
加湿処理の条件を表1に示す条件に変えたこと以外は実施例1と同様にして比較例2の偏光板を作製した。結果を表1に示す。
加湿処理を行う代わりに温度74℃の温水中に16分間浸漬したこと以外は実施例1と同様にして比較例3の偏光板を作製した。結果を表1に示す。ヨウ素抜け観察結果を図14に示す。この偏光板には、ヨウ素抜けに伴うヨウ素低濃度部位が生じており、その長さは約250μmであった。
12μm偏光子の一方の面に、水系接着剤を介して、コロナ放電処理を施した光学フィルムCOPを貼合し、他方の面に、水系接着剤を介して、コロナ放電処理を施した光学フィルムTACを貼合し、偏光板を作製した。得られた偏光板を5.5cm角にチップカットし、直径6mmの貫通孔を設ける異形加工を行った。
加湿処理の条件を表2に示す条件に変えたこと以外は実施例4と同様にして実施例5の偏光板を作製した。結果を表2に示す。
加湿処理の条件を表2に示す条件に変えたこと以外は実施例4と同様にして比較例4の偏光板を作製した。結果を表2に示す。
加湿処理の条件を表2に示す条件に変えたこと以外は実施例4と同様にして比較例5の偏光板を作製した。結果を表2に示す。
加湿処理の条件を表2に示す条件に変えたこと以外は実施例4と同様にして比較例6の偏光板を作製した。結果を表2に示す。
28μm偏光子の一方の面に、水系接着剤を介して、コロナ放電処理を施した光学フィルムCOPを貼合し、他方の面に、水系接着剤を介して、コロナ放電処理を施した光学フィルムTACを貼合し、偏光板を作製した。得られた偏光板を5.5cm角にチップカットし、直径6mmの貫通孔を設ける異形加工を行った。
加湿処理の条件を表3に示す条件に変えたこと以外は比較例7と同様にして比較例8の偏光板を作製した。結果を実施例1および実施例2の結果と共に表3に示す。
Claims (6)
- 偏光板の製造方法であって、
厚み15μm以下の偏光子の両面に光学フィルムを貼合して第1積層体を作製する第1積層工程と、
前記第1積層体を、温度35℃以上において相対湿度75%RH以上の気相中に0.5時間以上4時間以下保持する加湿処理工程と
を含み、
前記第1積層体において、前記偏光子は第1光学フィルムおよび第2光学フィルムの間に位置し、
前記第1光学フィルムおよび前記第2光学フィルムはいずれも環状オレフィンポリマー系樹脂を含み、
前記偏光子は、ホウ酸とヨウ素とを含有する樹脂フィルムである、
偏光板の製造方法。 - 前記第1積層体を成形加工する成形工程を前記加湿処理工程前にさらに含む、請求項1に記載の偏光板の製造方法。
- 前記成形工程において、前記第1積層体に異形部を形成する、請求項2に記載の偏光板の製造方法。
- 前記第1積層体を切削加工する切削工程を前記加湿処理工程前にさらに含む、請求項2または3に記載の偏光板の製造方法。
- 前記切削工程において、前記第1積層体の平面視において、光学フィルムの端部の位置と偏光子の端部の位置とが同一となるように前記第1積層体を切削加工する、請求項4に記載の偏光板の製造方法。
- 前記光学フィルムは、水系接着剤を介して前記偏光子の両面に貼合する、請求項1~5のいずれか一項に記載の偏光板の製造方法。