JP7349747B2 - 樹枝状ニッケル結晶粒子およびその製造方法 - Google Patents
樹枝状ニッケル結晶粒子およびその製造方法 Download PDFInfo
- Publication number
- JP7349747B2 JP7349747B2 JP2021192240A JP2021192240A JP7349747B2 JP 7349747 B2 JP7349747 B2 JP 7349747B2 JP 2021192240 A JP2021192240 A JP 2021192240A JP 2021192240 A JP2021192240 A JP 2021192240A JP 7349747 B2 JP7349747 B2 JP 7349747B2
- Authority
- JP
- Japan
- Prior art keywords
- crystal particles
- dendritic
- nickel crystal
- nickel
- dendritic nickel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(1) ニッケルからなる樹枝状ニッケル結晶粒子であって、前記樹枝状ニッケル結晶粒子の走査型電子顕微鏡写真の撮影画像において、前記樹枝状ニッケル結晶粒子の全体の長さが5~150μmであり、前記樹枝状ニッケル結晶粒子の全体の幅が1~15μmであり、前記樹枝状ニッケル結晶粒子が複数の中枝を有し、当該中枝の側面または端部に当該中枝とは異なる他の中枝の端部が結合して当該樹枝状ニッケル結晶粒子が形成されており、当該中枝の長さが2~25μmであり、当該中枝の幅が1~5μmであり、前記中枝が複数の微細小枝を有し、当該微細小枝同士が結合して当該中枝が形成されており、当該微細小枝の長さが20nm~2μmであり、当該微細小枝の幅が20nm~1μmであることを特徴とする樹枝状ニッケル結晶粒子、および
(2) 前記(1)に記載の樹枝状ニッケル結晶粒子を含有することを特徴とする導電性フィルム、導電膜または導電性ペースト
に関する。
陽極板としてニッケル板(縦:130mm、横:80mm、厚さ:2mm)、陰極板としてステンレス鋼板(材質:SUS304、縦:100mm、横:67mm、厚さ:0.3mm)を用いた。電解液として硫酸ニッケルをイオン交換水に溶解させた溶液を用い、硫酸ニッケルの濃度が20g/Lに調整され、硫酸アンモニウムの濃度が30g/Lに調整され、pHが7に調整された電解液を用いた。
陽極板としてニッケル板(縦:130mm、横:80mm、厚さ:2mm)、陰極板としてステンレス鋼板(材質:SUS304、縦:100mm、横:67mm、厚さ:0.3mm)を用いた。電解液として硫酸ニッケル六水和物をイオン交換水に溶解させた溶液を用い、硫酸ニッケルの濃度が20g/Lに調整され、グリシンの濃度が50g/Lに調整され、pHが4に調整された電解液を用いた。
陽極板としてニッケル板(縦:130mm、横:80mm、厚さ:2mm)、陰極板としてステンレス鋼板(材質:SUS304、縦:100mm、横:67mm、厚さ:0.3mm)を用いた。電解液として硫酸ニッケルをイオン交換水に溶解させた溶液を用い、硫酸ニッケルの濃度が10g/Lに調整され、コハク酸の濃度が20g/Lに調整され、pHが7に調整された電解液を用いた。
陽極板としてニッケル板(縦:130mm、横:80mm、厚さ:2mm)、陰極板としてステンレス鋼板(材質:SUS304、縦:100mm、横:67mm、厚さ:0.3mm)を用いた。電解液として硫酸ニッケル六水和物をイオン交換水に溶解させた溶液を用い、硫酸ニッケルの濃度が20g/Lに調整され、硫酸アンモニウムの濃度が55g/Lに調整され、pHが4に調整された電解液を用いた。
陽極板としてニッケル板(縦:130mm、横:80mm、厚さ:2mm)、陰極板としてステンレス鋼板(材質:SUS304、縦:100mm、横:67mm、厚さ:0.3mm)を用いた。電解液として塩化ニッケルをイオン交換水に溶解させた溶液を用い、塩化ニッケルの濃度が15g/Lに調整され、塩化アンモニウムの濃度が35g/Lに調整され、pHが7に調整された電解液を用いた。
従来の導電性材料としてデンドライト構造を有する銅粒子を用いた。当該銅粒子の走査型電子顕微鏡写真を図4に示す。
陽極板としてニッケル板(縦:130mm、横:80mm、厚さ:2mm)、陰極板としてステンレス鋼板(材質:SUS304、縦:100mm、横:67mm、厚さ:0.3mm)を用いた。電解液として硫酸ニッケル六水和物をイオン交換水に溶解させた溶液を用い、硫酸ニッケルの濃度が20g/Lに調整され、クエン酸の濃度が50g/Lに調整され、pHが5に調整された電解液を用いた。
陽極板としてニッケル板(縦:130mm、横:80mm、厚さ:2mm)、陰極板としてステンレス鋼板(材質:SUS304、縦:100mm、横:67mm、厚さ:0.3mm)を用いた。電解液として硫酸ニッケル六水和物をイオン交換水に溶解させた溶液を用い、硫酸ニッケルの濃度が40g/Lに調整され、グリシンの濃度が50g/Lに調整され、pHが4に調整された電解液を用いた。
100mL容のビーカー内に、樹枝状ニッケル結晶粒子50g、銅粒子50gまたはニッケル結晶粒子50gと酢酸ビニル70質量%を含有するトルエン溶液50gとを室温下で均一な組成となるように混合することにより、塗工液を得た。
EX:フィルムAとフィルムBとを引き剥がすときの応力が2.5N以上
A:フィルムAとフィルムBとを引き剥がすときの応力が2.0N以上2.5N未満
B:フィルムAとフィルムBとを引き剥がすときの応力が1.5N以上2.0N未満
C:フィルムAとフィルムBとを引き剥がすときの応力が1.0N以上1.5N未満
D:フィルムAとフィルムBとを引き剥がすときの応力が0.5N以上1.0N未満
F:フィルムAとフィルムBとを引き剥がすときの応力が0.5N未満(不合格)
樹枝状ニッケル結晶粒子を円筒形セル(内径:20mm、深さ:60mm)に詰め、20kNの圧力で加圧することにより、ペレットを作製した。前記で得られたペレットの上面と下面との間の電気抵抗を抵抗測定器〔(株)三菱化学アナリテック製、粉体抵抗測定システムMCP-PD51型〕で測定し、以下の評価基準に基づいて導電性を評価した。
○:電気抵抗が2×10-4Ω未満
△:電気抵抗が2×10-4Ω以上、5×10-4Ω未満
×:電気抵抗が5×10-4Ω以上(不合格)
樹枝状ニッケル結晶粒子(金属粒子)を円筒形セル(内径:20mm、深さ:60mm)に詰め、20kNの圧力で加圧することにより、ペレットを作製した。前記で得られたペレットに含まれている樹枝状ニッケル結晶粒子の加圧前後の形状を電子顕微鏡で観察し、機械的強度を以下の評価基準に基づいて評価した。
○:加圧前後の結晶粒子の形状に変形が認められない。
×:加圧前後の結晶粒子の形状に変形が認められる(不合格)。
2 中枝
Claims (2)
- ニッケルからなる樹枝状ニッケル結晶粒子であって、前記樹枝状ニッケル結晶粒子の走査型電子顕微鏡写真の撮影画像において、
前記樹枝状ニッケル結晶粒子の全体の長さが5~150μmであり、前記樹枝状ニッケル結晶粒子の全体の幅が1~15μmであり、
前記樹枝状ニッケル結晶粒子が複数の中枝を有し、当該中枝の側面または端部に当該中枝とは異なる他の中枝の端部が結合して当該樹枝状ニッケル結晶粒子が形成されており、当該中枝の長さが2~25μmであり、当該中枝の幅が1~5μmであり、
前記中枝が複数の微細小枝を有し、当該微細小枝同士が結合して当該中枝が形成されており、当該微細小枝の長さが20nm~2μmであり、当該微細小枝の幅が20nm~1μmであることを特徴とする樹枝状ニッケル結晶粒子。 - 請求項1に記載の樹枝状ニッケル結晶粒子を含有することを特徴とする導電性フィルム、導電膜または導電性ペースト。