JP7295472B2 - パーフルオロ(ポリ)エーテル基含有シラン化合物を含む組成物 - Google Patents
パーフルオロ(ポリ)エーテル基含有シラン化合物を含む組成物 Download PDFInfo
- Publication number
- JP7295472B2 JP7295472B2 JP2022000488A JP2022000488A JP7295472B2 JP 7295472 B2 JP7295472 B2 JP 7295472B2 JP 2022000488 A JP2022000488 A JP 2022000488A JP 2022000488 A JP2022000488 A JP 2022000488A JP 7295472 B2 JP7295472 B2 JP 7295472B2
- Authority
- JP
- Japan
- Prior art keywords
- group
- integer
- independently
- formula
- occurrence
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
PFPE1は、各出現においてそれぞれ独立して、式:
-(OC6F12)a-(OC5F10)b-(OC4F8)c-(OC3F6)d-(OC2F4)e-(OCF2)f-
(式中、a、b、c、d、eおよびfは、それぞれ独立して0以上200以下の整数であって、a、b、c、d、eおよびfの和は少なくとも1であり、a、b、c、d、eまたはfを付して括弧でくくられた各繰り返し単位の存在順序は式中において任意である。)
で表される基であり;
Rf1は、各出現においてそれぞれ独立して、1個またはそれ以上のフッ素原子により置換されていてもよい炭素数1~16のアルキル基を表し;
R1は、各出現においてそれぞれ独立して、水酸基または加水分解可能な基を表し;
R2は、各出現においてそれぞれ独立して、水素原子または炭素数1~22のアルキル基を表し;
R11は、各出現においてそれぞれ独立して、水素原子またはハロゲン原子を表し;
R12は、各出現においてそれぞれ独立して、水素原子または低級アルキル基を表し;
n1は、(-SiR1 n1R2 3-n1)単位毎に独立して、0~3の整数であり;
ただし、式(A1)、(A2)、(B1)および(B2)において、少なくとも1つのn1が、1~3の整数であり;
X1は、それぞれ独立して、単結合または2~10価の有機基を表し;
X2は、各出現においてそれぞれ独立して、単結合または2価の有機基を表し;
tは、各出現においてそれぞれ独立して、1~10の整数であり;
αは、それぞれ独立して、1~9の整数であり;
α’は、それぞれ独立して、1~9の整数であり;
X5は、それぞれ独立して、単結合または2~10価の有機基を表し;
βは、それぞれ独立して、1~9の整数であり;
β’は、それぞれ独立して、1~9の整数であり;
X7は、それぞれ独立して、単結合または2~10価の有機基を表し;
γは、それぞれ独立して、1~9の整数であり;
γ’は、それぞれ独立して、1~9の整数であり;
Raは、各出現においてそれぞれ独立して、-Z1-SiR71 p1R72 q1R73 r1を表し;
Z1は、各出現においてそれぞれ独立して、酸素原子または2価の有機基を表し;
R71は、各出現においてそれぞれ独立して、Ra’を表し;
Ra’は、Raと同意義であり;
Ra中、Z1基を介して直鎖状に連結されるSiは最大で5個であり;
R72は、各出現においてそれぞれ独立して、水酸基または加水分解可能な基を表し;
R73は、各出現においてそれぞれ独立して、水素原子または低級アルキル基を表し;
p1は、各出現においてそれぞれ独立して、0~3の整数であり;
q1は、各出現においてそれぞれ独立して、0~3の整数であり;
r1は、各出現においてそれぞれ独立して、0~3の整数であり;
ただし、式(C1)および(C2)において、少なくとも1つのq1が1~3の整数であり;
Rbは、各出現においてそれぞれ独立して、水酸基または加水分解可能な基を表し;
Rcは、各出現においてそれぞれ独立して、水素原子または低級アルキル基を表し;
k1は、各出現においてそれぞれ独立して、1~3の整数であり;
l1は、各出現においてそれぞれ独立して、0~2の整数であり;
m1は、各出現においてそれぞれ独立して、0~2の整数であり;
X9は、それぞれ独立して、単結合または2~10価の有機基を表し;
δは、それぞれ独立して、1~9の整数であり;
δ’は、それぞれ独立して、1~9の整数であり;
Rdは、各出現においてそれぞれ独立して、-Z2-CR81 p2R82 q2R83 r2を表し;
Z2は、各出現においてそれぞれ独立して、酸素原子または2価の有機基を表し;
R81は、各出現においてそれぞれ独立して、Rd’を表し;
Rd’は、Rdと同意義であり;
Rd中、Z2基を介して直鎖状に連結されるCは最大で5個であり;
R82は、各出現においてそれぞれ独立して、-Y-SiR85 n2R86 3-n2を表し;
Yは、各出現においてそれぞれ独立して、2価の有機基を表し;
R85は、各出現においてそれぞれ独立して、水酸基または加水分解可能な基を表し;
R86は、各出現においてそれぞれ独立して、水素原子または低級アルキル基を表し;
n2は、(-Y-SiR85 n2R86 3-n2)単位毎に独立して、1~3の整数を表し;
ただし、式(D1)および(D2)において、少なくとも1つのn2は1~3の整数であり;
R83は、各出現においてそれぞれ独立して、水素原子または低級アルキル基を表し;
p2は、各出現においてそれぞれ独立して、0~3の整数であり;
q2は、各出現においてそれぞれ独立して、0~3の整数であり;
r2は、各出現においてそれぞれ独立して、0~3の整数であり;
Reは、各出現においてそれぞれ独立して、-Y-SiR85 n2R86 3-n2を表し;
Rfは、各出現においてそれぞれ独立して、水素原子または低級アルキル基を表し;
k2は、各出現においてそれぞれ独立して、0~3の整数であり;
l2は、各出現においてそれぞれ独立して、0~3の整数であり;
m2は、各出現においてそれぞれ独立して、0~3の整数であり;
ただし、式(D1)および(D2)において、少なくとも1つのq2は2または3であるか、あるいは、少なくとも1つのl2は2または3である。]
のいずれかで表される少なくとも1種のパーフルオロ(ポリ)エーテル基含有シラン化合物、および
下記式(E1):
PFPE2は、各出現においてそれぞれ独立して、式:
-(OC6F12)a-(OC5F10)b-(OC4F8)c-(OC3F6)d-(OC2F4)e-(OCF2)f-
(式中、a、b、c、d、eおよびfは、それぞれ独立して0以上200以下の整数であって、a、b、c、d、eおよびfの和は少なくとも1であり、a、b、c、d、eまたはfを付して括弧でくくられた各繰り返し単位の存在順序は式中において任意である。)
で表される基であり;
Rf2は、各出現においてそれぞれ独立して、1個またはそれ以上のフッ素原子により置換されていてもよい炭素数1~16のアルキル基を表し;
Z2は、単結合または2価の有機基を表し;
xは1または2であり;
xが1である場合、Aは、-COOR3、-PO(OR3)2、-SO2(OR3)、または-SO(OR3)であり;
xが2である場合、Aは、-PO(OR3)-であり;
R3は、水素原子または炭化水素基である。]
で表される少なくとも1種の化合物
を含む組成物が提供される。
Rf2は、それぞれ独立して、1個またはそれ以上のフッ素原子により置換されていてもよい炭素数1~16のアルキル基を表し;
PFPE2は、それぞれ独立して、-(OC6F12)a-(OC5F10)b-(OC4F8)c-(OC3F6)d-(OC2F4)e-(OCF2)f-を表し、ここに、a、b、c、d、eおよびfは、それぞれ独立して0以上200以下の整数であって、a、b、c、d、eおよびfの和は少なくとも1であり、a、b、c、d、eまたはfを付して括弧でくくられた各繰り返し単位の存在順序は式中において任意であり;
Z2は、単結合または2価の有機基を表し;
xは1または2であり;
xが1である場合、Aは、-COOR3、-PO(OR3)2、-SO2(OR3)、または-SO(OR3)であり;
xが2である場合、Aは、-PO(OR3)-であり;
R3は、水素原子または炭化水素基である。]
で表される少なくとも1種の化合物を含む、パーフルオロ(ポリ)エーテル基含有シラン化合物の縮合促進剤が提供される。
下記式(E1):
を含んでなる組成物を提供する(以下、「本発明の組成物」ともいう)。
-(OC6F12)a-(OC5F10)b-(OC4F8)c-(OC3F6)d-(OC2F4)e-(OCF2)f-
で表される基である。式中、a、b、c、d、eおよびfは、それぞれ独立して0以上200以下の整数であって、a、b、c、d、eおよびfの和は少なくとも1である。好ましくは、a、b、c、d、eおよびfは、それぞれ独立して、0以上100以下の整数である。好ましくは、a、b、c、d、eおよびfの和は5以上であり、より好ましくは10以上、例えば10以上100以下である。また、a、b、c、d、eまたはfを付して括弧でくくられた各繰り返し単位の存在順序は式中において任意である。
-(R31)p’-(Xa)q’-
[式中:
R31は、それぞれ独立して、単結合、-(CH2)s’-またはo-、m-もしくはp-フェニレン基を表し、好ましくは-(CH2)s’-であり、
s’は、1~20の整数、好ましくは1~6の整数、より好ましくは1~3の整数、さらにより好ましくは1または2であり、
Xaは、-(Xb)l’-を表し、
Xbは、各出現においてそれぞれ独立して、-O-、-S-、o-、m-もしくはp-フェニレン基、-C(O)O-、-Si(R33)2-、-(Si(R33)2O)m’-Si(R33)2-、-CONR34-、-O-CONR34-、-NR34-および-(CH2)n’-からなる群から選択される基を表し、
R33は、各出現においてそれぞれ独立して、フェニル基、C1-6アルキル基またはC1-6アルコキシ基を表し、好ましくはフェニル基またはC1-6アルキル基であり、より好ましくはメチル基であり、
R34は、各出現においてそれぞれ独立して、水素原子、フェニル基またはC1-6アルキル基(好ましくはメチル基)を表し、
m’は、各出現において、それぞれ独立して、1~100の整数、好ましくは1~20の整数であり、
n’は、各出現において、それぞれ独立して、1~20の整数、好ましくは1~6の整数、より好ましくは1~3の整数であり、
l’は、1~10の整数、好ましくは1~5の整数、より好ましくは1~3の整数であり、
p’は、0、1または2であり、
q’は、0または1であり、
ここに、p’およびq’の少なくとも一方は1であり、p’またはq’を付して括弧でくくられた各繰り返し単位の存在順序は任意である。]
で表される2価の基が挙げられる。ここに、R31およびXa(典型的にはR31およびXaの水素原子)は、フッ素原子、C1-3アルキル基およびC1-3フルオロアルキル基から選択される1個またはそれ以上の置換基により置換されていてもよい。
単結合、
C1-20アルキレン基、
-R31-Xc-R32-、または
-Xd-R32-
[式中、R31およびR32は、上記と同意義である。]
であり得る。
単結合、
C1-20アルキレン基、
-(CH2)s’-Xc-、
-(CH2)s’-Xc-(CH2)t’-
-Xd-、または
-Xd-(CH2)t’-
[式中、s’およびt’は、上記と同意義である。]
である。
-O-、
-S-、
-C(O)O-、
-CONR34-、
-O-CONR34-、
-Si(R33)2-、
-(Si(R33)2O)m’-Si(R33)2-、
-O-(CH2)u’-(Si(R33)2O)m’-Si(R33)2-、
-O-(CH2)u’-Si(R33)2-O-Si(R33)2-CH2CH2-Si(R33)2-O-Si(R33)2-、
-O-(CH2)u’-Si(OCH3)2OSi(OCH3)2-、
-CONR34-(CH2)u’-(Si(R33)2O)m’-Si(R33)2-、
-CONR34-(CH2)u’-N(R34)-、または
-CONR34-(o-、m-またはp-フェニレン)-Si(R33)2-
[式中、R33、R34およびm’は、上記と同意義であり、
u’は1~20の整数、好ましくは2~6の整数、より好ましくは2~3の整数である。]を表す。Xcは、好ましくは-O-である。
-S-、
-C(O)O-、
-CONR34-、
-CONR34-(CH2)u’-(Si(R33)2O)m’-Si(R33)2-、
-CONR34-(CH2)u’-N(R34)-、または
-CONR34-(o-、m-またはp-フェニレン)-Si(R33)2-
[式中、各記号は、上記と同意義である。]
を表す。
単結合、
C1-20アルキレン基、
-(CH2)s’-Xc-(CH2)t’-、または
-Xd-(CH2)t’-
[式中、各記号は、上記と同意義である。]
であり得る。
単結合、
C1-20アルキレン基、
-(CH2)s’-O-(CH2)t’-、
-(CH2)s’-(Si(R33)2O)m’-Si(R33)2-(CH2)t’-、
-(CH2)s’-O-(CH2)u’-(Si(R33)2O)m’-Si(R33)2-(CH2)t’-、または
-(CH2)s’-O-(CH2)t’-Si(R33)2 -(CH2)u’-Si(R33)2-(CvH2v)-
[式中、R33、m’、s’、t’およびu’は、上記と同意義であり、vは1~20の整数、好ましくは2~6の整数、より好ましくは2~3の整数である。]
である。
Dは、
-CH2O(CH2)2-、
-CH2O(CH2)3-、
-CF2O(CH2)3-、
-(CH2)2-、
-(CH2)3-、
-(CH2)4-、
-CONH-(CH2)3-、
-CON(CH3)-(CH2)3-、
-CON(Ph)-(CH2)3-(式中、Phはフェニルを意味する)、および
から選択される基であり、
Eは、-(CH2)n-(nは2~6の整数)であり、
Dは、分子主鎖のPFPE1に結合し、Eは、PFPE1と反対の基に結合する。]
単結合、
-CH2O(CH2)2-、
-CH2O(CH2)3-、
-CH2O(CH2)6-、
-CH2O(CH2)3Si(CH3)2OSi(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2OSi(CH3)2OSi(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2O(Si(CH3)2O)2Si(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2O(Si(CH3)2O)3Si(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2O(Si(CH3)2O)10Si(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2O(Si(CH3)2O)20Si(CH3)2(CH2)2-、
-CH2OCF2CHFOCF2-、
-CH2OCF2CHFOCF2CF2-、
-CH2OCF2CHFOCF2CF2CF2-、
-CH2OCH2CF2CF2OCF2-、
-CH2OCH2CF2CF2OCF2CF2-、
-CH2OCH2CF2CF2OCF2CF2CF2-、
-CH2OCH2CF2CF2OCF(CF3)CF2OCF2-、
-CH2OCH2CF2CF2OCF(CF3)CF2OCF2CF2-、
-CH2OCH2CF2CF2OCF(CF3)CF2OCF2CF2CF2-、
-CH2OCH2CHFCF2OCF2-、
-CH2OCH2CHFCF2OCF2CF2-、
-CH2OCH2CHFCF2OCF2CF2CF2-、
-CH2OCH2CHFCF2OCF(CF3)CF2OCF2-、
-CH2OCH2CHFCF2OCF(CF3)CF2OCF2CF2-、
-CH2OCH2CHFCF2OCF(CF3)CF2OCF2CF2CF2-
-CH2OCF2CHFOCF2CF2CF2-C(O)NH-CH2-、
-CH2OCH2(CH2)7CH2Si(OCH3)2OSi(OCH3)2(CH2)2Si(OCH3)2OSi(OCH3)2(CH2)2-、
-CH2OCH2CH2CH2Si(OCH3)2OSi(OCH3)2(CH2)3-、
-CH2OCH2CH2CH2Si(OCH2CH3)2OSi(OCH2CH3)2(CH2)3-、
-CH2OCH2CH2CH2Si(OCH3)2OSi(OCH3)2(CH2)2-、
-CH2OCH2CH2CH2Si(OCH2CH3)2OSi(OCH2CH3)2(CH2)2-、
-CH2-、
-(CH2)2-、
-(CH2)3-、
-(CH2)4-、
-(CH2)5-、
-(CH2)6-、
-CO-
-CONH-
-CONH-CH2-、
-CONH-(CH2)2-、
-(CH2)2-Si(CH3)2-(CH2)2-
-CONH-(CH2)3-、
-CON(CH3)-(CH2)3-、
-CON(Ph)-(CH2)3-(式中、Phはフェニルを意味する)、
-CONH-(CH2)6-、
-CON(CH3)-(CH2)6-、
-CON(Ph)-(CH2)6-(式中、Phはフェニルを意味する)、
-CONH-(CH2)2NH(CH2)3-、
-CONH-(CH2)6NH(CH2)3-、
-CH2O-CONH-(CH2)3-、
-CH2O-CONH-(CH2)6-、
-S-(CH2)3-、
-(CH2)2S(CH2)3-、
-CONH-(CH2)3Si(CH3)2OSi(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2OSi(CH3)2OSi(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2O(Si(CH3)2O)2Si(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2O(Si(CH3)2O)3Si(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2O(Si(CH3)2O)10Si(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2O(Si(CH3)2O)20Si(CH3)2(CH2)2-
-C(O)O-(CH2)3-、
-C(O)O-(CH2)6-、
-CH2-O-(CH2)3-Si(CH3)2-(CH2)2-Si(CH3)2-(CH2)2-、
-CH2-O-(CH2)3-Si(CH3)2-(CH2)2-Si(CH3)2-CH(CH3)-、
-CH2-O-(CH2)3-Si(CH3)2-(CH2)2-Si(CH3)2-(CH2)3-、
-CH2-O-(CH2)3-Si(CH3)2-(CH2)2-Si(CH3)2-CH(CH3)-CH2-、
-OCH2-、
-O(CH2)3-、
-OCFHCF2-、
などが挙げられる。
-(CR8 2)k1-(O)k2-(NR9)k3-
[式中:
R8は、それぞれ独立して、水素原子またはフッ素原子であり;
R9は、それぞれ独立して、水素原子、フェニル基またはC1-6アルキル基を表し;
k1は、1~20の整数であり;
k2は、0~10の整数であり;
k3は、0~10の整数であり;
ここに、k1、k2またはk3を付して括弧でくくられた各繰り返し単位の存在順序は式中において任意である。]
で表される基であり得る。
-(CR20 2)k4-(O)k5-(NR21)k6-、
[式中:
R20は、それぞれ独立して、水素原子またはフッ素原子であり;
R21は、それぞれ独立して、水素原子、フェニル基またはC1-6アルキル基を表し;
k4は、1~20の整数であり;
k5は、0~10の整数であり;
k6は、0~10の整数であり;
ここに、k4、k5またはk6を付して括弧でくくられた各繰り返し単位の存在順序は式中において任意である。]
で表される基であり得る。
[式中:
k1’は、1~6の整数であり;
k2’は、1~3の整数であり;
ここに、k1’またはk2’を付して括弧でくくられた各繰り返し単位の存在順序は式中において任意である。]
であり、
Xdは、-(CH2)k4’-または-(CH2)k4’-Ok5’-
[式中:
k4’は、1~6の整数であり;
k5’は、1~3の整数であり;
ここに、k4’またはk5’を付して括弧でくくられた各繰り返し単位の存在順序は式中において任意である。]
である。
R41は、それぞれ独立して、水素原子、フェニル基、炭素数1~6のアルキル基、またはC1-6アルコキシ基好ましくはメチル基であり;
各X1基において、Tのうち任意のいくつかは、分子主鎖のPFPE1に結合する以下の基:
-CH2O(CH2)2-、
-CH2O(CH2)3-、
-CF2O(CH2)3-、
-(CH2)2-、
-(CH2)3-、
-(CH2)4-、
-CONH-(CH2)3-、
-CON(CH3)-(CH2)3-、
-CON(Ph)-(CH2)3-(式中、Phはフェニルを意味する)、または
であり、別のTのいくつかは、分子主鎖のPFPE1と反対の基(即ち、式(A1)、
(A2)、(D1)および(D2)においては炭素原子、また、下記する式(B1)、(B2)、(C1)および(C2)においてはSi原子)に結合する-(CH2)n”-(n”は2~6の整数)であり、存在する場合、残りは、それぞれ独立して、メチル基、フェニル基、C1-6アルコキシ基またはラジカル捕捉基もしくは紫外線吸収基であり得る。
PFPE1は、それぞれ独立して、式:
-(OC4F8)a-(OC3F6)b-(OC2F4)c-(OCF2)d-
(式中、a、b、cおよびdは、それぞれ独立して、0~200の整数であって、a、b、cおよびdの和は少なくとも1であり、添字a、b、cまたはdを付して括弧でくくられた各繰り返し単位の存在順序は式中において任意である。)
で表される基であり;
Rf1は、各出現においてそれぞれ独立して、1個またはそれ以上のフッ素原子により置換されていてもよい炭素数1~16のアルキル基を表し;
R1は、各出現においてそれぞれ独立して、水酸基または加水分解可能な基を表し;
R2は、各出現においてそれぞれ独立して、水素原子または炭素数1~22のアルキル基を表し;
R11は、各出現においてそれぞれ独立して、水素原子またはハロゲン原子を表し;
R12は、各出現においてそれぞれ独立して、水素原子または低級アルキル基を表し;
n1は、1~3の整数であり、好ましくは3であり;
X1は、-O-CFR13-(CF2)e-であり;
R13は、フッ素原子または低級フルオロアルキル基であり;
eは、0または1であり;
X2は、-(CH2)u-であり;
uは、0~2の整数であり(uが0の場合X2は単結合である);
tは、1~10の整数である。]
で表される化合物である。
単結合、
-CH2O(CH2)2-、
-CH2O(CH2)3-、
-CH2O(CH2)6-、
-CH2O(CH2)3Si(CH3)2OSi(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2OSi(CH3)2OSi(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2O(Si(CH3)2O)2Si(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2O(Si(CH3)2O)3Si(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2O(Si(CH3)2O)10Si(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2O(Si(CH3)2O)20Si(CH3)2(CH2)2-、
-CH2OCF2CHFOCF2-、
-CH2OCF2CHFOCF2CF2-、
-CH2OCF2CHFOCF2CF2CF2-、
-CH2OCH2CF2CF2OCF2-、
-CH2OCH2CF2CF2OCF2CF2-、
-CH2OCH2CF2CF2OCF2CF2CF2-、
-CH2OCH2CF2CF2OCF(CF3)CF2OCF2-、
-CH2OCH2CF2CF2OCF(CF3)CF2OCF2CF2-、
-CH2OCH2CF2CF2OCF(CF3)CF2OCF2CF2CF2-、
-CH2OCH2CHFCF2OCF2-、
-CH2OCH2CHFCF2OCF2CF2-、
-CH2OCH2CHFCF2OCF2CF2CF2-、
-CH2OCH2CHFCF2OCF(CF3)CF2OCF2-、
-CH2OCH2CHFCF2OCF(CF3)CF2OCF2CF2-、
-CH2OCH2CHFCF2OCF(CF3)CF2OCF2CF2CF2-
-CH2OCF2CHFOCF2CF2CF2-C(O)NH-CH2-、
-CH2OCH2(CH2)7CH2Si(OCH3)2OSi(OCH3)2(CH2)2Si(OCH3)2OSi(OCH3)2(CH2)2-、
-CH2OCH2CH2CH2Si(OCH3)2OSi(OCH3)2(CH2)3-、
-CH2OCH2CH2CH2Si(OCH2CH3)2OSi(OCH2CH3)2(CH2)3-、
-CH2OCH2CH2CH2Si(OCH3)2OSi(OCH3)2(CH2)2-、
-CH2OCH2CH2CH2Si(OCH2CH3)2OSi(OCH2CH3)2(CH2)2-、
-CH2-、
-(CH2)2-、
-(CH2)3-、
-(CH2)4-、
-(CH2)5-、
-(CH2)6-、
-CO-
-CONH-
-CONH-CH2-、
-CONH-(CH2)2-、
-(CH2)2-Si(CH3)2-(CH2)2-
-CONH-(CH2)3-、
-CON(CH3)-(CH2)3-、
-CON(Ph)-(CH2)3-(式中、Phはフェニルを意味する)、
-CONH-(CH2)6-、
-CON(CH3)-(CH2)6-、
-CON(Ph)-(CH2)6-(式中、Phはフェニルを意味する)、
-CONH-(CH2)2NH(CH2)3-、
-CONH-(CH2)6NH(CH2)3-、
-CH2O-CONH-(CH2)3-、
-CH2O-CONH-(CH2)6-、
-S-(CH2)3-、
-(CH2)2S(CH2)3-、
-CONH-(CH2)3Si(CH3)2OSi(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2OSi(CH3)2OSi(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2O(Si(CH3)2O)2Si(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2O(Si(CH3)2O)3Si(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2O(Si(CH3)2O)10Si(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2O(Si(CH3)2O)20Si(CH3)2(CH2)2-
-C(O)O-(CH2)3-、
-C(O)O-(CH2)6-、
-CH2-O-(CH2)3-Si(CH3)2-(CH2)2-Si(CH3)2-(CH2)2-、
-CH2-O-(CH2)3-Si(CH3)2-(CH2)2-Si(CH3)2-CH(CH3)-、
-CH2-O-(CH2)3-Si(CH3)2-(CH2)2-Si(CH3)2-(CH2)3-、
-CH2-O-(CH2)3-Si(CH3)2-(CH2)2-Si(CH3)2-CH(CH3)-CH2-、
-OCH2-、
-O(CH2)3-、
-OCFHCF2-、
などが挙げられる。
PFPE1は、それぞれ独立して、式:
-(OC4F8)a-(OC3F6)b-(OC2F4)c-(OCF2)d-
(式中、a、b、cおよびdは、それぞれ独立して、0~200の整数であって、a、b、cおよびdの和は少なくとも1であり、添字a、b、cまたはdを付して括弧でくくられた各繰り返し単位の存在順序は式中において任意である。)
で表される基であり;
Rf1は、各出現においてそれぞれ独立して、1個またはそれ以上のフッ素原子により置換されていてもよい炭素数1~16のアルキル基を表し;
R1は、各出現においてそれぞれ独立して、水酸基または加水分解可能な基を表し;
R2は、各出現においてそれぞれ独立して、水素原子または炭素数1~22のアルキル基を表し;
n1は、1~3の整数であり、好ましくは3であり;
X5は、-CH2O(CH2)2-、-CH2O(CH2)3-または-CH2O(CH2)6-である]
で表される化合物である。
PFPE1は、それぞれ独立して、式:
-(OC4F8)a-(OC3F6)b-(OC2F4)c-(OCF2)d-
(式中、a、b、cおよびdは、それぞれ独立して、0~200の整数であって、a、b、cおよびdの和は少なくとも1であり、添字a、b、cまたはdを付して括弧でくくられた各繰り返し単位の存在順序は式中において任意である。)
で表される基であり;
Rf1は、各出現においてそれぞれ独立して、1個またはそれ以上のフッ素原子により置換されていてもよい炭素数1~16のアルキル基を表し;
X5’は、それぞれ独立して、単結合または2~10価の有機基を表し;
βは、それぞれ独立して、1~9の整数であり;
β’は、それぞれ独立して、1~9の整数であり;
R92は、単結合または2価の有機基である。]
で表される化合物を、HSiM3(式中、Mは、それぞれ独立して、ハロゲン原子、R1またはR2であり、R1は、各出現においてそれぞれ独立して、水酸基または加水分解可能な基であり、R2は、各出現においてそれぞれ独立して、水素原子または炭素数1~22のアルキル基である)と反応させて、必要に応じて、上記ハロゲン原子を、R1またはR2に変換して、式(B1”)または(B2”):
n1は、0~3の整数である。]
で表される化合物として得ることができる。
単結合、
-CH2O(CH2)2-、
-CH2O(CH2)3-、
-CH2O(CH2)6-、
-CH2O(CH2)3Si(CH3)2OSi(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2OSi(CH3)2OSi(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2O(Si(CH3)2O)2Si(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2O(Si(CH3)2O)3Si(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2O(Si(CH3)2O)10Si(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2O(Si(CH3)2O)20Si(CH3)2(CH2)2-、
-CH2OCF2CHFOCF2-、
-CH2OCF2CHFOCF2CF2-、
-CH2OCF2CHFOCF2CF2CF2-、
-CH2OCH2CF2CF2OCF2-、
-CH2OCH2CF2CF2OCF2CF2-、
-CH2OCH2CF2CF2OCF2CF2CF2-、
-CH2OCH2CF2CF2OCF(CF3)CF2OCF2-、
-CH2OCH2CF2CF2OCF(CF3)CF2OCF2CF2-、
-CH2OCH2CF2CF2OCF(CF3)CF2OCF2CF2CF2-、
-CH2OCH2CHFCF2OCF2-、
-CH2OCH2CHFCF2OCF2CF2-、
-CH2OCH2CHFCF2OCF2CF2CF2-、
-CH2OCH2CHFCF2OCF(CF3)CF2OCF2-、
-CH2OCH2CHFCF2OCF(CF3)CF2OCF2CF2-、
-CH2OCH2CHFCF2OCF(CF3)CF2OCF2CF2CF2-
-CH2OCF2CHFOCF2CF2CF2-C(O)NH-CH2-、
-CH2OCH2(CH2)7CH2Si(OCH3)2OSi(OCH3)2(CH2)2Si(OCH3)2OSi(OCH3)2(CH2)2-、
-CH2OCH2CH2CH2Si(OCH3)2OSi(OCH3)2(CH2)3-、
-CH2OCH2CH2CH2Si(OCH2CH3)2OSi(OCH2CH3)2(CH2)3-、
-CH2OCH2CH2CH2Si(OCH3)2OSi(OCH3)2(CH2)2-、
-CH2OCH2CH2CH2Si(OCH2CH3)2OSi(OCH2CH3)2(CH2)2-、
-CH2-、
-(CH2)2-、
-(CH2)3-、
-(CH2)4-、
-(CH2)5-、
-(CH2)6-、
-CO-
-CONH-
-CONH-CH2-、
-CONH-(CH2)2-、
-(CH2)2-Si(CH3)2-(CH2)2-
-CONH-(CH2)3-、
-CON(CH3)-(CH2)3-、
-CON(Ph)-(CH2)3-(式中、Phはフェニルを意味する)、
-CONH-(CH2)6-、
-CON(CH3)-(CH2)6-、
-CON(Ph)-(CH2)6-(式中、Phはフェニルを意味する)、
-CONH-(CH2)2NH(CH2)3-、
-CONH-(CH2)6NH(CH2)3-、
-CH2O-CONH-(CH2)3-、
-CH2O-CONH-(CH2)6-、
-S-(CH2)3-、
-(CH2)2S(CH2)3-、
-CONH-(CH2)3Si(CH3)2OSi(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2OSi(CH3)2OSi(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2O(Si(CH3)2O)2Si(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2O(Si(CH3)2O)3Si(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2O(Si(CH3)2O)10Si(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2O(Si(CH3)2O)20Si(CH3)2(CH2)2-
-C(O)O-(CH2)3-、
-C(O)O-(CH2)6-、
-CH2-O-(CH2)3-Si(CH3)2-(CH2)2-Si(CH3)2-(CH2)2-、
-CH2-O-(CH2)3-Si(CH3)2-(CH2)2-Si(CH3)2-CH(CH3)-、
-CH2-O-(CH2)3-Si(CH3)2-(CH2)2-Si(CH3)2-(CH2)3-、
-CH2-O-(CH2)3-Si(CH3)2-(CH2)2-Si(CH3)2-CH(CH3)-CH2-、
-OCH2-、
-O(CH2)3-、
-OCFHCF2-、
などが挙げられる。
PFPE1は、それぞれ独立して、式:
-(OC4F8)a-(OC3F6)b-(OC2F4)c-(OCF2)d-
(式中、a、b、cおよびdは、それぞれ独立して、0~200の整数であって、a、b、cおよびdの和は少なくとも1であり、添字a、b、cまたはdを付して括弧でくくられた各繰り返し単位の存在順序は式中において任意である。)
で表される基であり;
Rf1は、各出現においてそれぞれ独立して、1個またはそれ以上のフッ素原子により置換されていてもよい炭素数1~16のアルキル基を表し;
X7は、-CH2O(CH2)2-、-CH2O(CH2)3-または-CH2O(CH2)6-を表し;
Raは、各出現においてそれぞれ独立して、-Z1-SiR71 p1R72 q1R73 r1を表し;
Z1は、C1-6アルキレン基を表し;
R71は、各出現においてそれぞれ独立して、Ra’を表し;
Ra’は、Raと同意義であり;
Ra中、Z1基を介して直鎖状に連結されるSiは最大で5個であり;
R72は、各出現においてそれぞれ独立して、水酸基または加水分解可能な基を表し;
R73は、各出現においてそれぞれ独立して、水素原子または低級アルキル基を表し;
p1は、各出現においてそれぞれ独立して、0~2の整数であり;
q1は、各出現においてそれぞれ独立して、1~3の整数、好ましくは3であり;
r1は、各出現においてそれぞれ独立して、0~2の整数であり;
ただし、一のRaにおいて、p1、q1およびr1の和は3である。]
で表される化合物である。
PFPE1は、それぞれ独立して、式:
-(OC4F8)a-(OC3F6)b-(OC2F4)c-(OCF2)d-
(式中、a、b、cおよびdは、それぞれ独立して、0~200の整数であって、a、b、cおよびdの和は少なくとも1であり、添字a、b、cまたはdを付して括弧でくくられた各繰り返し単位の存在順序は式中において任意である。)
で表される基であり;
Rf1は、各出現においてそれぞれ独立して、1個またはそれ以上のフッ素原子により置換されていてもよい炭素数1~16のアルキル基を表し;
X7’は、それぞれ独立して、単結合または2~10価の有機基を表し;
γは、それぞれ独立して、1~9の整数であり;
γ’は、それぞれ独立して、1~9の整数であり;
R92は、単結合または2価の有機基である。]
で表される化合物を、HSiR93 k1Rb l1Rc m1(式中、R93はハロゲン原子、例えばフッ素原子、塩素原子、臭素原子またはヨウ素原子、好ましくは塩素原子であり、Rbは、各出現においてそれぞれ独立して、水酸基または加水分解可能な基を表し、Rcは、各出現においてそれぞれ独立して、水素原子または低級アルキル基を表し、k1は1~3の整数であり、l1およびm1は、それぞれ独立して、0~2の整数であり、k1、l1およびm1の和は3である。)で表される化合物と反応させて、式(C1-5)または(C2-5):
で表される化合物を得る。
で表される化合物を得る。
q1は、各出現においてそれぞれ独立して、1~3の整数であり;
r1は、各出現においてそれぞれ独立して、0~2の整数である。]
で表される化合物を得ることができる。
単結合、
-CH2O(CH2)2-、
-CH2O(CH2)3-、
-CH2O(CH2)6-、
-CH2O(CH2)3Si(CH3)2OSi(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2OSi(CH3)2OSi(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2O(Si(CH3)2O)2Si(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2O(Si(CH3)2O)3Si(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2O(Si(CH3)2O)10Si(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2O(Si(CH3)2O)20Si(CH3)2(CH2)2-、
-CH2OCF2CHFOCF2-、
-CH2OCF2CHFOCF2CF2-、
-CH2OCF2CHFOCF2CF2CF2-、
-CH2OCH2CF2CF2OCF2-、
-CH2OCH2CF2CF2OCF2CF2-、
-CH2OCH2CF2CF2OCF2CF2CF2-、
-CH2OCH2CF2CF2OCF(CF3)CF2OCF2-、
-CH2OCH2CF2CF2OCF(CF3)CF2OCF2CF2-、
-CH2OCH2CF2CF2OCF(CF3)CF2OCF2CF2CF2-、
-CH2OCH2CHFCF2OCF2-、
-CH2OCH2CHFCF2OCF2CF2-、
-CH2OCH2CHFCF2OCF2CF2CF2-、
-CH2OCH2CHFCF2OCF(CF3)CF2OCF2-、
-CH2OCH2CHFCF2OCF(CF3)CF2OCF2CF2-、
-CH2OCH2CHFCF2OCF(CF3)CF2OCF2CF2CF2-
-CH2OCF2CHFOCF2CF2CF2-C(O)NH-CH2-、
-CH2OCH2(CH2)7CH2Si(OCH3)2OSi(OCH3)2(CH2)2Si(OCH3)2OSi(OCH3)2(CH2)2-、
-CH2OCH2CH2CH2Si(OCH3)2OSi(OCH3)2(CH2)3-、
-CH2OCH2CH2CH2Si(OCH2CH3)2OSi(OCH2CH3)2(CH2)3-、
-CH2OCH2CH2CH2Si(OCH3)2OSi(OCH3)2(CH2)2-、
-CH2OCH2CH2CH2Si(OCH2CH3)2OSi(OCH2CH3)2(CH2)2-、
-CH2-、
-(CH2)2-、
-(CH2)3-、
-(CH2)4-、
-(CH2)5-、
-(CH2)6-、
-CO-
-CONH-
-CONH-CH2-、
-CONH-(CH2)2-、
-(CH2)2-Si(CH3)2-(CH2)2-
-CONH-(CH2)3-、
-CON(CH3)-(CH2)3-、
-CON(Ph)-(CH2)3-(式中、Phはフェニルを意味する)、
-CONH-(CH2)6-、
-CON(CH3)-(CH2)6-、
-CON(Ph)-(CH2)6-(式中、Phはフェニルを意味する)、
-CONH-(CH2)2NH(CH2)3-、
-CONH-(CH2)6NH(CH2)3-、
-CH2O-CONH-(CH2)3-、
-CH2O-CONH-(CH2)6-、
-S-(CH2)3-、
-(CH2)2S(CH2)3-、
-CONH-(CH2)3Si(CH3)2OSi(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2OSi(CH3)2OSi(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2O(Si(CH3)2O)2Si(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2O(Si(CH3)2O)3Si(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2O(Si(CH3)2O)10Si(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2O(Si(CH3)2O)20Si(CH3)2(CH2)2-
-C(O)O-(CH2)3-、
-C(O)O-(CH2)6-、
-CH2-O-(CH2)3-Si(CH3)2-(CH2)2-Si(CH3)2-(CH2)2-、
-CH2-O-(CH2)3-Si(CH3)2-(CH2)2-Si(CH3)2-CH(CH3)-、
-CH2-O-(CH2)3-Si(CH3)2-(CH2)2-Si(CH3)2-(CH2)3-、
-CH2-O-(CH2)3-Si(CH3)2-(CH2)2-Si(CH3)2-CH(CH3)-CH2-、
-OCH2-、
-O(CH2)3-、
-OCFHCF2-、
などが挙げられる。
-(OC6F12)a-(OC5F10)b-(OC4F8)c-(OC3F6)d-(OC2F4)e-(OCF2)f-
で表される基である。式中、a、b、c、d、eおよびfは、それぞれ独立して0以上200以下の整数であって、a、b、c、d、eおよびfの和は少なくとも1である。好ましくは、a、b、c、d、eおよびfは、それぞれ独立して、0以上100以下の整数である。好ましくは、a、b、c、d、eおよびfの和は5以上であり、より好ましくは10以上、例えば10以上100以下である。また、a、b、c、d、eまたはfを付して括弧でくくられた各繰り返し単位の存在順序は式中において任意である。
-(CR18 2)k7-(O)k8-(NR19)k9-、
[式中:
R18は、それぞれ独立して、水素原子またはフッ素原子であり;
R19は、それぞれ独立して、水素原子、フェニル基またはC1-6アルキル基を表し;
k7は、1~20の整数であり;
k8は、0~10の整数であり;
k9は、0~10の整数であり;
ここに、k7、k8またはk9を付して括弧でくくられた各繰り返し単位の存在順序は式中において任意である。]
である。
-(CF2)k7’-または-(CF2)k7’-(O)k8’-
[式中:
k7’は、1~6の整数であり;
k8’は、1~3の整数であり;
ここに、k7’またはk8’を付して括弧でくくられた各繰り返し単位の存在順序は式中において任意である。]
である。
Rf5-(OC4F8)a’-(OC3F6)b’-(OC2F4)c’-(OCF2)d’-Rf6 ・・・(3)
式中、Rf5は、1個またはそれ以上のフッ素原子により置換されていてもよいC1-16のアルキル基(好ましくは、C1―16のパーフルオロアルキル基)を表し、Rf6は、1個またはそれ以上のフッ素原子により置換されていてもよいC1-16のアルキル基(好ましくは、C1-16のパーフルオロアルキル基)、フッ素原子または水素原子を表し、Rf5およびRf6は、より好ましくは、それぞれ独立して、C1-3のパーフルオロアルキル基である。
a’、b’、c’およびd’は、ポリマーの主骨格を構成するパーフルオロ(ポリ)エーテルの4種の繰り返し単位数をそれぞれ表し、互いに独立して0以上300以下の整数であって、a’、b’、c’およびd’の和は少なくとも1、好ましくは1~300、より好ましくは20~300である。添字a’、b’、c’またはd’を付して括弧でくくられた各繰り返し単位の存在順序は、式中において任意である。これら繰り返し単位のうち、-(OC4F8)-は、-(OCF2CF2CF2CF2)-、-(OCF(CF3)CF2CF2)-、-(OCF2CF(CF3)CF2)-、-(OCF2CF2CF(CF3))-、-(OC(CF3)2CF2)-、-(OCF2C(CF3)2)-、-(OCF(CF3)CF(CF3))-、-(OCF(C2F5)CF2)-および-(OCF2CF(C2F5))-のいずれであってもよいが、好ましくは-(OCF2CF2CF2CF2)-である。-(OC3F6)-は、-(OCF2CF2CF2)-、-(OCF(CF3)CF2)-および-(OCF2CF(CF3))-のいずれであってもよく、好ましくは-(OCF2CF2CF2)-である。-(OC2F4)-は、-(OCF2CF2)-および-(OCF(CF3))-のいずれであってもよいが、好ましくは-(OCF2CF2)-である。
Rf5-(OCF2CF2CF2)b’’-Rf6 ・・・(3a)
Rf5-(OCF2CF2CF2CF2)a’’-(OCF2CF2CF2)b’’-(OCF2CF2)c’’-(OCF2)d’’-Rf6 ・・・(3b)
これら式中、Rf5およびRf6は上記の通りであり;式(3a)において、b’’は1以上100以下の整数であり;式(3b)において、a’’およびb’’は、それぞれ独立して1以上30以下の整数であり、c’’およびd’’はそれぞれ独立して1以上300以下の整数である。添字a’’、b’’、c’’、d’’を付して括弧でくくられた各繰り返し単位の存在順序は、式中において任意である。
樹脂としては、アクリル樹脂、ポリカーボネートが好ましい。
・パーフルオロポリエーテル変性メチルエステル化合物の合成
反応器に、メタノール240g、トリエチルアミン19.6gを仕込み、窒素気流下、5℃で平均組成CF3CF2CF2O(CF2CF2CF2O)32CF2CF2COFで表されるパーフルオロポリエーテル変性酸フルオロ化合物500gを滴下し、その後、室温まで昇温させて、撹拌した。続いて、パーフルオロヘキサン300gを加えて撹拌した後、分液ロートに移送し静置後、パーフルオロヘキサン層を分取した。続いて、3規定塩酸水溶液による洗浄操作を行った。次に、パーフルオロヘキサン層に無水硫酸マグネシウム30gを加えて、撹拌した後、不溶物を濾別した。続いて、減圧下で揮発分を留去することにより、末端にメチルエステル基を有する下記のパーフルオロポリエーテル変性メチルエステル体(A)476gを得た。
・パーフルオロポリエーテル変性メチルエステル化合物(A):
CF3CF2CF2O(CF2CF2CF2O)32CF2CF2CO2CH3
・パーフルオロポリエーテル変性カルボン酸化合物の合成
反応器に、純水100g、トリエチルアミン20.4gを仕込み、窒素気流下、5℃で平均組成CF3CF2CF2O(CF2CF2CF2O)32CF2CF2COFで表されるパーフルオロポリエーテル変性酸フルオロ化合物500gを滴下し、その後、室温まで昇温させて、撹拌した。続いて、パーフルオロヘキサン400gを加えて撹拌した後、分液ロートに移送し静置後、パーフルオロヘキサン層を分取した。続いて、3規定塩酸水溶液による洗浄操作を行った。次に、パーフルオロヘキサン層に無水硫酸マグネシウム30gを加えて、撹拌した後、不溶物を濾別した。続いて、減圧下で揮発分を留去することにより、末端にカルボン酸基を有する下記のパーフルオロポリエーテル変性カルボン酸化合物(B)476gを得た。
・パーフルオロポリエーテル変性カルボン酸化合物(B):
CF3CF2CF2O(CF2CF2CF2O)32CF2CF2CO2H
・パーフルオロポリエーテル変性リン酸エステル化合物の合成
反応器に、1,3-ビス(トリフルオロメチル)ベンゼン200g、塩化ホスホリル54.5gを仕込み、窒素気流下、5℃で平均組成CF3CF2CF2O(CF2CF2CF2O)32CF2CF2CH2OHで表されるパーフルオロポリエーテル変性アルコール化合物200gを滴下し、その後、室温まで昇温させて、撹拌した。続いて、パーフルオロヘキサン400gを加えて撹拌した後、純水を100g滴下し、撹拌した。その後、分液ロートに移送し静置後、パーフルオロヘキサン層を分取した。続いて、3規定塩酸水溶液による洗浄操作を行った。次に、パーフルオロヘキサン層に無水硫酸マグネシウム10gを加えて、撹拌した後、不溶物を濾別した。続いて、減圧下で揮発分を留去することにより、末端にリン酸基を有する下記のパーフルオロポリエーテル変性リン酸エステル化合物(C)202gを得た。
・パーフルオロポリエーテル基含有リン酸エステル化合物(C):
CF3CF2CF2O(CF2CF2CF2O)32CF2CF2CH2OP(=O)(OH)2
上記合成例1で得たパーフルオロポリエーテル変性メチルエステル化合物(A)および下記に示すパーフルオロポリエーテル変性シラン化合物(X)を、モル比2:98で混合し、ノベック7200(スリーエム社製)に溶解させて、濃度20wt%になるように、表面処理剤1を調製した。
・パーフルオロポリエーテル変性シラン化合物(X)
CF3CF2CF2O(CF2CF2CF2O)32CF2CF2CH2OCH2CH2CH2Si(OCH3)3
パーフルオロポリエーテル変性化合物(A)~(C)とパーフルオロポリエーテル変性シラン化合物(X)~(Z)を下記表の組み合わせで、モル比2:98で混合して表面処理剤を作成した以外は、実施例1と同様にして、表面処理剤を調製し、表面処理層を形成した。
・パーフルオロポリエーテル変性シラン化合物(Y)
CF3CF2CF2O(CF2CF2CF2O)32CF2CF2CON(CH3)CH2CH2CH2Si(OCH3)3
・パーフルオロポリエーテル変性シラン化合物(Z)
CF3CF2CF2O(CF2CF2CF2O)32CF2CF2CH2OCH2CH2CH2Si[CH2CH2CH2Si(OCH3)3]3
酢酸と上記のパーフルオロポリエーテル変性シラン化合物(X)をモル比2:98で混合して表面処理剤を作成した以外は、実施例1と同様にして、表面処理剤を調製し、表面処理層を形成した。
Claims (30)
- 下記一般式(D1)および(D2):
PFPE1は、各出現においてそれぞれ独立して、式:
-(OC6F12)a-(OC5F10)b-(OC4F8)c-(OC3F6)d-(OC2F4)e-(OCF2)f-
(式中、a、b、c、d、eおよびfは、それぞれ独立して0以上200以下の整数であって、a、b、c、d、eおよびfの和は少なくとも1であり、a、b、c、d、eまたはfを付して括弧でくくられた各繰り返し単位の存在順序は式中において任意である。)
で表される基であり;
Rf1は、各出現においてそれぞれ独立して、1個またはそれ以上のフッ素原子により置換されていてもよい炭素数1~16のアルキル基を表し;
X9は、それぞれ独立して、単結合または2~10価の有機基を表し;
δは、それぞれ独立して、1~9の整数であり;
δ’は、それぞれ独立して、1~9の整数であり;
Rdは、各出現においてそれぞれ独立して、-Z2-CR81 p2R82 q2R83 r2を表し;
Z2は、各出現においてそれぞれ独立して、酸素原子または2価の有機基を表し;
R81は、各出現においてそれぞれ独立して、Rd’を表し;
Rd’は、Rdと同意義であり;
Rd中、Z2基を介して直鎖状に連結されるCは最大で5個であり;
R82は、各出現においてそれぞれ独立して、-Y-SiR85 n2R86 3-n2を表し;
Yは、各出現においてそれぞれ独立して、2価の有機基を表し;
R85は、各出現においてそれぞれ独立して、水酸基または加水分解可能な基を表し;
R86は、各出現においてそれぞれ独立して、水素原子または低級アルキル基を表し;
n2は、(-Y-SiR85 n2R86 3-n2)単位毎に独立して、1~3の整数を表し;
ただし、式(D1)および(D2)において、少なくとも1つのn2は1~3の整数であり;
R83は、各出現においてそれぞれ独立して、水素原子または低級アルキル基を表し;
p2は、各出現においてそれぞれ独立して、0~3の整数であり;
q2は、各出現においてそれぞれ独立して、0~3の整数であり;
r2は、各出現においてそれぞれ独立して、0~3の整数であり;
Reは、各出現においてそれぞれ独立して、-Y-SiR85 n2R86 3-n2を表し;
Rfは、各出現においてそれぞれ独立して、水素原子または低級アルキル基を表し;
k2は、各出現においてそれぞれ独立して、0~3の整数であり;
l2は、各出現においてそれぞれ独立して、0~3の整数であり;
m2は、各出現においてそれぞれ独立して、0~2の整数であり;
ただし、式(D1)および(D2)において、少なくとも1つのq2は2または3であるか、あるいは、少なくとも1つのl2は2または3である。]
のいずれかで表される少なくとも1種のパーフルオロ(ポリ)エーテル基含有シラン化合物、および
下記式(E1):
PFPE2は、各出現においてそれぞれ独立して、式:
-(OC6F12)a-(OC5F10)b-(OC4F8)c-(OC3F6)d-(OC2F4)e-(OCF2)f-
(式中、a、b、c、d、eおよびfは、それぞれ独立して0以上200以下の整数であって、a、b、c、d、eおよびfの和は少なくとも1であり、a、b、c、d、eまたはfを付して括弧でくくられた各繰り返し単位の存在順序は式中において任意である。)
で表される基であり;
Rf2は、各出現においてそれぞれ独立して、1個またはそれ以上のフッ素原子により置換されていてもよい炭素数1~16のアルキル基を表し;
Z2は、単結合または2価の有機基を表し;
xは1であり;
Aは、-COOR3、または-PO(OH) 2 であり;
R3は、水素原子または炭化水素基である。]
で表される少なくとも1種の化合物
を含み、
式(D1)または(D2)で表されるパーフルオロ(ポリ)エーテル基含有シラン化合物の数平均分子量は、5×10 2 ~1×10 5 であり、
式(E1)で表されるパーフルオロ(ポリ)エーテル変性化合物の数平均分子量は、5×10 2 ~1×10 5 である、
組成物。 - Rf1が、炭素数1~16のパーフルオロアルキル基である、請求項1に記載の組成物。
- PFPE1が下記式(a)、(b)または(c):
-(OC3F6)d- (a)
[式中、dは1以上200以下の整数である。]
-(OC4F8)c-(OC3F6)d-(OC2F4)e-(OCF2)f- (b)
[式中、cおよびdは、それぞれ独立して、0以上30以下の整数であり;
eおよびfは、それぞれ独立して、1以上200以下の整数であり;
c、d、eおよびfの和は、10以上200以下の整数であり;
添字c、d、eまたはfを付して括弧でくくられた各繰り返し単位の存在順序は、式中において任意である。]
-(R6-R7)q- (c)
[式中、R6は、OCF2またはOC2F4であり;
R7は、OC3F6、OC4F8、OC5F10およびOC6F12から選択される基であるか、あるいは、これらの基から選択される2または3つの基の組み合わせであり;
qは、2~100の整数である。]
である、請求項1または2に記載の組成物。 - X9が2価の有機基であり、δが1であり、δ’が1である、請求項1~3のいずれか1項に記載の組成物。
- X 9 が、それぞれ独立して、-(R31)p’-(Xa)q’-
[式中:
R31は、それぞれ独立して、単結合、-(CH2)s’-(式中、s’は、1~20の整数である)またはo-、m-もしくはp-フェニレン基を表し;
Xaは、-(Xb)l’-(式中、l’は、1~10の整数である)を表し;
Xbは、各出現においてそれぞれ独立して、-O-、-S-、o-、m-もしくはp-フェニレン基、-C(O)O-、-Si(R33)2-、-(Si(R33)2O)m’-Si(R33)2-(式中、m’は1~100の整数である)、-CONR34-、-O-CONR34-、-NR34-および-(CH2)n’-(式中、n’は1~20の整数である)からなる群から選択される基を表し;
R33は、各出現においてそれぞれ独立して、フェニル基、C1-6アルキル基またはC1-6アルコキシ基を表し;
R34は、各出現においてそれぞれ独立して、水素原子、フェニル基またはC1-6アルキル基を表し;
p’は、0、1または2であり;
q’は、0または1であり;
ここに、p’およびq’の少なくとも一方は1であり、p’またはq’を付して括弧でくくられた各繰り返し単位の存在順序は式中において任意であり;
R31およびXaは、フッ素原子、C1-3アルキル基およびC1-3フルオロアルキル基から選択される1個またはそれ以上の置換基により置換されていてもよい。]
で表される基である、請求項1~4のいずれか1項に記載の組成物。 - X 9 が、それぞれ独立して:
単結合、
-CH2O(CH2)2-、
-CH2O(CH2)3-、
-CH2O(CH2)6-、
-CH2O(CH2)3Si(CH3)2OSi(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2OSi(CH3)2OSi(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2O(Si(CH3)2O)2Si(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2O(Si(CH3)2O)3Si(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2O(Si(CH3)2O)10Si(CH3)2(CH2)2-、
-CH2O(CH2)3Si(CH3)2O(Si(CH3)2O)20Si(CH3)2(CH2)2-、
-CH2OCF2CHFOCF2-、
-CH2OCF2CHFOCF2CF2-、
-CH2OCF2CHFOCF2CF2CF2-、
-CH2OCH2CF2CF2OCF2-、
-CH2OCH2CF2CF2OCF2CF2-、
-CH2OCH2CF2CF2OCF2CF2CF2-、
-CH2OCH2CF2CF2OCF(CF3)CF2OCF2-、
-CH2OCH2CF2CF2OCF(CF3)CF2OCF2CF2-、
-CH2OCH2CF2CF2OCF(CF3)CF2OCF2CF2CF2-、
-CH2OCH2CHFCF2OCF2-、
-CH2OCH2CHFCF2OCF2CF2-、
-CH2OCH2CHFCF2OCF2CF2CF2-、
-CH2OCH2CHFCF2OCF(CF3)CF2OCF2-、
-CH2OCH2CHFCF2OCF(CF3)CF2OCF2CF2-、
-CH2OCH2CHFCF2OCF(CF3)CF2OCF2CF2CF2-
-CH2OCF2CHFOCF2CF2CF2-C(O)NH-CH2-、
-CH2OCH2(CH2)7CH2Si(OCH3)2OSi(OCH3)2(CH2)2Si(OCH3)2OSi(OCH3)2(CH2)2-、
-CH2OCH2CH2CH2Si(OCH3)2OSi(OCH3)2(CH2)3-、
-CH2OCH2CH2CH2Si(OCH2CH3)2OSi(OCH2CH3)2(CH2)3-、
-CH2OCH2CH2CH2Si(OCH3)2OSi(OCH3)2(CH2)2-、
-CH2OCH2CH2CH2Si(OCH2CH3)2OSi(OCH2CH3)2(CH2)2-、
-CH2-、
-(CH2)2-、
-(CH2)3-、
-(CH2)4-、
-(CH2)5-、
-(CH2)6-、
-CO-
-CONH-
-CONH-CH2-、
-CONH-(CH2)2-、
-(CH2)2-Si(CH3)2-(CH2)2-
-CONH-(CH2)3-、
-CON(CH3)-(CH2)3-、
-CON(Ph)-(CH2)3-(式中、Phはフェニルを意味する)、
-CONH-(CH2)6-、
-CON(CH3)-(CH2)6-、
-CON(Ph)-(CH2)6-(式中、Phはフェニルを意味する)、
-CONH-(CH2)2NH(CH2)3-、
-CONH-(CH2)6NH(CH2)3-、
-CH2O-CONH-(CH2)3-、
-CH2O-CONH-(CH2)6-、
-S-(CH2)3-、
-(CH2)2S(CH2)3-、
-CONH-(CH2)3Si(CH3)2OSi(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2OSi(CH3)2OSi(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2O(Si(CH3)2O)2Si(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2O(Si(CH3)2O)3Si(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2O(Si(CH3)2O)10Si(CH3)2(CH2)2-、
-CONH-(CH2)3Si(CH3)2O(Si(CH3)2O)20Si(CH3)2(CH2)2-
-C(O)O-(CH2)3-、
-C(O)O-(CH2)6-、
-CH2-O-(CH2)3-Si(CH3)2-(CH2)2-Si(CH3)2-(CH2)2-、
-CH2-O-(CH2)3-Si(CH3)2-(CH2)2-Si(CH3)2-CH(CH3)-、
-CH2-O-(CH2)3-Si(CH3)2-(CH2)2-Si(CH3)2-(CH2)3-、
-CH2-O-(CH2)3-Si(CH3)2-(CH2)2-Si(CH3)2-CH(CH3)-CH2-、
-OCH2-、
-O(CH2)3-、
-OCFHCF2-、
からなる群から選択される、請求項1~5のいずれか1項に記載の組成物。 - l2が3であり、n2が3である、請求項1~6のいずれか1項に記載の組成物。
- Yが、C1-6アルキレン基、-(CH2)g’-O-(CH2)h’-(式中、g’は0~6の整数であり、h’は0~6の整数である)、または-フェニレン-(CH2)i’-(式中、i’は、0~6の整数である)である、請求項1~7のいずれか1項に記載の組成物。
- X 9 が、それぞれ独立して、3~10価の有機基である、請求項1~3のいずれか1項に記載の組成物。
- X 9 が、それぞれ独立して:
-CH2O(CH2)2-、
-CH2O(CH2)3-、
-CF2O(CH2)3-、
-(CH2)2-、
-(CH2)3-、
-(CH2)4-、
-CONH-(CH2)3-、
-CON(CH3)-(CH2)3-、
-CON(Ph)-(CH2)3-(式中、Phはフェニルを意味する)、および
別のTのうち少なくとも1つは、式(D1)および(D2)において、炭素原子またはSi原子に結合する-(CH2)n-(nは2~6の整数)であり、残りは、それぞれ独立して、メチル基、フェニル基、炭素数1~6のアルコキシ基またはラジカル捕捉基もしくは紫外線吸収基であり、
R41は、それぞれ独立して、水素原子、フェニル基、炭素数1~6のアルコキシ基または炭素数1~6のアルキル基であり、
R42は、それぞれ独立して、水素原子、C1-6のアルキル基またはC1-6のアルコキシ基を表す。]
からなる群から選択される、請求項9に記載の組成物。 - 式(D1)または(D2)で表されるパーフルオロ(ポリ)エーテル基含有シラン化合物の数平均分子量が、1,000~30,000である、請求項1~10のいずれか1項に記載の組成物。
- Rf2が、炭素数1~16のパーフルオロアルキル基である、請求項1~11のいずれか1項に記載の組成物。
- PFPE2が下記式(a)、(b)または(c):
-(OC3F6)d- (a)
[式中、dは1以上200以下の整数である。]
-(OC4F8)c-(OC3F6)d-(OC2F4)e-(OCF2)f- (b)
[式中、cおよびdは、それぞれ独立して、0以上30以下の整数であり;
eおよびfは、それぞれ独立して、1以上200以下の整数であり;
c、d、eおよびfの和は、10以上200以下の整数であり;
添字c、d、eまたはfを付して括弧でくくられた各繰り返し単位の存在順序は、式中において任意である。]
-(R6-R7)q- (c)
[式中、R6は、OCF2またはOC2F4であり;
R7は、OC3F6、OC4F8、OC5F10およびOC6F12から選択される基であるか、あるいは、これらの基から独立して選択される2または3つの基の組み合わせであり;
qは、2~100の整数である。]
である、請求項1~12のいずれか1項に記載の組成物。 - Z2における2価の有機基が、
-(CR18 2)k7-(O)k8-(NR19)k9-、
[式中:
R18は、それぞれ独立して、水素原子またはフッ素原子であり;
R19は、それぞれ独立して、水素原子、フェニル基またはC1-6アルキル基を表し;
k7は、1~20の整数であり;
k8は、0~10の整数であり;
k9は、0~10の整数であり;
ここに、k7、k8またはk9を付して括弧でくくられた各繰り返し単位の存在順序は式中において任意である。]
である、請求項1~13のいずれか1項に記載の組成物。 - Z2が、-(CF2)k7’-または-(CF2)k7’-(O)k8’-
[式中:
k7’は、1~6の整数であり;
k8’は、1~3の整数であり;
ここに、k7’またはk8’を付して括弧でくくられた各繰り返し単位の存在順序は式中において任意である。]
である、請求項1~13のいずれか1項に記載の組成物。 - Aが、-COOR3である、請求項1~15のいずれか1項に記載の組成物。
- 式(E1)で表される化合物の数平均分子量が、1,000~30,000である、請求項1~16のいずれか1項に記載の組成物。
- 式(D1)または(D2)で表されるパーフルオロ(ポリ)エーテル基含有シラン化合物の数平均分子量と、式(E1)で表される化合物の数平均分子量の差が2000以内である、請求項1~17のいずれか1項に記載の組成物。
- 前記式(D1)または(D2)で表されるパーフルオロ(ポリ)エーテル基含有シラン化合物と前記式(E1)で表される化合物の含有量の比は、99.99:0.01~97:3である、請求項1~18のいずれか1項に記載の組成物。
- 含フッ素オイル、シリコーンオイル、および触媒から選択される1種またはそれ以上の他の成分をさらに含有する、請求項1~19のいずれかに記載の組成物。
- 含フッ素オイルが、式(3):
Rf3-(OC4F8)a1-(OC3F6)b1-(OC2F4)c1-(OCF2)d1-Rf4 (3)
[式中:
Rf3は、1個またはそれ以上のフッ素原子により置換されていてもよい炭素数1~16のアルキル基を表し;
Rf4は、1個またはそれ以上のフッ素原子により置換されていてもよい炭素数1~16のアルキル基、フッ素原子または水素原子を表し;
a1、b1、c1およびd1は、ポリマーの主骨格を構成するパーフルオロ(ポリ)エーテルの4種の繰り返し単位数をそれぞれ表し、互いに独立して0以上300以下の整数であって、a1、b1、c1およびd1の和は少なくとも1であり、添字a1、b1、c1またはd1を付して括弧でくくられた各繰り返し単位の存在順序は、式中において任意である。]
で表される1種またはそれ以上の化合物である、請求項20に記載の組成物。 - さらに溶媒を含む、請求項1~21のいずれか1項に記載の組成物。
- 表面処理剤である、請求項1~22のいずれか1項に記載の組成物。
- 防汚性コーティング剤または防水性コーティング剤として使用される、請求項1~23のいずれか1項に記載の組成物。
- 請求項1~24のいずれか1項に記載の組成物を含有するペレット。
- 基材と、該基材の表面に、請求項1~24のいずれか1項に記載の組成物より形成された層とを含む物品。
- 基材がガラスである、請求項26に記載の物品。
- 基材がサファイアガラス、ソーダライムガラス、アルカリアルミノケイ酸塩ガラス、ホウ珪酸ガラス、無アルカリガラス、クリスタルガラスおよび石英ガラスから成る群から選択されるガラスである、請求項26に記載の物品。
- 光学部材である、請求項26~28のいずれか1項に記載の物品。
- ディスプレイである、請求項26~28のいずれか1項に記載の物品。