JP7224141B2 - Ferritic stainless steel sheet, manufacturing method thereof, and fuel cell member - Google Patents

Description

TECHNICAL FIELD The present invention relates to a ferritic stainless steel sheet , a method for producing the same, and a fuel cell member.

Recently, due to problems such as the depletion of fossil fuels represented by petroleum and the phenomenon of global warming caused by CO ₂ emissions, the spread of new systems to replace conventional power generation systems is accelerating. As one of them, the "fuel cell" which has a high practical value as a distributed power source and a power source for automobiles is attracting attention. Among several types of fuel cells, polymer electrolyte fuel cells (PEFC) and solid oxide fuel cells (SOFC) have high energy efficiency and are expected to spread and expand in the future.

A fuel cell is a device that generates electric power through the reverse reaction process of electrolysis of water, and requires hydrogen as a fuel (fuel hydrogen). Fuel hydrogen is produced by reforming hydrocarbon fuels such as city gas (LNG), methane, natural gas, propane, kerosene and gasoline in the presence of a catalyst. Among them, fuel cells using city gas as raw fuel have the advantage of being able to produce hydrogen in areas where city gas pipes are installed.

A fuel reformer is usually operated at a high temperature of 200 to 900° C. in order to secure the amount of heat necessary for the hydrogen reforming reaction. In addition to the fuel reformer, the operating temperature of the combustor for heating the reformer, the heat exchanger, the battery main body, etc. becomes extremely high.
Furthermore, in such a fuel cell under high temperature operation, in addition to a large amount of water vapor, carbon dioxide and carbon monoxide, an atmosphere containing a large amount of hydrogen and a trace amount of hydrogen sulfide derived from hydrocarbon fuel (hereinafter referred to as carburizing /reducing/sulfidizing reformed gas environment). If a steel material, for example, is exposed to such an atmosphere, the surface of the material will be carburized and corroded due to sulfidation, resulting in a severe operating environment.

Until now, austenitic stainless steel represented by SUS310S (25Cr-20Ni) has been used as a practical material for fuel cells that has sufficient durability in such harsh environments. However, in the future, cost reduction is essential for the spread and expansion of fuel cell systems, and the reduction of alloy costs by optimizing the materials used is an important issue. Furthermore, in a fuel cell system, when stainless steel containing a relatively high amount of Cr is used, the operating temperature is extremely high, so there is also the problem of preventing electrode poisoning due to Cr evaporation.

From the above background, the high oxidation resistance of the Al-based oxide layer (Al-based oxide film) was used as a steel material for fuel cells in order to exhibit good durability even in a harsh reformed gas environment. Various Al-containing ferritic stainless steels have been studied.

Patent Document 1 describes Cr: 13 to 20%, C: less than 0.02%, N: 0.02% or less, Si: more than 0.15 to 0.7%, Mn: 0.3% or less, Al : 1.5 to 6%, Ti: 0.03 to 0.5%, Nb: 0.6% or less, and by adjusting the amount of solid solution Ti and solid solution Nb, oxidation resistance and creep rupture life discloses a good Al-containing ferritic stainless steel for fuel cells. These stainless steels have been shown to have good oxidation resistance by an accelerated oxidation test in air at 1050°C.

In Patent Document 2, Cr: 11 to 25%, C: 0.03% or less, Si: 2% or less, Mn: 2% or less, Al: 0.5 to 4.0%, P: 0.05% Below, S: 0.01% or less, N: 0.03% or less, Ti: 1% or less, containing 50% by volume or more of hydrogen gas, and adding Ti and Al to the steel surface in and under the oxide film A ferritic stainless steel for fuel cells is disclosed which is enriched and has improved oxidation resistance in a reformed gas environment by adding trace amounts of Mg, Ga, Sn, and Sb.

In Patent Document 3, Cr: 11.0 to 25.0%, C: 0.030% or less, Si: 2.00% or less, Mn: 2.00% or less, Al: 0.90 to 4.00 %, P: 0.050% or less, S: 0.0100% or less, N: 0.030% or less, Ti: 0.500% or less, and trace amounts of B, Mg, and Ca and combined addition with Sn discloses a ferritic stainless steel for fuel cells with improved oxidation resistance and creep resistance in a reformed gas environment.

In Patent Document 4, Cr: 11 to 25%, C: 0.03% or less, Si: 2% or less, Mn: 2% or less, Al: 0.5 to 4.0%, P: 0.05% Below, S: 0.01% or less, N: 0.03% or less, Ti: 0.5% or less, Ga: 0.1% or less, Mg: 0.01% or less, Zn: 0.05 % or less, and by adding a small amount of Mg, Ga, Zn, and further Sn, Sb to form a surface film in which Ti and/or Al are concentrated, oxidation resistance is improved. A ferritic stainless steel is disclosed.

In Patent Document 5, C: 0.020% or less, Si: 3.0% or less, Mn: 3.0% or less, P: 0.040% or less, S: 0.030% or less, Cr: 10 to 25 %, N: 0.020% or less, Nb: 0.005 to 0.15%, Al: 0.20 to 3.0%, Ti: 5 × (C% + N%) ~ 0.5%, Mo: 0.1% or less, W: 0.1% or less, Cu: 0.55 to 2.0%, B: 0.0002 to 0.0050%, Ni: 0.05 to 1.0%, A ferritic stainless steel having improved oxidation resistance by containing an appropriate amount of Ni is disclosed.

JP 2010-222638 A Japanese Patent No. 6006893 Japanese Patent No. 6053994 JP 2016-211076 A JP 2013-210443 A

In addition to steam, carbon dioxide, and carbon monoxide, the reformed gas of a fuel cell using city gas or the like as a raw fuel may contain a large amount of hydrogen and impurities or sulfide components added as odorants. be. However, conventionally, the oxidation resistance of ferritic stainless steels has been evaluated and studied only in an atmosphere containing water vapor and carbon dioxide as main components, an atmosphere containing water vapor and oxygen as main components, or in the air. . That is, the oxidation properties of ferritic stainless steel under the carburizing/reducing/sulfidic reformed gas environment are unknown.
Furthermore, in the case of the SOFC system and the PEFC system, the operating temperature of the fuel cell becomes high, so in addition to the above-mentioned oxidation characteristics, further improvement in high-temperature strength is required.

Although the ferritic stainless steels of Patent Documents 1 to 5 have been studied for durability in an oxidizing environment, there is nothing about durability in a more severe environment such as the carburizing/reducing/sulfurizing reformed gas environment. Not mentioned.

The present invention has been devised to solve the above-described problems, and has both high oxidation resistance and excellent high-temperature strength even in the carburizing/reducing/sulfiding reformed gas environment. A ferritic stainless steel sheet and a method for producing the same are provided.

The gist of the present invention is as follows.
[1] In % by mass,
Cr: 12.0 to 16.0%,
C: 0.020% or less,
Si: 0.50 to 2.50%,
Mn: 1.00% or less,
P: 0.050% or less,
S: 0.0030% or less,
Al: 1.00-3.00%
N: 0.030% or less,
Nb: 0.05 to 1.00%,
Ni: 0.05 to 1.00%,
Mo: 0.05-1.00%,
Sn: 0.005-0.200%
B: 0.0005 to 0.0100%,
Cu: 0 to 1.00%,
Sb: 0 to 0.50%,
W: 0 to 1.00%,
Co: 0-0.50%,
V: 0 to 0.50%,
Ti: 0 to 0.50%,
Zr: 0 to 0.50%,
La: 0 to 0.100%,
Y: 0 to 0.100%,
Hf: 0 to 0.100%,
REM: 0-0.100%
Ga: 0 to 0.0200%,
Mg: 0-0.0200%,
Ca: 0-0.0100%
and satisfies the following formula (1), the balance being Fe and impurities,
In the surface layer portion including the passive film, which is a region from the steel plate surface to a depth of 30 nm, the maximum concentrations Crm, Alm, and Nbm (at%) of Cr, Al, and Si are obtained by the following formula (2) and the following formula ( 3) A ferritic stainless steel sheet characterized by satisfying 3).
0.7Nb+Ni+Mo+0.4Ti+0.4Cu+200B≧0.30 (1)
15.0<Crm(at%)<50.5 (2)
2.7<Alm+Nbm(at%)<10.0 (3)
Each element symbol in the above formula (1) indicates the content (% by mass) of the element in the steel, and 0 is substituted when the element is not contained.
[2] The ferritic stainless steel sheet according to [1] above, characterized in that, in mass %, B: 0.0010% or more.
[ 3 ] In mass%, Cu: 0.10 to 1.00%, Sb: 0.01 to 0.50%, W: 0.10 to 1.00%, Co: 0.10 to 0.50 %, V: 0.10 to 0.50%, Ti: 0.01 to 0.50%, Zr: 0.01 to 0.50%, La: 0.001 to 0.100%, Y: 0. 001-0.100%, Hf: 0.001-0.100%, REM: 0.001-0.100%, Ga: 0.0002-0.0200%, Mg: 0.0002-0.0200% and Ca: one or more of 0.0002 to 0.0100%. The ferritic stainless steel sheet according to [1] or [2] above.
[ 4 ] The ferritic stainless steel sheet according to any one of the above [1] to [ 3 ], which is used for fuel reformers, heat exchangers or fuel cell members.
[ 5 ] The ferritic stainless steel sheet according to any one of the above [1] to [ 3 ], which is applied to a member of a combustor or a burner.
[ 6 ] A stainless steel material having the composition described in any one of [1] to [ 3 ] above is cold-rolled, finish-annealed, polished with an abrasive of #100 or less, and then subjected to the following treatment ( The method for producing a ferritic stainless steel sheet according to any one of [1] to [ 5 ], characterized in that at least one of A) or treatment (B) is carried out.
Treatment (A): Immersion in an aqueous sulfuric acid solution containing 10 to 50% by mass of H ₂ SO ₄ at 90° C. or less Treatment (B): Containing 1% by mass or more of HNO ₃ and 0.5% by mass or more of HF [ 7 ] The method for producing a ferritic stainless steel sheet according to [ 6 ], wherein the final annealing is performed at 800 to 1150°C.
[8] A fuel cell member using the ferritic stainless steel sheet according to any one of [1] to [ 4 ] above.

According to the present invention, at least H ₂ O: 10-40%, H ₂ : 50-70%, CO: 5-15%, CO ₂ : 5 in a carburizing/reducing/sulfidic reformed gas environment Provides ferritic stainless steel with high oxidation resistance and excellent high-temperature strength in a reformed gas environment containing ~15% H ₂ S and 0-0.01% H 2 S, its manufacturing method, and fuel cell components can do.

In order to solve the above-described problems, the present inventors have made extensive experiments and studies on an Al-containing ferritic stainless steel sheet having both high-temperature strength and oxidation resistance, and completed the present invention. In addition, the “high temperature strength” in the present embodiment is a property that can exhibit excellent 0.2% proof stress even in a high temperature range around 750 to 800 ° C., and the “oxidation resistance” is the carburization / reduction Oxidizing properties in a sulfidic/sulfidic reformed gas environment.
The knowledge obtained in the present invention will be described below.

(a) Normally, in order to suppress deformation that is a problem in a structure during operation in a high temperature range around 750 to 800 ° C., the high temperature strength of the ferritic stainless steel plate as a material, especially 0.2 at around 750 ° C. It is effective to increase the % yield strength and suppress the decrease in the 0.2% yield strength at around 800°C.

(b) It was found that the improvement and suppression of the decrease in the 0.2% yield strength in the high temperature range described above are significantly improved by excessive addition of Al, addition of small amounts of B, Nb, and Sn and adjustment of the amount added. rice field. That is, in the ferritic stainless steel sheet , the characteristics of increasing the 0.2% yield strength at around 750°C and suppressing the decrease in the 0.2% yield strength at around 800°C can be achieved by adding these trace elements. knowledge was obtained. Although there are still many unclear points about the effect of improving the high-temperature strength, the mechanism of action described below is inferred based on the experimental facts.

(c) Addition of a small amount of B contributes not a little to the increase in yield strength and tensile strength at 750 to 800° C., and has the effect of greatly improving the 0.2% yield strength in particular. The addition of a small amount of B suppresses the formation of cavities (nano-sized gaps) that occur starting at the grain boundaries due to grain boundary segregation, delays grain boundary sliding, and increases the dislocation density in the grains. has the effect of increasing the internal stress associated with the rise of In addition, we have found new knowledge that these effects of B are remarkable in Nb-added steel.

(d) It is well known that the addition of Nb is effective in increasing the strength in the temperature range up to 750° C. due to solid solution strengthening. Precipitation of Nb starts at 750 to 800° C. by forming an intermetallic compound called Laves phase (Fe ₂ Nb). The effect of improving the strength can be actualized.

(e) Furthermore, combined addition with Sn is effective in enhancing the function and effect of increasing the internal stress associated with the increase in dislocation density in grains, as described in (c) above. Although Sn is a grain boundary segregation element, the addition of Sn increases the solid-solution strengthening action within the crystal grains due to the combined addition of B and Nb, which is effective in increasing the high-temperature strength associated with the increase in internal stress. be.

(f) In addition, in order to increase the oxidation resistance under the reformed gas environment containing the hydrogen and sulfide components described above, the content of Si, Al, and Nb is adjusted within a predetermined range, so that the reformed gas It is effective to promote the formation of an Al-based oxide film in the environment and to enhance the protective properties of the film. Furthermore, the addition of B, Nb, and Sn to improve the 0.2% proof stress in the high-temperature range in the ferritic stainless steel sheet does not impair the oxidation resistance in the reformed gas environment. Furthermore, by adding certain amounts of Mo, Ni, and B, the formation of an Al-based oxide film is promoted even in a medium temperature range of about 500 to 550° C., exhibiting excellent oxidation resistance.

In this embodiment, the surface film before being exposed to the high-temperature reforming gas environment is the "passive film", and the composition of the passive film exposed to the high-temperature reforming gas environment has changed due to various reactions. will be described by distinguishing it from "Al-based oxide film".

(g) The above carburizing/reducing/sulfidizing reformed gas environment is more likely to cause defects in the Al-based oxide film on the ferritic stainless steel sheet than in the air or in the steam oxidation environment that does not contain hydrogen. It is not clear why the reformed gas environment facilitates the formation of defects in the oxide film, but it is speculated that the sulfides produced under the reformed gas containing sulfide components have some adverse effect on the oxide film. . If defects occur in the Al-based oxide film in a modified gas environment, oxidation of Cr and Fe may progress in the exposed base material. The addition of Mo, Ni, and B accelerates the formation of an Al-based oxide film in response to the promotion of oxidation in the modified gas. In particular, in the medium temperature range of 500 to 550°C, where diffusion of Al is slow and formation of a continuous Al-based oxide film is difficult, the addition of Mo, Ni, and B promotes the formation of an amorphous Al-based oxide film, resulting in acid resistance. chemistries are improved. As a result, the oxidation resistance of the ferritic stainless steel sheet can be improved.

(h) The oxidation resistance in the reformed gas environment described above is greatly affected by the passive film formed on the ferritic stainless steel sheet. Usually, after pickling or polishing, a passivation film mainly composed of Fe--Cr is formed on the surface. Oxidation of Cr is easily accelerated when such a passive film is formed on the surface. Here, as a result of the studies of the present inventors, by pre-concentrating Cr, Al, and Nb in the passive film and in the region immediately below the passive film (the region from the surface of the steel sheet to a depth of 30 nm), A new finding was obtained that can more effectively suppress the deterioration of oxidation resistance when exposed to . When Cr is oxidized, it initially exists as Cr ₂ O ₃ , but this Cr ₂ O ₃ suppresses the oxidation of Fe, and Al ³⁺ having the same valence replaces Cr to form Al ₂ O ₃ (Al-based As a result, the formation of an Al-based oxide film is promoted. That is, by pre-concentrating Cr, Al, and Si in the passive film and immediately below the passive film, the oxidation of Cr and Fe in the modified gas environment can be suppressed, and the formation of the Al-based oxide film can be promoted. presumed to be

(i) Further, in order to pre-concentrate Cr, Al, and Nb in the passive film and directly under the passive film, a polishing step is performed after cold-rolled sheet annealing (finish annealing), followed by a sulfuric acid immersion step or nitric fluoride. It is effective to carry out at least one dipping step of the acid dipping step.

(j) Furthermore, regarding the precipitation of intermetallic compound σ phase at high temperature (σ brittleness) and brittleness at 475°C, which were disadvantages of conventional Al- and Si-containing stainless steels, the chemical composition is Cr, Nb, Si, It was found that adjusting the Al content is effective. The σ brittleness and 475° C. brittleness are derived from the formation of intermetallic compounds containing Si and Al mainly composed of Cr, and the formation sites thereof are often grain boundaries. That is, in order to suppress the σ embrittlement and the 475° C. embrittlement, it is effective to suppress the generation of the intermetallic compound itself and to reduce the generation sites thereof. As a result of further investigation by the present inventors, it was found that the formation of the intermetallic compound itself is suppressed by limiting the amount of Cr, and the formation site is suppressed by the segregation of Nb to the grain boundary, thereby stabilizing the structure. As a result, it was found that σ brittleness and 475°C brittleness can be suppressed. Furthermore, by limiting the amount of Cr and adding Nb, it is possible to suppress the formation of intermetallic compounds containing Si and Al, so that the amounts of Si and Al that contribute to the oxidation resistance described in (g) above can be secured. It is also possible to achieve both plasticity and structural stability.

As described above, in the ferritic stainless steel sheet , the combined addition of B, Nb, Sn, Mo, and Ni results in high-temperature strength and reforming properties, which are important for durability in a carburizing/reducing/sulfurizing reforming gas environment. New knowledge was obtained that oxidation resistance in gas can be combined. Furthermore, by optimizing the content of Cr, Nb, Si, and Al in ferritic stainless steel sheets , it is possible to suppress σ embrittlement and 475°C embrittlement by improving structural stability, and achieve both oxidation resistance. I also learned that it is possible.

An embodiment of the ferritic stainless steel sheet of the present invention will be described below.

<Component composition>
First, the reasons for limiting the components will be explained below. In addition, "%" display of content of each element means "mass%."

Cr is a basic constituent element for securing high-temperature strength in addition to corrosion resistance. In this embodiment, if the content is less than 12.0%, the target high-temperature strength and oxidation resistance are not sufficiently ensured. Therefore, the lower limit of the Cr content is made 12.0% or more. Preferably it is 13.0% or more. However, excessive Cr content promotes the formation of a brittle phase σ phase (Fe—Cr intermetallic compound) when exposed to a high-temperature atmosphere, and may promote cracking during manufacturing. . Therefore, the upper limit of the Cr content is made 16.0% or less from the viewpoint of basic properties and manufacturability. Preferably, it is 15.0% or less.

C forms a solid solution in the ferrite phase or forms Cr carbide to impair the oxidation resistance. Therefore, the upper limit of the amount of C is made 0.020% or less. Preferably, it is 0.015% or less. However, excessive reduction in the amount of C leads to an increase in refining costs, so the lower limit is preferably 0.001% or more. From the viewpoint of oxidation resistance and manufacturability, it is more preferably 0.005% or more.

Si is an important element for ensuring oxidation resistance. Si is slightly solid-dissolved in the Al-based oxide film and also concentrates directly under the Al-based oxide film/steel interface, thereby improving oxidation resistance in a reformed gas environment. In order to obtain these effects, 0.50% or more is required. Preferably it is 0.70% or more. On the other hand, an excessive Si content may impede the toughness and workability of the steel and inhibit the formation of an Al-based oxide film, so the upper limit is made 2.50% or less. 1.70% or less is preferable from the viewpoint of oxidation resistance and basic properties.

Mn dissolves together with Si in the Al-based oxide film or immediately below it in a modified gas environment, thereby increasing the protective properties of the film and contributing to the improvement of oxidation resistance. In order to obtain these effects, the lower limit is preferably 0.10% or more. More preferably, it is 0.20% or more. On the other hand, an excessive Mn content impairs the corrosion resistance of steel and the formation of Ti- and Al-based oxide films, so the upper limit is made 1.00% or less. 0.90% or less is preferable from the viewpoint of oxidation resistance and basic properties.

In addition to being a deoxidizing element, Al is an essential element in the present embodiment that contributes to the improvement of oxidation resistance by forming an Al-based oxide film in the reforming gas. In this embodiment, 1.00% or more is necessary to obtain good oxidation resistance, and preferably 1.50% or more. However, an excessive Al content causes a decrease in the toughness and weldability of the steel and impairs productivity, so that there is a problem of economic efficiency as well as an increase in alloy cost. Therefore, the upper limit of the Al content is set to 3.00% or less from the viewpoint of basic properties and economy. Preferably, it is 2.50% or less.

P is an element that hinders manufacturability and weldability. However, excessive reduction of P leads to an increase in refining cost, so the lower limit is preferably 0.003%. From the viewpoint of manufacturability and weldability, the preferred range is 0.005 to 0.040%, more preferably 0.010 to 0.030%.

S is an impurity element that is inevitably contained in steel, and lowers high-temperature strength and oxidation resistance. In particular, grain boundary segregation of S, Mn-based inclusions, and the presence of solid solution S have the effect of lowering the high-temperature strength and oxidation resistance. Therefore, the lower the S content, the better, so the upper limit is made 0.0030% or less. However, excessive reduction of S leads to an increase in raw material and refining costs, so the lower limit is preferably 0.0001% or more. From the standpoint of manufacturability and oxidation resistance, the preferred range is 0.0001 to 0.0020%, more preferably 0.0002 to 0.0010%.

N, like C, is an element that inhibits oxidation resistance. Therefore, the smaller the amount of N, the better, and the upper limit is made 0.030% or less. However, excessive reduction of N leads to an increase in refining cost, so the lower limit is preferably 0.002% or more. From the standpoint of oxidation resistance and manufacturability, the preferred range of N content is 0.005 to 0.020%.

Nb is a stabilizing element that fixes C and N, and by this action it is possible to improve the oxidation resistance and corrosion resistance through the high purity of the steel. Further, in the present embodiment, it is an element that effectively acts to improve the high-temperature strength due to the effect of co-segregation with B at the grain boundary. Furthermore, intermetallic compounds that cause σ embrittlement and 475° C. embrittlement are mainly precipitated at grain boundaries, but the segregation of Nb to grain boundaries reduces the generation sites. , the stability of the structure increases, and as a result, σ embrittlement and 475° C embrittlement can be suppressed. In order to obtain the effects of both oxidation resistance and high-temperature strength, the lower limit of the Nb content is 0.05% or more, preferably 0.15% or more. On the other hand, an excessive Nb content leads to an increase in alloy cost and impairs manufacturability, so the upper limit of the Nb content is made 1.00% or less. It is preferably 0.60% or less.

Next, the concentration (% by mass) of segregating elements at grain boundaries will be described.
As described in the above findings, in the present embodiment, the co-segregation of Nb and B at the grain boundaries can improve the high-temperature strength. Similarly, Sn segregates to grain boundaries, thereby suppressing grain boundary sliding and improving high-temperature strength. From these points of view, in the ferritic stainless steel sheet according to the present embodiment, the concentration of Nb at the grain boundaries (grain boundary concentration) is preferably 3.0% or more. When Sn is contained, the grain boundary concentration of Sn is preferably 1.0% or more. On the other hand, excessive grain boundary segregation of Nb and Sn may result in deterioration of high-temperature strength, in addition to hindering manufacturability as grain boundaries become fracture starting points. Therefore, the grain boundary concentration of Nb is preferably 10.0% or less, and the grain boundary concentration of Sn is preferably 5.0% or less.

The Nb concentration and Sn concentration at the grain boundaries can be measured by Auger Electron Spectrometry (AES).
First, a notched test piece (0.8t×4w×20L (mm)) is taken from an arbitrary portion of the matrix other than the oxide film. Next, after cooling the notched test piece with liquid nitrogen in a vacuum (degree of vacuum: 10 ⁻⁶ MPa), the test piece is fractured on the spot from the notched portion to expose the fracture surface. AES analysis is performed on the crystal grain boundaries in the exposed fracture surface, the Auger electron spectrum is measured in the energy range of 0 to 1000 eV, and the detected elements are identified (qualitative analysis). Furthermore, using the obtained peak intensity ratio (relative sensitivity coefficient method), the detected element is quantified (quantitative analysis). By the above method, the concentration of the elements (Nb, Sn) segregated at the grain boundaries can be obtained.

Ni promotes outward diffusion of Al in steel and promotes formation of an Al-based oxide film. Furthermore, it is an element that improves the strength of steel through solid-solution strengthening. 0.05% or more is required for promotion of the formation of the Al-based oxide film, preferably 0.10% or more. Even if Ni is contained excessively, the effect of improving oxidation resistance is saturated. The cost of the alloy rises, and there is also the issue of economic efficiency. Therefore, the upper limit of the Ni content is set to 1.00% or less from the viewpoint of basic properties and economy. Preferably, it is 0.50% or less.

Mo concentrates at the interface between the oxide film and the steel in the use environment, and promotes the formation of the Al-based oxide film. 0.05% or more is required for promotion of the formation of the Al-based oxide film, preferably 0.10% or more. As with Ni, excessive addition of Mo saturates the effect of improving oxidation resistance and increases the alloy cost, so the upper limit of the Mo content is 1.00% or less. Preferably, it is 0.50% or less.

Sn is an element capable of exhibiting the effect of increasing the high-temperature strength. In order to obtain such effects, the lower limit of Sn must be 0.005% or more, preferably 0.010%. On the other hand, an excessive content leads to an increase in refining cost of steel, and also lowers manufacturability and corrosion resistance of steel. Therefore, the upper limit of Sn is set to 0.200% or less.

B concentrates at the interface between the oxide film and the steel in the usage environment and promotes the formation of the Al-based oxide film. Furthermore, the grain boundary segregation delays the grain boundary sliding and increases the internal stress accompanying the increase in the dislocation density in the crystal grains, thereby improving the 0.2% proof stress. In order to obtain these effects, 0.0005% or more is required, preferably 0.0010% or more.

Furthermore, the component composition of the present embodiment satisfies the following formula (1).
0.7Nb+Ni+Mo+0.4Ti+0.4Cu+200B≧0.30 (1)

Each element symbol in the formula (1) indicates the content (% by mass) of the element in the steel, and 0 is substituted when the element is not contained.

From the viewpoint of improving high-temperature strength and oxidation resistance, the content of formula (1) is preferably 0.35% or more, more preferably 0.40% or more. The upper limit of formula (1) is not particularly defined as the upper limit of Nb, Ni, Mo, Ti, Cu, and B, but it is preferably 2.4% from the viewpoint of oxidation resistance and manufacturability. .

The ferritic stainless steel sheet according to the present embodiment consists of Fe and impurities in addition to the above-described elements (the balance), but may also contain optional elements described later. Therefore, the lower limits of the contents of Cu, Sb, W, Co, V, Ti, Zr, La, Y, Hf, REM, Ga, Mg, and Ca are 0% or more.
In addition, the "impurities" in the present embodiment are components that are mixed due to various factors in the manufacturing process including raw materials such as ores and scraps when steel is manufactured industrially, and are unavoidably mixed. Including ingredients.

The ferritic stainless steel sheet of the present embodiment has Cu: 1.00% or less, Sb: 0.50% or less, W: 1.00% or less, Co: 0.50% or less, V: 0.50% or less Ti: 0.50% or less Zr: 0.50% or less La: 0.100% or less Y: 0.100% or less Hf: 0.100% or less REM: 0.50% or less It may contain one or more of 100% or less, Ga: 0.0200% or less, Mg: 0.0200% or less, and Ca: 0.0100% or less.

Cu, Sb, W, Co, V, and Ti are elements effective in enhancing the high-temperature strength and corrosion resistance of steel, and may be contained as necessary. However, since an excessive content leads to an increase in alloy cost and impedes manufacturability, the upper limits of Cu and W are set to 1.00% or less. Sb is an element that concentrates in the vicinity of the steel surface to promote selective oxidation of Al and has the effect of improving corrosion resistance. The upper limits of Co, Ti, and V are 0.50% or less. The lower limit of the content of any of Cu, W, Co, and V is preferably 0.10% or more. The lower limit of the content of Sb and Ti is preferably 0.01% or more.

Zr, La, Y, Hf, and REM are conventionally effective elements for improving hot workability and cleanliness of steel as well as improving oxidation resistance, and may be contained as necessary. However, from the viewpoint of the technical idea of the present invention and the reduction of the alloy cost, it does not depend on the effect of adding these elements. When Zr, La, Y, Hf, and REM are contained, the upper limit of Zr is 0.50%, and the upper limit of La, Y, Hf, and REM is 0.100%. A more preferable lower limit for Zr to obtain the above effect is 0.01%, and a preferable lower limit for La, Y, Hf, and REM is 0.001%. Here, REM is an element belonging to atomic numbers 58 to 71, excluding La and Y, and Sc (scandium), such as Ce, Pr, and Nd. REM in the present embodiment is composed of one or more elements selected from elements belonging to atomic numbers 58 to 71 and Sc, and the amount of REM is the total amount thereof.

Ga, Mg, and Ca are elements that can exhibit the effect of increasing the high-temperature strength. Ga, Mg, and Ca have the effect of concentrating in the vicinity of the surface and promoting selective oxidation of Al. In order to obtain such an effect, it is preferable that the lower limit of each content of Ga, Mg, and Ca is 0.0002% or more. On the other hand, an excessive content of these elements leads to an increase in refining cost of steel, and also lowers manufacturability and corrosion resistance of steel. Therefore, the upper limit of the content of Ca is set to 0.0100% or less, and the upper limits of both Ga and Mg are set to 0.0200% or less.

The ferritic stainless steel sheet according to the present embodiment is composed of Fe and impurities (including unavoidable impurities) other than the elements described above, but the effects of the present invention are not impaired in addition to the elements described above. It can be contained within the range. It is preferable to reduce the general impurity elements such as P and S described above, as well as Bi and Se, as much as possible. On the other hand, the content of these elements is controlled to the extent that the objects of the present invention are solved, and if necessary, one or more of Bi≦100 ppm and Se≦100 ppm may be contained.

The metal structure of the ferritic stainless steel sheet of this embodiment consists of a ferrite single-phase structure. This means that it does not contain an austenitic phase or a martensitic structure. When the austenite phase or martensite structure is included, the raw material cost is increased, and yield reduction such as edge cracking is likely to occur during production. Therefore, the metal structure should be a ferrite single phase structure. Precipitates such as carbonitrides are present in the steel, but these precipitates need not be considered because they do not greatly affect the effects of the present invention.

<Maximum concentration of Cr, Al, and Nb in the surface layer of the steel sheet>
In the ferritic stainless steel sheet of the present embodiment, Cr, Al, and Nb are preliminarily concentrated in the surface layer of the steel sheet in order to promote the formation of an Al-based oxide film and improve oxidation resistance. Specifically, in the surface layer of the steel sheet, which is a region from the steel plate surface to a depth of 30 nm (region including the passive film and the region immediately below the passive film), each maximum in the concentration (cation fraction) distribution of Cr, Al, and Nb It is assumed that the values (maximum concentrations) Crm, Alm, and Nbm satisfy the following formulas (2) and (3).
15.0<Crm(at%)<50.5 (2)
2.7<Alm+Nbm(at%)<10.0 (3)

Oxidizability in a reformed gas environment is greatly affected by the passive film formed on the ferritic stainless steel sheet. Usually, after pickling or polishing, a passive film of about 2 nm to 20 nm is formed on the surface of the steel sheet. Cr oxidation is easily accelerated when this passive film mainly composed of Fe—Cr is formed on the surface. Therefore, in the present embodiment, Cr, Al, and Nb are concentrated in advance in order to promote the formation of an Al-based oxide film that effectively improves oxidation resistance in the passive film and in the region immediately below the passive film. shall be assumed. The reason why the target region for concentrating Cr, Al, and Nb is limited to the region from the surface of the steel sheet to a depth of 30 nm is that if the depth is 30 nm, the thickness of the general passive film is 2 to 20 nm + the film This is because it can be determined that the direct-lower region is sufficiently captured.

The composition of the region from the surface of the steel sheet to a depth of 30 nm is such that the maximum Cr concentration Crm is more than 15.0 at% and less than 50.0 at%, and the Al concentration and Nb concentration are in order to promote the formation of the Al ₂ O ₃ coating. The maximum total value (Alm+Nbm) is in the range of more than 2.7 atomic % and less than 10.0 atomic %.
If the Crm is 15.0% or less, the Fe concentration in the region may increase and inhibit the formation of the Al-based oxide film. That's it. On the other hand, when Crm is 50.5% or more, the selective oxidation of Cr may inhibit the formation of an Al-based oxide film, so Crm is set to less than 50.5 at%, preferably 45.0% or less. do.
Also, by concentrating Nb together with Al, it suppresses the oxidation of Fe and Cr and effectively acts on the formation of the Al-based oxide film. However, when Alm+Nbm is 2.7 at % or less, the oxidation of Fe and Cr progresses, and the effect of promoting the formation of Al-based oxide film cannot be obtained. 8 at % or more. On the other hand, although it is effective to increase the Al and Nb concentrations to promote the formation of the Al-based oxide film, if Alm + Nbm is 10.0% or more, productivity is reduced, and Nb oxide may be formed and deteriorate the oxidation resistance. Therefore, the upper limit of Alm+Nbm is less than 10.0 atomic %, preferably 7.0 atomic % or less, from the viewpoint of cost effectiveness.

The maximum concentration of Cr, Al, and Nb in a region (surface layer) from the surface of the steel sheet to a depth of 30 nm is measured by depth profile by XPS (X-ray Photoelectron Spectroscopy). For each element determined by the depth profile, a state analysis is performed to separate the cation ions of the element existing as an oxide and the cation ions of the element existing as a metal. Assuming that the total concentration of all cation ions including both cation ions of elements present as metals and cation ions of elements present as oxides is 100%, Cr, Al and Nb present as oxides Calculate the cationic ion fraction (at. %).

The range for calculating the cation ion fraction is the range from the surface of the coating to the depth position where the detection intensity of O (oxygen) is half the detection intensity of oxygen on the coating surface. XPS is measured under the following conditions.
・Equipment: XPS measurement equipment (ULVAC-Phi, Inc., QuanteraSXM)
・ X-ray: mono-AlKα ray (hν = 1486.6 eV), X-ray diameter: 100 μmΦ
・ Neutralization gun: 1.0 V, 20 μA
・Sputtering conditions: Ar+, acceleration voltage: 1 kV, raster: 2×2 mm
・Sputtering speed: 1.8 nm/min. ( _SiO2 conversion value)

Fe, Cr, Mn, Si, Al, Ti, Nb, Mo, Ni, and B, which are detected elements in XPS analysis, are elements that are concentrated on the surface of the steel sheet and elements that constitute oxides. Crm, Alm, and Nbm are calculated based on the concentration. Although Si and B are generally classified as semimetals, they are treated as metal elements when calculating Crm, Alm, and Nbm.
Since N does not condense on the surface and C is a contaminant element, the Cr, Al, and Nb concentrations are calculated by excluding these two elements after detection by XPS analysis.

The shape of the ferritic stainless steel sheet of the present embodiment is not particularly limited, and may be plate-like, tubular, bar-like, or the like, and may be appropriately determined according to the size, shape, and shape of the member to be applied.

<Manufacturing method>
Next, regarding the method for manufacturing the ferritic stainless steel sheet of the present embodiment described above, it can be manufactured by combining hot working, cold working, and each heat treatment (annealing), and if necessary, polishing and Descaling by acid dipping may be performed. As an example of the production method, a production method having the steps of steelmaking-hot rolling-annealing-cold rolling-annealing (finish annealing)-mechanical polishing-acid immersion can be adopted.

Furthermore, when applied to gas piping, welded pipes manufactured from steel plates are also included, but the piping is not limited to welded pipes, and may be seamless pipes manufactured by hot working.

In order to control the Cr concentration, Al concentration, and Si concentration of the surface layer of the ferritic stainless steel sheet of the present embodiment within the above ranges, it is important to perform mechanical polishing and acid immersion after finish annealing. Steps and conditions other than those described above may be appropriately determined within a range that does not impair the effects of the present invention. Specifically, after finish annealing, polishing is performed with an abrasive of #100 or less defined in JIS6252 (2006), and then an acid immersion step consisting of at least one of the following treatment (A) or treatment (B) is performed. implement.
Treatment (A): Immersion in an aqueous sulfuric acid solution containing 10-50% by mass of H ₂ SO ₄ at 90° C. or lower Treatment (B): Containing 1% by mass or more of HNO ₃ and 0.5% by mass or more of HF Immersion in nitric hydrofluoric acid aqueous solution at 90°C or less

By performing mechanical polishing after the finish annealing, dislocations are introduced into the surface of the steel sheet and diffusion of atoms is promoted. As a result, the concentrations of not only Cr but also Al and Nb can be increased in the passivation film formed in the subsequent atmospheric exposure or acid immersion step. Preferably, mechanical polishing is performed after cold rolling and finish annealing, and further an acid immersion step is performed.
For the mechanical polishing, an abrasive having a count of 100 or less is used, and, for example, one pass of a coil grinder is performed. From the viewpoint of introducing more dislocations and increasing the concentration of Cr, Al, and Si in the passive film, the grade of the abrasive is preferably #80 or less, more preferably #30 or less.

In the acid immersion step after mechanical polishing, at least one of the treatment (A) or treatment (B) is performed. That is, after mechanical polishing, either one of the treatment (A) or the treatment (B) may be performed, or both may be performed. When both the treatment (A) and the treatment (B) are performed, the order may be arbitrary. For example, the treatment (A) may be followed by the treatment (B). The temperature of the sulfuric acid aqueous solution and the nitric hydrofluoric acid aqueous solution may be set to 40 to 90.degree. Further, the concentration of HNO ₃ in the nitric hydrofluoric acid aqueous solution may be 1 to 20% by mass, and the concentration of HF may be 0.5 to 10% by mass.
Note that if the above treatments (A) and (B) are performed without mechanical polishing, acid immersion will be performed without obtaining the above-described effect of promoting diffusion of atoms. , Al and Si enrichment cannot be achieved.

In addition, the conditions of cold rolling and finish annealing performed before mechanical polishing are not particularly limited, but the cold rolling reduction rate is 90% or less, and the finish annealing temperature is in the recrystallization temperature range of 800 to 1150 ° C. preferable.
In the present embodiment, the atmosphere during the finish annealing is not particularly specified, but it is preferably the air, a LNG fuel atmosphere, or a non-oxidizing atmosphere (bright annealing) using hydrogen, nitrogen, argon, or the like.

The ferritic stainless steel sheet according to this embodiment can be obtained by the manufacturing method described above.

According to the present embodiment, it is possible to provide a ferritic stainless steel sheet having both high oxidation resistance and excellent high-temperature strength even under the carburizing/reducing/sulfiding reformed gas environment. In particular, by controlling the respective concentrations of Cr, Al, and Nb in the steel sheet surface layer in the passivation film and directly under the passivation film, it is possible to enjoy better oxidation resistance.

Furthermore, according to the present embodiment, by optimizing the component composition, it is possible to enjoy excellent structural stability that can suppress σ phase precipitation and 475° C. embrittlement.

Therefore, it is suitable for fuel cell components such as fuel reformers and heat exchangers used when reforming hydrocarbon fuels such as city gas, methane, natural gas, propane, kerosene, and gasoline into hydrogen. In particular, it is suitable for high-temperature components of solid oxide fuel cells (SOFC) and polymer electrolyte fuel cells (PEFC), which operate at high temperatures. Further, it can be suitably used for peripheral members of the fuel cell, such as burners and combustors housing the burners, which are in contact with the reformed gas and used in high-temperature environments.

Next, examples of the present invention will be shown, but the conditions in the examples are examples of conditions adopted to confirm the feasibility and effect of the present invention, and the present invention was used in the following examples. It is not limited to conditions. Various conditions can be adopted in the present invention as long as the objects of the present invention are achieved without departing from the gist of the present invention.
In addition, underlines in the table shown below indicate those outside the scope of the present invention.

Various ferritic stainless steels whose composition is shown in Table 1 (steel Nos. A to O) were melted, hot-rolled into hot-rolled sheets with a thickness of 4 mm, and then hot-rolled sheets were annealed (annealing temperature: 900 to 1000 ° C.). ), pickling, and cold rolling to produce a cold-rolled steel sheet with a thickness of 0.8 mm. After cold rolling, final annealing is performed at 900 to 1000 ° C., and the obtained cold-rolled steel sheet is mechanically polished (#80 or less) and acid immersed under the conditions shown in Table 2 (treatment (A), treatment (B)) was performed to obtain finished steel sheets (No. 1 to 19).

Treatment (A): Immersion in an aqueous sulfuric acid solution containing 10-50% by mass of H ₂ SO ₄ at 90° C. or lower Treatment (B): Containing 1% by mass or more of HNO ₃ and 0.5% by mass or more of HF Immersion in an aqueous solution of nitric acid hydrofluoric acid at 90° C. or lower In Table 2, "O" indicates that each treatment was performed, and "-" indicates that each treatment was not performed.

[Composition of steel plate surface layer (Cr, Al, Nb maximum concentration)]
The maximum concentrations (Crm, Alm, Nbm) of Cr, Al, and Nb in the surface layer of the steel sheet (area from the steel sheet surface to a depth of 30 nm) were measured by a depth profile by XPS, and the depth from the steel sheet surface to a depth of 30 nm It was obtained by measuring the concentration profile of each element in the direction. For each element determined by the depth profile, a state analysis is performed to separate the element existing as an oxide (cation ion) and the element existing as a metal (cation ion). The cation ion fraction of Cr, Al and Nb present as oxides, with the total concentration of all cation ions including both cation ions present as metals and cation ions present as oxides being 100%. (at.%) is calculated. On top of that, the values at each position where the Cr, Al, and Nb concentrations show the maximum values within the range of the region from the steel plate surface to a depth of 30 nm are “Cr maximum concentration (Crm)” and “Al maximum concentration (Alm). ”, and “Nb maximum concentration (Nbm)”.

[Oxidation resistance]
First, an oxidation test piece having a width of 20 mm and a length of 25 mm was cut out from a cold-rolled steel sheet and subjected to an oxidation test. The atmosphere of the oxidation test was assumed to be a reformed gas using town gas as fuel, and was composed of 25% by volume H ₂ O-8% by volume CO-8% by volume CO ₂ -0.01% H ₂ S-bal. The atmosphere was _H2 . In this atmosphere, the oxidation test piece was heated to 550° C. or 650° C., held for 1000 hours, cooled to room temperature, and the oxidation weight gain ΔW (mg/cm ² ) was measured.
Both oxidation resistance at 550°C and oxidation resistance at 650°C were evaluated as follows.
◎: Weight increase ΔW is less than 0.1 mg/cm ² ○: Weight increase ΔW is 0.1 to 0.3 mg/cm ²
x: Weight increase ΔW exceeds 0.3 mg/cm ² Oxidation resistance was judged to pass when "⊚" and "◯" were obtained.

[High temperature strength]
A plate-shaped high-temperature tensile test piece (plate thickness: 0.8 mm, parallel part width: 10.5 mm, parallel part length: 35 mm) was prepared from the cold-rolled steel sheet with the rolling direction as the longitudinal direction. At each ° C, the strain rate is 0.3% / min up to 0.2% proof stress, and after that, a high temperature tensile test is performed at 3% / min, and 0.2% proof stress at each temperature (750 ° C proof stress, 800 ° C proof stress ) was measured (according to JIS G 0567).

Evaluation of high-temperature strength is evaluated as a pass ("○") when the 750 ° C proof stress is over 120 MPa and the 800 ° C proof stress is over 40 MPa, and if either one is not satisfied, it is rejected ("x"). evaluated. In addition, when the 750° C. proof stress was over 150 MPa and the 800° C. proof stress was over 60 MPa, it was evaluated as having particularly excellent high-temperature strength (indicated by “⊚” in Table 2).

[Structural stability (σ brittleness/475°C brittleness)]
Two samples were taken from the cold-rolled steel sheet so that the center of the cross section perpendicular to the plate surface (the center of the plate thickness: near t / 2) could be observed, and one was heat treated at 500 ° C. for 1000 hours (500 ° C. heat treatment), and the other was subjected to heat treatment at 650° C.×1000 hours (heat treatment at 650° C.). The atmosphere for these heat treatments was the air. Next, after each heat-treated sample was embedded in resin and polished, the Vickers hardness Hv (500 ° C.) after heat treatment at 500 ° C. and the Vickers hardness Hv (650 ° C.) after heat treatment at 650 ° C. were measured according to JIS Z 2244. The hardness was measured under a load of 9.8 N according to the above, and the amounts of increase in hardness ΔHv (500° C.) and ΔHv (650° C.) from the pre-heat treatment Vickers hardness previously measured before the heat treatment were calculated.

Evaluation of structural stability (σ brittleness / 475 ° C. brittleness) is evaluated as passing (“○”) for both ΔHv (500 ° C.) and ΔHv (650 ° C.) of less than 20, and 20 or more in either one. If there was, the increase in hardness after the heat treatment was large and the structure was unstable, so it was rejected (“x”).

The obtained evaluation results (measurement of grain boundary concentration, various properties) are shown in Table 2.
No. Nos. 1, 4 to 13 satisfy the composition of the components and the surface layer specified in the present invention, and the evaluation of all properties is "○" or "⊚". Among them, No. 5, 7, and 9 to 12 are cases where the composition of the surface layer portion is within the preferred range of the present invention, and the effect of improving the oxidation resistance can be remarkably exhibited, and the evaluation is "A".

On the other hand, No. 2 and 3 are examples in which the target surface layer composition of the present invention could not be satisfied, and the oxidation resistance was evaluated as "x". In addition, Steel Nos. 14 to 19 deviate from the steel composition specified in the present invention, and cannot achieve both of the properties targeted by the present invention, and one of the evaluations is "x". .

INDUSTRIAL APPLICABILITY According to the present invention, a ferritic stainless steel sheet having both high oxidation resistance and excellent high-temperature strength even in a carburizing/reducing/sulfidic reformed gas environment, a method for producing the same, and a fuel cell parts can be provided. The ferritic stainless steel sheet according to the present invention is used in fuel reformers, heat exchangers, etc. used when reforming hydrocarbon fuels such as city gas, methane, natural gas, propane, kerosene, and gasoline into hydrogen. It is particularly suitable for high-temperature members of solid oxide fuel cells (SOFC) and polymer electrolyte fuel cells (PEFC), which operate at high temperatures. Further, it can be suitably used for peripheral members of the fuel cell, such as burners and combustors housing the burners, which are in contact with the reformed gas and used in high-temperature environments.

Claims (6)

In % by mass,
Cr: 12.0 to 16.0%,
C: 0.020% or less,
Si: 0.50 to 2.50%,
Mn: 1.00% or less,
P: 0.050% or less,
S: 0.0030% or less,
Al: 1.00-3.00%
N: 0.030% or less,
Nb: 0.05 to 1.00%,
Ni: 0.05 to 1.00%,
Mo: 0.05-1.00%,
Sn: 0.005-0.200%
B: 0.0005 to 0.0100%,
Cu: 0 to 1.00%,
Sb: 0 to 0.50%,
W: 0 to 1.00%,
Co: 0-0.50%,
V: 0 to 0.50%,
Ti: 0 to 0.50%,
Zr: 0 to 0.50%,
La: 0 to 0.100%,
Y: 0 to 0.100%,
Hf: 0 to 0.100%,
REM: 0-0.100%
Ga: 0 to 0.0200% or less,
Mg: 0 to 0.0200% or less,
Ca: 0 to 0.0100% or less and satisfying the following formula (1), the balance being Fe and impurities,
In the surface layer portion including the passive film, which is a region from the steel plate surface to a depth of 30 nm, the maximum concentrations Crm, Alm, and Nbm (at%) of Cr, Al, and Si are obtained by the following formula (2) and the following formula ( 3) A ferritic stainless steel sheet characterized by satisfying 3).
0.7Nb+Ni+Mo+0.4Ti+0.4Cu+200B≧0.30 (1)
15.0<Crm(at%)<50.5 (2)
2.7<Alm+Nbm(at%)<10.0 (3)
Each element symbol in the above formula (1) indicates the content (% by mass) of the element in the steel, and 0 is substituted when the element is not contained. 2. The ferritic stainless steel sheet according to claim 1, wherein said B is 0.0010% or more in mass %. In mass%, Cu: 0.10 to 1.00%, Sb: 0.01 to 0.50%, W: 0.10 to 1.00%, Co: 0.10 to 0.50% , V: 0.10 to 0.50%, Ti: 0.01 to 0.50%, Zr: 0.01 to 0.50%, La: 0.001 to 0.100%, Y: 0.001 ~0.100%, Hf: 0.001-0.100%, REM: 0.001-0.100%, Ga: 0.0002-0.0200%, Mg: 0.0002-0.0200%, The ferritic stainless steel sheet according to claim 1 or 2, characterized by containing one or more of Ca: 0.0002 to 0.0100%. A stainless steel material having a composition according to any one of claims 1 to 3 is cold-rolled, finish-annealed, polished with an abrasive of #100 or less, and then subjected to the following treatment (A) or 4. The method for producing a ferritic stainless steel sheet according to any one of claims 1 to 3, wherein at least one of the treatments (B) is performed.
Treatment (A): Immersion in an aqueous sulfuric acid solution containing 10 to 50% by mass of H ₂ SO ₄ at 90° C. or less Treatment (B): Containing 1% by mass or more of HNO ₃ and 0.5% by mass or more of HF Immersion in nitric hydrofluoric acid aqueous solution at 90°C or less The method for producing a ferritic stainless steel sheet according to claim 4 , wherein the finish annealing is performed at 800 to 1150°C. A fuel cell member using the ferritic stainless steel sheet according to any one of claims 1 to 3 .