JP7093431B2 - ペロブスカイト型複合酸化物粉末およびその製造方法 - Google Patents
ペロブスカイト型複合酸化物粉末およびその製造方法 Download PDFInfo
- Publication number
- JP7093431B2 JP7093431B2 JP2021011914A JP2021011914A JP7093431B2 JP 7093431 B2 JP7093431 B2 JP 7093431B2 JP 2021011914 A JP2021011914 A JP 2021011914A JP 2021011914 A JP2021011914 A JP 2021011914A JP 7093431 B2 JP7093431 B2 JP 7093431B2
- Authority
- JP
- Japan
- Prior art keywords
- composite oxide
- perovskite
- type composite
- carbon dioxide
- oxide powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
まず、ビーズミル(アシザワファインテック株式会社製のパールミルAMS1(有効容量1.2L))の粉砕室(ベッセル)内に直径1.75mmのZrO2ビーズ3100gを充填した。また、このビーズミルのバッファータンク内に純水20kgと分散剤としてのポリアクリル酸アンモニウム2000gとを入れた後、組成式LaxSr1-xCoyFe1-yO3(x=0.6、y=0.2)で示されるペロブスカイト型複合酸化物(LSCF)を得るために、ペロブスカイト型複合酸化物の原料として、酸化ランタン(La2O3)粉末2165gと、炭酸ストロンチウム(SrCO3)粉末1299gと、酸化コバルト(Co3O4)粉末350gと、酸化鉄(Fe2O3)粉末1399gとをバッファータンクに投入してベッセル内に導入し、このベッセル内の攪拌機を回転数680rpmで80分間回転させて原料を粉砕し、固形分として原料の粉砕物を含む原料スラリーを得た。
組成式LaxSr1-xCoyFe1-yO3(x=0.6、y=0.2)で示されるペロブスカイト型複合酸化物(LSCF)を得るために、ペロブスカイト型複合酸化物の原料として、金属ランタン濃度14.8質量%の硝酸ランタン(La(NO3)3)水溶液307gと、硝酸ストロンチウム(Sr(NO3)2)粉末46gと、硝酸コバルト六水和物(Co(NO3)2・6H2O)粉末31gと、硝酸鉄九水和物(Fe(NO3)3・9H2O)粉末174gとを純水572gに溶解させて混合し、硝酸ランタンと硝酸ストロンチウムと硝酸コバルトと硝酸鉄の合計の濃度を約0.20モル/Lとして、硝酸塩の混合溶液を得た。
焼成温度を1100℃、熱処理温度を300℃とした以外は、実施例2と同様の方法により、ペロブスカイト型複合酸化物粉末を得た。なお、焼成サヤを取り出してから5分経過後の(熱処理後の)粉末の温度を測定したところ、常温まで冷却されており、熱処理から常温までの冷却時間は5分以下であった。
組成式LaxSr1-xCoO3(x=0.6)で示されるペロブスカイト型複合酸化物(LSC)を得るために、ペロブスカイト型複合酸化物の原料として、金属ランタン濃度14.8質量%の硝酸ランタン(La(NO3)3)水溶液275gと、硝酸ストロンチウム(Sr(NO3)2)粉末42gと、硝酸コバルト六水和物(Co(NO3)2・6H2O)粉末135gとを混合して得られた硝酸塩の混合溶液を使用した以外は、実施例2と同様の方法により、ペロブスカイト型複合酸化物粉末を得た。なお、焼成サヤを取り出してから5分経過後の(熱処理後の)粉末の温度を測定したところ、常温まで冷却されており、熱処理から常温までの冷却時間は5分以下であった。
組成式LaxSr1-xMnO3(x=0.8)で示されるペロブスカイト型複合酸化物(LSM)を得るために、ペロブスカイト型複合酸化物の原料として、金属ランタン濃度14.8質量%の硝酸ランタン(La(NO3)3)水溶液298gと、硝酸ストロンチウム(Sr(NO3)2)粉末17gと、金属マンガン濃度15.4質量%の硝酸マンガン(Mn(NO3)2)水溶液143gとを混合して得られた硝酸塩の混合溶液を使用した以外は、実施例2と同様の方法により、ペロブスカイト型複合酸化物粉末を得た。なお、焼成サヤを取り出してから5分経過後の(熱処理後の)粉末の温度を測定したところ、常温まで冷却されており、熱処理から常温までの冷却時間は5分以下であった。
組成式LaxNiyFe1-yO3(x=1.0、y=0.6)で示されるペロブスカイト型複合酸化物(LNF)を得るために、ペロブスカイト型複合酸化物の原料として、酸化ランタン(La2O3)粉末3596gと、酸化ニッケル(NiO)粉末982gと、酸化鉄(Fe2O3)粉末699gとを使用した以外は、実施例1と同様の方法により、ペロブスカイト型複合酸化物粉末を得た。なお、焼成サヤを取り出してから5分経過後の(熱処理後の)粉末の温度を測定したところ、常温まで冷却されており、熱処理から常温までの冷却時間は5分以下であった。
組成式LaxSryCa1-xMnwO3(x=0.49、y=0.24、w=1.03)で示されるペロブスカイト型複合酸化物(LSCM)を得るために、ペロブスカイト型複合酸化物の原料として、酸化ランタン(La2O3)粉末1976gと、炭酸ストロンチウム(SrCO3)粉末888gと、炭酸カルシウム(CaCO3)粉末605gと、炭酸マンガン(MnCO3)粉末2942gとを使用し、焼成温度を1150℃とした以外は、実施例1と同様の方法により、ペロブスカイト型複合酸化物粉末を得た。なお、焼成サヤを取り出してから5分経過後の(熱処理後の)粉末の温度を測定したところ、常温まで冷却されており、熱処理から常温までの冷却時間は5分以下であった。
熱処理温度を1000℃とした以外は、実施例7と同様の方法により、ペロブスカイト型複合酸化物粉末を得た。なお、焼成サヤを取り出してから5分経過後の(熱処理後の)粉末の温度を測定したところ、常温まで冷却されており、熱処理から常温までの冷却時間は5分以下であった。
熱処理温度を300℃とした以外は、実施例7と同様の方法により、ペロブスカイト型複合酸化物粉末を得た。なお、焼成サヤを取り出してから5分経過後の(熱処理後の)粉末の温度を測定したところ、常温まで冷却されており、熱処理から常温までの冷却時間は5分以下であった。
熱処理を行わなかった以外は、実施例2と同様の方法により、ペロブスカイト型複合酸化物粉末を得た。
熱処理を行わなかった以外は、実施例7と同様の方法により、ペロブスカイト型複合酸化物粉末を得た。
Claims (4)
- LaSrCoFeO 3 、LaSrCoO 3 、LaSrMnO 3 、LaNiFeO 3 またはLaSrCaMnO 3 で示されるペロブスカイト型複合酸化物であって、単位表面積当たりの炭酸ガス吸着量が8μmol/m2以上であることを特徴とする、ペロブスカイト型複合酸化物粉末。
- 前記単位表面積当たりの炭酸ガス吸着量が100μmol/m2以下であることを特徴とする、請求項1に記載のペロブスカイト型複合酸化物粉末。
- 前記ペロブスカイト型複合酸化物のマイクロトラック粒度分布測定装置により測定された体積基準の累積50%粒径D50が0.1~5μmであることを特徴とする、請求項1または2に記載のペロブスカイト型複合酸化物粉末。
- 前記ペロブスカイト型複合酸化物のBET比表面積が0.5~20m2/gであることを特徴とする、請求項1乃至3のいずれかに記載のペロブスカイト型複合酸化物粉末。