JP7055171B2 - オーステナイト系マトリックスを有するtwip鋼板 - Google Patents
オーステナイト系マトリックスを有するtwip鋼板 Download PDFInfo
- Publication number
- JP7055171B2 JP7055171B2 JP2020116150A JP2020116150A JP7055171B2 JP 7055171 B2 JP7055171 B2 JP 7055171B2 JP 2020116150 A JP2020116150 A JP 2020116150A JP 2020116150 A JP2020116150 A JP 2020116150A JP 7055171 B2 JP7055171 B2 JP 7055171B2
- Authority
- JP
- Japan
- Prior art keywords
- steel sheet
- less
- sheet according
- steel
- amount
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
・鋼の組成におけるすべての百分率「%」は、重量によって規定されている
・UTS:極限引張強度(MPa)及び
・TE:全伸び(%)。
0.71%<C<1.20%、
13.0%≦Mn<25.0%、
S≦0.030%、
P≦0.080%、
N≦0.10%以下、
0.1%≦Si≦3.0%、
0.1%≦V≦2.50%以下、
及び純粋に任意選択的に、
Cu≦5.0%、
Al≦4.0%、
Nb≦0.50%、
B≦0.0050%、
Cr≦1.0%、
Mo≦0.40%、
Ni≦1.0%、
Ti≦0.50%、
0.06≦Sn≦0.2%
のような元素1種以上を含み、組成の残部が、鉄及び製錬に起因する不可避的不純物から構成される、
オーステナイト系マトリックスを有する冷間圧延及び回復されたTWIP鋼板に関する。
A.上記組成を有するスラブの供給ステップ、
B.このようなスラブを再加熱し、熱間圧延するステップ、
C.巻取りステップ、
D.第1の冷間圧延ステップ、
E.再結晶焼鈍ステップ、
F.第2の冷間圧延ステップ及び
G.回復熱処理ステップ
を含む。
Claims (12)
- 重量により、
0.71%<C<1.2%、
13.0%≦Mn<25.0%、
S≦0.030%、
P≦0.080%、
N≦0.1%以下、
0.1%≦Si≦3.0%、
0.1%≦V≦2.50%以下、
及び純粋に任意選択的に、
Cu≦5.0%、
Al≦4.0%、
Nb≦0.5%、
B≦0.005%、
Cr≦1.0%、
Mo≦0.40%、
Ni≦1.0%、
Ti≦0.5%、
0.06≦Sn≦0.2%
のような元素1種以上
を含み、
組成の残部が、鉄及び製錬に起因する不可避的不純物から構成される、
オーステナイト系マトリックスを有し、極限引張強度(UTS)は少なくとも1515.5MPaであり、全伸び(TE)は少なくとも9.2%であり、及び鋼の粒子の平均粒径は最大5μmである、自動車製造用の冷間圧延及び回復されたTWIP鋼板。 - Cの量が、0.71~1.1%の間である、請求項1に記載の鋼板。
- Cの量が、0.80~1.0%の間である、請求項2に記載の鋼板。
- Cの量が、0.9~1.0%の間である、請求項3に記載の鋼板。
- Cuの量が、2.0%未満である、請求項1から4のいずれか一項に記載の鋼板。
- Siの量が、0.6%以下である、請求項1から5のいずれか一項に記載の鋼板。
- Al含量が、2%以下である、請求項1から6のいずれか一項に記載の鋼板。
- Vの量が、0.1~1.0%の間である、請求項1から7のいずれか一項に記載の鋼板。
- 鋼板が、金属コーティングによって被覆されている、請求項1から8のいずれか一項に記載の鋼板。
- アルミニウム系コーティング又は亜鉛系コーティングによって被覆されている、請求項1から9のいずれか一項に記載の鋼板。
- アルミニウム系コーティングが、15%未満のSi、5.0%未満のFe、任意選択的に0.1~8.0%のMg、及び任意選択的に0.1~30.0%のZnを含み、残部が、Alである、請求項10に記載の鋼板。
- 亜鉛系コーティングが、0.01~8.0%のAl、任意選択的に0.2~8.0%のMgを含み、残部が、Znである、請求項10に記載の鋼板。