JP6978185B2 - 合わせガラス用中間膜及び合わせガラス - Google Patents
合わせガラス用中間膜及び合わせガラス Download PDFInfo
- Publication number
- JP6978185B2 JP6978185B2 JP2015553974A JP2015553974A JP6978185B2 JP 6978185 B2 JP6978185 B2 JP 6978185B2 JP 2015553974 A JP2015553974 A JP 2015553974A JP 2015553974 A JP2015553974 A JP 2015553974A JP 6978185 B2 JP6978185 B2 JP 6978185B2
- Authority
- JP
- Japan
- Prior art keywords
- laminated glass
- light emitting
- interlayer film
- emitting layer
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
HUDの機構としては、これまで種々の形態のものが開発されている。例えば、HUD表示部がフロントガラス表面にはなく、コントロールユニットから送信される速度情報等をインストゥルメンタル・パネルの表示ユニットからフロントガラスに反射させることにより運転者にフロントガラスと同じ位置(すなわち、同一視野内)で視認させる形態のものがある。このような反射型のHUDには、焦点距離を適切に調節することで、表示される情報が遠方に存在するように視認され、運転者の眼の焦点を変更する必要が無く安全であるという利点がある。
しかしながら、実際に発光材料を配合した断面形状が楔形の合わせガラス用中間膜を用いると、発光材料により表示される画像の輝度が合わせガラスの部位によって異なってしまうという新たな問題が生じた。
以下に本発明を詳述する。
本発明者らは、更に鋭意検討の結果、発光材料を含む発光層の厚みを最大厚さと最小厚さの差を100μm以下として蛍光材料の面密度の変動を一定以下にするとともに、樹脂層を積層した多層構造として、合わせガラス用中間膜全体としての断面形状を楔形とすることにより、二重像の発生を防止しながら、一定範囲の輝度で画像を表示することができる合わせガラスを得ることができることを見出し、本発明を完成した。
本発明の合わせガラス用中間膜は、断面形状が楔形である。合わせガラスの取り付け角度に応じて、楔形の楔角θを調整することにより、二重像の発生を防止した画像表示が可能となる。二重像をより一層抑制する観点から、上記楔角θの好ましい下限は0.1mrad、より好ましい下限は0.2mrad、更に好ましい下限は0.3mradであり、好ましい上限は1mrad、より好ましい上限は0.9mradである。
なお、例えば押出機を用いて樹脂組成物を押出し成形する方法により断面形状が楔形の合わせガラス用中間膜を製造した場合、薄い側の一方の端部からわずかに内側の領域(具体的には、一端と他端との間の距離をXとしたときに、薄い側の一端から内側に向かって0X〜0.2Xの距離の領域)に最小厚みを有し、厚い側の一方の端部からわずかに内側の領域(具体的には、一端と他端との間の距離をXとしたときに、厚い側の一端から内側に向かって0X〜0.2Xの距離の領域)に最大厚みを有する形状となることがある。本明細書においては、このような形状も楔形に含まれる。
上記形状補助層は、上記発光層の一方の面にのみ積層されていてもよく、両方の面に積層されていてもよい。更に、複数の形状補助層を積層してもよい。
上記発光層の最大厚さと最小厚さの差は100μm以下である。これにより、一定範囲の輝度で画像を表示することができる。上記発光層の最大厚さと最小厚さの差は95μm以下であることが好ましく、90μm以下であることがより好ましく、60μm以下であることが更に好ましく、50μm以下であることが特に好ましい。上記発光層の最大厚さと最小厚さの差の下限は特に限定されないが、0であることが好ましい。
上記形状補助層は、断面形状が楔形、三角形、又は、台形であることが好ましい。断面形状が楔形、三角形、又は、台形の形状補助層を積層することにより、合わせガラス用中間膜全体としての断面形状を楔形となるように調整することができる。なお、上記形状補助層としての役割を果たせるのであれば、上記形状補助層は、例えば、五角形、六角形、楕円形等の形状をしていてもよい。また、複数の形状補助層を組み合わせて、合わせガラス用中間膜全体としての断面形状を整えてもよい。この場合、全ての形状補助層の断面形状が同一である必要はなく、異なっていてもよい。
なお、上記形状補助層の厚みの下限は、形状補助層の最小厚さの部分の厚みを意味し、上記形状補助層の厚みの上限は、形状補助層の最大厚さの部分の厚みを意味する。また、複数の形状補助層を組み合わせて用いる場合は、その合計の厚みを意味する。
なお、上記合わせガラス用中間膜全体の厚みの下限は、合わせガラス用中間膜全体の最小厚さの部分の厚みを意味し、上記合わせガラス用中間膜全体の厚みの上限は、合わせガラス用中間膜全体の最大厚さの部分の厚みを意味する。
合わせガラス用中間膜1は、発光材料を含有する発光層11の一方の面に形状補助層12が積層された2層構造を有する。
ここで発光層11は矩形であるのに対して、形状補助層12の形状を楔形、三角形、又は、台形とすることにより、合わせガラス用中間膜1全体として楔角θが0.1〜1mradである楔形となっている。
合わせガラス用中間膜2は、発光材料を含有する発光層21の両面に形状補助層22と形状補助層23とが積層された3層構造を有する。
ここで発光層21と形状補助層23とが厚みが一定の矩形であるのに対して、形状補助層22の形状を楔形、三角形、又は、台形とすることにより、合わせガラス用中間膜2全体として楔角θが0.1〜1mradである楔形となっている。
合わせガラス用中間膜3は、発光材料を含有する発光層31の両面に形状補助層32と形状補助層33とが積層された3層構造を有する。
ここで発光層31は最大厚さと最小厚さの差が100μm以下の緩やかな楔形であり、楔形の形状補助層32、33を積層することにより、合わせガラス用中間膜3全体として楔角θが0.1〜1mradである楔形となっている。
上記発光層は、熱可塑性樹脂と可塑剤と発光材料とを含有する。発光材料を含有する発光層を有することにより、本発明の合わせガラス用中間膜は、光線を照射することにより、コントラストが高い画像を表示することができる。
上記ポリビニルアセタール樹脂は、水酸基量の好ましい下限が10モル%、好ましい上限が32モル%である。上記発光層に含まれるポリビニルアセタール樹脂の水酸基量がこの範囲内であると、発光層の成形が容易であり、かつ、得られる合わせガラス用中間膜の耐貫通性が高くなる。上記ポリビニルアセタール樹脂の水酸基量のより好ましい下限は15モル%、より好ましい上限は30モル%、更に好ましい下限は18モル%、更に好ましい上限は28モル%、特に好ましい下限は20モル%、特に好ましい上限は25モル%である。
なお、上記アセタール化度及び水酸基量は、例えば、JIS K6728「ポリビニルブチラール試験方法」に準拠して測定できる。
上記ポリビニルアルコールは、通常、ポリ酢酸ビニルを鹸化することにより得られ、鹸化度70〜99.8モル%のポリビニルアルコールが一般的に用いられる。上記ポリビニルアルコールの鹸化度は、80〜99.8モル%であることが好ましい。
上記ポリビニルアルコールの重合度の好ましい下限は500、好ましい上限は4000である。上記ポリビニルアルコールの重合度が500以上であると、得られる合わせガラスの耐貫通性が高くなる。上記ポリビニルアルコールの重合度が4000以下であると、合わせガラス用中間膜の成形が容易になる。上記ポリビニルアルコールの重合度のより好ましい下限は1000、より好ましい上限は3600である。
上記発光粒子及び上記発光顔料は、例えば、Y2O2S:Eu、BaMg2Al16O27:Eu,Mn、(SrCaBaMg)5(PO4)3Cl:Eu、BaMg2Al16O27:Eu、BaMg2Al16O27:Eu,Mn、Sr5(PO4)3Cl:Eu、LaPO4:Ce,Tb、MgAl11O19:Ce,Tb、Y2O3:Eu、Y(PV)O4:Eu、3.5MgO・0.5MgF2・GeO2:Mn、Ca10(PO4)6FCl:Sb,Mn、Sr10(PO4)6FCl:Sb,Mn、(SrMg)2P2O7:Eu、Sr2P2O7:Eu、CaWO4、CaWO4:Pb、MgWO4、(BaCa)5(PO4)3Cl:Eu、Sr4Al14O25:Eu、Zn2SiO4:Mn等で示される蛍光体やそれらからなる複合体や、ZnS粒子、GaSe粒子、SiC粒子、CdTe粒子等の粒子型等が挙げられる。
上記R1の有機基は炭化水素基であることが好ましく、炭素数が1〜10の炭化水素基であることがより好ましく、炭素数が1〜5の炭化水素基であることが更に好ましく、炭素数が1〜3の炭化水素基であることが特に好ましい。上記炭化水素基の炭素数が10以下であると、上記テレフタル酸エステル構造を有する発光材料を合わせガラス用中間膜に容易に分散させることができる。上記炭化水素基はアルキル基であることが好ましい。
上記R2の有機基は炭化水素基であることが好ましく、炭素数が1〜10の炭化水素基であることがより好ましく、炭素数が1〜5の炭化水素基であることが更に好ましく、炭素数が1〜3の炭化水素基であることが特に好ましい。上記炭化水素基の炭素数が上記上限以下であると、上記テレフタル酸エステル構造を有する発光材料を合わせガラス用中間膜に容易に分散させることができる。上記炭化水素基はアルキル基であることが好ましい。上記一般式(2)中、NR3R4はアミノ基である。R3及びR4は、水素原子であることが好ましい。上記一般式(2)で表される構造を有する化合物のベンゼン環の水素原子のうち、一つの水素原子が上記アミノ基であってもよく、二つの水素原子が上記アミノであってもよく、三つの水素原子が上記アミノ基であってもよく、四つの水素原子が上記アミノ基であってもよい。
上記分散剤は、例えば、直鎖アルキルベンゼンスルホン酸塩等のスルホン酸構造を有する化合物や、ジエステル化合物、リシノール酸アルキルエステル、フタル酸エステル、アジピン酸エステル、セバシン酸エステル、リン酸エステル等のエステル構造を有する化合物や、ポリオキシエチレングリコール、ポリオキシプロピレングリコールやアルキルフェニル−ポリオキシエチレン−エーテル等のエーテル構造を有する化合物や、ポリカルボン酸等のカルボン酸構造を有する化合物や、ラウリルアミン、ジメチルラウリルアミン、オレイルプロピレンジアミン、ポリオキシエチレンの2級アミン、ポリオキシエチレンの3級アミン、ポリオキシエチレンのジアミン等のアミン構造を有する化合物や、ポリアルキレンポリアミンアルキレンオキシド等のポリアミン構造を有する化合物や、オレイン酸ジエタノールアミド、アルカノール脂肪酸アミド等のアミド構造を有する化合物や、ポリビニルピロリドン、ポリエステル酸アマイドアミン塩等の高分子量型アミド構造を有する化合物等や、トリエトキシプロピルイソシアネートシラン、トリエトキシブチルシラン等のアルキル基を有するシラン構造を有する化合物や、トリエトキシプロピルアクリロキシシラン等のアクリロキシ基を有するシラン構造を有する化合物や、トリエトキシプロピルビニルシラン等のビニル基を有するシラン構造を有する化合物や、エポキシ基やリン酸基、カルボキシル基、メルカプト基等の側鎖を有する高分子量体であるポリシロキサン構造を有する化合物や、イソシアネート等のイソシアネート基を有する化合物や、イソシアヌレート等のイソシアヌレート基を有する化合物等の従来公知の分散剤を用いることができる。また、ポリオキシエチレンアルキルエーテルリン酸(塩)や高分子ポリカルボン酸、縮合リシノール酸エステル等の高分子量分散剤を用いてもよい。なお、高分子量分散剤とは、その分子量が1万以上である分散剤と定義される。
上記紫外線吸収剤は、例えば、マロン酸エステル構造を有する化合物、シュウ酸アニリド構造を有する化合物、ベンゾトリアゾール構造を有する化合物、ベンゾフェノン構造を有する化合物、トリアジン構造を有する化合物、ベンゾエート構造を有する化合物、ヒンダードアミン構造を有する化合物等の紫外線吸収剤が挙げられる。
上記酸化防止剤は特に限定されず、フェノール構造を有する酸化防止剤、硫黄を含む酸化防止剤、リンを含む酸化防止剤等が挙げられる。
上記フェノール構造を有する酸化防止剤はフェノール骨格を有する酸化防止剤である。上記フェノール構造を有する酸化防止剤としては、例えば、2,6−ジ−t−ブチル−p−クレゾール(BHT)、ブチル化ヒドロキシアニソール(BHA)、2,6−ジ−t−ブチル−4−エチルフェノール、ステアリル−β−(3,5−ジ−t−ブチル−4−ヒドロキシフェニル)プロピオネート、2,2’−メチレンビス−(4−メチル−6−ブチルフェノール)、2,2’−メチレンビス−(4−エチル−6−t−ブチルフェノール)、4,4’−ブチリデン−ビス−(3−メチル−6−t−ブチルフェノール)、1,1,3−トリス−(2−メチル−ヒドロキシ−5−t−ブチルフェニル)ブタン、テトラキス[メチレン−3−(3’,5’−ブチル−4−ヒドロキシフェニル)プロピオネート]メタン、1,3,3−トリス−(2−メチル−4−ヒドロキシ−5−t−ブチルフェノール)ブタン、1,3,5−トリメチル−2,4,6−トリス(3,5−ジ−t−ブチル−4−ヒドロキシベンジル)ベンゼン、ビス(3,3’−t−ブチルフェノール)ブチリックアッシドグリコールエステル、ペンタエリスリトールテトラキス[3−(3,5−ジ−tert−ブチル−4−ヒドロキシフェニル)プロピオナート]等が挙げられる。上記酸化防止剤は、単独で用いてもよいし、2種以上を併用してもよい。
上記熱線吸収剤は、赤外線を遮蔽する性能を有すれば特に限定されないが、錫ドープ酸化インジウム(ITO)粒子、アンチモンドープ酸化錫(ATO)粒子、アルミニウムドープ酸化亜鉛(AZO)粒子、インジウムドープ酸化亜鉛(IZO)粒子、錫ドープ酸化亜鉛粒子、珪素ドープ酸化亜鉛粒子、6ホウ化ランタン粒子及び6ホウ化セリウム粒子からなる群より選択される少なくとも1種が好適である。
上記マグネシウム元素は、例えば、金属マグネシウムやマグネシウム塩として、上記発光層に含まれていてもよい。
なお、変色とは、合わせガラス用中間膜が2枚のクリアガラス(厚み2.5mm)の間に積層された合わせガラスのYI値が20を超えることを意味する。YI値は、分光光度計(日立ハイテクノロジーズ社製、「U−4100」)を使用して、JIS Z 8722に準拠して、測定することができる。上記YI値は、20以下であることが好ましく、15以下であることがより好ましく、10以下であることが更に好ましい。また、上記YI値は、0以上であることが好ましい。
上記接着力調整剤は特に限定されず、金属塩であることが好ましく、アルカリ金属塩、アルカリ土類金属塩及びマグネシウム塩からなる群から選択された少なくとも1種の金属塩であることが好ましい。上記金属塩は、カリウム及びマグネシウムの内の少なくとも1種の金属を含むことが好ましい。上記金属塩は、炭素数1〜16の有機酸のアルカリ金属塩、炭素数1〜16の有機酸のアルカリ土類金属塩又は炭素数1〜16の有機酸のマグネシウム塩であることがより好ましく、炭素数2〜16の有機酸のアルカリ金属塩、炭素数2〜16の有機酸のアルカリ土類金属塩又は炭素数2〜16のマグネシウム塩であることが更に好ましく、炭素数2〜16のカルボン酸のマグネシウム塩又は炭素数2〜16のカルボン酸のカリウム塩であることが特に好ましい。上記炭素数2〜16のカルボン酸のマグネシウム塩及び上記炭素数2〜16のカルボン酸のカリウム塩としては特に限定されないが、例えば、酢酸マグネシウム、酢酸カリウム、プロピオン酸マグネシウム、プロピオン酸カリウム、2−エチルブタン酸マグネシウム、2−エチルブタン酸カリウム、2−エチルヘキサン酸マグネシウム、2−エチルヘキサン酸カリウム等が挙げられる。上記有機酸の炭素数の好ましい下限は1、好ましい上限は10、より好ましい下限は2、より好ましい上限は8である。
合わせガラス用中間膜の変色をより一層防止できることから、上記形状補助層に含まれるマグネシウム元素の濃度は150ppm以下であることが好ましく、100ppm以下であることがより好ましく、50ppm以下であることが更に好ましく、30ppm以下であることが特に好ましい。上記形状補助層に含まれるマグネシウム濃度は0ppmであってもよく、0ppmを超えてもよい。
また、本発明の合わせガラス用中間膜の一部の領域に着色帯を設ける場合には、上記形状補助層の一部に青色顔料、青色染料、緑色顔料、緑色染料等の着色剤を配合してもよい。
発光材料が発光層から形状補助層へ移行することをより一層防止できることから、上記発光層に含まれるポリビニルアセタール樹脂の水酸基量と、上記形状補助層に含まれるポリビニルアセタール樹脂の水酸基量との差は、6.5モル%未満であることが好ましい。上記水酸基量の差は、6.4モル%以下であることがより好ましく、6.2モル%以下であることが更に好ましく、6.0モル%以下であることが特に好ましく、5.8モル%以下であることが最も好ましい。
また、上記水酸基量の差は、1モル%以上であることが好ましく、2モル%以上であることがより好ましく、3モル%以上であることが更に好ましい。
例えば、上記発光層に含まれる可塑剤の含有量を、上記形状補助層に含まれる可塑剤の含有量よりも多くすることにより、本発明の合わせガラス用中間膜に遮音性能を付与することができる。具体的には、上記可塑剤の含有量の差を、好ましくは5重量部以上、より好ましくは10重量部以上、更に好ましくは15重量部以上とすることにより、高い遮音性を付与することができる。上記可塑剤の含有量の差は、50重量部以下であることが好ましく、40重量部以下であることがより好ましく、35重量部以下であることが更に好ましい。
遮音性をより一層高める観点から、上記発光層に含まれるポリビニルアセタール樹脂の水酸基量は、上記形状補助層に含まれるポリビニルアセタール樹脂の水酸基量よりも低いことが好ましい。具体的には、上記水酸基量の差を、1モル%以上とすることが好ましく、3モル%以上とすることがより好ましく、5モル%以上とすることが更に好ましい。
遮音性をより一層高める観点から、上記発光層に含まれるポリビニルアセタール樹脂のアセタール化度は、上記形状補助層に含まれるポリビニルアセタール樹脂のアセタール化度よりも高いことが好ましい。
上記特定の波長の光線を照射するための装置として、例えば、スポット光源(浜松ホトニクス社製、「LC−8」)、キセノン・フラッシュランプ(ヘレウス社製、「CWランプ」)、ブラックライト(井内盛栄堂社製、「キャリーハンド」)等が挙げられる。
上記ガラス板は、一般に使用されている透明板ガラスを使用することができる。例えば、フロート板ガラス、磨き板ガラス、型板ガラス、線入り板ガラス、着色された板ガラス、熱線吸収ガラス、熱線反射ガラス、グリーンガラス等の無機ガラスが挙げられる。また、ガラスの表面に紫外線遮蔽コート層が形成された紫外線遮蔽ガラスも用いることができるが、特定の波長の光線を照射する側とは反対のガラス板として用いることが好ましい。更に、上記ガラス板としてポリエチレンテレフタレート、ポリカーボネート、ポリアクリレート等の有機プラスチックス板を用いることもできる。
上記ガラス板として、2種類以上のガラス板を用いてもよい。例えば、透明フロート板ガラスと、グリーンガラスのような着色されたガラス板との間に、本発明の合わせガラス用中間膜を積層した合わせガラスが挙げられる。また、上記ガラス板として、2種以上の厚さの異なるガラス板を用いてもよい。
(1)発光層用樹脂組成物の調製
トリエチレングリコールジ−2−エチルヘキサノエート(3GO)60重量部に、発光材料として上記一般式(1)で表される構造を有する化合物であるジエチル−2,5−ジヒドロキシテレフタレート(Aldrich社製、「2,5−ジヒドロキシテレフタル酸ジエチル」)1.5重量部を加え、発光性の可塑剤溶液を調製した。得られた可塑剤溶液の全量と、重合度が2300であるポリビニルアルコールをn−ブチルアルデヒドでアセタール化することにより得られたポリビニルブチラール(アセチル基量12.5モル%、水酸基量23.6モル%、ブチラール化度63.9モル%)100重量部とをミキシングロールで充分に混練することにより、発光層用樹脂組成物を調製した。
トリエチレングリコールジ−2−エチルヘキサノエート(3GO)40重量部に、接着力調整剤として酢酸マグネシウムを加え、可塑剤溶液を調製した。得られた可塑剤溶液の全量と、重合度が1700であるポリビニルアルコールをn−ブチルアルデヒドでアセタール化することにより得られたポリビニルブチラール(アセチル基量0.9モル%、水酸基量30.0モル%、ブチラール化度69.1モル%)100重量部とをミキシングロールで充分に混練することにより、形状補助層用樹脂組成物を調製した。
なお、形状補助層中のマグネシウム元素の濃度が70ppmとなるように、酢酸マグネシウムをトリエチレングリコールジ−2−エチルヘキサノエート(3GO)に添加した。
得られた発光層用樹脂組成物及び形状補助層用樹脂組成物を、押出機を用いて共押出することにより、形状補助層、発光層及び形状補助層がこの順に積層した、図3に記載された3層構造の合わせガラス用中間膜を得た。
なお、得られた中間膜の押出方向に対する垂直方向における一端と他端の最短距離を測定すると1mであった。
また、得られた合わせガラス用中間膜における発光層は最小厚み90μm、最大厚み140μmの楔形の断面形状を有し、合わせガラス用中間膜全体では最小厚み800μm、最大厚み1200μmの楔形の断面形状を有していた。なお、合わせガラス用中間膜の一端が最小厚みを有し、他端が最大厚みを有しており、光学顕微鏡で観察し、最小厚み及び最大厚みを測定した。
得られた中間膜を、2枚の透明なフロートガラス(縦1000mm×横300mm×厚さ2.5mm)で挟み込んで、積層体を得た。230℃の加熱ロールを用いて、得られた積層体を仮圧着した。その後、仮圧着された積層体を、加熱ロール法により、オートクレーブを用いて、135℃、圧力1.2MPaの条件で20分間圧着し、合わせガラス(縦1000mm×横300mm)を作製した。
一端と他端の最短距離上における、一端から10cmの点を中心となるように、縦10cm×横10cmの中間膜(薄い部分)を切り抜いた。同様に、一端と他端の最短距離上における、他端から10cmの点を中心となるように、縦10cm×横10cmの中間膜(厚い部分)を切り抜いた。
得られた中間膜(薄い部分)及び中間膜(厚い部分)それぞれを、2枚の透明なフロートガラス(縦100mm×横100mm×厚さ2.5mm)で挟み込んで、積層体を得た。230℃の加熱ロールを用いて、得られた積層体を仮圧着した。その後、仮圧着された積層体を、加熱ロール法により、オートクレーブを用いて、135℃、圧力1.2MPaの条件で20分間圧着し、輝度測定用合わせガラス(縦100mm×横100mm)を作製した。
発光材料の種類、発光層の厚み方向の最大厚み及び最小厚みを表1に示すようにしたこと以外は、実施例1と同様にして、合わせガラス用中間膜及び合わせガラスを得た。
発光材料の種類、発光層の厚み方向の最大厚み及び最小厚みを表1に示すようにし、形状補助層を積層しなかったこと以外は、実施例1と同様にして、合わせガラス用中間膜及び合わせガラスを得た。
発光層の厚み方向の最大厚み及び最小厚み、並びに、中間膜の最小厚み、最大厚み及び楔角を表2に示すように変更したこと以外は、実施例1と同様にして、合わせガラス用中間膜及び合わせガラスを得た。
用いるポリビニルブチラールの組成、可塑剤の含有量、発光層の厚み方向の最大厚み及び最小厚み、並びに、中間膜の最小厚み、最大厚み及び楔角を表3に示すように変更したこと以外は、実施例1と同様にして、合わせガラス用中間膜及び合わせガラスを得た。
(1)発光層用樹脂組成物の調製
トリエチレングリコールジ−2−エチルヘキサノエート(3GO)40重量部に、発光材料として上記一般式(1)で表される構造を有する化合物であるジエチル−2,5−ジヒドロキシテレフタレート(Aldrich社製、「2,5−ジヒドロキシテレフタル酸ジエチル」)1.5重量部を加え、発光性の可塑剤溶液を調製した。得られた可塑剤溶液の全量と、重合度が1700であるポリビニルアルコールをn−ブチルアルデヒドでアセタール化することにより得られたポリビニルブチラール(アセチル基量0.9モル%、水酸基量30.0モル%、ブチラール化度69.1モル%)100重量部とをミキシングロールで充分に混練することにより、発光層用樹脂組成物を調製した。
トリエチレングリコールジ−2−エチルヘキサノエート(3GO)40重量部に、接着力調整剤として酢酸マグネシウムを加え、可塑剤溶液を調製した。得られた可塑剤溶液の全量と、重合度が1700であるポリビニルアルコールをn−ブチルアルデヒドでアセタール化することにより得られたポリビニルブチラール(アセチル基量0.9モル%、水酸基量30.0モル%、ブチラール化度69.1モル%)100重量部とをミキシングロールで充分に混練することにより、第1の樹脂層及び第2の樹脂層用樹脂組成物を調製した。
なお、第1の樹脂層及び第2の樹脂層中のマグネシウム元素の濃度が70ppmとなるように、酢酸マグネシウムをトリエチレングリコールジ−2−エチルヘキサノエート(3GO)に添加した。
トリエチレングリコールジ−2−エチルヘキサノエート(3GO)60重量部と、重合度が2300であるポリビニルアルコールをn−ブチルアルデヒドでアセタール化することにより得られたポリビニルブチラール(アセチル基量12.5モル%、水酸基量23.6モル%、ブチラール化度63.9モル%)100重量部とをミキシングロールで充分に混練することにより、遮音層用樹脂組成物を調製した。
第1の樹脂層及び第2の樹脂層用樹脂組成物と、遮音層用樹脂組成物とを、共押出機を用いて共押出することにより、第1の樹脂層、遮音層及び第2の樹脂層がこの順に積層した、3層構造の積層体を形状補助層として得た。
得られた発光層用樹脂組成物を、単層で押し出すことにより発光層を得た。形状補助層及び発光層を、第1の樹脂層、遮音層、第2の樹脂層、発光層の順に積層することで4層構造の合わせガラス用中間膜を得た。
なお、得られた中間膜の押出方向に対する垂直方向における一端と他端の最短距離を測定すると1mであった。
また、得られた合わせガラス用中間膜における発光層は最小厚み90μm、最大厚み140μmの楔形の断面形状を有し、合わせガラス用中間膜全体では最小厚み800μm、最大厚み1200μmの楔形の断面形状を有していた。更に、得られた合わせガラス用中間膜における第1の樹脂層は最小厚み305μm、最大厚み480μmの楔形の断面形状を有し、遮音層は平均厚み100μmの矩形の断面形状を有し、第2の樹脂層は最小厚み305μm、最大厚み480μmの楔形の断面形状を有していた。なお、合わせガラス用中間膜の一端が最小厚みを有し、他端が最大厚みを有しており、光学顕微鏡で観察し、最小厚み及び最大厚みを測定した。
得られた中間膜を、2枚の透明なフロートガラス(縦1000mm×横300mm×厚さ2.5mm)で挟み込んで、積層体を得た。230℃の加熱ロールを用いて、得られた積層体を仮圧着した。その後、仮圧着された積層体を、加熱ロール法により、オートクレーブを用いて、135℃、圧力1.2MPaの条件で20分間圧着し、合わせガラス(縦1000mm×横300mm)を作製した。
一端と他端の最短距離上における、一端から10cmの点を中心となるように、縦10cm×横10cmの中間膜(薄い部分)を切り抜いた。同様に、一端と他端の最短距離上における、他端から10cmの点を中心となるように、縦10cm×横10cmの中間膜(厚い部分)を切り抜いた。
得られた中間膜(薄い部分)及び中間膜(厚い部分)それぞれを、2枚の透明なフロートガラス(縦100mm×横100mm×厚さ2.5mm)で挟み込んで、積層体を得た。230℃の加熱ロールを用いて、得られた積層体を仮圧着した。その後、仮圧着された積層体を、加熱ロール法により、オートクレーブを用いて、135℃、圧力1.2MPaの条件で20分間圧着し、輝度測定用合わせガラス(縦100mm×横100mm)を作製した。
発光層の最小厚み及び最大厚み、第1の樹脂層の最小厚み及び最大厚み、並びに、第2の樹脂層の最小厚み及び最大厚みを表4に示すように変更したこと以外は、実施例13と同様にして、合わせガラス用中間膜及び合わせガラスを得た。
実施例及び比較例で得られた合わせガラスについて、以下の方法で評価を行った。
結果を表1〜4に示した。
得られた合わせガラス(縦1000mm×横300mm)をフロントガラスの位置に設置した。合わせガラスの下方に設置した表示ユニットから表示情報を合わせガラスに反射させ、所定の位置で二重像の有無を目視で確認した。二重像が確認されない場合を「○」、二重像が確認される場合を「×」として評価した。
得られた輝度測定用合わせガラスを、暗室下にて、合わせガラスの面に対して垂直方向に10cm離れた位置に配置したHigh Powerキセノン光源(朝日分光社製、「REX−250」、照射波長405nm)から合わせガラスの全面へ光を照射し、光を照射した合わせガラスの面から45度の角度で、合わせガラス面からの最短距離として、35cm離れた位置に配置した輝度計(トプコンテクノハウス社製、「SR−3AR」)によって輝度を測定した。
中間膜(薄い部分)及び中間膜(厚い部分)における輝度の差の絶対値が200以下である場合を「○」、200を超える場合を「×」と評価した。
11 発光層
12 形状補助層
2 合わせガラス用中間膜
21 発光層
22 形状補助層
23 形状補助層
3 合わせガラス用中間膜
31 発光層
32 形状補助層
33 形状補助層
Claims (5)
- 熱可塑性樹脂と可塑剤と発光材料とを含有する発光層と、前記発光層の少なくとも一方の面に積層された、熱可塑性樹脂と可塑剤とを含有する樹脂層とを含む多層構造の合わせガラス用中間膜であって、
合わせガラス用中間膜の断面形状が楔形であり、前記発光層の最大厚さと最小厚さの差が100μm以下であり、
前記発光材料は、テレフタル酸エステル構造を有する発光材料である
ことを特徴とする合わせガラス用中間膜。 - 合わせガラス用中間膜の断面形状が、楔角θが0.1〜1mradである楔形であることを特徴とする請求項1記載の合わせガラス用中間膜。
- 発光層及び樹脂層に含まれる熱可塑性樹脂が、ポリビニルアセタール樹脂であることを特徴とする請求項1又は2記載の合わせガラス用中間膜。
- 発光層に含まれるポリビニルアセタール樹脂の水酸基量が、樹脂層に含まれるポリビニルアセタール樹脂の水酸基量よりも低いことを特徴とする請求項3記載の合わせガラス用中間膜。
- 請求項1、2、3又は4記載の合わせガラス用中間膜が、一対のガラス板の間に積層されていることを特徴とする合わせガラス。