JP6959809B2 - 流し込み施工用の不定形耐火物 - Google Patents
流し込み施工用の不定形耐火物 Download PDFInfo
- Publication number
- JP6959809B2 JP6959809B2 JP2017174234A JP2017174234A JP6959809B2 JP 6959809 B2 JP6959809 B2 JP 6959809B2 JP 2017174234 A JP2017174234 A JP 2017174234A JP 2017174234 A JP2017174234 A JP 2017174234A JP 6959809 B2 JP6959809 B2 JP 6959809B2
- Authority
- JP
- Japan
- Prior art keywords
- mass
- raw material
- less
- refractory
- content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
耐火原料100質量%に占める割合で、粒径1mm以上の炭化珪素原料を20質量%以上50質量%以下、粒径1μm以上10μm以下のアルミナ微粉を2質量%以上15質量%以下、粒径1μm未満のシリカ超微粉を1質量%以上8質量%以下、それぞれ含有し、
前記耐火原料100質量%に占める割合で、アルミナセメントの含有量は15質量%以下(0を含む。)、粒径1mm未満の炭化珪素原料の含有量は5質量%以下(0を含む。)である不定形耐火物。
各例の耐火原料中の粒径1mm未満の原料に所定量の水及び樹脂を添加して混練し、型枠に鋳込んで20×20×80mm形状の硬化体を作製した。そして、硬化体を110℃で24hの熱処理により乾燥したものを試験片として用いた。測定の雰囲気は大気中、温度は室温から1500℃までを測定した。測定方法は、JIS R 2207−1に準拠した。表1及び表2では、1000℃での熱膨張率が0.2%以下の場合を○(良)、0.2%超の場合を×(不良)と表記した。
各例に所定量の水を加えて混練し、型枠に鋳込んで114×65×230mm形状の硬化体を作製した。そして、硬化体を養生し、110℃で24hの熱処理により乾燥し、その後、1400℃で5hの熱処理により焼成したものを試験片として用いた。測定はJIS R 2616に準拠した熱線法で行った。測定温度は、室温、1200℃の2点とした。
各例に所定量の水を加えて混練し、所定形状の型枠に鋳込んで所定形状の硬化体を作製した。そして、硬化体を養生した後、110℃で24hの熱処理により乾燥したものを試験片として用いた。試験片に対して転炉スラグを用いて1550℃で3hのスラグ回転浸食試験を実施し、溶損量と浸潤量を測定した。表1及び表2では、溶損浸潤量(溶損量と浸潤量の合計)が5mm以下の場合を◎(優)、5mmより大きく7mm以下の場合を○(良)、7mmより大きく11mm以下の場合を△(可)、11mmより大きい場合を×(不良)と表記した。なお、溶損浸潤量は耐食性の指標であり、溶損浸潤量が少ないほど耐食性は高いことを示す。
各例に所定量の水を加えて混練し、型枠に鋳込んで230×114×65mm形状の硬化体を作製した。そして、硬化体を養生した後、110℃で24hの熱処理により乾燥し、その後1000℃で3hの熱処理により焼成したものを試験片として用いた。この試験片を用いて加熱と冷却を繰り返し、亀裂の発生状況を観察した。具体的には、230×65mm面をガスバーナーで1600℃に5分間で昇温し、10分間保持してから10分間放冷する操作を2回繰り返して亀裂の発生状況を観察した。表1及び表2では、亀裂の発生が軽微であった場合を○(良)、やや大きな亀裂が発生した場合を△(可)、大きな亀裂が発生した場合を×(不良)と表記した。
以下の基準により、○(良)、△(可)、×(不良)の3段階で評価した。
○(良):1mm未満の原料で構成した耐火物の1000℃での膨張率が○、室温及び1200℃での熱伝導率が6.5以下、耐食性が◎又は○、かつ耐熱衝撃性が○の場合。
△(可):総合評価が上記○以外の場合であって、下記の要件を満たす場合。
1mm未満の原料で構成した耐火物の1000℃での膨張率が○、室温又は1200℃での熱伝導率が9以下、耐食性が◎、○又は△、かつ耐熱衝撃性が○又は△。
×(不良):評価項目のいずれか一つが下記に該当する場合。
1mm未満の原料で構成した耐火物の1000℃での膨張率が×、室温及び1200℃での熱伝導率が9超、耐食性が×、耐熱衝撃性が×。
Claims (6)
- 耐火原料100質量%に占める割合で、粒径1mm以上の炭化珪素原料を20質量%以上50質量%以下、粒径1μm以上10μm以下のアルミナ微粉を2質量%以上15質量%以下、粒径1μm未満のシリカ超微粉を1質量%以上8質量%以下、それぞれ含有し、
前記耐火原料100質量%に占める割合で、アルミナセメントの含有量は15質量%以下(0を含む。)、粒径1mm未満の炭化珪素原料の含有量は5質量%以下(0を含む。)である流し込み施工用の不定形耐火物。 - 前記耐火原料100質量%に占める割合で、前記粒径1mm以上の炭化珪素原料の含有量は30質量%以上50質量%以下、前記シリカ超微粉の含有量は2質量%以上5質量%以下、前記アルミナセメントの含有量は5質量%以下(0を含む。)、前記粒径1mm未満の炭化珪素原料の含有量は2.5質量%以下(0を含む。)である請求項1に記載の流し込み施工用の不定形耐火物。
- 前記耐火原料の残部はアルミナ原料、スピネル原料、ムライト原料及びアンダリュサイト質原料の少なくとも一つからなる請求項1又は2に記載の流し込み施工用の不定形耐火物。
- 前記耐火原料100質量%に占める割合で、炭素原料の含有量は1質量%以下(0を含む。)である請求項1から3のいずれかに記載の流し込み施工用の不定形耐火物。
- 前記耐火原料中の粒径1mm未満の原料で構成した耐火物の膨張量が1000℃で0.2%以下である請求項1から4のいずれかに記載の流し込み施工用の不定形耐火物。
- ランス、インペラー又はタンディッシュカバーに適用される請求項1から5のいずれかに記載の流し込み施工用の不定形耐火物。