JP6942232B1 - 樹脂組成物 - Google Patents
樹脂組成物 Download PDFInfo
- Publication number
- JP6942232B1 JP6942232B1 JP2020216195A JP2020216195A JP6942232B1 JP 6942232 B1 JP6942232 B1 JP 6942232B1 JP 2020216195 A JP2020216195 A JP 2020216195A JP 2020216195 A JP2020216195 A JP 2020216195A JP 6942232 B1 JP6942232 B1 JP 6942232B1
- Authority
- JP
- Japan
- Prior art keywords
- acrylonitrile
- styrene
- mass
- resin
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
従来の技術では、難燃性、耐衝撃性を維持しつつ、これらの要求を満足することはできなかった。
[1]
(A)アクリロニトリル・スチレン系樹脂100質量部と、(A)アクリロニトリル・スチレン系樹脂を100質量部に対して(B)ゴム重合体2.5〜40質量部と、(C)塩素系樹脂10〜90質量部と、を含み、(A)アクリロニトリル・スチレン系樹脂として、アクリロニトリル比が3質量%以上差のある2種類以上のアクリロニトリル・スチレン系樹脂を併用する、スチレン系樹脂組成物。
[2]
前記(A)アクリロニトリル・スチレン系樹脂のアクリロニトリル比は15〜40質量%の範囲である、[1]に記載のスチレン系樹脂組成物。
[3]
前記(A)アクリロニトリル・スチレン系樹脂のうち、少なくとも1種のアクリロニトリル・スチレン系樹脂のアクリロニトリル比が26質量%以上である、[1]又は[2]に記載のスチレン系樹脂組成物。
[4]
前記(B)ゴム重合体が、アクリロニトリル・スチレン・ブタジエン樹脂(ABS樹脂)及びメタクリル酸メチル・ブタジエン・スチレン樹脂(MBS樹脂)からなる群より選ばれる少なくとも1種である、[1]〜[3]のいずれかに記載のスチレン系樹脂組成物。
[5]
前記(C)塩素系樹脂が、塩化ビニル樹脂(PVC)、塩素化ポリエチレン(CPE)及び塩化ビニリデン樹脂(PVDC)からなる群より選ばれる少なくとも1成分である、[1]〜[4]のいずれかに記載のスチレン系樹脂組成物。
[6]
樹脂組成物全体100質量部に対し、更に(D)酸化アンチモンを1〜10質量部含む、[1]〜[5]のいずれかに記載のスチレン系樹脂組成物。
[7]
樹脂組成物全体100質量部に対し、更に(E)安定剤を0.1〜10質量部含む、[1]〜[6]のいずれかに記載のスチレン系樹脂組成物。
[8]
[1]〜[7]のいずれかに記載のスチレン系樹脂組成物を含む成形体。
本実施形態のスチレン系樹脂組成物(以下、単に「樹脂組成物」とも記す)は、(A)アクリロニトリル・スチレン系樹脂100質量部と、(A)アクリロニトリル・スチレン系樹脂を100質量部に対して(B)ゴム重合体2.5〜40質量部と、(C)塩素系樹脂10〜90質量部と、を含み、(A)アクリロニトリル・スチレン系樹脂として、アクリロニトリル比が3質量%以上差のある2種類以上のアクリロニトリル・スチレン系樹脂を併用する。
アクリロニトリル・スチレン系樹脂をテトラヒドロフラン(以下「THF」とも記す)に溶解させ測定用試料とし、高速液体クロマトグラフ(HPLC) Prominence(株式会社島津製作所製)を用い、n−ヘキサン/THF溶剤の2液グラジエント、カラム温度40℃にてアクリロニトリル・スチレン系樹脂のアクリロニトリル比を測定することができる。標準サンプルには元素分析にて既知のアクリロニトリル比(AN比)であるアクリロニトリル・スチレン樹脂を用いることができる。
本実施形態の樹脂組成物において使用することができる(A)アクリロニトリル・スチレン系樹脂について、詳細に説明する。
本実施形態の樹脂組成物において使用することができる(B)ゴム重合体について、詳細に説明する。
本実施形態の樹脂組成物において使用することができる(C)塩素系樹脂について、詳細に説明する。
本実施形態の樹脂組成物において、更に(D)酸化アンチモンを含むことが好ましい。
本実施形態の樹脂組成物において、更に(E)安定剤を含むことが好ましい。
本実施形態の樹脂組成物は、本発明の目的を損なわない範囲で、公知の添加剤を添加できる。具体的には、特に限定されないが、例えば、充填材(タルク、マイカ、炭酸カルシウム等)、導電付与剤(カーボンブラック、カーボンナノチューブ、グラファイト等)、着色剤(酸化チタン、酸化亜鉛、酸化鉄、酸化アルミニウム、有機染料等)、紫外線吸収剤、耐候剤、滑剤、酸化防止剤を含有することができる。これらの含有量は、樹脂組成物100質量部に対し、充填材、導電付与剤は30質量部以下が好ましく、それ以外は5質量部以下であることが好ましい。これらは単独であっても、複数を組み合わせて使用してもよい。
本実施形態の樹脂組成物は、公知の方法による製造を行うことができる。具体的には、特に限定されないが、例えば、一軸又は多軸混練押出機、ロール、バンバリーミキサー等により、以下のように原料成分を混合及び溶融混練し、成形することにより製造することができる。
本実施形態における成形体は、上述のスチレン系樹脂組成物を含む。
本実施形態における成形体を得るための成形方法については、特に限定されず、公知の成形方法を利用できる。具体的には、特に限定されないが、例えば、押出成形、射出成形、真空成形、ブロー成形、射出圧縮成形、加飾成形、他材質成形、ガスアシスト射出成形、発泡射出成形、低圧成形、超薄肉射出成形(超高速射出成形)、金型内複合成形(インサート成形、アウトサート成形)等の成形方法のいずれかによって成形することができる。
本実施形態の樹脂組成物は、難燃性、機械的強度及び外観が要求される成形体の原料として使用することができる。
原料を一括ブレンドし、シリンダ温度を160〜200℃に設定し、二軸押出機(ZSK−25、コペリオン製)にて押出を実施して樹脂組成物を得た。
射出成形機(EC−75SXII、東芝機械(株)製)を用いて、得られた樹脂組成物から、JIS K7152−1及びISO294−1に準拠した小型試験片の樹脂成形体を得た。また、燃焼性試験用試験片としては、得られた樹脂組成物から、IEC−60695−11−10に準拠した小型試験片の樹脂成形体を得た。
前記IEC−60695−11−10に準拠して成形された125mm×13mm×1.5mm厚の小型試験片の樹脂成形体を用い、UL94に準拠した燃焼試験を行い、難燃性を以下のように評価した。
○:(合格)自己消火性あり
×:(不合格)自己消火性なし
前記ISO294−1に準拠して成形された小型試験片の樹脂成形体を用い、ISO179に準拠した切削後衝撃強度試験を行い、シャルピー衝撃強度を測定し、耐衝撃性を以下のように評価した。
○:(合格)シャルピー衝撃強度6kJ/m2以上
×:(不合格)シャルピー衝撃強度6kJ/m2未満
前記ISO294−1に準拠して成形された小型試験片の樹脂成形体を用い、ISO178に準拠した曲げ弾性率を測定し、剛性を以下のように評価した。
◎:(合格)曲げ弾性率2,550MPa以上
○:(合格)曲げ弾性率2,400MPa以上2,550MPa未満
×:(不合格)曲げ弾性率2,400MPa未満
成形機温度を200℃とし、30分間成形機内に溶融滞留後成形したサンプルの変色の色差ΔE(分光5nm光学反射、光源:D65光10°視野、正反射光を除いた測定(d/8)条件、観察視野:直径15mm)を測定し、色調保持性(熱滞留性安定性)を以下のように評価した。
◎:(合格)ΔE≦3
〇:(合格)3<ΔE≦5
×:(不合格)5<ΔE
前記ISO294−1に準拠して成形された小型試験片の樹脂成形体を用い、スーパーキセノンウェザーメーター(スガ試験機製、SX75)により、63℃の温度において200時間試験をし、色調保持性(耐候性)を以下のように評価した。
◎:(合格)耐候変色ΔE≦3
○:(合格)耐候変色3<△E≦5
×:(不合格)耐候変色5<ΔE
(A)アクリロニトリル・スチレン系樹脂は、以下のものを用いた。
(A1)アクリロニトリル・スチレン樹脂(AS樹脂):アクリロニトリル比20質量%、数平均分子量55,000
(A2)アクリロニトリル・スチレン樹脂(AS樹脂):アクリロニトリル比25質量%、数平均分子量55,000
(A3)アクリロニトリル・スチレン樹脂(AS樹脂):アクリロニトリル比27質量%、数平均分子量55,000
(A4)アクリロニトリル・スチレン樹脂(AS樹脂):アクリロニトリル比30質量%、数平均分子量55,000
(A5)アクリロニトリル・スチレン樹脂(AS樹脂):アクリロニトリル比35質量%、数平均分子量55,000
なお、本実施例において、(A)アクリロニトリル・スチレン系樹脂の数平均分子量は以下の方法で測定した。(A)アクリロニトリル・スチレン系樹脂をテトラヒドロフラン(THF)中に浸漬し、溶解した(A)アクリロニトリル・スチレン系樹脂成分をろ別した。得られたろ液を用い、ゲル浸透クロマトグラフィー(GPC)で測定した。当該測定結果に基づき、(A)アクリロニトリル・スチレン系樹脂の数平均分子量を、ポリスチレン(PS)を標準物質として算出した。
(B1)(b1)ブタジエンゴムに(b2)アクリロニトリル・スチレン樹脂(平均ゴム粒径500nm)をグラフトさせたゴム重合体
(C1)ポリ塩化ビニル(PVC):平均重合度600
(C2)塩素化ポリエチレン(CPE):MFR1.5g/10min、塩素含有量30質量%
(D1)三酸化二アンチモン:平均粒子径1μm
(E1)ジブチルスズマレイン酸塩
(E2)ジブチルスズ−3メルカプトプロピオン酸塩
各成分がそれぞれ表1に記載の割合となるように原料を配合して上記方法により押出し、樹脂組成物を製造した。得られた樹脂組成物を用い、上記条件にて成形し、成形体を製造した。各物性を評価した結果を表1に示す。
Claims (8)
- (A)アクリロニトリル・スチレン系樹脂(ただし、α−メチルスチレンとアクリロニトリルとを重合して得られる共重合体を除く)100質量部と、(A)アクリロニトリル・スチレン系樹脂を100質量部に対して(B)ゴム重合体2.5〜40質量部と、(C)塩素系樹脂10〜90質量部と、を含み、(A)アクリロニトリル・スチレン系樹脂のアクリロニトリル比の下限が15質量%以上であり、かつ(A)アクリロニトリル・スチレン系樹脂として、アクリロニトリル比が3質量%以上差のある2種類以上のアクリロニトリル・スチレン系樹脂を併用する、スチレン系樹脂組成物。
- 前記(C)塩素系樹脂が、塩素化ポリエチレン(CPE)を含む、請求項1に記載のスチレン系樹脂組成物。
- 前記(A)アクリロニトリル・スチレン系樹脂のアクリロニトリル比は15〜40質量%の範囲である、請求項1又は2に記載のスチレン系樹脂組成物。
- 前記(A)アクリロニトリル・スチレン系樹脂のうち、少なくとも1種のアクリロニトリル・スチレン系樹脂のアクリロニトリル比が26質量%以上である、請求項1〜3のいずれか一項に記載のスチレン系樹脂組成物。
- 前記(B)ゴム重合体が、アクリロニトリル・スチレン・ブタジエン樹脂(ABS樹脂)及びメタクリル酸メチル・ブタジエン・スチレン樹脂(MBS樹脂)からなる群より選ばれる少なくとも1種である、請求項1〜4のいずれか一項に記載のスチレン系樹脂組成物。
- 樹脂組成物全体100質量部に対し、更に(D)酸化アンチモンを1〜10質量部含む、請求項1〜5のいずれか一項に記載のスチレン系樹脂組成物。
- 樹脂組成物全体100質量部に対し、更に(E)安定剤を0.1〜10質量部含む、請求項1〜6のいずれか一項に記載のスチレン系樹脂組成物。
- 請求項1〜7のいずれか一項に記載のスチレン系樹脂組成物を含む成形体。