JP6870822B2 - 高比重繊維からなるマルチフィラメント糸 - Google Patents
高比重繊維からなるマルチフィラメント糸 Download PDFInfo
- Publication number
- JP6870822B2 JP6870822B2 JP2017036729A JP2017036729A JP6870822B2 JP 6870822 B2 JP6870822 B2 JP 6870822B2 JP 2017036729 A JP2017036729 A JP 2017036729A JP 2017036729 A JP2017036729 A JP 2017036729A JP 6870822 B2 JP6870822 B2 JP 6870822B2
- Authority
- JP
- Japan
- Prior art keywords
- specific gravity
- high specific
- component
- core component
- multifilament yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
芯成分を構成するポリマーが、結晶融点200〜220℃、ガラス転移温度70〜80℃の共重合ポリエステルであり、鞘成分を構成するポリマーがポリエチレンテレフタレートであり、
マルチフィラメント糸の強度が4.7cN/dtex以上、かつ毛羽数が20個/100万m以下であることを特徴とする高比重繊維からなるマルチフィラメント糸を要旨とする。
0.0≦A≦10.0
5.0<B≦15.0
(上式中、Aは共重合ポリエステルの全酸成分に対するイソフタル酸のモル分率(%)、Bは共重合ポリエステルの全グリコール成分に対するビスフェノールAのエチレンオキシド付加物のモル分率(%)である。)
(A)極限粘度
フェノールと四塩化エタンとの等質量混合物を溶媒とし、濃度0.5g/dl、温度20℃で測定した。
(B)ポリエステルの組成
ポリエステル樹脂を重水素化ヘキサフルオロイソプロパノールと重水素化クロロホルムとの容量比が1/20の混合溶媒に溶解させ、日本電子社製LA−400型NMR装置にて1H−NMRを測定し、得られたチャートの各成分のプロトンのピークの積分強度から、共重合成分の種類と含有量を求めた。
(C)強伸度
JIS L−1013 引張強さおよび伸び率の標準時試験に従い、島津製作所オートグラフDSS−500を用い、試料長25cm、引張速度30cm/分で測定した。
(D)繊維の比重
JIS l−1013 比重(浮沈法)に従い測定した。
(E)毛羽数
春日電機製毛羽発見器F9−AN型を用い、引き取り速度300m/分で測定した。
(F)融点(℃)
パーキンエルマー社製の示差走査型熱量計DSC−7型を使用し、昇温速度20℃/分で測定した。
(G)ガラス転移温度(℃)
パーキンエルマー社製の示差走査型熱量計DSC−7型を使用し、昇温速度20℃/分で測定した。なお、補外ガラス転移開始温度(Tig)をガラス転移温度とした。
(H)操業性
口金当たりの連続操業時間により下記三段階で評価した。
○:20時間以上
△:10時間以上、20時間未満
×:10時間未満
鞘成分として、極限粘度1.2のPETにカーボンブラックを高濃度に含有したマスターバッチとレギュラーのPET(極限粘度1.2)とを混合し、鞘成分中のカーボンブラック濃度が0.8質量%となるようにしたブレンドチップを用いた。一方、芯成分として、極限粘度0.58でイソフタル酸共重合率が8.0モル%、ビスフェノールAのエチレンオキシド付加物共重合率が6.5モル%である共重合ポリエステルに平均粒子径が0.6μm、最大粒子径2.0μm、比重4.3の沈降性硫酸バリウムを芯成分中に65質量%およびカーボンブラックを1.5質量%となるように溶融混合したもの(チップ)を用いた。
芯成分中のイソフタル酸共重合率(A)およびビスフェノールAのエチレンオキシド付加物共重合率(B)を表1に記載したように変更したこと以外は、実施例1と同様に行った。
実施例1において、芯成分としてイソフタル酸共重合率(A)を8.0モル%である共重合ポリエステルを用いたこと、芯成分中に混合する沈降性硫酸バリウムの量を50質量%としたこと、芯鞘質量比(芯:鞘)を36:64として溶融紡糸したこと以外は、実施例1と同様に行った。
芯成分中のジオール成分をビスフェノールAのエチレンオキシド付加物に代えて、表2に記載した成分に変更したこと以外は、実施例1と同様に行った。
得られたマルチフィラメント糸を用いて8本組紐を作成し、これを試料とした。耐摩耗試験装置(米倉製作所製)を用いて、試料を試験装置に取り付けた。すなわち、試料の一端に質量300gのおもりをつるし、他端を丸やすり(ツボミヤ社製 優良鉄工用ヤスリ 丸中目)の上を渡して設置し、試料を繰り返し速度30±1回/分、ストローク幅230±30mmにて往復運動させ、試料と丸やすりの周面とが約90度の角度で接触させて往復摩擦させ、破断に至る往復回数を計測した。
測定は、室温で耐摩耗性を評価したものは「乾摩耗」、一方、試料を工業用水に5分浸漬後、取り出して耐摩耗性を評価したものを「湿摩耗」とした。なお、「湿摩耗」は、試験開始直前と摩耗100回毎に1ccの水を滴下して測定した。
Claims (3)
- 芯成分中に高比重粒子を含有し、比重が1.50以上である芯鞘型複合繊維からなるマルチフィラメント糸であり、
芯成分を構成するポリマーが、結晶融点200〜220℃、ガラス転移温度70〜80℃の共重合ポリエステルであり、鞘成分を構成するポリマーがポリエチレンテレフタレートであり、
マルチフィラメント糸の強度が4.7cN/dtex以上、かつ毛羽数が20個/100万m以下であることを特徴とする高比重繊維からなるマルチフィラメント糸。 - 芯鞘比率(質量比)が、芯成分/鞘成分=30〜20/70〜80であり、芯成分と鞘成分を構成するポリマーがポリエステル系ポリマーであることを特徴とする請求項1記載の高比重繊維からなるマルチフィラメント糸。
- 請求項1または2記載のマルチフィラメント糸により構成されてなるネット。