JP6846927B2 - 熱硬化性シート状成形材料及び繊維強化プラスチックの製造方法 - Google Patents
熱硬化性シート状成形材料及び繊維強化プラスチックの製造方法 Download PDFInfo
- Publication number
- JP6846927B2 JP6846927B2 JP2016253061A JP2016253061A JP6846927B2 JP 6846927 B2 JP6846927 B2 JP 6846927B2 JP 2016253061 A JP2016253061 A JP 2016253061A JP 2016253061 A JP2016253061 A JP 2016253061A JP 6846927 B2 JP6846927 B2 JP 6846927B2
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- thermosetting
- layer
- molding material
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
[1]一方向炭素繊維シート(A1)に熱硬化性樹脂組成物(B)が含浸された層(以下、「A1B層」と記載することもある)とランダムに配向した短繊維束(A2)に熱硬化性樹脂組成物(B)が含浸された層(以下、「A2B層」と記載することもある)とがA1B層、A2B層及びA1Bの順に積層されたものであって、2つのA1B層の一方向炭素繊維シート(A1)の繊維の方向が同一である熱硬化性シート状成形材料。
[2]前記一方向炭素繊維シート(A1)の目付重量が50〜200g/m2である[1]に記載の熱硬化性シート状成形材料。
[3]前記熱硬化性樹脂組成物(B)が、エポキシ樹脂、ビニルエステル樹脂及び不飽和ポリエステル樹脂から選ばれる少なくとも1種の熱硬化性樹脂(B1)を含む[1]又は[2]に記載の熱硬化性シート状成形材料。
[4]前記熱硬化性樹脂(B1)が、ビニルエステル樹脂である[3]に記載の熱硬化性シート状成形材料。
[5]前記熱硬化性樹脂組成物(B)が、ポリイソシアネート(B3)を含む[1]〜[4]のいずれかに記載の熱硬化性シート状成形材料。
[6]前記熱硬化性シート状成形材料100質量部に対して、前記一方向炭素繊維シート(A1)及び前記短繊維束(A2)の合計量が、30〜60質量部である[1]〜[5]のいずれかに記載の熱硬化性シート状成形材料。
[7]前記熱硬化性シート状成形材料100質量部に対して、前記一方向炭素繊維シート(A1)が、3〜13質量部含まれる[1]〜[6]のいずれかに記載の熱硬化性シート状成形材料。
[8][1]〜[7]のいずれかに記載の熱硬化性シート状成形材料を加熱、加圧することを含む繊維強化プラスチックの製造方法。
本発明に係る熱硬化性シート状成形材料は、一方向炭素繊維シート(A1)に熱硬化性樹脂組成物(B)が含浸された層(A1B層)とランダムに配向した短繊維束(A2)に熱硬化性樹脂組成物(B)が含浸された層(A2B層)とがA1B層、A2B層及びA1B層の順に積層され、2つのA1B層の一方向炭素繊維シート(A1)の繊維の方向が略同一であるものである。
本発明の熱硬化性シート状成形材料は、一般的なSMC製造装置を用いて製造することができる。後述の原材料を混合して熱硬化性樹脂組成物(B)を得た後、その熱硬化性樹脂組成物(B)を一方向炭素繊維シート(A1)及び/又は短繊維束(A2)に含浸してシート化し、それをA1B層、A2B層及びA1B層の順に積層することで製造することができる。例えば、A1B層からなるシートとA2B層からなるシートとをそれぞれ製造し、それらをA1B層、A2B層及びA1B層の順に積層することで本発明の熱硬化性シート状成形材料を得ることができる。また、一方向炭素繊維シート(A1)、短繊維束(A2)及び一方向炭素繊維シート(A1)の順に積層したところに熱硬化性樹脂組成物(B)を一度に含浸させることで本発明の熱硬化性シート状成形材料を得ることもできる。A1B層のみ、及びA2B層のみを先にシート化してから積層する方法で図1の熱硬化性シート状成形材料を得る方法を例に、以下に、本発明の熱硬化性シート状成形材料を製造する具体的な方法を説明する。
一方向炭素繊維シート(A1)は、緯糸を含まない形態であり、例えば、予め炭素繊維を一方向に引き揃えてシート状にした一方向炭素繊維基材や、シート状にした一方向炭素繊維基材をマトリックス樹脂や集束剤で含浸し固定したプリプレグ状シートを用いることができる。
短繊維束(A2)に用いる繊維の種類には特に制限は無く、炭素繊維、アラミド繊維、ボロン繊維、ガラス繊維などが例示できる。これらの繊維束は、単独で用いてもよいし、又は二種類以上を用いてもよい。これらの中でも、炭素繊維は比強度及び比弾性に優れるので好ましく、ガラス繊維はこれらの繊維束の中で比較的安価で強度も優れるので好ましい。短繊維束(A2)の繊維長は、SMCにおいて通常用いられる長さであればよく、具体的には12〜25mmである。
本発明で用いる熱硬化性樹脂組成物(B)は、加熱により硬化可能であり、一方向炭素繊維シート(A1)及び短繊維束(A2)に含浸できるものであれば特に制限は無い。
熱硬化性樹脂組成物(B)は、主成分として、エポキシ樹脂、ビニルエステル樹脂及び不飽和ポリエステル樹脂から選ばれる少なくとも1種の熱硬化性樹脂(B1)を含むことが好ましい。
熱硬化性樹脂組成物(B)は、重合性モノマー(B2)を含むことが好ましい。特に、熱硬化性樹脂(B1)としてビニルエステル樹脂又は不飽和ポリエステル樹脂を用いた場合、重合性モノマー(B2)を熱硬化性樹脂(B1)の適切な希釈溶媒として用いることができる。重合性モノマー(B2)は、熱硬化性樹脂(B1)と重合可能なエチレン性不飽和結合を有しているものであれば適宜なものを用いることができる。重合性モノマー(B2)としては、例えば、スチレン、ビニルトルエン、α−メチルトルエン、ジアリルフタレート、トリアリルイソシアヌレート、ジアリルフタレートプレポリマー、(メタ)アクリル酸エチル、(メタ)アクリル酸メチルなどが挙げられる。
熱硬化性樹脂組成物(B)は、ポリイソシアネート(B3)を含むことが好ましい。ポリイソシアネート(B3)は、一分子中に少なくとも二つのイソシアナト基を有するものであれば特に限定されない。ポリイソシアネート(B3)としては、トリレンジイソシアネート(TDI)、4,4’−ジフェニルメタンジイソシアネート(MDI)、水素添加キシリレンジイソシアネート(H6XDI)、イソホロンジイソシアネート(IPDI)、シクロヘキサンジイソシアネート(CHDI)、水素添加4,4’−ジフェニルメタンジイソシアネート(H12MDI)、キシリレンジイソシアネート(XDI)、テトラメチルキシリエンジイソシアネート(TMXDI)、1,6−ヘキサメチレンジイソシアネート(HDI)などが挙げられる。これらのポリイソシアネート(B3)は、単独で用いてもよいし、二種以上を併用してもよい。
熱硬化性樹脂組成物(B)を加熱硬化させるための硬化剤には特に制限はなく、選定した熱硬化性樹脂(B1)及び重合性モノマー(B2)に適した公知のものを使用することができる。熱硬化性樹脂(B1)としてエポキシ樹脂を使用する場合の硬化剤としては、例えば、アミン、酸無水物、フェノール樹脂、メルカプタン、ルイス酸アミン錯体、オニウム塩、イミダゾールなどが挙げられる。エポキシ樹脂の硬化剤は、熱硬化性樹脂組成物(B)100質量部に対して、3〜10質量部の範囲で添加することが好ましい。
本発明で用いる熱硬化性樹脂組成物(B)には、本発明の効果を損なわない範囲で、内部離型剤、無機充填材、低収縮化剤、重合禁止剤、着色剤などの添加剤を添加してもよい。
本発明に係る繊維強化プラスチックは、上述した熱硬化性シート状成形材料を加熱・加圧により硬化させたものである。
連続した炭素繊維トウ(東レ株式会社製トレカ(登録商標)T700−12K)から、長さ1mの炭素繊維トウを複数本切出し、それらを一方向に引き揃えて目付重量が100g/m2となるように並べ、その長さ方向の両端部を粘着テープで固定することで、一方向炭素繊維シートを得た。
下記表1に示す組成となるように以下の材料(B1)〜(B5)を25℃で混合し、熱硬化性樹脂組成物Baを得た。
(B1)ビニルエステル樹脂、(B2)重合性モノマー(スチレン)
昭和電工株式会社製リポキシ(登録商標)R−804。ビスフェノールA型ビニルエステル樹脂のスチレン溶解品。スチレン含有率40質量%。
(B3)ポリイソシアネート
日本ポリウレタン工業株式会社製、4,4’−ジフェニルメタンジイソシアネート。
(B4)硬化剤
日油株式会社製、t−ブチルパーオキシベンゾエート
(B5)内部離型剤
日油株式会社製、ステアリン酸亜鉛。
(B5)無機充填材
昭和電工株式会製ハイジライト(登録商標)H−42、水酸化アルミニウム。
(B5)重合禁止剤
精工化学株式会社製p−ベンゾキノンを三井化学株式会社製メチルメタアクリレートに5質量%の濃度で溶解したもの。
〔実施例1−1〕
SMC製造装置を用いて、熱硬化性樹脂組成物Baを上下キャリアフィルム(ポリプロピレン)に厚さが均一になるよう塗布した。
次いで、下側のキャリアフィルムにのみ一方向炭素繊維シート(目付重量100g/m2)1枚を配置した。その一方向炭素繊維シート上に短繊維束(A2)として25mmの長さに機械的に切断された炭素繊維トウを散布し、上側のキャリアフィルムで挟み込んで熱硬化性樹脂組成物を含浸させた。40℃で24時間熟成させた後、280×280mmの大きさに2枚切り出し、2枚の一方向炭素繊維シートの繊維の配向方向が同一になるようにA2B層同士を対向させて重ね合せて、図2に示されるような熱硬化性シート状成形材料(A1B層が積層方向の両側の最外に位置する)として実施例1−1の熱硬化性シート状成形材料を得た。実施例1−1の熱硬化性シート状成形材料は、一方向炭素繊維シート(A1)、短繊維束(A2)及び熱硬化性樹脂組成物Baの含有量が、熱硬化性シート状成形材料100質量部に対して、それぞれ5質量部、45質量部及び50質量部となるような条件で作製した。また、単位面積当たりのシート重量は約4kg/m2であった。
一方向炭素繊維シート(目付重量100g/m2)2枚を同一方向に重ねて目付重量を200g/m2とした一方向炭素繊維シートを下側のキャリアフィルムにのみ配置したこと以外は、実施例1−1と同様にして、実施例2−1の熱硬化性シート状成形材料を得た。実施例2−1の熱硬化性シート状成形材料は、一方向炭素繊維シート(A1)、短繊維束(A2)及び熱硬化性樹脂組成物Baの含有量が、熱硬化性シート状成形材料100質量部に対して、それぞれ10質量部、40質量部及び50質量部となるような条件で作製した。
一方向炭素繊維シート(A1)を使用せず、短繊維束(A2)及び熱硬化性樹脂組成物Baの含有量を、熱硬化性シート状成形材料100質量部に対して、それぞれ50質量部及び50質量部とした以外は、実施例1−1と同様にして、比較例1−1の熱硬化性シート状成形材料(A2B層のみからなる)を得た。
A2B層ではなくA1B層を対向させて重ね合せたこと以外は、実施例1−1と同様にして、比較例2−1の熱硬化性シート状成形材料(A2B層が積層方向の両側の最外に位置する)を得た。
実施例1−1、2−1及び比較例1−1、2−1で得られた熱硬化性シート状成形材料を成形品寸法が300mm×300mmとなる金型に置き、金型温度140℃、成形圧力15MPa及び成形時間180秒の条件で加熱・加圧して硬化させ、それぞれ厚さ2mm×300mm×300mmの平板形状の繊維強化プラスチックを得た。
〔実施例1−2〕
SMC製造装置を用いて、熱硬化性樹脂組成物Baを上下キャリアフィルム(ポリプロピレン)に厚さが均一になるよう塗布した。
次いで、下側のキャリアフィルムにのみ一方向炭素繊維シート(目付重量100g/m2)1枚を配置した。その一方向炭素繊維シート上に短繊維束(A2)として25mmの長さに機械的に切断された炭素繊維トウを散布し、上側のキャリアフィルムで挟み込んで熱硬化性樹脂組成物を含浸させた。40℃で24時間熟成させた後、160×140mmの大きさの成形材料を2枚切り出し、2枚の熱硬化性シート状成形材料の一方向炭素繊維シートの繊維の配向方向が同一になるようにA2B層同士を対向させて重ね合せて、図2に示されるような熱硬化性シート状成形材料(A1B層が積層方向の両側の最外に位置する)として実施例1−2の熱硬化性シート状成形材料を得た。
一方向炭素繊維シート(目付重量100g/m2)2枚を同一方向に重ねて目付重量を200g/m2とした一方向炭素繊維シートを下側のキャリアフィルムにのみ配置したこと以外は、実施例1−2と同様にして、実施例2−2の熱硬化性シート状成形材料を得た。実施例2−1の熱硬化性シート状成形材料は、一方向炭素繊維シート(A1)、短繊維束(A2)及び熱硬化性樹脂組成物Baの含有量が、熱硬化性シート状成形材料100質量部に対して、それぞれ10質量部、40質量部及び50質量部となるような条件で作製した。
一方向炭素繊維シート(A1)を使用せず、短繊維束(A2)及び熱硬化性樹脂組成物Baの含有量を、熱硬化性シート状成形材料100質量部に対して、それぞれ50質量部及び50質量部とした以外は、実施例1−2と同様にして、比較例1−2の熱硬化性シート状成形材料(A2B層のみからなる)を得た。
A2B層ではなくA1B層を対向させて重ね合せたこと以外は、実施例1−2と同様にして、比較例2−2の熱硬化性シート状成形材料(A2B層が積層方向の両側の最外に位置する)を得た。
実施例1−2、2−2及び比較例1−2、2−2で得られた熱硬化性シート状成形材料を、成形品形状が170×150mmの曲面板形状にリブ及びボスが設けられたものとなる金型に置き、金型温度140℃、成形圧力15MPa及び成形時間180秒の条件で加熱・加圧して硬化させ、それぞれ繊維強化プラスチックを得た。
Claims (7)
- 一方向炭素繊維シート(A1)に熱硬化性樹脂組成物(B)が含浸された層(「A1B層」と略す。)とランダムに配向した短繊維束(A2)に熱硬化性樹脂組成物(B)が含浸された層(「A2B層」と略す。)とがA1B層、A2B層及びA1B層の順に積層されたものであって、2つのA1B層の一方向炭素繊維シート(A1)の繊維の方向が同一であり、一方向炭素繊維シート(A1)の目付重量が50〜200g/m 2 である熱硬化性シート状成形材料。
- 前記熱硬化性樹脂組成物(B)が、エポキシ樹脂、ビニルエステル樹脂及び不飽和ポリエステル樹脂から選ばれる少なくとも1種の熱硬化性樹脂(B1)を含む請求項1に記載の熱硬化性シート状成形材料。
- 前記熱硬化性樹脂(B1)が、ビニルエステル樹脂である請求項2に記載の熱硬化性シート状成形材料。
- 前記熱硬化性樹脂組成物(B)が、ポリイソシアネート(B3)を含む請求項1〜3のいずれかに記載の熱硬化性シート状成形材料。
- 前記熱硬化性シート状成形材料100質量部に対して、前記一方向炭素繊維シート(A1)及び前記短繊維束(A2)の合計量が、30〜60質量部である請求項1〜4のいずれかに記載の熱硬化性シート状成形材料。
- 前記熱硬化性シート状成形材料100質量部に対して、前記一方向炭素繊維シート(A1)が、3〜13質量部含まれる請求項1〜5のいずれかに記載の熱硬化性シート状成形材料。
- 請求項1〜6のいずれかに記載の熱硬化性シート状成形材料を加熱、加圧することを含む繊維強化プラスチックの製造方法。