JP6835939B2 - 植物由来成分を含有するシート状又は板状押出発泡体の製造方法 - Google Patents
植物由来成分を含有するシート状又は板状押出発泡体の製造方法 Download PDFInfo
- Publication number
- JP6835939B2 JP6835939B2 JP2019206022A JP2019206022A JP6835939B2 JP 6835939 B2 JP6835939 B2 JP 6835939B2 JP 2019206022 A JP2019206022 A JP 2019206022A JP 2019206022 A JP2019206022 A JP 2019206022A JP 6835939 B2 JP6835939 B2 JP 6835939B2
- Authority
- JP
- Japan
- Prior art keywords
- shaped
- extruded foam
- foaming
- weight
- plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
押出発泡体は、主成分と、発泡用プラスチックと、発泡剤と、改質剤、添加剤とを含む。
主成分は、自然環境にやさしい成分であり、デンプン及び/又は植物性セルロースを用いる。また、デンプン及び/又は植物性セルロース成分としては、デンプン(例えば、コーンスターチ、タピオカデンプン、馬鈴薯デンプン、もち米デンプン、小麦デンプン)、紙パルプ等がある。なお、この主成分には、官製葉書古紙は含まれないことが好ましい。なお、主成分の定義として、ここでは発泡用プラスチックよりもデンプン及び/又は植物性セルロースの重量比率が大きいことを意味する。
発泡用プラスチックは、ポリプロピレン、スチレン系樹脂(例えばポリスチレン、高衝撃性ポリスチレン、ABS等)、エチレン系樹脂(例えば高密度ポリエチレン、低密度ポリエチレン、エチレン酢酸ビニル共重合樹脂等)、ポリエステル等があるが、製造容易性の面から、ポリプロピレン、ポリスチレンが中心的に使用される。
発泡剤として、有機系、無機系の公知発泡剤を適宜選択して用いることができるが、有機系の発泡剤の場合には、防爆管理、製品安全性の確保、さらには環境保護等の面から好ましくはない。それゆえ、無機系の発泡剤を用いることが好ましい。無機系の発泡剤としては、水、空気、炭酸ガス、窒素、アルゴン、ヘリウム、等があるが、大気下の開放系で使用が可能という取扱いの容易さから、水を用いることが好ましい。
添加剤としては、例えば、改質剤、核剤、色材、消臭剤、抗菌剤等がある。
改質剤は、混合物(特に、デンプン及び/又は植物性セルロースと発泡用プラスチック)の溶融張力の向上や、混合物における相溶性の向上を図るためのものである。改質剤は、ポリテトラフルオロエチレンのアクリル変性体であり、より具体的にいえば、ポリテトラフルオロエチレン(A)および炭素数5〜30のアルキル(メタ)アクリレート系ポリマー(B)からなるものであり、その具体例として、メタブレンA3000 三菱レイヨン社製がある。押出発泡体全体に対する改質剤の含有量は、例えば、0.1重量%以上0.4重量%以下であることが好ましい。
核剤として、公知の物質(例えば、タルク)を適宜選択して用いることができる。核剤としては、粉末のものを用いることが好ましい。押出発泡体全体に対する核剤の含有量は、押出発泡体が得られる程度の範囲であれば、特に限定されない。例えば、その含有量の範囲は、0.1重量%以上3重量%以下であることが好ましい。
押出発泡体は、主成分と、発泡用プラスチックと、発泡剤と、改質剤、添加剤とを含む。
発泡用プラスチックは、ポリプロピレン、スチレン系樹脂(例えばポリスチレン、高衝撃性ポリスチレン、ABS等)、エチレン系樹脂(例えば高密度ポリエチレン、低密度ポリエチレン、エチレン酢酸ビニル共重合樹脂等)、ポリエステル等があるが、製造容易性の面から、ポリプロピレン、ポリスチレンが中心的に使用される。
デンプン及び/又は植物性セルロース成分としては、デンプン(例えば、コーンスターチ、タピオカデンプン、馬鈴薯デンプン、もち米デンプン、小麦デンプン)、紙パルプ等がある。なお、官製葉書古紙は含まれないことが好ましい。
発泡剤として、有機系、無機系の公知発泡剤を適宜選択して用いることができるが、有機系の発泡剤の場合には、防爆管理、製品安全性の確保、さらには環境保護等の面から好ましくはない。それゆえ、無機系の発泡剤を用いることが好ましい。無機系の発泡剤としては、水、空気、炭酸ガス、窒素、アルゴン、ヘリウム、等があるが、大気下の開放系で使用が可能という取扱いの容易さから、水を用いることが好ましい。
添加剤としては、例えば、改質剤、核剤、色材、消臭剤、抗菌剤等がある。
改質剤は、混合物(特に、デンプン及び/又は植物性セルロースと発泡用プラスチック)の溶融張力の向上や、混合物における相溶性の向上を図るためのものである。改質剤は、ポリテトラフルオロエチレンのアクリル変性体であり、より具体的にいえば、ポリテトラフルオロエチレン(A)および炭素数5〜30のアルキル(メタ)アクリレート系ポリマー(B)からなるものであり、その具体例として、メタブレンA3000 三菱レイヨン社製がある。押出発泡体全体に対する改質剤の含有量は、例えば、0.1重量%以上0.4重量%以下であることが好ましい。
核剤として、公知の物質(例えば、タルク)を適宜選択して用いることができる。核剤としては、粉末のものを用いることが好ましい。押出発泡体全体に対する核剤の含有量は、押出発泡体が得られる程度の範囲であれば、特に限定されない。例えば、その含有量の範囲は、0.1重量%以上3重量%以下であることが好ましい。
図1に示すように、押出発泡体の製造方法2は、デンプン及び/又は植物性セルロースAと、主成分となる発泡用プラスチックBと、所定の添加剤Cを含む混合物M1を調製する混合物調製ステップ10と、混合物M1に対し発泡剤Fを添加する発泡剤添加ステップ20と、発泡剤Fが添加された混合物M1から粉状の配合物M2を調製する配合物調製ステップ30と、配合物M2に対して押出発泡を行う押出発泡ステップ40とを有する。
表2に示したこと以外は、実験B−1と同様にして、実験B−2〜B−4を行った。主成分となる発泡用プラスチックとして、ポリプロピレン樹脂(日本ポリプロ社製 ノバテックPP MH4)にポリエチレン樹脂(日本ポリエチレン社製 ノバテックLDPE LC500)、ポリスチレン樹脂(Chimei Corporation 製 HIPS PH-88S )を変量して配合し、樹脂配合量による特性を調べた。尚、タルクは日本タルク社製 タルクSW、改質剤は、ポリテトラフルオロエチレンのアクリル変生体として、三菱レーヨン社製 メタブレンA-3000 を使用した。
10 混合物調製ステップ
20 発泡剤添加ステップ
30 配合物調製ステップ
40 押出発泡ステップ
Claims (4)
- シート状又は板状に成型され、主成分となるデンプン、又は、主成分となるデンプン及び植物性セルロースと、ポリプロピレンを含む発泡用プラスチックと、ポリテトラフルオロエチレンのアクリル変性体を含み、前記主成分と前記発泡用プラスチックを含む混合物に対する改質剤と、を混合して得られる原材料を用い、
前記原材料における前記主成分の含有量は、前記発泡用プラスチックに対して100重量%以上且つ350重量%以下とし、
前記原材料の全体に対して3重量%から8重量%の水を発泡剤として用い、
前記原材料を、幅方向に複数の開口を有するダイスの前記開口を通過させ、前記開口を経て発泡する複数の紐状部材を互いに融着させることでシート状又は板状に成形すること
を特徴とする植物由来成分を含有するシート状又は板状押出発泡体の製造方法。 - 前記ポリテトラフルオロエチレンのアクリル変生体は、前記シート状又は板状押出発泡体の全体に対して0.1重量%以上含むことを特徴とする請求項1に記載の植物由来成分を含有するシート状又は板状押出発泡体の製造方法。
- 前記原材料における前記デンプンの含有量は、前記発泡用プラスチックに対して100重量%以上且つ350重量%以下となることを特徴とする請求項1又は2記載の植物由来成分を含有するシート状又は板状押出発泡体の製造方法。
- 前記発泡用プラスチックは、ポリプロピレン樹脂と、エチレン系樹脂及び/又はスチレ
ン系樹脂と、の混合物であることを特徴とする請求項1乃至3のいずれか1項に記載の植物由来成分を含有するシート状又は板状押出発泡体の製造方法。