JP6823084B2 - ガラス繊維組成物及びそのガラス繊維、並びに複合材料 - Google Patents
ガラス繊維組成物及びそのガラス繊維、並びに複合材料 Download PDFInfo
- Publication number
- JP6823084B2 JP6823084B2 JP2018563591A JP2018563591A JP6823084B2 JP 6823084 B2 JP6823084 B2 JP 6823084B2 JP 2018563591 A JP2018563591 A JP 2018563591A JP 2018563591 A JP2018563591 A JP 2018563591A JP 6823084 B2 JP6823084 B2 JP 6823084B2
- Authority
- JP
- Japan
- Prior art keywords
- glass fiber
- iron oxide
- feo
- glass
- content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
SiO2 54.2〜64%
Al2O3 11〜18%
CaO 20〜25.5%
MgO 0.3〜3.9%
Na2O+K2O 0.1〜2%
TiO2 0.1〜1.5%
鉄酸化物の合計量 0.1〜1%
SiO2 57〜62%
Al2O3 12〜17%
CaO+MgO 21〜26.5%
CaO 20.5〜25%
MgO 0.3〜2.7%
Na2O+K2O 0.2〜2%
Na2O 0.1〜1.2%
K2O 0.1〜1.2%
TiO2 0.1〜1.5%
鉄酸化物の合計量 0.1〜0.8%
SiO2 57.5〜61%
Al2O3 13〜15.5%
CaO 21〜24.5%
MgO 0.4%超え、且つ1%未満
Na2O+K2O 0.1〜2%
TiO2 0.1〜1.2%
鉄酸化物の合計量 0.1〜0.8%
SiO2 57.5〜61%
Al2O3 13〜15.5%
CaO 21〜24.5%
MgO 0.4%超え且つ1%未満
Na2O+K2O 0.1〜2%
TiO2 0.1〜1.2%
鉄酸化物の合計量 0.1〜0.8%
SiO2 54.2〜64%
Al2O3 11〜18%
CaO 20〜25.5%
MgO 0.3〜3.9%
Na2O+K2O 0.1〜2%
TiO2 0.1〜1.5%
鉄酸化物の合計量 0.1〜1%
本発明に係るガラス繊維組成物は下記の成分を含有する。各成分の含有量は、重量百分率で、以下のとおりである。
SiO2 54.2〜64%
Al2O3 11〜18%
CaO 20〜25.5%
MgO 0.3〜3.9%
Na2O+K2O 0.1〜2%
TiO2 0.1〜1.5%
鉄酸化物の合計量 0.1〜1%
本発明に係るガラス繊維組成物は下記の成分からなる。各成分の含有量は、重量百分率で、以下のとおりである。
SiO2 54.2〜64%
Al2O3 11〜18%
CaO 20〜25.5%
MgO 0.3〜3.9%
Na2O+K2O 0.1〜2%
TiO2 0.1〜1.5%
鉄酸化物の合計量 0.1〜1%
本発明に係るガラス繊維組成物は下記の成分を含有する。各成分の含有量は、重量百分率で、以下のとおりである。
SiO2 54.2〜64%
Al2O3 11〜18%
CaO 20〜25.5%
MgO 0.3〜3.9%
Na2O+K2O 0.1〜2%
TiO2 0.1〜1.5%
鉄酸化物の合計量 0.1〜1%
本発明に係るガラス繊維組成物は下記の成分を含有する。各成分の含有量は、重量百分率で、以下のとおりである。
SiO2 54.2〜64%
Al2O3 11〜18%
CaO 20〜25.5%
MgO 0.3〜3.9%
Na2O+K2O 0.1〜2%
TiO2 0.1〜1.5%
鉄酸化物の合計量 0.1〜1%
本発明に係るガラス繊維組成物は下記の成分を含有する。各成分の含有量は、重量百分率で、以下のとおりである。
SiO2 54.2〜64%
Al2O3 11〜18%
CaO 20〜25.5%
MgO 0.3〜3.9%
Na2O+K2O 0.1〜2%
TiO2 0.1〜1.5%
鉄酸化物の合計量 0.1〜1%
本発明に係るガラス繊維組成物は下記の成分を含有する。各成分の含有量は、重量百分率で、以下のとおりである。
SiO2 57〜62%
Al2O3 12〜17%
CaO+MgO 21〜26.5%
CaO 20.5〜25%
MgO 0.3〜2.7%
Na2O+K2O 0.2〜2%
Na2O 0.1〜1.2%
K2O 0.1〜1.2%
TiO2 0.1〜1.5%
鉄酸化物の合計量 0.1〜0.8%
本発明に係るガラス繊維組成物は下記の成分を含有する。各成分の含有量は、重量百分率で、以下のとおりである。
SiO2 57.5〜61%
Al2O3 13〜15.5%
CaO 21〜24.5%
MgO 0.4%超え1%未満
Na2O+K2O 0.1〜2%
TiO2 0.1〜1.2%
鉄酸化物の合計量 0.1〜0.8%
本発明に係るガラス繊維組成物は下記の成分を含有する。各成分の含有量は、重量百分率で、以下のとおりである。
SiO2 54.2〜64%
Al2O3 11〜18%
CaO 20〜25.5%
MgO 0.3〜3.9%
Na2O+K2O 0.1〜2%
TiO2 0.1〜1.5%
鉄酸化物の合計量 0.1〜1%
本発明に係るガラス繊維組成物は下記の成分を含有する。各成分の含有量は、重量百分率で、以下のとおりである。
SiO2 54.2〜64%
Al2O3 11〜18%
CaO 20〜25.5%
MgO 0.3〜3.9%
Na2O+K2O 0.1〜2%
TiO2 0.1〜1.5%
鉄酸化物の合計量 0.1〜1%
本発明に係るガラス繊維組成物は下記の成分を含有する。各成分の含有量は、重量百分率で、以下のとおりである。
SiO2 54.2〜64%
Al2O3 11〜18%
CaO 20〜25.5%
MgO 0.3〜3.9%
Na2O+K2O 0.1〜2%
TiO2 0.1〜1.5%
鉄酸化物の合計量 0.1〜1%
Claims (13)
- 以下の成分を含有し、各成分の含有量が重量百分率で、以下の通りであるガラス繊維組成物であって、
SiO2 54.2〜64%
Al2O3 11〜18%
CaO 20〜25.5%
MgO 0.3〜3.9%
Na2O+K2O 0.1〜2%
TiO2 0.1〜1.5%
鉄酸化物の合計量 0.1〜1%
前記鉄酸化物は2価鉄酸化物を(FeOとして)含有し、重量百分率の比C1=FeO/(鉄酸化物−FeO)の範囲が1.25以上であり、且つ上記成分の合計含有量が97%を超えることを特徴とする、
ガラス繊維組成物。 - 重量百分率の比C2=(FeO+CaO−MgO)/SiO2の範囲が0.33を超え
ることを特徴とする、
請求項1に記載のガラス繊維組成物。 - 前記SiO2、Al2O3、CaO、MgO、Na2O、K2O、TiO2及び鉄酸化物の重量百分率の合計含有量が99%を超えることを特徴とする、
請求項1に記載のガラス繊維組成物。 - 前記FeOの重量比率で表される含有量の範囲が0.10%以上であることを特徴とする、
請求項1に記載のガラス繊維組成物。 - 以下の成分を含有し、各成分の含有量が重量百分率で、以下の通りであるガラス繊維組成物であって、
SiO2 57〜62%
Al2O3 12〜17%
CaO+MgO 21〜26.5%
CaO 20.5〜25%
MgO 0.3〜2.7%
Na2O+K2O 0.2〜2%
Na2O 0.1〜1.2%
K2O 0.1〜1.2%
TiO2 0.1〜1.5%
鉄酸化物の合計量 0.1〜0.8%
前記鉄酸化物は2価鉄酸化物を(FeOとして)含有し、重量百分率の比C1=FeO/(鉄酸化物−FeO)の範囲が1.25以上であり、且つ上記成分の合計含有量は99%を超えることを特徴とする、
請求項1に記載のガラス繊維組成物。 - 以下の成分を含有し、各成分の含有量が重量百分率で、以下の通りであるガラス繊維組成物であって、
SiO2 57.5〜61%
Al2O3 13〜15.5%
CaO 21〜24.5%
MgO 0.4%超え1%未満
Na2O+K2O 0.1〜2%
TiO2 0.1〜1.2%
鉄酸化物の合計量 0.1〜0.8%
前記鉄酸化物は2価鉄酸化物を(FeOとして)含有し、重量百分率の比C1=FeO/(鉄酸化物−FeO)の範囲が1.25以上であり、且つ上記成分の合計含有量が99.2%以上であることを特徴とする、
請求項1に記載のガラス繊維組成物。 - 以下の成分を含有し、各成分の含有量が重量百分率で、以下の通りであるガラス繊維組成物であって、
SiO2 57.5〜61%
Al2O3 13〜15.5%
CaO 21〜24.5%
MgO 0.4%超え1%未満
Na2O+K2O 0.1〜2%
TiO2 0.1〜1.2%
鉄酸化物の合計量 0.1〜0.8%
前記鉄酸化物は2価鉄酸化物を(FeOとして)含有し、重量百分率の比C1=FeO/(鉄酸化物−FeO)の範囲が1.25以上であり、且つ上記成分の合計含有量が99%を超えることを特徴とする、
請求項1に記載のガラス繊維組成物。 - 重量比率で表される含有量の範囲が0.4%未満のLi2Oを更に含有することを特徴
とする、
請求項1に記載のガラス繊維組成物。 - 重量比率で表される含有量の範囲が0.15〜0.65%のF2を更に含有することを
特徴とする、
請求項1に記載のガラス繊維組成物。 - P2O5の重量比率で表される含有量は、前記ガラス繊維組成物に対して0〜0.03%であることを特徴とする、
請求項1に記載のガラス繊維組成物。 - Li2Oの重量比率で表される含有量は、前記ガラス繊維組成物に対して0〜0.03%であることを特徴とする、
請求項1に記載のガラス繊維組成物。 - 請求項1〜11のいずれか1項に記載のガラス繊維組成物から製造された、
ガラス繊維。 - 請求項12に記載のガラス繊維を含むことを特徴とする、
複合材料。