JP6677433B2 - 熱交換器及び加熱炉の汚れ防止方法 - Google Patents
熱交換器及び加熱炉の汚れ防止方法 Download PDFInfo
- Publication number
- JP6677433B2 JP6677433B2 JP2018056370A JP2018056370A JP6677433B2 JP 6677433 B2 JP6677433 B2 JP 6677433B2 JP 2018056370 A JP2018056370 A JP 2018056370A JP 2018056370 A JP2018056370 A JP 2018056370A JP 6677433 B2 JP6677433 B2 JP 6677433B2
- Authority
- JP
- Japan
- Prior art keywords
- cleaning
- acid
- water
- dirt
- test
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
また、特許文献2では、被精製油の供給を停止したのち石油精製プラントに洗浄用灯軽油留分油を注入し、プラント内の滞油を洗浄用灯軽油留分油で置換し、置換した洗浄用灯軽油留分油はブローすることなくこれに洗浄剤を添加し、この洗浄液で石油精製プラント内を循環洗浄する洗浄方法が提案されている。
さらに、特許文献3では、酵素と界面活性剤を含む水溶液を用いる、石油精製プラントの石油分解プロセスに設置されている塔槽類や熱交換器の洗浄方法が提案されている。
さらに、特許文献5では、リン酸エステル系防食剤や多硫化物系防食剤と、分散剤とを併用して腐食生成物の付着を防止する方法が提案されている。
この、従来の技術とは全く異なる技術的思想に基づいて、運転開始〜定常運転段階の石油精製プラントの熱交換器や加熱炉の汚れを防止できることを見出したことは上記の通りであるが、停止中の石油精製プラントの熱交換器や加熱炉内を洗浄し汚れを除去する工程については、充分な検討がされておらず、この新たな汚れ防止剤を適用するに当たっては、従来の適用方法とは異なる、より効果的な適用方法を見出す必要があった。
このように、本発明者は、先に出願した初期処理工程と平常処理工程の前段階である、プラントを停止して熱交換器や加熱炉内を洗浄し汚れを除去する段階においても、効果的な防食被膜の形成方法を確立したことにより、石油精製プラントに設置された熱交換器や加熱炉の洗浄〜プラントの運転開始〜定常運転までの各段階で鉄系金属表面の防食を切れ目なく継続・維持することができるため、前記鉄系金属表面での硫化鉄の生成・付着を防止し、硫化鉄に前記有機物汚れが結合して汚れが成長することを防止することができる。
本発明の洗浄工程及び被膜形成工程の作用機構について、図1の模式図によって説明する。本発明の洗浄工程では、停止中の石油精製プラントの鉄系金属からなる熱交換器1の表面に堆積したアスファルテンやスラッジ等の有機物と硫化鉄との複合汚れ2を、溶媒3を用いて除去をする。その際、前記複合汚れ2を除去することで、鉄系金属からなる熱交換器1の清浄な面が露出した状態となる。ここに水溶性の防食剤を含む汚れ防止剤4を添加し、被膜形成工程を行うことで、汚れ防止剤4が親水性である鉄系金属からなる熱交換器1(あるいは図示しない加熱炉)の伝熱面に吸着し、熱交換器1の表面を覆うようにして防食被膜5が均一に形成される。そのため、運転中の石油精製プラントにおいても、鉄系金属からなる熱交換器1は防食被膜により硫化腐食を受け難くなる。その結果、硫化鉄が形成し難くなり、前記複合汚れの付着も防止されるため、伝熱効率の低下を防ぐことができる。
[洗浄工程]
本発明における洗浄工程とは、停止中の石油精製プラントにおいて、伝熱効率の低下の原因となるアスファルテンやスラッジ等の有機物と硫化鉄との複合汚れが堆積している鉄系金属表面に対し、溶媒を用いて該複合汚れを除去し、鉄系金属表面を清浄にする工程である。前記複合汚れを除去することで、上述の被膜形成工程において、鉄系金属表面に均一な防食被膜を形成することができ、鉄系金属表面における硫化鉄が形成し難くなり、伝熱効率の低下の原因となる前記複合汚れの付着を防止することができる。
[被膜形成工程]
本発明において、被膜形成工程とは、洗浄工程でアスファルテンやスラッジ等の有機物と硫化鉄との複合汚れを除去した鉄系金属表面に対し、水溶性の防食剤を含む汚れ防止剤を接触させて防食被膜を形成する工程である。
水溶性の防食剤を含む汚れ防止剤を接触させ、防食被膜を形成させる方法として特に限定はされないが、通常であれば、鉄系金属表面の前記複合汚れを洗浄液によって除去した後、洗浄液を系外へ排出した後、水溶性の防食剤を含む汚れ防止剤の溶液を系内に入れ、該汚れ防止剤を対象の鉄系金属表面を接触させ防食被膜を形成させる、もしくは洗浄工程の洗浄液中に該汚れ防止剤を添加し、対象の鉄系金属表面を接触させ、防食被膜を形成させる方法が挙げられる。
モノエチレン性不飽和カルボン酸のホモ重合体としては、例えば、アクリル酸重合体、メタクリル酸重合体、マレイン酸重合体、無水マレイン酸重合体の加水分解物、イタコン酸重合体、フマル酸重合体等が挙げられ、2種以上の異なるモノエチレン性不飽和カルボン酸の共重合体としては、アクリル酸とマレイン酸の共重合体、アクリル酸とイタコン酸の共重合体、マレイン酸とイタコン酸の共重合体、マレイン酸とフマル酸の共重合体、アクリル酸とイタコン酸とマレイン酸の三元共重合体、アクリル酸とイタコン酸とフマル酸の三元共重合体等が挙げられるが、好ましくは、ホモマレイン酸重合体およびマレイン酸と共重合可能なモノエチレン性不飽和単量体との共重合体、及びホモイタコン酸重合体およびイタコン酸と共重合可能なモノエチレン性不飽和単量体との共重合体である。
本発明を適用する際、前記汚れ防止剤を含んだ循環液の温度は0℃〜100℃が好ましく、より好ましくは5℃〜50℃である。温度が100℃以上においては、防食被膜の形成速度よりも腐食の進行速度の方が早くなり、0℃以下においては防食被膜の形成速度が遅くなる。
脱酸素剤としては、ジエチルヒドロキシルアミン、亜硫酸ナトリウム、ヒドラジン、エリソルビン酸、カルボヒドラジド等が挙げられる。これらは、本発明の汚れ防止剤に含有させるほか、別々に添加してもよい。
実施例に用いた装置を図3に示す。この装置は、ステンレス製のオートクレーブ31の蓋31aの中心に回転軸32が挿通されており、回転軸32には6枚タービン翼33が取り付けられている。また、回転軸32には軟鉄からなるテストピース34、テストピース35が着脱可能とされている。回転軸32は図示しない撹拌機で回転可能とされている。
(実施例1)
[汚れ付着処理1]
オートクレーブ31の蓋31aを開けて、原油250mlを入れ、そして回転軸32にあらかじめ重量を測定しておいたテストピース34、テストピース35(材質:軟鉄)を取り付けた後、蓋31aを閉め、オートクレーブ内の空気を窒素で置換した。撹拌機を駆動して回転軸32を500rpmの撹拌速度で回転させ、オートクレーブ31の周囲を図示しないマントルヒーターによって300℃に加熱し、96時間維持した。その後、室温まで冷却した後、蓋31aを開けてテストピース34、テストピース35を取り出し、オートクレーブ31内の溶液を廃棄し、オートクレーブ31内部をヘキサンで洗浄した。また、取り出したテストピース34、テストピース35をヘキサンで洗浄して原油を洗い流した。
[洗浄工程及び被膜形成工程]
テストピース34、35をオートクレーブ31の回転軸32に再び取り付けた。オートクレーブ31の内部に、水性の溶媒として温水を250mLと洗浄薬剤としてZymeFlow657(商品名、United Laboratories International社製)を20000ppm(製品換算)となるように添加した後、蓋31aを閉め、オートクレーブ内の空気を窒素で置換した。撹拌機を駆動して回転軸32を500rpmの撹拌速度で回転させ、オートクレーブ31の周囲を図示しないマントルヒーターによって105℃に加熱し、10時間維持した。その後、室温まで冷却した後、蓋31aを開け、汚れ防止剤として水溶性の防食剤である1−ヒドロキシエチリデン−1,1−ジホスホン酸(HEDP、Belclene660LA、BWA社製)をオートクレーブ内容液に対して1000ppm(有効成分換算)となるように添加した後、蓋31aを閉め、オートクレーブ内の空気を窒素で置換した。撹拌機を駆動して回転軸32を500rpmの撹拌速度で回転させ、25℃で48時間撹拌した。撹拌終了後、オートクレーブ31の蓋31aを開けて、オートクレーブ31内の溶液を廃棄し、オートクレーブ31内部を水で洗浄した。
[汚れ付着処理2]
オートクレーブ31の内部に、原油を250mL入れ、蓋31aを閉め、オートクレーブ内の空気を窒素で置換した。撹拌機を駆動して回転軸32を500rpmの撹拌速度で回転させ、オートクレーブ31の周囲を図示しないマントルヒーターによって300℃に加熱し、96時間維持した。その後、室温まで冷却した後、蓋31aを開けてテストピース34、35を取り出した。
取り出したテストピース34、35をヘキサンで洗浄して原油を洗い流し、乾燥後、重量を測定した。さらにヘキサン洗浄を行ったテストピースを3.5%塩酸に浸漬し、表面の腐食生成物を溶解除去したのち、乾燥後の重量を測定した。
下記式により、テストピース毎の付着量、腐食減量を算出し、テストピース2枚の数値の平均値を試験結果とした。
付着量(%)={(ヘキサン洗浄後重量(g)−塩酸洗浄後重量(g))/テストピース初期重量(g)}×100
腐食減量(%)={(テストピース初期重量(g)−塩酸洗浄後重量(g))/テストピース初期重量(g)}×100
[汚れ付着処理1]
実施例1と同様に試験を行った。
[洗浄工程及び被膜形成工程]
汚れ防止剤である水溶性の防食剤を、2−ホスホノブタン−1,2,4−トリカルボン酸(PBTC、Belclene650、BWA社製)に変更した以外は、実施例1と同様に試験を行った。
[汚れ付着処理2]
実施例1と同様に試験を行った。
[汚れ付着処理1]
実施例1と同様に試験を行った。
[洗浄工程及び被膜形成工程]
汚れ防止剤である水溶性の防食剤を、ビス(ポリ−2−カルボキシエチル)ホスフィン酸(BELSPERSE164、BWA社製)に変更した以外は、実施例1と同様に試験を行った。
[汚れ付着処理2]
実施例1と同様に試験を行った。
[汚れ付着処理1]
実施例1と同様に試験を行った。
[洗浄工程及び被膜形成工程]
汚れ防止剤である水溶性の防食剤を、ポリマレイン酸(分子量2000、Belclene200LA、BWA社製)に変更した以外は、実施例1と同様に試験を行った。
[汚れ付着処理2]
実施例1と同様に試験を行った。
[汚れ付着処理1]
実施例1と同様に試験を行った。
[洗浄工程及び被膜形成工程]
汚れ防止剤である水溶性の防食剤を、りん酸(試薬、和光純薬工業社製)に変更した以外は、実施例1と同様に試験を行った。
[汚れ付着処理2]
実施例1と同様に試験を行った。
[汚れ付着処理1]
実施例1と同様に試験を行った。
[洗浄工程及び被膜形成工程]
汚れ防止剤である水溶性の防食剤を添加しなかった以外は、実施例1と同様に試験を行った。
[汚れ付着処理2]
実施例1と同様に試験を行った。
なお、比較例1の付着物をSEM−EDXによって表面分析したところ、図4に示すように、鉄及び硫黄が大量に検出されることから、付着物は硫化鉄主体であることが分かった。
(実施例6)
[汚れ付着処理1]
実施例1と同様に試験を行った。
[洗浄工程及び被膜形成工程]
洗浄薬剤を、ポリオキシエチレンラウリルエーテル(エマルゲン150、HLB=18.4、花王社製)に変更し、また、その添加量を、1000ppm(有効成分換算)に変更した以外は、実施例1と同様に試験を行った。
[汚れ付着処理2]
実施例1と同様に試験を行った。
[汚れ付着処理1]
実施例1と同様に試験を行った。
[洗浄工程及び被膜形成工程]
汚れ防止剤である水溶性の防食剤を、2−ホスホノブタン−1,2,4−トリカルボン酸に変更した以外は、実施例6と同様に試験を行った。
[汚れ付着処理2]
実施例1と同様に試験を行った。
[汚れ付着処理1]
実施例1と同様に試験を行った。
[洗浄工程及び被膜形成工程]
汚れ防止剤である水溶性の防食剤を添加しなかった以外は、実施例6と同様に試験を行った。
[汚れ付着処理2]
実施例1と同様に試験を行った。
(実施例8)
[汚れ付着処理1]
実施例1と同様に試験を行った。
[洗浄工程及び被膜形成工程]
汚れ付着処理1終了後に取り出したテストピース34、テストピース35を台座に固定し、汚れ防止剤として水溶性の防食剤である1−ヒドロキシエチリデン−1,1−ジホスホン酸を1000ppm(有効成分換算)となるように添加した高圧水を用いて、圧力:2MPa、洗浄温度:25℃、洗浄時間:10分間、続いて圧力:1MPa、洗浄温度:25℃、洗浄時間:20分間の条件で高圧水洗浄を行った。
[汚れ付着処理2]
テストピース34、35を台座から取り外してオートクレーブ31の回転軸32に再び取り付けた。オートクレーブ31の内部に、原油を250mL入れ、蓋31aを閉め、オートクレーブ内の空気を窒素で置換した。撹拌機を駆動して回転軸32を500rpmの撹拌速度で回転させ、オートクレーブ31の周囲を図示しないマントルヒーターによって300℃に加熱し、96時間維持した。その後、室温まで冷却した後、蓋31aを開けてテストピース34、35を取り出した。
取り出したテストピース34、35をヘキサンで洗浄して原油を洗い流し、乾燥後、重量を測定した。さらにヘキサン洗浄を行ったテストピースを3.5%塩酸に浸漬し、表面の腐食生成物を溶解除去したのち、乾燥後の重量を測定した。前記の式に従って、付着量(%)と腐食減量(%)を算出した。
[汚れ付着処理1]
実施例1と同様に試験を行った。
[洗浄工程及び被膜形成工程]
汚れ防止剤である水溶性の防食剤を、2−ホスホノブタン−1,2,4−トリカルボン酸に変更した以外は、実施例8と同様に試験を行った。
[汚れ付着処理2]
実施例8と同様に試験を行った。
[汚れ付着処理1]
実施例1と同様に試験を行った。
[洗浄工程及び被膜形成工程]
汚れ防止剤である水溶性の防食剤を、ビス(ポリ−2−カルボキシエチル)ホスフィン酸に変更した以外は、実施例8と同様に試験を行った。
[汚れ付着処理2]
実施例8と同様に試験を行った。
[汚れ付着処理1]
実施例1と同様に試験を行った。
[洗浄工程及び被膜形成工程]
汚れ防止剤である水溶性の防食剤を、ポリマレイン酸に変更した以外は、実施例8と同様に試験を行った。
[汚れ付着処理2]
実施例8と同様に試験を行った。
[汚れ付着処理1]
実施例1と同様に試験を行った。
[洗浄工程及び被膜形成工程]
汚れ防止剤である水溶性の防食剤を、りん酸に変更した以外は、実施例8と同様に試験を行った。
[汚れ付着処理2]
実施例8と同様に試験を行った。
[汚れ付着処理1]
実施例1と同様に試験を行った。
[洗浄工程及び被膜形成工程]
汚れ防止剤である水溶性の防食剤を、高圧水に添加しなかった以外は、実施例8と同様に試験を行った。
[汚れ付着処理2]
実施例8と同様に試験を行った。
(実施例13)
[汚れ付着処理1]
実施例1と同様に試験を行った。
[洗浄工程及び被膜形成工程]
テストピース34、35をオートクレーブ31の回転軸32に再び取り付けた。オートクレーブ31の内部に、油性の溶媒として軽油80%とアルキルベンゼン系芳香族溶剤であるハイゾール100(商品名、JXTGエネルギー社製)20%の混合溶剤を250mLと、洗浄薬剤としてポリオキシアルキレンアルキルエーテルサルフェートアンモニウム(ハイテノール08E、第一工業製薬社製)を有効成分換算で1000ppmとなるように添加した後、蓋31aを閉め、オートクレーブ内の空気を窒素で置換した。撹拌機を駆動して回転軸32を500rpmの撹拌速度で回転させ、オートクレーブ31の周囲を図示しないマントルヒーターによって105℃に加熱し、10時間維持した。その後、室温まで冷却した後、蓋31aを開け、汚れ防止剤として水溶性の防食剤である1−ヒドロキシエチリデン−1,1−ジホスホン酸をオートクレーブ内容液に対して1000ppm(有効成分換算)となるように添加した後、蓋31aを閉め、オートクレーブ内の空気を窒素で置換した。撹拌機を駆動して回転軸32を500rpmの撹拌速度で回転させ、25℃で48時間撹拌した。撹拌終了後、オートクレーブ31の蓋31aを開けて、オートクレーブ31内の溶液を廃棄し、オートクレーブ31内部をヘキサンで洗浄した。
[汚れ付着処理2]
実施例1と同様に試験を行った。
[汚れ付着処理1]
実施例1と同様に試験を行った。
[洗浄工程及び被膜形成工程]
汚れ防止剤である水溶性の防食剤を添加しなかった以外は、実施例13と同様に試験を行った。
[汚れ付着処理2]
実施例1と同様に試験を行った。
[汚れ付着処理1]
実施例1と同様に試験を行った。
[洗浄工程及び被膜形成工程]
汚れ防止剤である水溶性の防食剤を、油溶性の防食剤である2−エチルヘキシルアシッドホスフェート(JP−508、城北化学工業社製)に変更した以外は、実施例13と同様に試験を行った。
[汚れ付着処理2]
実施例1と同様に試験を行った。
21、23、25…予熱交換器
22…デソルター、24…プレフラッシュ塔、26…加熱炉、27…蒸留塔、28…ポンプ
31…オートクレーブ、31a…蓋、32…回転軸、33…6枚タービン翼、34、35…テストピース
Claims (4)
- 石油精製プラントにおいて油性流体が流れる熱交換器及び加熱炉の伝熱面内表面汚れを防止する汚れ防止方法であって、停止中の石油精製プラントの熱交換器及び加熱炉の汚れを、溶媒を用いて除去する洗浄工程と、該洗浄工程後または該洗浄工程と同時に有機ホスホン酸、ホスホノカルボン酸、ホスフィノポリカルボン酸、カルボン酸重合体及び無機リン酸化合物からなる群より選ばれる1種類以上を含む水溶性の防食剤を用いて防食被膜を形成する被膜形成工程の、2工程を有することを特徴とする汚れ防止方法。
- 前記洗浄工程で用いられる溶媒が水性または油性であることを特徴とする請求項1記載の汚れ防止方法。
- 前記洗浄工程で用いられる溶媒が水であることを特徴とする請求項1又は2記載の汚れ防止方法。
- 前記洗浄工程が、水を溶媒として用いた物理洗浄または化学洗浄のいずれかであることを特徴とする請求項3記載の汚れ防止方法。