JP6442925B2 - 水素化nbrの重合体溶液の濃縮方法 - Google Patents
水素化nbrの重合体溶液の濃縮方法 Download PDFInfo
- Publication number
- JP6442925B2 JP6442925B2 JP2014171252A JP2014171252A JP6442925B2 JP 6442925 B2 JP6442925 B2 JP 6442925B2 JP 2014171252 A JP2014171252 A JP 2014171252A JP 2014171252 A JP2014171252 A JP 2014171252A JP 6442925 B2 JP6442925 B2 JP 6442925B2
- Authority
- JP
- Japan
- Prior art keywords
- polymer solution
- evaporator
- concentrating
- hydrogenated nbr
- spray
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(1) 蒸発缶内の重合体溶液を濃縮する重合体溶液の濃縮方法であって、前記蒸発缶は、前記蒸発缶内を減圧するための減圧手段と、前記重合体溶液を前記蒸発缶内で噴霧体とする噴霧手段と、前記重合体溶液を前記噴霧手段へ供給するための循環手段と、を備え、前記噴霧体は、前記重合体溶液の液面へ向けて、中空体状に噴霧されることを特徴とする、重合体溶液の濃縮方法、
(2) 前記重合体溶液の液面の中心を通る最短径の30%の長さを半径とする円の内部を前記重合体溶液の液面の中心部としたときに、前記中心部での前記噴霧体の最大噴霧量が、前記重合体溶液の液面全体での前記噴霧体の最大噴霧量に対し、40質量%以下であることを特徴とする、(1)記載の重合体溶液の濃縮方法、
(3) 前記中空体状が、中空錐体状であることを特徴とする、(1)または(2)に記載の重合体溶液の濃縮方法、
(4) 前記噴霧体における液滴のザウター平均粒子径が900μm以上2000μm以下であることを特徴とする、(1)〜(3)のいずれかに記載の重合体溶液の濃縮方法、
(5) 前記蒸発缶は、攪拌翼を備え無いことを特徴とする、(1)〜(4)のいずれかに記載の重合体溶液の濃縮方法
が提供される。
なお、図4に、重合体溶液の液面における噴霧体量の様子の一例を示す。
ザウター平均粒子径=Σ(ni・di3)/Σ(ni・di2)
(式中、diは成分iの粒子径、niは成分iの粒子数を示す。)。
本発明において、濃縮を行う重合体溶液に含まれる重合体は特に限定されないが、例えば、重合体の種類としては、スチレン−ブタジエン共重合体(SBR)、ニトリルゴム、アクリル樹脂、ポリアセタール樹脂、塩化ビニル樹脂等が挙げられる。これらのなかでも、本発明はニトリルゴムに好適に用いることができる。
ニトリルゴムとしては、特に限定されないが、たとえば、α,β−エチレン性不飽和ニトリル単量体、共役ジエン単量体、および、必要に応じて用いられるこれらと共重合可能なその他の単量体を共重合することで得られる共重合体が挙げられる。
実施例及び比較例において得られた濃縮操作後の重合体溶液1,000gを、200メッシュ金網にて濾過し、金網上に残るCGの乾燥重量を測定し、試料の固形分全量に対する割合を求めた。
噴霧体における液滴のザウター平均粒子径は、位相ドップラー粒子分析計(「PDI」、西華産業社製)を用いて測定した。
攪拌機付きタンクに、オレイン酸カリウム2部、イオン交換水180部、アクリロニトリル37部、t−ドデシルメルカプタン0.5部を順次仕込んだ。反応器内部を窒素で置換した後、ブタジエン63部を封入した。反応器を10℃に冷却して、クメンハイドロパーオキサイド0.01部、硫酸第一鉄0.01部を添加した。次に反応器を10℃に保ったまま16時間攪拌し、内容物をよく混合した。その後、反応器内へ10%のハイドロキノン水溶液を添加して重合停止させた。重合転化率は90%であった。その重合反応液から未反応単量体を除去し、水素化反応に供するアクリロニトリル−ブタジエン共重合体(NBR)の重合体溶液を得た。
噴霧器26として、中空円錐体状に噴霧することができ、噴射角度120°、液滴径1500μmで噴射可能なノズルを用い、また、コンプレッサー24により上記系を−90kPaGに減圧し、さらに、蒸発缶4内の重合体溶液の温度を40℃に維持するために、外部加熱装置12(外部熱交換器)の出口における重合体溶液の温度を90℃とした以外は、実施例1と同様に重合体溶液濃縮を行った。
噴霧器として、充円錐体状に噴霧することができ(即ち、蒸発缶4内の重合体溶液の液面の全体に噴霧することができ)、噴射角度45°、液滴径850μmで噴射可能なノノズルを備える噴霧器28が設けられた濃縮装置30を用い(図2参照)、また、コンプレッサー24により上記系を−95kPaGに減圧した以外は、実施例1と同様に重合体溶液の濃縮を行ったが、発泡が激しく途中で濃縮操作を停止した。
噴霧器として充円錐体状に噴霧することができ(即ち、蒸発缶4内の重合体溶液の液面の全体に噴霧することができ)、噴射角度120°、液滴径850μmで噴射可能なノズルを備える噴霧器28が設けられた濃縮装置30を用い(図2参照)、また、コンプレッサー24により上記系を−88kPaGに減圧した以外は、実施例1と同様に重合体溶液の濃縮を行ったが、発泡が激しく途中で濃縮操作を停止した。
濃縮装置として噴霧器26を備えず、外部加熱装置12(外部熱交換器)により加熱された重合体溶液を重合体溶液フィードライン14により蒸発缶4内の液相に戻す構成とした濃縮装置32を用い(図3参照)、また、コンプレッサー24により上記系を−90kPaGに減圧した以外は、実施例1と同様に重合体溶液の濃縮を行った。なお、発泡が激しく、濃縮操作の中断が多発した。
Claims (4)
- 蒸発缶内の水素化NBRの重合体溶液を濃縮する水素化NBRの重合体溶液の濃縮方法であって、
前記蒸発缶は、前記蒸発缶内を減圧するための減圧手段と、
前記水素化NBRの重合体溶液を前記蒸発缶内で噴霧体とする噴霧手段と、
前記水素化NBRの重合体溶液を前記噴霧手段へ供給するための循環手段と、
を備え、
前記噴霧体における液滴のザウター平均粒子径が900μm以上2000μm以下であり、前記噴霧体は、前記水素化NBRの重合体溶液の液面へ向けて、中空体状に噴霧されることを特徴とする、水素化NBRの重合体溶液の濃縮方法。 - 前記重合体溶液の液面の中心を通る最短径の30%の長さを半径とする円の内部を前記重合体溶液の液面の中心部としたときに、
前記中心部での前記噴霧体の最大噴霧量が、前記重合体溶液の液面全体での前記噴霧体の最大噴霧量に対し、40質量%以下であることを特徴とする、請求項1記載の水素化NBRの重合体溶液の濃縮方法。 - 前記中空体状が、中空錐体状であることを特徴とする、請求項1または2に記載の水素化NBRの重合体溶液の濃縮方法。
- 前記蒸発缶は、攪拌翼を備え無いことを特徴とする、請求項1〜3のいずれかに記載の水素化NBRの重合体溶液の濃縮方法。