JP6379467B2 - 光硬化性組成物およびこれを用いて形成したフィルム - Google Patents
光硬化性組成物およびこれを用いて形成したフィルム Download PDFInfo
- Publication number
- JP6379467B2 JP6379467B2 JP2013201597A JP2013201597A JP6379467B2 JP 6379467 B2 JP6379467 B2 JP 6379467B2 JP 2013201597 A JP2013201597 A JP 2013201597A JP 2013201597 A JP2013201597 A JP 2013201597A JP 6379467 B2 JP6379467 B2 JP 6379467B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- photocurable composition
- photopolymerization initiator
- meth
- acrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
表1に示す材料を混合攪拌して光硬化性組成物を調整した。このとき、固形分比率が70質量%となるように調製を行った。なお、表1中の数値の単位は重量部である。
・MEK:メチルエチルケトン
・LUCIRIN TPO:(2,4,6−トリメチルベンゾイル)−ジフェニル−ホスフィンオキシド(BASF社製)
・Irg127:2−ヒドロキシ−1−{4−[4−(2−ヒドロキシ−2−メチル−プロピオニル)−ベンジル]−フェニル}−2−メチル−プロパン−1−オン(BASF社製)
支持体上に、上記で調整した光硬化性組成物を、アプリケーターにて乾燥後の膜厚が50μmになるように塗布し、塗膜を100℃のオーブンにて2分間乾燥させ、高圧水銀灯により300mJ/cm2の紫外線を照射することにより、乾燥させた塗膜を硬化させて、大気下にて硬化膜を形成した。その後、硬化膜を支持体から剥離し、フィルムを作製した。
初期黄変度に関して、分光光度計U−4100(日立ハイテクノロジーズ社製)を用い、JISK7373に準拠して測定を行った。
表面タック性に関して、指を押し当て、粘着性が有る場合を×とし、無い場合を○とした。
Claims (5)
- 光硬化性組成物であって、
1分子中に2個以上の(メタ)アクリロイル基を分子中に有する多官能性モノマーを含有するウレタンアクリレートと、
光重合開始剤と、
溶剤とを含有し、
前記光重合開始剤として、(2,4,6−トリメチルベンゾイル)ジフェニルホスフィンオキシドと、2−ヒドロキシ−1−{4−[4−(2−ヒドロキシ−2−メチル−プロピオニル)−ベンジル]−フェニル}−2−メチル−プロパン−1−オンを用い、
前記光重合開始剤の添加比率が、前記アクリレートに対して1質量%以上10質量%以下であることを特徴とする、光硬化性組成物。 - 前記光重合開始剤として用いられる(2,4,6−トリメチルベンゾイル)ジフェニルホスフィンオキシドの比率が、前記光重合開始剤全体に対して50質量%以上70質量%以下であることを特徴とする、請求項1に記載の光硬化性組成物。
- ロール化可能な支持体上に、請求項1または2に記載の光硬化性組成物を塗布し、塗膜を乾燥後に大気下にて光硬化を行って硬化膜を形成し、支持体を剥離して得ることを特徴とする、フィルム。
- 前記硬化膜の膜厚が30μm以上100μm以下であることを特徴とする、請求項3に記載のフィルム。
- 初期黄変度が1.5以下であることを特徴とする、請求項3または4に記載のフィルム。