JP6354124B2 - 反射防止フィルム - Google Patents
反射防止フィルムInfo
- Publication number
- JP6354124B2 JP6354124B2 JP2013131745A JP2013131745A JP6354124B2 JP 6354124 B2 JP6354124 B2 JP 6354124B2 JP 2013131745 A JP2013131745 A JP 2013131745A JP 2013131745 A JP2013131745 A JP 2013131745A JP 6354124 B2 JP6354124 B2 JP 6354124B2
- Authority
- JP
- Japan
- Prior art keywords
- antireflection film
- refractive index
- acrylate
- meth
- low refractive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
ここで、反射防止フィルムにおける反射防止設計中心波長λは通常、人間が最も感知しやすい緑色の波長帯(例えば、550nm)が選ばれる。
一般式(1):Si(OR)4
一般式(1)において、Rは直鎖状または分岐状アルキル基であり、一般式(1)で表される有機シリコーン化合物としては、Si(OCH3)4、Si(OC2H5)4、Si(OC3H7)4、Si〔OCH(CH3)2)〕4、Si(OC4H9)4等が例示でき、それらを単独に、あるいは2種類以上併せて用いてもよい。
(ハードコート層形成用塗液)
ジペンタエリスリトールヘキサアクリレート(商品名:A−DPH、新中村化学工業株式会社製)25質量部、ペンタエリスリトールテトラアクリレート(商品名:A−TMMT、新中村化学工業株式会社製)25質量部、ウレタンアクリレート(商品名:UA−306H、共栄社化学株式会社製)50質量部、イルガキュア184(BASF社製(光重合開始剤))5質量部を用い、これをアセトンに溶解してハードコート層形成塗液を調製した。
(低屈折率層形成用塗液1)
多孔質シリカ微粒子分散液(平均粒径60nm、固形分20%、溶剤:メチルイソブチルケトン)70質量部、ペンタエリスリトールトリアクリレート(商品名:A−TMM−3LM−N、新中村化学株式会社製)6質量部、重合開始剤(BASF社製、商品名;イルガキュア184)0.9質量部、TSF4460(商品名、モメンティブ・パフォーマンス・マテリアルズ(株)製:アルキルポリエーテル変性シリコーンオイル)0.6質量部を、溶媒であるメチルイソブチルケトン80重量部で希釈して低屈折率層形成塗液を調製した。
(低屈折率層形成用塗液2)
多孔質シリカ微粒子分散液(平均粒径60nm、固形分20%、溶剤:メチルイソブチルケトン)70質量部、ペンタエリスリトールトリアクリレート(商品名:A−TMM−3LM−N、新中村化学株式会社製)6質量部、重合開始剤(BASF社製、商品名;イルガキュア184)0.9質量部、TSF4460(商品名、モメンティブ・パフォーマンス・マテリアルズ(株)製:アルキルポリエーテル変性シリコーンオイル)0.3質量部を、溶媒であるメチルイソブチルケトン79.7重量部で希釈して低屈折率層形成塗液を調製した。
(低屈折率層形成用塗液3)
多孔質シリカ微粒子分散液(平均粒径60nm、固形分20%、溶剤:メチルイソブチルケトン)45質量部、ペンタエリスリトールトリアクリレート(商品名:A−TMM−3LM−N、新中村化学株式会社製)6質量部、重合開始剤(BASF社製、商品名;イルガキュア184)0.9質量部、TSF4460(商品名、モメンティブ・パフォーマンス・マテリアルズ(株)製:アルキルポリエーテル変性シリコーンオイル)0.6質量部を、溶媒であるメチルイソブチルケトン54.2重量部で希釈して低屈折率層形成塗液を調製した。
(低屈折率層形成用塗液4)
多孔質シリカ微粒子分散液(平均粒径60nm、固形分20%、溶剤:メチルイソブチルケトン)70質量部、ジペンタエリスリトールヘキサアクリレート(商品名:A−DPH、新中村化学工業株式会社製)6質量部、重合開始剤(BASF社製、商品名;イルガキュア184)0.9質量部、TSF4460(商品名、モメンティブ・パフォーマンス・マテリアルズ(株)製:アルキルポリエーテル変性シリコーンオイル)0.6質量部を、溶媒であるメチルイソブチルケトン80重量部で希釈して低屈折率層形成塗液を調製した。
(低屈折率層形成用塗液5)
多孔質シリカ微粒子分散液(平均粒径60nm、固形分20%、溶剤:メチルイソブチルケトン)120質量部、ペンタエリスリトールトリアクリレート(商品名:A−TMM−3LM−N、新中村化学株式会社製)6質量部、重合開始剤(BASF社製、商品名;イルガキュア184)0.9質量部、TSF4460(商品名、モメンティブ・パフォーマンス・マテリアルズ(株)製:アルキルポリエーテル変性シリコーンオイル)0.6質量部を、溶媒であるメチルイソブチルケトン131.6重量部で希釈して低屈折率層形成塗液を調製した。
(低屈折率層形成用塗液6)
多孔質シリカ微粒子分散液(平均粒径60nm、固形分20%、溶剤:メチルイソブチルケトン)70質量部、ペンタエリスリトールトリアクリレート(商品名:A−TMM−3LM−N、新中村化学株式会社製)6質量部、重合開始剤(BASF社製、商品名;イルガキュア184)0.9質量部を、溶媒であるメチルイソブチルケトン79.4重量部で希釈して低屈折率層形成塗液を調製した。
(低屈折率層形成用塗液7)
多孔質シリカ微粒子分散液(平均粒径60nm、固形分20%、溶剤:メチルイソブチルケトン)70質量部、ライトアクリレートBP−4PA(共栄社科学(株)製)6質量部、重合開始剤(BASF社製、商品名;イルガキュア184)0.9質量部、TSF4460(商品名、モメンティブ・パフォーマンス・マテリアルズ(株)製:アルキルポリエーテル変性シリコーンオイル)0.6質量部を、溶媒であるメチルイソブチルケトン80重量部で希釈して低屈折率層形成塗液を調製した。
(ハードコート層の形成)
トリアセチルセルロースフィルム(富士フィルム製:膜厚60μm)の片面にハードコート層形成用塗液を塗布し、65℃・30秒オーブンで乾燥し、乾燥後、紫外線照射装置(フュージョンUVシステムジャパン、光源Hバルブ)を用いて照射線量200mJ/m2で紫外線照射をおこなうことにより乾燥膜厚5μmの透明なハードコート層を形成させた。ハードコート層の屈折率は1.52であった。
(低屈折率層の形成)
上記方法にて形成した高屈折率層上に低屈折率層形成用塗液を乾燥後の膜厚が105nmとなるように塗布した。紫外線照射装置(フュージョンUVシステムジャパン、光源Hバルブ)を用いて照射線量300mJ/m2で紫外線照射をおこなって硬化させて低屈折率層を形成し、反射防止フィルムを作製した。
実施例および比較例に係る反射防止フィルムは、具体的には次のように行った。
実施例1は、ハードコート層においては<調製例1>の塗液を用い<形成例1>の手法にて製膜を行い、低屈折率層においては<調製例2>の塗液を用い<形成例2>の手法にて製膜を行い、反射防止フィルムを形成した例である。
実施例2は、ハードコート層においては<調製例1>の塗液を用い<形成例1>の手法にて製膜を行い、低屈折率層においては<調製例3>の塗液を用い<形成例2>の手法にて製膜を行い、反射防止フィルムを形成した例である。
実施例3は、ハードコート層においては<調製例1>の塗液を用い<形成例1>の手法にて製膜を行い、低屈折率層においては<調製例4>の塗液を用い<形成例2>の手法にて製膜を行い、反射防止フィルムを形成した例である。
実施例4は、ハードコート層においては<調製例1>の塗液を用い<形成例1>の手法にて製膜を行い、低屈折率層においては<調製例5>の塗液を用い<形成例2>の手法にて製膜を行い、反射防止フィルムを形成した例である。
参考例5は、ハードコート層においては<調製例1>の塗液を用い<形成例1>の手法にて製膜を行い、低屈折率層においては<調製例6>の塗液を用い<形成例2>の手法にて製膜を行い、反射防止フィルムを形成した例である。
比較例1は、ハードコート層においては<調製例1>の塗液を用い<形成例1>の手法にて製膜を行い、低屈折率層においては<調製例7>の塗液を用い<形成例2>の手法にて製膜を行い、反射防止フィルムを形成した例である。
比較例2は、ハードコート層においては<調製例1>の塗液を用い<形成例1>の手法にて製膜を行い、低屈折率層においては<調製例8>の塗液を用い<形成例2>の手法にて製膜を行い、反射防止フィルムを形成した例である。
実施例1から実施例4、参考例5、及び比較例1から比較例2で得られた反射防止フィルムについて、以下の方法で評価を行った。
作製した反射防止フィルムに対し、塗布膜の面内均一性を評価した。塗布膜の面内均一性は、作成した反射防止フィルムの低屈折率層の形成されていない面につや消し黒色塗料を塗布し、反射防止の処置を行った後に、目視にて評価を行った。判定基準を以下に示す(冒頭の記号(○、×)は、表1中の記号に対応する)。
×:ムラあり
(ブリードアウト)
作製した反射防止フィルムの塗工表面をティッシュペーパー〔エリエール社製〕で拭取り、塗工表面において拭き取った箇所と拭き取ってない箇所を蛍光灯下で目視にて確認することによりブリードアウトの有無を評価した。判定基準を以下に示す(冒頭の記号(○、×)は、表1中の記号に対応する)。
×:ブリードあり(拭き取った箇所が目視により確認できる)
(静摩擦係数μs)
作製した反射防止フィルムに対し、塗布膜の金属平滑面に対する静摩擦係数を評価した。平滑面に静置した反射防止フィルムを被試験体とし、当該被試験体に対し、摩擦計〔TRIBOGEAR、TYPE94i−II:新東科学株式会社製〕を静置した反射防止フィルムの表面上に置き測定を行った。測定結果は、同測定を5回行った平均値である。当該摩擦計のスライダー(接触子)には、ハードクロム処理黄銅(40g)、接触面積は12cm2であるものを使用した。
作製した反射防止フィルムに対し、塗布膜の表面粗さRaを評価した。原子間力顕微鏡AFM(NanoScopeIIIa DimensionSeriese Tapping mode AFM;日本ビーコ株式会社)を用い走査範囲1μm×1μmにて測定を行った。
塗布膜の機械強度は、低屈折率層表面をスチールウール〔ボンスター#0000:日本スチールウール(株)製〕により200g/cm2、300g/cm2、400g/cm2、500g/cm2でそれぞれ10回擦り、傷の有無を目視評価した(スチールウール試験)。判定基準を以下に示す(冒頭の記号(○、△、×)は、表1中の記号に対応する)。
△:薄く傷あり
×:傷あり。
得られた反射防止フィルムの低屈折率層表面について、自動分光光度計(日立製作所製、U−4100)を用い、入射角5°における分光反射率を測定した。また、得られた分光反射率曲線からJISR3106に従って平均視感反射率を求めた。なお、測定の際には透明支持体であるトリアセチルセルロースフィルムのうち低屈折率層の形成されていない面につや消し黒色塗料を塗布し、反射防止の処置を行った。
11…透明支持体
12…ハードコート層
13…低屈折率層
Claims (5)
- 透明支持体上にハードコート層と低屈折率層を順に積層した反射防止フィルムであって、
前記低屈折率層が、多孔質シリカ微粒子(A)と、ペンタエリスリトールトリアクリレート及びジペンタエリスリトールヘキサアクリレートのいずれかであるバインダ樹脂(B)と、重合開始剤と、アルキルポリエーテル変性シリコーンオイルとを含有する塗液の硬化膜よりなり、
前記塗液における前記多孔質シリカ微粒子(A)と前記バインダ樹脂(B)との固形分質量比(A):(B)が、70:30〜60:40であり、
前記反射防止フィルムの表面粗さRaが、1.12nm以上であって3.0nmより小さく、
前記低屈折率層表面の金属平滑面に対する静摩擦係数が0.16から0.22までの範囲内であり、
前記塗液における前記アルキルポリエーテル変性シリコーンオイルの添加量が、前記バインダ樹脂(B)の固形分100重量部に対して5重量部以上10重量部以下であることを特徴とする、反射防止フィルム。 - 前記反射防止フィルム表面の平均視感反射率が、0.1%以上1.0%以下の範囲内である、請求項1に記載の反射防止フィルム。
- 請求項1または2に記載の反射防止フィルムを備える、偏光板。
- 請求項1または2に記載の反射防止フィルムを備える、タッチパネル。
- 請求項1または2に記載の反射防止フィルムを備える、表示装置。