JP6231800B2 - 微細通路を備えた熱交換器用Al部材及びその製造方法 - Google Patents
微細通路を備えた熱交換器用Al部材及びその製造方法 Download PDFInfo
- Publication number
- JP6231800B2 JP6231800B2 JP2013150007A JP2013150007A JP6231800B2 JP 6231800 B2 JP6231800 B2 JP 6231800B2 JP 2013150007 A JP2013150007 A JP 2013150007A JP 2013150007 A JP2013150007 A JP 2013150007A JP 6231800 B2 JP6231800 B2 JP 6231800B2
- Authority
- JP
- Japan
- Prior art keywords
- brazing
- groove
- passage
- mass
- brazing sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
◎:溝が全く封止されていない合格レベル
○:一部の溝の断面積が狭くなっているレベル
△:一部の溝に封止が生じたレベル
×:多くの溝に封止が生じた不合格レベル
<溝頂部のフィレット形成状況の評価基準>
◎:全ての溝に均一にフィレットを形成した合格レベル
○:一部でフィレット形状の乱れがあるレベル
△:一部でフィレット切れが発生したレベル
×:フィレット切れが多く発生した不合格レベル
6 Al芯材 8 Al合金ろう材
10 ブレージングシート 12 積層物
14 ろう付け製品 16 通孔
18 フィレット 20 ろう材層
Claims (6)
- 溝断面積が0.2mm2 以下となる通路形成用の溝を所定パターンで板面に形成してなるAl板材と、Al芯材に対して、Si:3.5〜13質量%と共に、Li:0.004〜0.1質量%、Be:0.005〜0.04質量%、Ba:0.007〜0.05質量%、Ca:0.005〜0.03質量%及びMg:0.05〜0.4質量%のうちの少なくとも何れか1種を含むAl合金ろうからなるろう材層を所定厚さで一体的に形成してなるブレージングシートとを、フラックスを塗布することなく、該Al板材の溝形成面と該ブレージングシートのろう材層側の面とが対向するように積層して、該Al板材の通路形成用溝を該ブレージングシートにて覆蓋した後、それらAl板材及びブレージングシートの積層物を加熱して、該ブレージングシートのろう材層部位を溶融せしめて、該Al板材における前記通路形成用溝の両側部の頂部に、前記ブレージングシートのAl芯材を接合せしめることにより、微細な通路が内部に形成されるようにしたことを特徴とする微細通路を備えた熱交換器用Al部材の製造方法。
- 前記通路形成用溝上に位置する前記ブレージングシートのろう材層が、該通路形成用溝の体積の60%以下の体積を与える厚さにおいて、形成されている請求項1に記載の微細通路を備えた熱交換器用Al部材の製造方法。
- 前記ブレージングシートのろう材層を与える前記Al合金ろうが、3.5〜6質量%のSiを含有していると共に、前記通路形成用溝上に位置する該ブレージングシートのろう材層が、該通路形成用溝の体積の100%以下の体積を与える厚さにおいて、形成されている請求項1に記載の微細通路を備えた熱交換器用Al部材の製造方法。
- 前記積層物の加熱によるろう付け接合操作が、酸素濃度が50ppm以下の不活性ガス雰囲気中において、実施されることを特徴とする請求項1乃至請求項3の何れか1項に記載の微細通路を備えた熱交換器用Al部材の製造方法。
- 前記ブレージングシートのろう材層を与える前記Al合金ろうが、更に、0.004〜0.2質量%のBiを含有している請求項1乃至請求項4の何れか1項に記載の微細通路を備えた熱交換器用Al部材の製造方法。
- 前記ブレージングシートを構成する前記Al芯材が、合金成分として、0.2〜1.3質量%のMgを含有するAl合金にて構成されている請求項1乃至請求項5の何れか1項に記載の微細通路を備えた熱交換器用Al部材の製造方法。