JP6064453B2 - 包装材料およびそれを用いた包装容器 - Google Patents
包装材料およびそれを用いた包装容器 Download PDFInfo
- Publication number
- JP6064453B2 JP6064453B2 JP2012194100A JP2012194100A JP6064453B2 JP 6064453 B2 JP6064453 B2 JP 6064453B2 JP 2012194100 A JP2012194100 A JP 2012194100A JP 2012194100 A JP2012194100 A JP 2012194100A JP 6064453 B2 JP6064453 B2 JP 6064453B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- particles
- packaging
- packaging material
- adhesion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
あり、その付着量が0.1〜1.0g/m2であることを特徴とする提案がある(特許文献4)。
前記熱接着層の表面に、球形粒子または不定形粒子が分散されることによって、前記熱接着層の表面から球形粒子または不定形粒子が飛び出していることにより、凹凸が形成され、
前記付着防止層が、疎水性酸化物微粒子と無機バインダー樹脂からなり、前記凹凸を覆うように積層され、
前記付着防止層の表面の算術平均粗さRaが、Ra>5μmであることを特徴とする包装材料である。
付着防止性を発現することができる。また無機バインダー樹脂を介することにより、疎水性酸化物微粒子が強固に接着し、機械的強度を有する包装材料を提供できる。
本発明の包装材料は、包装容器の強度向上やガスバリア性向上などの要求があれば、包装材料に物性を向上させるための素材を中間に積層することができる。食品、飲料品、医薬品、化粧品などを包装するための包装材料およびそれを用いた包装容器に好適である。
図9は、本発明の包装材料の他の構成の一例を示す説明図である。図9−1は、中間にガスバリア層を積層した一例である。基材層1/接着層4/ガスバリア層5/接着層4/熱接着層2/付着防止層3が順次積層されたものである。
の後付着防止層を凹凸が形成された全面を覆うように積層する。付着防止層の表面積が大きくなり付着防止性能が向上される。また熱接着層の表面に球形粒子または不定形粒子を一様に分散して凹凸にしてもよい。
、カルシュウム、カリウム、錫、ナトリウム、ホウ素、チタン、鉛、ジルコニウム、イットリウムなどの金属の酸化物が使用できる。中でも生産性、価格面から酸化珪素、酸化マグネシウムが好ましい。無機酸化物の蒸着層の厚みは5〜300nmの範囲が好ましく、中でも5〜100nmの範囲が好ましい。その値は適宜選択すればよい。
アクリル樹脂からなる熱接着剤を酢酸エチルに分散して固形分20重量%に調整した分散液を、実施例1の基材層のアンカーコート面に、グラビアコート法により2.0g/m2(DRY)塗布し熱接着層を形成した。
アクリル樹脂からなる平均粒径15μmの球形粒子とアクリル樹脂からなる熱接着剤を酢酸エチルに分散して固形分30重量%に調整した分散液を作成した。該分散液を、実施例1の基材層のアンカーコート面にバーコート法により20.0g/m2(DRY)塗布して熱接着層を形成した。尚、熱接着層の表面を、球形粒子による凹凸が熱接着層内にほぼ埋没した状態になるようにした。
アクリル樹脂からなる平均粒径15μmの不定形粒子とアクリル樹脂からなる熱接着剤を酢酸エチルに分散して固形分30重量%に調整した分散液を作成した。該分散液を、実施例1の基材層のアンカーコート面にバーコート法により20.0g/m2(DRY)塗布して熱接着層を形成した。尚、熱接着層の表面を、不定形粒子による凹凸が熱接着層内にほぼ埋没した状態になるようにした。
・シール強度(N/15mm)、引張り速度300mm/min、剥離角度180°、シール幅10mm、n=3平均、条件で行った。引張り試験機(テンシロン)を用いた。
・シール強度(水浸漬後)(シールしたものを室温の水に7日間浸漬した後のシール強度を測定)。測定条件は、上記同等。
包装材料に水滴およびヨーグルト(ダノンヨーグルト/プレーン無糖)を滴下し、その後接触角および転落角を測定した。接触角は、接触測定装置(固液界面解析装置「Drop
Master300」協和界面科学株式会社)を用いて接触角を測定した。
転落角は、水平な平台を傾け、水およびヨーグルトの液滴が転げ落ちたときの角度を測定した。転落角は、目視により測定した。
水、ヨーグルトの液滴が転落した後の付着性の評価を行った。○:付着あり、×:付着あり、と目視で評価した。
2 熱接着層
3 付着防止層
4 接着層
5 ガスバリア層
6 アルミニウム層
10 球形粒子
11 無機バインダー樹脂
12 疎水性酸化物微粒子
13 不定形粒子
20 内容物(ヨーグルト)
21 フランジ
22 容器本体
23 付着物
30 本発明の包装材料
40 包装袋(自立性包装袋)
50 密封容器
60 本発明の蓋材
70 従来の蓋材
Claims (5)
- 少なくとも、基材層/熱接着層/付着防止層が順次積層されてなる包装材料であって、前記熱接着層の表面に、球形粒子または不定形粒子が分散されることによって、前記熱接着層の表面から球形粒子または不定形粒子が飛び出していることにより、凹凸が形成され、
前記付着防止層が、疎水性酸化物微粒子と無機バインダー樹脂からなり、前記凹凸を覆うように積層され、
前記付着防止層の表面の算術平均粗さRaが、Ra>5μmであることを特徴とする包装材料。 - 前記球形粒子または不定形粒子の平均粒径が10〜50μmの範囲であり、前記疎水性酸化物微粒子の平均粒径が5nm〜1μmの範囲であることを特徴とする請求項1記載の包装材料。
- 前記球形粒子または不定形粒子が、前記熱接着層の表面から平均粒径の50%以上飛び出していることを特徴とする請求項1または2記載の包装材料。
- 請求項1〜3のいずれか1項に記載の包装材料を用いたことを特徴とする包装容器。
- 前記包装容器が、包装袋または前記包装材料からなる蓋材を用いた密封容器であること特徴とする請求項4記載の包装容器。