JP5892267B2 - 電縫鋼管 - Google Patents
電縫鋼管 Download PDFInfo
- Publication number
- JP5892267B2 JP5892267B2 JP2014559807A JP2014559807A JP5892267B2 JP 5892267 B2 JP5892267 B2 JP 5892267B2 JP 2014559807 A JP2014559807 A JP 2014559807A JP 2014559807 A JP2014559807 A JP 2014559807A JP 5892267 B2 JP5892267 B2 JP 5892267B2
- Authority
- JP
- Japan
- Prior art keywords
- less
- pearlite
- steel pipe
- steel
- strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
はじめに、本発明の鋼の成分組成を規定した理由を説明する。なお、成分%はすべて質量%を意味する。
Cが0.35%未満では、十分な強度が得られず、要求される耐疲労特性が得られない。一方で、0.55%を超えると、溶接性が悪くなる為、安定した電縫溶接品質が得られない。よって、C量は0.35〜0.55%の範囲とする。好ましくは0.40〜0.45%の範囲である。
Siは脱酸のために添加する場合もあり、0.01%未満では十分な脱酸効果(deoxidation effect)が得られない。同時に、Siは固溶強化元素(solute strengthening elements)でもあり、その効果を得るためには0.01%以上の含有が必要である。一方で、1.0%を超えると、鋼管の焼入れ性が低下する。Si量は0.01〜1.0%の範囲とする。好ましくは0.1〜0.4%である。
Mnはパーライト変態を促進させ、また焼入れ性を向上させる元素であり、その効果を得るには1.0%以上の添加が必要である。一方で、3.0%を超えると電縫溶接品質(welding quality of ERW)を低下させ、さらに残留オーステナイト量(amount of residual austenite)が増加し耐疲労特性が低下する。Mn量は1.0〜3.0%の範囲とする。好ましくは1.4〜2.0%の範囲である。
本発明でPは不可避的不純物であり、その量の上限を0.02%以下とする。Pは連続鋳造時に形成される偏析部(segregation part)に濃化する傾向があり、管素材の熱延鋼板においても残存する。電縫溶接時には鋼帯のエッジ(edges)を突合せアプセット(upset)をかけるため、Pが濃化した偏析部分は管の外表面および内表面に露出する場合があり、この部分に扁平加工(flattening forming)などの二次加工(secondary processing)が付与された場合に割れを生じる危険性がある。したがって、好ましくは0.01%以下である。
本発明でSは不可避的不純物であり、その量の上限を0.01%以下とする。Sはその量が多いと素材の靭性を低下させるほか、鋼中のMnと結合しMnSを形成する。これは熱延工程で長手方向に伸ばされた長い介在物になり、加工性、靭性を低下させることになる。したがって、好ましくは0.005%以下、さらに好ましく0.003%以下である。
Alは本発明において所望の旧オーステナイト粒径とそれにともなうねじり疲労強度を達成する上で重要な元素であるが、0.005%を超えて含有するとAlN析出量が増大し、焼準工程でピン止め効果を発揮するため、オーステナイトの粒成長が抑制され、所望のオーステナイト粒径が得られない。従って、Al量は0.005%以下とする。好ましく0.003%以下である。
Nは、Alと結合しAlNを形成し、焼準工程でのオーステナイトの粒成長の抑制に寄与する元素であり、この効果を抑制するためには0.0050%以下とする必要がある。なお、好ましくは0.0035%以下である。
Crは、パーライト変態温度を低下させる元素であり、これによりパーライトのラメラ間隔が狭小化し、パーライトの強度が上昇するため、ねじり疲労強度が上昇する。この効果を発揮するためには0.1%以上の含有が必要である。一方で、0.5%を超えて含有すると、酸化物を形成しこれが電縫部に残存するため、電縫溶接性(weldability of ERW)が劣化する可能性がある。よって、Cr量は、0.1〜0.5%の範囲とする。なお、好ましくは0.15〜0.30%の範囲である。
Tiは鋼中のNをTiNとして固定する作用を有する。しかし、0.005%未満ではNを固定する能力が十分に発揮されず、一方で0.1%を超えると鋼の加工性および靭性が低下する。Tiを含有する場合は、Ti量は0.005〜0.1%の範囲とすることが好ましい。より好ましくは0.01〜0.04%の範囲である。
Bは焼入れ性を向上させる元素である。0.0003%未満では焼入れ性向上効果が十分に発揮されない。一方で、0.0050%を超えて含有しても、その効果は飽和し、粒界に偏析して粒界破壊(intergranular fracture)を促進し耐疲労特性を劣化させる。Bを含有する場合は、B量は0.0003〜0.0050%の範囲とすることが好ましい。より好ましくは0.0010〜0.0040%の範囲である。
Moは焼入れ性を向上させる元素であり、鋼の強度を高め疲労強度の向上に有効である。その効果を得るためには、0.001%以上の含有が好ましい。しかし、2%を超えて含有すると加工性が著しく低下する。Moを含有する場合は、Mo量は2%以下とすることが好ましい。より好ましくは0.001〜0.5%の範囲である。
Wは炭化物を形成することで鋼の強度を向上させるのに有効である。その効果を得るためには、0.001%以上の含有が好ましい。しかし、2%を超えて含有すると不必要な炭化物が析出し、耐疲労特性を低下させ加工性(workability)を低下させることになる。Wを含有する場合は、W量は2%以下とすることが好ましい。より好ましくは0.001〜0.5%の範囲である。
Nbは焼入れ性を向上させる元素であるほか、炭化物を形成し強度上昇に寄与する。その効果を得るためには、0.001%以上の含有が好ましい。しかし、0.1%を超えて含有してもその効果は飽和し、加工性が低下する。Nbを含有する場合は、Nb量は0.1%以下とすることが好ましい。より好ましくは0.001〜0.04%の範囲である。
Vは炭化物を形成し、鋼の強度を上昇させるのに有効でかつ焼戻し軟化抵抗(temper softening resistance)を有する元素である。その効果を得るためには、0.001%以上の含有が好ましい。しかしながら0.1%を超えて含有するとその効果は飽和し、加工性が低下する。Vを含有する場合は、V量は0.1%以下とすることが好ましい。より好ましくは0.001〜0.5%の範囲である。
Niは焼入れ性を向上させる元素であり、鋼の強度を高め疲労強度の向上に有効である。その効果を得るためには、0.001%以上の含有が好ましい。しかし、2%を超えて含有すると加工性が著しく低下する。Niを含有する場合は、Ni量は2%以下とすることが好ましい。より好ましくは0.001〜0.5%の範囲である。
Cuは焼入れ性を向上させる元素であり、鋼の強度を高め疲労強度の向上に有効である。その効果を得るためには、0.001%以上の含有が好ましい。しかし、2%を超えて含有すると加工性が著しく低下する。Cuを含有する場合は、Cu量は2%以下とすることが好ましい。より好ましくは0.001〜0.5%の範囲である。
Ca、REMは、いずれも非金属介在物(non−metal inclusion)の形態を球状とし、繰り返し応力(cyclic stress)が付与されるような使用環境下での疲労破壊時の割れ起点の低減に有効な元素であり、必要に応じて選択して含有できる。このような効果は、Ca、REMともに0.0020%以上の含有で認められる。一方で、0.02%を超えて含有すると、介在物量が多くなりすぎて清浄度(cleaning level)が低減する。このためCa、REMを含有する場合は、Ca、REMともにそれぞれ0.02%以下とすることが好ましい。Ca、REMの両者を併用する場合には、合計量で0.03%以下とすることが好ましい。
本発明では、パーライトを面積分率(area ratio)で85%以上、フェライトの面積分率およびベイナイトの面積分率(0を含む)の合計を15%以下の金属組織とする。
フェライト層に囲まれた見かけ上のパーライト粒径が大きい方が疲労亀裂の偏向が大きくなり、亀裂伝播抵抗は高くなる。フェライトが旧オーステナイトの粒界に生成するため、旧オーステナイトの粒が大きいほど、みかけ上のパーライト粒径は大きくなる。亀裂伝播抵抗を上昇させるためには旧オーステナイト粒径が25μm以上である必要があり、25μm未満では疲労亀裂伝播抵抗の上昇は十分ではない。
Claims (2)
- 成分組成が、質量%で、C:0.35〜0.55%、Si:0.01〜1.0%、Mn:1.0〜3.0%、P:0.02%以下、S:0.01%以下、Al:0.005%以下、N:0.0050%以下、Cr:0.1〜0.5%を含有し、残部Fe及び不可避的不純物からなり、金属組織が、パーライト、フェライトおよびベイナイトからなり、前記パーライトの面積分率を85%以上、前記フェライトの面積分率および前記ベイナイトの面積分率(0を含む)の合計を15%以下とし、旧オーステナイト粒径が25μm以上である電縫鋼管。
- 前記成分組成に加えて、さらに、質量%で、Ti:0.005〜0.1%、B:0.0003〜0.0050%、Mo:2%以下、W:2%以下、Nb:0.1%以下、V:0.1%以下、Ni:2%以下、Cu:2%以下、Ca:0.02%以下、REM:0.02%以下の中から選ばれる1種以上を含有する請求項1に記載の電縫鋼管。