JP5807322B2 - セメント組成物 - Google Patents
セメント組成物 Download PDFInfo
- Publication number
- JP5807322B2 JP5807322B2 JP2010190103A JP2010190103A JP5807322B2 JP 5807322 B2 JP5807322 B2 JP 5807322B2 JP 2010190103 A JP2010190103 A JP 2010190103A JP 2010190103 A JP2010190103 A JP 2010190103A JP 5807322 B2 JP5807322 B2 JP 5807322B2
- Authority
- JP
- Japan
- Prior art keywords
- cement composition
- weight
- cement
- parts
- composition according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
このようなセメント組成物によれば、CO2の排出量の低減と強度発現との両立を図ることが可能である。
このようなセメント組成物によれば、CO2の排出量のさらなる低減と強度発現との両立を図ることが可能である。
このようなセメント組成物によれば、CO2の排出量の低減と強度発現とのバランスをさらに良くすることができる。
このようなセメント組成物によれば、CO2の排出量をより一層低減しつつ強度発現とのバランスをさらに良くすることができる。
また、標準養生28日圧縮強度が16〜70N/mm2であることが望ましい。
このようなセメント組成物によれば、セメント組成物のフレッシュ性状における流動性を向上させることが可能である。
本実施形態においては、セメント組成物として、水、セメント、細骨材、粗骨材等を含んで構成されるコンクリートを例に挙げて説明する。本実施形態では、CO2排出量の多いセメントの使用量を減らし、セメントの代替材料としてCO2排出量が少ない混和材(結合材)を使用するようにした。このように、セメントの使用量を極力減らすことで、コンクリート製造時のCO2の排出量を削減することが可能となる。しかしながら、セメントの使用量が少なくなることによってコンクリートの強度が低下する虞がある。
前述したようにCO2排出量の多いセメントの使用量を極力少なくし、CO2排出量の少ない結合材を増やすようにした。本実施形態では、高炉スラグ、フライアッシュ、シリカフュームを結合材として用いた。但し、結合材は、CO2排出の他に強度発現やフレッシュ性状に影響するため、セメント、高炉スラグ、フライアッシュ、シリカフューム、水の使用割合のバランスを検討した。
本実施形態では、セメントとして普通ポルトランドセメントと耐硫酸塩ポルトランドセメントとについて検討し、シリカフュームとしては、フェロシリコン起源のシリカフュームとジルコニア起源のシリカフュームについて検討し、フライアッシュとしては、JISA6201により規定されたフライアッシュI種とフライアッシュII種とについて検討した。
強度の向上を図るため、水酸化カルシウム(アルカリ成分に相当する)、石膏、強度増進剤、石灰石微粉末の配合について検討を行った。
水酸化カルシウムは、アルカリの刺激によりスラグ、フライアッシュなどの硬化を促進させるものである。本実施形態ではスラッジ水を模擬した水酸化カルシウム溶液を使用した。
また、石膏には、二水石膏、半水石膏、無水石膏があるが、本実施形態では無水石膏を使用した。さらに、無水石膏には、フッ素製造時に副生する(産業副産物の)無水石膏や、天然に産出する無水石膏等があるが、本実施形態では天然の無水石膏を使用した。なお、石膏は、前述した高炉スラグの一部とする。
また、本実施形態では、トリイソプロパノールアミンを主成分とする強度増進剤を使用した。
さらに、化学混和剤(AD)の配合について検討を行った。化学混和剤(AD)としては、例えば、減水剤、高性能AE減水剤、AE減水剤、高性能減水剤がある。
CO2を低減するにはセメントを含む結合材の量を低減することが有効である。一方、強度は水結合材比(結合材量と水量の割合)に依存する。従って、結合材の量を低減させる場合の水量(単位水量)も併せて検討した。
(1)フレッシュ性状試験(サンプルNo.1〜35)
フレッシュ性状試験として、練り上がりのスランプ、空気量、温度を測定した。なお、スランプ及び空気量の試験方法は、それぞれJIS A 1101(BS 1881 Part102)、JIS A 1128(BS 1881 Part106)に準拠した。また、コンクリートの温度は温度計によって測定した。
(2)圧縮強度試験(サンプルNo.1〜35)
φ100*200mm(150*150*150mm)の供試体を作成して水中養生後、JIS A 1108(BS EN 206)に準じて20℃(23℃)および50℃の圧縮強度を測定した。
(3)乾燥収縮試験(サンプルNo.5〜11,サンプルNo.23〜35)
100*100*400mm(75*75*285mm)の供試体を作成して材齢7日まで水中養生後、JIS A 1129(ASTM C 157)に準じて乾燥による収縮変化(長さ変化)を測定した。
[注]上記の( )内の規準及び寸法は、サンプルNo.11の場合に適用した。
[注]上記の( )内の温度は、サンプルNo.11の場合に適用した。
表8に示すように、乾燥による長さ変化(収縮量)は、比較例よりも本実施例の方が小さくなっている。つまり、本実施例では、比較例よりもひび割れが生じにくいと言える。
さらに、細骨材及び粗骨材を含む骨材と、水と、高性能AE減水剤等の化学混和剤とによりコンクリートを構成した。
こうすることにより、CO2の排出量が低く、フレッシュ性状や強度発現の優れたコンクリートを得ることが可能である。
Claims (14)
- 5〜30重量部のセメントと、0〜20重量部のシリカフュームと、0〜50重量部のフライアッシュと、42〜75重量部の高炉スラグと、を有する結合材(B)100重量部と、
単位水量80〜185kg/m3に相当する水(W)と、
骨材(A)と、
化学混和剤(AD)と、
を有し、
添加材としてアルカリ成分を備え、
前記アルカリ成分は、水酸化カルシウムであり、
前記結合材(B)に対する前記水酸化カルシウムの重量比が0.1%未満であることを特徴とするセメント組成物。 - 5〜30重量部のセメントと、0〜20重量部のシリカフュームと、0〜50重量部のフライアッシュと、42〜75重量部の高炉スラグと、を有する結合材(B)100重量部と、
単位水量80〜185kg/m3に相当する水(W)と、
骨材(A)と、
化学混和剤(AD)と、
を有し、
前記セメントは、耐硫酸塩ポルトランドセメントであることを特徴とするセメント組成物。 - 請求項1又は請求項2に記載のセメント組成物であって、
前記水(W)の前記単位水量が100〜150kg/m3であることを特徴とするセメント組成物。 - 請求項1乃至請求項3のいずれかに記載のセメント組成物であって、
前記セメントを5〜20重量部とし、前記フライアッシュを5〜50重量部としたことを特徴とするセメント組成物。 - 請求項1乃至請求項4のいずれかに記載のセメント組成物であって、
前記セメントは、5〜15重量部であることを特徴とするセメント組成物。 - 請求項1乃至請求項5のいずれかに記載のセメント組成物であって、
前記水(W)と前記結合材(B)との重量比である水結合材比(W/B)が35%以上45%以下であることを特徴とするセメント組成物。 - 請求項1乃至請求項6のいずれかに記載のセメント組成物であって、
標準養生28日圧縮強度が16〜70N/mm2であることを特徴とするセメント組成物。 - 請求項1乃至請求項7のいずれかに記載のセメント組成物であって、
アルカリ成分、石膏、トリイソプロパノールアミン、石灰石微粉のうちの少なくとも1種以上の添加材を有することを特徴とするセメント組成物。 - 請求項8に記載のセメント組成物であって、
前記石膏は、天然の無水石膏であることを特徴とするセメント組成物。 - 請求項8又は請求項9に記載のセメント組成物であって、
前記結合材(B)に対する前記石膏の重量比が1.2%以上6.0%以下であることを特徴とするセメント組成物。 - 請求項8乃至請求項10に記載のセメント組成物であって、
前記結合材(B)に対する前記石灰石微粉の重量比が0.3%以上108.0%以下であることを特徴とするセメント組成物。 - 請求項8乃至請求項11に記載のセメント組成物であって、
前記結合材(B)に対する前記トリイソプロパノールアミンの重量比が1.0%未満であることを特徴とするセメント組成物。 - 請求項1乃至請求項12に記載のセメント組成物であって、
前記シリカフュームはジルコニア起源のシリカフュームであることを特徴とするセメント組成物。 - 請求項1乃至請求項13に記載のセメント組成物であって、
前記フライアッシュは、JISA6201により規定されたフライアッシュI種の値を満たすフライアッシュであることを特徴とするセメント組成物。