JP5794102B2 - 表示装置 - Google Patents
表示装置 Download PDFInfo
- Publication number
- JP5794102B2 JP5794102B2 JP2011234274A JP2011234274A JP5794102B2 JP 5794102 B2 JP5794102 B2 JP 5794102B2 JP 2011234274 A JP2011234274 A JP 2011234274A JP 2011234274 A JP2011234274 A JP 2011234274A JP 5794102 B2 JP5794102 B2 JP 5794102B2
- Authority
- JP
- Japan
- Prior art keywords
- display device
- refractive index
- layer
- polarizing plate
- light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
1.表示装置本体の視認側に円偏光板が配置されてなる表示装置であって、前記円偏光板が、視認側から、表面反射抑止層と、偏光子と、λ/4板と、がこの順に積層されてなる構成を有し、表示装置の視認側の表面の法線に対して5°の方向から入射した光の表示装置における反射率として定義される正面反射率(R0)が、下記数式1を満たすことを特徴とする、表示装置:
2.前記λ/4板が、下記数式2を満たすことを特徴とする、上記1に記載の表示装置:
3.表示装置の視認側の表面の法線に対して70°の方向から入射した光の表示装置における反射率として定義される70°斜め反射率(R70)が、下記数式3を満たすことを特徴とする、上記1または2に記載の表示装置:
4.前記70°斜め反射率が、下記数式4を満たすことを特徴とする、上記3に記載の表示装置:
5.前記表面反射抑止層の視認側の表面の法線方向から入射した光の表面反射抑止層の表面における反射率として定義される表面反射率(RS)が、下記数式5を満たすことを特徴とする、上記1〜4のいずれか1項に記載の表示装置:
6.前記表面反射率(RS)が、下記数式6を満たすことを特徴とする、上記5に記載の表示装置:
7.前記表示装置本体が、有機ELパネル、または半透過型液晶パネルを備えることを特徴とする、上記1〜6のいずれか1項に記載の表示装置;
8.前記表示装置本体と前記円偏光板との間に、タッチパネルが介在することを特徴とする、上記1〜6のいずれか1項に記載の表示装置。
まず、表示装置の全体的な構成について、説明する。
有機ELパネルは、本実施形態に係る有機EL表示装置の表示装置本体であり、薄型であることによる省スペース性および軽量性、10V程度の印加電圧であっても高輝度な発光が得られるなどの特徴を有するものである。この有機ELパネルは、発光可能な有機層を電極で挟んだ構成を有する。有機層は基本的に正孔輸送層、発光層、および電子輸送層を積層したものである。電極としては、光を取り出す側に例えばITO(Indium Tin Oxide)などの透明電極を用い、対向する基板に例えばアルミニウムなどの金属電極を用いる。このような構成において、両電極より各々電子と正孔を、電子輸送層および正孔輸送層を介して発光層に注入し、発光層において電子と正孔を再結合させて発光させるのである。なお、有機EL表示装置は、TFTが配置される位置に応じて、これが発光層よりも視認側に配置されるボトムエミッション方式と、これが発光層よりも奥面に配置されるトップエミッション方式とに分類されるが、本発明はいずれの方式にも適用可能である。
続いて、円偏光板の構成について、説明する。図1や図2に示すように、本発明に係る円偏光板20は、視認側から、表面反射抑止層22と、偏光子26と、λ/4板28と、がこの順に積層されてなる構成を必須に有する。そして、図1や図2に示すように、表面反射抑止層22と偏光子26との間には、偏光板保護フィルム24が介在することが好ましい。
偏光子26は、円偏光板の主構成要素であり、一定方向の偏波面の光だけを通す素子である。そして、偏光子26は、後述するλ/4板28と積層されることで、円偏光板としての機能を発揮するようになる。
なお、このような偏光子を用いる場合には、偏光子26の表面反射抑止層22側に偏光板保護フィルム24を配置することが必要である。偏光板保護フィルム24としては、従来公知のフィルムが適宜用いられ、例えば、ポリメチルメタクリレート、ポリアクリレート等のアクリル系樹脂、ポリカーボネートや、ポリカーボネートとスチレン系化合物の共重合体、または混合体、ポリカーボネートとフルオレン系化合物の共重合体または混合体等のポリカーボネート系樹脂、ポリオレフィン系樹脂、シクロオレフィン系樹脂、ポリイミド系樹脂、セルロース系樹脂、ポリエステル系樹脂等が挙げられる。このなかでも特に、セルロース系樹脂からなるフィルム(特に、セルロースエステルフィルム)が好適に用いられる。市販のセルロースエステルフィルムとしては、例えば、コニカミノルタタック KC8UX、KC5UX、KC8UCR3、KC8UCR4、KC8UCR5、KC8UY、KC4UY、KC4UE、KC8UE、KC6UA、KC4UA、KC8UY−HA、KC8UX−RHA、KC8UXW−RHA−C、KC8UXW−RHA−NC、KC4UXW−RHA−NC(以上、コニカミノルタオプト株式会社製)等が好ましく用いられる。
λ/4板28は、上述した偏光子24と積層されることで、円偏光板としての機能を発揮する。この際、円偏光板としての機能に優れるという観点から、偏光子24の吸収軸と、λ/4板28の面内の遅相軸とのなす角は45°であることが理想である。実際には、この角が45°±2°の範囲であることが好ましい。
λ/4板の具体的な構成について特に制限はなく、従来公知の知見が適宜参照されうる。ただし、λ/4板は透明樹脂から構成されることが好ましく、当該透明樹脂の可視光の透過率は、好ましくは60%以上であり、より好ましくは80%以上であり、特に好ましくは90%以上である。また、λ/4板を構成する透明樹脂は、熱可塑性樹脂であることが好ましい。また、この透明樹脂は、固有複屈折値が正である樹脂であることが好ましい。λ/4板を構成する透明樹脂としては、例えばセルロースエステル系樹脂、ポリオレフィン系樹脂、ポリスルホン系樹脂、ポリカーボネート系樹脂、ポリメチルメタクリレート系樹脂、ポリエステル系樹脂、ポリビニルアルコール系樹脂等が挙げられる。
表面反射抑止層22は、表示装置1、2(円偏光板20)の最も視認側に配置される層であり、表示装置1、2の視認側の表面における反射(表面反射RS)を防止する層である。
偏光板保護フィルム/ハードコート層/中屈折率層/高屈折率層/低屈折率層
偏光板保護フィルム/ハードコート層/高屈折率層/低屈折率層
偏光板保護フィルム/防眩層/中屈折率層/高屈折率層/低屈折率層
偏光板保護フィルム/帯電防止層/ハードコート層/中屈折率層/高屈折率層/低屈折率層
偏光板保護フィルム/帯電防止層/防眩層/中屈折率層/高屈折率層/低屈折率層
もちろん、光学干渉により反射率を低減できるものであれば、特にこれらの層構成のみに限定されるものではない。また、帯電防止層は導電性ポリマー粒子または金属酸化物微粒子(例えば、SnO2、ITOなど)を含む層であることが好ましく、塗布または大気圧プラズマ処理等によって設けることができる。帯電防止層はハードコート層や、中、高屈折率層を兼ねることができ、特に中、高屈折率層と兼ねることが、性能上および生産上好ましい。
表面反射抑止層22自体の反射率の値について特に制限はなく、表示装置全体として上述した数式1の関係を満たすものであればよい。
上述したように、本発明に係る表示装置は、視認側の表面の法線に対して5°の方向から入射した光の表示装置における反射率として定義される正面反射率(R0)が数式1を満たすことを必須の構成要件とするものである。そして、本発明に係る表示装置は、より好ましくは、斜め方向からの入射光に対しても、数式1のように波長依存性が低減されたものである。かような構成とすることで、表示装置を斜め方向から視認した際における色味の発生も防止されうる。具体的には、本発明に係る表示装置において、視認側の表面の法線に対して70°の方向から入射した光の表示装置における反射率として定義される70°斜め反射率(R70)は、下記数式3を満たすことが好ましい。
≪偏光子の準備≫
液晶ディスプレイ(SONY社製、KDL−55HX920)の偏光板から偏光板保護フィルムを剥離することで偏光子(ポリビニルアルコール系フィルムにヨウ素を染色させたもの)を単離し、以下のすべての実施例および比較例において用いた。
以下の手法により、セルロースエステルフィルムからなる偏光板保護フィルムを作製し、以下のすべての実施例および比較例において用いた。
下記の材料を順次密閉容器中に投入し、容器内温度を20℃から80℃まで昇温した後、温度を80℃に保ったままで3時間攪拌を行って、セルロースエステルを完全に溶解した。酸化ケイ素微粒子は予め添加する溶媒と少量のセルロースエステルの溶液中に分散して添加した。このドープを濾紙(安積濾紙株式会社製、安積濾紙No.244)を使用して濾過し、ドープ液Aを得た。
セルローストリアセテート(アセチル基置換度2.9) 100質量部
トリメチロールプロパントリベンゾエート 5質量部
エチルフタリルエチルグリコレート 5質量部
酸化ケイ素微粒子(アエロジルR972V、日本アエロジル株式会社製)
0.1質量部
チヌビン109(チバ・スペシャルティ・ケミカルズ社製) 1質量部
チヌビン171(チバ・スペシャルティ・ケミカルズ社製) 1質量部
メチレンクロライド 400質量部
エタノール 40質量部
ブタノール 5質量部
上記の材料を混合してドープ液Aを調製し、得られたドープ液Aを、温度35℃に保温した流延ダイを通より、ステンレス鋼製エンドレスベルトよりなる温度35℃の支持体上に流延して、ウェブを形成した。
以下の手法により、上記で作製した偏光板保護フィルムの一方の面に、表面反射抑止層を形成した。
ジペンタエリスリトールヘキサアクリレート(2量体以上の成分を2割程度含む)
108質量部
イルガキュア184(チバスペシャルティケミカルズ(株)製) 2質量部
プロピレングリコールモノメチルエーテル 180質量部
酢酸エチル 120質量部
これにより、厚さ5μmのハードコート層(屈折率1.55)を形成した。
テトラ(n)ブトキシチタン 250質量部
末端反応性ジメチルシリコーンオイル(日本ユニカー社製L−9000)
0.48質量部
アミノプロピルトリメトキシシラン(信越化学社製KBE903)
22質量部
UV硬化性エポキシ樹脂(旭電化社製KR500) 21質量部
プロピレングリコールモノメチルエーテル 4900質量部
イソプロピルアルコール 4840質量部
(高屈折率層塗布組成物)
テトラ(n)ブトキシチタン 310質量部
末端反応性ジメチルシリコーンオイル(日本ユニカー社製L−9000)
0.4質量部
アミノプロピルトリメトキシシラン(信越化学社製KBE903)
4.8質量部
UV硬化性エポキシ樹脂(旭電化社製KR500) 4.6質量部
プロピレングリコールモノメチルエーテル 4900質量部
イソプロピルアルコール 4800質量部
(低屈折率層塗布組成物1)
下記のシリカ系微粒子P−1 35質量部
フッ素含有樹脂オプスターJM5010(JSR(株)製) 64.5質量部
FZ−2222(日本ユニカー製、10%プロピレングリコールモノメチルエーテル溶液) 0.5質量部
イソプロピルアルコール 500質量部
プロピレングリコールモノメチルエーテル(PGME) 300質量部
メチルエチルケトン(MEK) 100質量部
〈シリカ系微粒子P−1の調製〉
平均粒径5nm、SiO2濃度20質量%のシリカゾル100gと純水1900gの混合物を80℃に加温した。この反応母液のpHは10.5であり、同母液にSiO2として0.98質量%のケイ酸ナトリウム水溶液9000gとAl2O3として1.02質量%のアルミン酸ナトリウム水溶液9000gとを同時に添加した。その間、反応液の温度を80℃に保持した。反応液のpHは添加直後、12.5に上昇し、その後、ほとんど変化しなかった。添加終了後、反応液を室温まで冷却し、限外濾過膜で洗浄して固形分濃度20質量%のSiO2・Al2O3核粒子分散液を調製した(工程(a))。
ジペンタエリスリトールヘキサアクリレート単量体 60質量部
ジペンタエリスリトールヘキサアクリレート2量体 20質量部
ジペンタエリスリトールヘキサアクリレート3量体以上の成分 20質量部
光反応開始剤(イルガキュア184(チバスペシャルティケミカルズ(株)製))
4質量部
プロピレングリコールモノメチルエーテル 75質量部
メチルエチルケトン 75質量部
それぞれの実施例および比較例における表面反射抑止層を構成する3つの層の屈折率および膜厚を下記の表1に示す。また、それぞれの実施例および比較例における表面反射抑止層(比較例1〜6については表面反射抑止層を形成していないため、ハードコート層)の表面における5°正面反射率および70°斜め反射率の測定値も下記の表1に併せて示す。なお表面反射率の測定には、まず、表面反射抑止層もハードコート層も形成していない偏光板保護フィルムの一方の面に黒色テープを貼付した。そして、黒色テープを貼付した側とは反対側の面から、3つの波長(480nm、550nm、650nm)について、CM−2500(コニカミノルタ社製)を用いて5°正面反射率を測定し、絶対反射測定装置(日本分光社製、V−670・ARMN−735)を用いて70°斜め反射率を測定した。これらの測定値から、偏光板保護フィルムの屈折率に基づき理論的に計算される表面反射率の値を引いて得られた値を、黒色テープと偏光板保護フィルムとの間の5°正面反射率および70°斜め反射率とした。そして、それぞれの実施例および比較例における表面反射抑止層における表面反射抑止層(またはハードコート層)についての測定値から、上述した偏光板保護フィルムの屈折率に基づき理論的に計算される表面反射率の値および黒色テープと偏光板保護フィルムとの間の反射率の値を引き、得られた値を表面反射抑止層(またはハードコート層)の5°正面反射率および70°斜め反射率とした。
λ/4板としては、以下のものを準備(作製)した。
(1)帝人社製、TT−138(ポリカーボネート(PC)フィルム)
(2)下記の手法で作製したシクロオレフィンポリマー(COP)フィルム
熱可塑性ノルボルネン系樹脂のペレットを、熱風乾燥機を用いて100℃で4時間乾燥したのち押出機に供給した。溶融樹脂温度260℃で押し出し、T型ダイスから第1冷却ロールまでの間のフィルムから10mm以内の雰囲気温度が260℃になるように加熱し、フィルムの両端部に静電気を印加した。第1冷却ロールの温度120℃、引き取り速度18.0m/min、第2冷却ロールの温度125℃、引き取り速度18.1m/min、第3冷却ロールの温度110℃、引き取り速度17.9m/minとした。得られた未延伸フィルムの平均厚さは71μmであった。
(3)帝人社製、ピュアエースWRS(ポリカーボネート系共重合体フィルム)
(4)帝人社製、ピュアエースWRW(ポリカーボネート系共重合体フィルム)
(5)帝人社製、ピュアエースWRZ(ポリカーボネート系共重合体フィルム)
(6)下記の手法で作製したセルロースアセテートプロピオネート(CAP)フィルム
(ポリエステル系可塑剤の合成)
窒素雰囲気下、テレフタル酸ジメチル4.85g、1,2−プロピレングリコール4.4g、テトライソプロピルチタネート10mgを混合し、140℃で2時間攪拌を行った後、p−トルイル酸6.8gを加え、さらに2時間撹拌した。その後210℃で16時間攪拌を行った。次に、170℃まで降温し、未反応物の1,2−プロピレングリコールを減圧留去することにより、下記の構造を有するポリエステル系可塑剤を得た。
撹拌装置、還流冷却器、温度計及び窒素ガス導入管を備えた四頭コルベンに、ショ糖34.2g(0.1モル)、無水安息香酸180.8g(0.8モル)、ピリジン379.7g(4.8モル)を仕込み、撹拌下に窒素ガス導入管から窒素ガスをバブリングさせながら昇温し、70℃で5時間エステル化反応を行なった。次に、コルベン内を4×102Pa以下に減圧し、60℃で過剰のピリジンを留去した後に、コルベン内を1.3×10Pa以下に減圧し、120℃まで昇温させ、無水安息香酸、生成した安息香酸の大部分を留去した。そして、次にトルエン1L、0.5質量%の炭酸ナトリウム水溶液300gを添加し、50℃で30分間撹拌後、静置して、トルエン層を分取した。最後に、分取したトルエン層に水100gを添加し、常温で30分間水洗後、トルエン層を分取し、減圧下(4×102Pa以下)、60℃でトルエンを留去させ、下記の構造を有する糖エステル化合物を得た。
微粒子(アエロジル R812 日本アエロジル(株)製) 11質量部
エタノール 89質量部
以上をディゾルバーで50分間攪拌混合した後、マントンゴーリンで分散を行った。
メチレンクロライドを入れた溶解タンクに十分攪拌しながら、微粒子分散液をゆっくりと添加した。さらに、二次粒子の粒径が所定の大きさとなるようにアトライターにて分散を行った。これを日本精線(株)製のファインメットNFで濾過し、微粒子添加液を調製した。
微粒子分散液 5質量部
(主ドープ液の調製)
下記組成の主ドープ液を調製した。まず加圧溶解タンクに溶剤としてメチレンクロライドとエタノールを添加した。溶剤の入った加圧溶解タンクに上記で製造したCE−1を攪拌しながら投入した。これを加熱し、攪拌しながら、完全に溶解し。これを安積濾紙(株)製の安積濾紙No.244を使用して濾過し、主ドープ液を調製した。
エタノール 64質量部
セルロースアセテートプロピオネート(アセチル基置換度1.5、プロピオニル基置換度0.9、総置換度2.4) 100質量部
糖エステル化合物 7.0質量部
下記の構造を有するポリエステル系可塑剤 2.5質量部
TINUVIN928(BASFジャパン社製) 1.5質量部
微粒子添加液 11質量部
次いで、無端ベルト流延装置を用い、ドープ液を温度33℃、1500mm幅でステンレスベルト支持体上に流延した。ステンレスベルトの温度は30℃に制御した。
上記で準備した偏光子の各面に、上記で作製した偏光板保護フィルムとλ/4板とを、粘着剤を介してそれぞれ貼合した。その際、λ/4板の面内の遅相軸が偏光子の吸収軸となす角が45°となるように、貼合の向きを調整した。
Clix2(iRiver社製)に貼合されている円偏光板を剥離し、上記で作製した円偏光板を粘着剤を介して貼合して、有機EL表示装置を作製した。
(反射率の測定)
上記と同様の測定装置を用い、それぞれの実施例および比較例で作製した有機EL表示装置の表面反射抑止層(比較例1〜6については表面反射抑止層を形成していないため、ハードコート層)の側から入射した光の5°正面反射率および70°斜め反射率を測定した。結果を下記の表3に示す。なお、比較例13の「理想」のλ/4板については、理論上内部反射がゼロとみなせることから、上記の表1に記載の表面反射率の値がそのまま、表3においても反射率の値として記載されている。
外光の照度が1000Lxの環境、および、外光の照度が2000Lxの環境において、有機EL表示装置の正面(面法線)の方向、および面法線に対して50°の方向から、目視で色味を評価した。黒を○、他の色づきをわずかに感じるものを△、他の色づきを明確に感じるものを×とした。結果を表3に示すが、表3に示す目視評価の結果は10名による評価結果の平均である。また、「理想」のλ/4板を用いている比較例13では有機EL表示装置の作製ができないことから、色味目視評価は行わなかった。
10 有機ELパネル(表示装置本体)、
20 円偏光板、
22 表面反射抑止層、
22a 低屈折率層、
22b 高屈折率層、
22c 中屈折率層、
24 偏光板保護フィルム、
26 偏光子、
28 λ/4板、
30 タッチパネル、
32a、32b 透明導電膜、
34 ガラス層。
Claims (10)
- 表示装置本体の視認側に円偏光板が配置されてなる表示装置であって、
前記円偏光板が、視認側から、表面反射抑止層と、偏光子と、λ/4板と、がこの順に積層されてなる構成を有し、
前記表面反射抑止層が、視認側から、膜厚84〜115nmの低屈折率層、膜厚146〜170nmの高屈折率層、および膜厚106〜217nmの中屈折率層がこの順に積層されてなる(ただし、屈折率は低屈折率層<中屈折率層<高屈折率層の関係を満たす)構成を有し、
表示装置の視認側の表面の法線に対して5°の方向から入射した光の表示装置における反射率として定義される正面反射率(R0)が、下記数式1を満たし、かつ、
表示装置の視認側の表面の法線に対して70°の方向から入射した光の表示装置における反射率として定義される70°斜め反射率(R70)が、下記数式3を満たすことを特徴とする、表示装置:
- 前記低屈折率層の屈折率が1.00〜1.50であり、前記高屈折率層の屈折率が1.60〜2.50であり、前記中屈折率層の屈折率が1.40〜2.00である、請求項1に記載の表示装置。
- 前記表面反射抑止層と前記偏光子との間に、視認側から、ハードコート層および偏光板保護フィルムがさらに積層されてなる、請求項1または2に記載の表示装置。
- 前記λ/4板がセルロースエステル系樹脂から構成されるものである、請求項1〜3のいずれか1項に記載の表示装置。
- 前記λ/4板が、下記数式2を満たすことを特徴とする、請求項1〜4のいずれか1項に記載の表示装置:
- 前記70°斜め反射率が、下記数式4を満たすことを特徴とする、請求項1〜5のいずれか1項に記載の表示装置:
- 前記表面反射抑止層の視認側の表面の法線方向から入射した光の表面反射抑止層の表面における反射率として定義される表面反射率(RS)が、下記数式5を満たすことを特徴とする、請求項1〜6のいずれか1項に記載の表示装置:
- 前記表面反射率(RS)が、下記数式6を満たすことを特徴とする、請求項7に記載の表示装置:
- 前記表示装置本体が、有機ELパネル、反射型液晶パネル、または半透過型液晶パネルを備えることを特徴とする、請求項1〜8のいずれか1項に記載の表示装置。
- 前記表示装置本体と前記円偏光板との間に、タッチパネルが介在することを特徴とする、請求項1〜9のいずれか1項に記載の表示装置。