JP5734269B2 - 潤滑グリース組成物 - Google Patents
潤滑グリース組成物 Download PDFInfo
- Publication number
- JP5734269B2 JP5734269B2 JP2012276616A JP2012276616A JP5734269B2 JP 5734269 B2 JP5734269 B2 JP 5734269B2 JP 2012276616 A JP2012276616 A JP 2012276616A JP 2012276616 A JP2012276616 A JP 2012276616A JP 5734269 B2 JP5734269 B2 JP 5734269B2
- Authority
- JP
- Japan
- Prior art keywords
- oil
- group
- sec
- lubricating grease
- grease composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(A)動粘度(40℃)が150〜1500mm2/秒である、一般式
RfO〔CF(CF3)CF2O〕a(CF2O)cRf
(ここで、Rfは炭素数1〜5のパーフルオロアルキル基であり、aは15〜150、cは0または1以上の整数であり、CF(CF3)CF2O基およびCF2O基は主鎖中にランダムに結合されている)で表わされるパーフルオロポリエーテル油および
(B)動粘度(40℃)が150〜1000mm2/秒である、一般式
RfO(CF2CF2O)m(CF2O)nRf
(ここで、Rfは前記定義と同じであり、m+n=20〜200、m:n=10〜90:90〜10であり、CF2CF2O基およびCF2O基は主鎖中にランダムに結合されている)で表わされるパーフルオロポリエーテル油
よりなる混合物基油が85〜70重量%、増稠剤が15〜30重量%を占める割合で用いられた、内径36mmのアルミニウム皿にグリース0.4gを塗布した状態で250℃の恒温槽中に24時間放置した後の蒸発損失率が10%未満、JIS K2220.5.7に準拠し、250℃、24時間の条件での離油度が20%未満、JIS K2220.5.14に準拠した-30℃の起動トルクが15N・cm未満である、-30℃になる寒冷地で使用される潤滑グリース組成物によって達成される。
パーフルオロポリエーテル油(A):ヘキサフルオロプロペンおよびテトラフルオロエチレンの光酸化重合により得られる。これは、40℃における動粘度が150〜1500mm2/秒、好ましくは150〜1200mm2/秒の範囲にあるものを使用することができ、このようなものはパーフルオロポリエーテル油(A)の一般式でa=15〜150という条件を満足させる。
パーフルオロポリエーテル油(B):テトラフルオロエチレンの光酸化重合により得られる。これは、40℃における動粘度が150〜1000mm 2 /秒の範囲にあるものを使用することができ、このようなものはパーフルオロポリエーテル油(B)の一般式でm+n=20〜200、m:n=10〜90:90〜10という条件を満足させる。
(a)パーフルオロポリエーテル基油に増稠剤をそれぞれ所定量配合し、3本ロールもしくは高圧ホモジナイザで十分に混練する方法、(b)加熱攪拌が可能な反応釜に、パーフルオロポリエーテル油と脂肪族カルボン酸とを加えて加熱溶融させ、そこに金属水酸化物(およびアミド化合物またはアルコール化合物)を所定量添加して金属塩化反応(およびアミド化反応またはエステル化反応)させて冷却した後、3本ロールもしくは高圧ホモジナイザで十分に混練する方法、あるいは(c)加熱攪拌が可能な反応釜に、パーフルオロポリエーテル油とイソシアンネートを加えて加熱し、そこにアミンを所定量添加して反応させ冷却した後、3本ロールもしくは高圧ホモジナイザで十分に混練する方法などによって行われる。
〔基油;Rfはパーフルオロ低級アルキル基〕
A-1:RfO〔CF(CF3)CF2O〕 a Rf 動粘度(40℃) 230mm2/秒
A-2:RfO〔CF(CF3)CF2O〕 a Rf 動粘度(40℃) 400mm2/秒
A-3:RfO〔CF(CF3)CF2O〕 a Rf 動粘度(40℃) 800mm2/秒
A-4:RfO〔CF(CF3)CF2O〕 a Rf 動粘度(40℃)1200mm2/秒
A-5:RfO〔CF(CF3)CF2O〕 a (CF2O) c Rf 動粘度(40℃) 400mm2/秒
A-6:RfO〔CF(CF3)CF2O〕 a (CF2O) c Rf 動粘度(40℃) 700mm2/秒
A-7:RfO〔CF(CF3)CF2O〕 a Rf 動粘度(40℃) 100mm2/秒
B-1:RfO(CF2CF2O)m(CF2O)nRf 動粘度(40℃) 160mm2/秒
B-2:RfO(CF2CF2O)m(CF2O)nRf 動粘度(40℃) 320mm2/秒
B-3:RfO(CF2CF2O)m(CF2O)nRf 動粘度(40℃) 90mm2/秒
C-1:ポリ(α-オレフィン) 動粘度(40℃) 400mm2/秒
C-2:ジペンタエリスリトールエステル 動粘度(40℃) 400mm2/秒
〔増稠剤〕
D-1:乳化重合法PTFE (Mn約10〜20万、平均一次粒径0.2μm)
D-2:けん濁重合法PTFE (Mn約1〜10万、平均一次粒径5μm)
D-3:溶液重合法FEP (Mn約5〜15万、平均一次粒径0.2μm)
D-4:ヘキサメチレンジイソシアネートとオクチルアミンとの反応生成物
D-5:アゼライン酸リチウムと12-ヒドロキシステアリン酸リチウムとのコンプレック ス石けん
上記基油の1〜2種類および増稠剤を用い、前記(a)の組成物調製方法でグリース組成物を調製した。
蒸発損失:36mm径のアルミニウム皿にグリース組成物約0.4gを塗布し、250℃の恒温 槽内に入れ、5時間後の蒸発損失率を測定
離油度:JIS K2220.5.7準拠;250℃、24時間後の離油度を測定
低温トルク:JIS K2220.5.14準拠;-30℃における起動トルクを測定
表
蒸発損 離油度 低温トル
例 基油 増稠剤 失率(%) (%) ク(N・cm)
実施例1 (A-2) 40% (B-1) 30% (D-1) 30% 2.0 9.9 9.8
〃 2 (A-5) 30% (B-2) 40% (D-1) 30% 2.5 8.7 9.3
〃 3 (A-2) 50% (B-2) 30% (D-3) 20% 2.3 10.2 9.0
〃 4 (A-2) 40% (B-2) 30% (D-1) 15% (D-5) 15% 2.4 11.0 9.5
〃 5 (A-3) 50% (B-1) 20% (D-1) 30% 1.5 7.5 10.4
〃 6 (A-3) 30% (B-2) 50% (D-4) 20% 1.1 9.4 9.8
〃 7 (A-4) 35% (B-2) 35% (D-1) 30% 0.8 5.7 10.2
〃 8 (A-1) 50% (B-1) 20% (D-1) 30% 7.5 14.9 10.0
〃 9 (A-6) 20% (B-2) 50% (D-1) 30% 7.7 11.3 7.0
比較例1 (A-5) 70% (D-1) 30% 10.5 16.0 >100
〃 2 (A-2) 50% (B-3) 20% (D-1) 30% 11.2 15.3 19.7
〃 3 (A-7) 20% (B-3) 50% (D-2) 40% 15.6 17.6 15.5
〃 4 (A-7) 35% (B-1) 30% (D-2) 30% 18.0 19.3 15.2
〃 5 (B-2) 60% (D-1) 40% 2.3 5.7 18.8
〃 6 (C-1) 80% (D-5) 20% 固化 固化 >100
〃 7 (A-3) 70% (D-1) 30% 3.2 6.2 >100
〃 8 (C-2) 80% (D-4) 20% 固化 1.5 >100
〃 9 (A-1) 54% (B-1) 36% (D-1) 10% − − −
Claims (3)
- 組成物合計中、
(A)動粘度(40℃)が150〜1500mm2/秒である、一般式
RfO〔CF(CF3)CF2O〕a(CF2O)cRf
(ここで、Rfは炭素数1〜5のパーフルオロアルキル基であり、aは15〜150、cは0または1以上の整数であり、CF(CF3)CF2O基およびCF2O基は主鎖中にランダムに結合されている)で表わされるパーフルオロポリエーテル油および
(B)動粘度(40℃)が150〜1000mm2/秒である、一般式
RfO(CF2CF2O)m(CF2O)nRf
(ここで、Rfは前記定義と同じであり、m+n=20〜200、m:n=10〜90:90〜10であり、CF2CF2O基およびCF2O基は主鎖中にランダムに結合されている)で表わされるパーフルオロポリエーテル油
よりなる混合物基油が85〜70重量%、増稠剤が15〜30重量%を占める割合で用いられた、内径36mmのアルミニウム皿にグリース0.4gを塗布した状態で250℃の恒温槽中に24時間放置した後の蒸発損失率が10%未満、JIS K2220.5.7に準拠し、250℃、24時間の条件での離油度が20%未満、JIS K2220.5.14に準拠した-30℃の起動トルクが15N・cm未満である、-30℃になる寒冷地で使用される潤滑グリース組成物。 - 組成物合計中、パーフルオロポリエーテル油(A)が10〜60重量%、パーフルオロポリエーテル油(B)が10〜60重量%を占める割合で用いられた請求項1記載の潤滑グリース組成物。
- 転がり軸受用途に用いられる請求項1または2記載の潤滑グリース組成物。