JP5712815B2 - インクジェット用紙 - Google Patents
インクジェット用紙 Download PDFInfo
- Publication number
- JP5712815B2 JP5712815B2 JP2011145141A JP2011145141A JP5712815B2 JP 5712815 B2 JP5712815 B2 JP 5712815B2 JP 2011145141 A JP2011145141 A JP 2011145141A JP 2011145141 A JP2011145141 A JP 2011145141A JP 5712815 B2 JP5712815 B2 JP 5712815B2
- Authority
- JP
- Japan
- Prior art keywords
- parts
- paper
- size press
- inkjet
- printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
また、商業印刷等の分野においては、デジタル情報を製版することなく紙などのメディアに直接印刷できるため少部数の印刷や可変情報印刷(バリアブル印刷)に最適であるインクジェット記録方式や電子写真記録方式が、オンデマンド印刷分野で導入されている。なかでも、インクジェット方式は記録時の騒音が少なく、カラー化が容易であること、高速記録が可能であること等の理由から近年、急速に発展をとげている。
こうした問題を解決するために、サイズ度の低い用紙を用いる技術(例えば、特許文献1参照)や、適度なサイズ性を有し、炭酸カルシウム等の填料を含有した電子写真とインクジェット記録共用紙(例えば、特許文献2参照)が提案されている。しかしながら、上記の提案にある記録媒体は、水性インクによる記録が行われるため、媒体上に形成された記録画像に水などが付着した場合、耐水性に劣り、再溶出により記録画像が損なわれるという欠点を有している。
また、本発明と同様、硫酸アルミニウムを用いる技術(例えば、特許文献13〜15参照)、界面活性剤を用いる技術、例えば、特許文献15〜16参照)が提案されているが、バーコード印刷適性あるいは印刷部耐水性が十分ではなかった。
(2)前記、表面サイズプレス処理剤にカチオン化ポリビニルアルコールあるいは、カチオン化デンプンを含有する(1)記載のインクジェット用紙。
(3)前記、表面サイズプレス処理剤に表面サイズ剤としてスチレン-アクリル系共重合体を含有する事を特徴とする(1)又は(2)項記載のインクジェット用紙。
本発明で使用される表面サイズプレス処理剤は、硫酸アルミニウムとHLB値が8.0以上12.5以下の界面活性剤を含有する。
本発明で用いるインクジェット用紙の原紙としては、原料パルプとして化学パルプ(NBKP、LBKP等)、機械パルプ(GP、CGP、RGP、PGW、TMP等)、脱墨古紙パルプ(DIP等)等の木材パルプを単独または任意の比率で混合して使用される。また、ホワイトカーボン、クレー、無定形シリカ、タルク、酸化チタン、炭酸カルシウムなどの製紙用填料が抄紙時に添加される。また、必要に応じて、内添サイズ剤、定着剤、紙力増強剤、歩留り向上剤、耐水化剤、紫外線吸収剤等の公知公用の抄紙用薬品が適宜添加され、公知公用の抄紙機にて抄紙される。原紙の抄造条件についても、特に限定はない。抄紙機としては、例えば、長網式抄紙機、ギャップフォーマー型抄紙機、円網式抄紙機、短網式抄紙機等の商業規模の抄紙機が、目的に応じて適宜選択して使用できる。
本発明のインクジェット用紙に使用する原紙は、特に限定されるものではないが、一般的には、坪量が50〜200g/m2程度の範囲にある原紙が、目的に応じて適宜選択して使用される。
表面サイズプレス処理剤を紙原紙へ塗布するための装置としては、特に限定されるものではないが、例えば2ロールサイズプレス、ブレードメタリングサイズプレス、ロッドメタリングサイズプレス、ゲートロールコーターなどのロールコーター、トレーリング、フレキシブル、ロールアプリケーション、ファウンテンアプリケーション、ショートドゥエル等のベベルタイプやベントタイプのブレードコーターロッドブレードコーター、バーコーター、エアーナイフコーター、カーテンコーター、スプレーコーター、グラビアコーターなどの公知公用の装置が適宜使用される。なお、表面処理剤組成物を塗布後の湿潤塗被層を乾燥する方法としては、例えば、蒸気乾燥、ガスヒーター乾燥、電気ヒーター乾燥、赤外線ヒーター乾燥等の各種方式が採用できる。
ユーカリ、オーク材を原料としてECF漂白されたLBKP100%を380mlCSFに叩解し、填料として軽質炭酸カルシウムを10.0%、内添サイズ剤としてアルケニル無水コハク酸(ナショナルスターチ社製、ファイブラン81)を0.07%、歩留向上剤(協和産業社製、パーコール182)を0.02%で長網多筒型抄紙機によって抄紙し、坪量81.4g/m2の原紙を作成した。
上記原紙上に、硫酸アルミニウム30部、ポリオキシエチレンラウリルエーテル(花王製、エマルゲン106 、HLB値10.5)5部、カチオン化デンプン(王子コーンスターチ製、エースK220)64部、カチオン性スチレン-アクリル系共重合体(星光PMC社、SE2220)1部の混合塗布液を両面で2.5g/m2となるように2ロールサイズプレス機で、塗布後乾燥しインクジェット用紙を得た。
上記原紙上に、硫酸アルミニウム30部、ポリオキシエチレンラウリルエーテル(花王製、エマルゲン106 、HLB値10.5)2部、カチオン化デンプン(王子コーンスターチ製、エースK220)67部、カチオン性スチレン-アクリル系共重合体(星光PMC社、SE2220)1部の混合塗布液を両面で2.5g/m2となるように2ロールサイズプレス機で、塗布後乾燥しインクジェット用紙を得た。
上記原紙上に、硫酸アルミニウム30部、ポリオキシエチレンラウリルエーテル(花王製、エマルゲン106 、HLB値10.5)8部、カチオン化デンプン(王子コーンスターチ製、エースK220)61部、カチオン性スチレン-アクリル系共重合体(星光PMC社、SE2220)1部の混合塗布液を両面で2.5g/m2となるように2ロールサイズプレス機で、塗布後乾燥しインクジェット用紙を得た。
上記原紙上に、硫酸アルミニウム15部、ポリオキシエチレンラウリルエーテル(花王製、エマルゲン106 、HLB値10.5)5部、カチオン化デンプン(王子コーンスターチ製、エースK220)79部、カチオン性スチレン-アクリル系共重合体(星光PMC社、SE2220)1部の混合塗布液を両面で2.5g/m2となるように2ロールサイズプレス機で、塗布後乾燥しインクジェット用紙を得た。
上記原紙上に、硫酸アルミニウム35部、ポリオキシエチレンラウリルエーテル(花王製、エマルゲン106 、HLB値10.5)5部、カチオン化デンプン(王子コーンスターチ製、エースK220)59部、カチオン性スチレン-アクリル系共重合体(星光PMC社、SE2220)1部の混合塗布液を両面で2.5g/m2となるように2ロールサイズプレス機で、塗布後乾燥しインクジェット用紙を得た。
上記原紙上に、硫酸アルミニウム30部、ポリオキシエチレンラウリルエーテル(花王製、エマルゲン404 、HLB値8.8)5部、カチオン化デンプン(王子コーンスターチ製、エースK220)64部、カチオン性スチレン-アクリル系共重合体(星光PMC社、SE2220)1部の混合塗布液を両面で2.5g/m2となるように2ロールサイズプレス機で、塗布後乾燥しインクジェット用紙を得た。
上記原紙上に、硫酸アルミニウム30部、ポリオキシエチレンラウリルエーテル(花王製、エマルゲン404、HLB値8.8)5部、カチオン化デンプン(王子コーンスターチ製、エースK220)64部、カチオン性スチレン-アクリル系共重合体(星光PMC社、SE2220)1部の混合塗布液を両面で2.5g/m2となるように2ロールサイズプレス機で、塗布後乾燥しインクジェット用紙を得た。
上記原紙上に、硫酸アルミニウム30部、ポリオキシエチレンラウリルエーテル(花王製、エマルゲン106、HLB値10.5)5部、酸化デンプン(王子コーンスターチ製、エースA)64部、カチオン性スチレン-アクリル系共重合体(星光PMC社、SE2220)1部の混合塗布液を両面で2.5g/m2となるように2ロールサイズプレス機で、塗布後乾燥しインクジェット用紙を得た。
上記原紙上に、硫酸アルミニウム30部、ポリオキシエチレンラウリルエーテル(花王製、エマルゲン106 、HLB値10.5)5部、カチオン化ポリビニールアルコール(電気化学製、PC5500)64部、カチオン性スチレン-アクリル系共重合体(星光PMC社、SE2220)1部の混合塗布液を両面で2.5g/m2となるように2ロールサイズプレス機で、塗布後乾燥しインクジェット用紙を得た。
上記原紙上に、硫酸アルミニウム30部、ポリオキシエチレンラウリルエーテル(花王製、エマルゲン106 、HLB値10.5)5部、カチオン化デンプン(王子コーンスターチ製、エースK220)65部の混合塗布液を両面で2.5g/m2となるように2ロールサイズプレス機で、塗布後乾燥しインクジェット用紙を得た。
上記原紙上に、実施例1と同様の混合塗布液を両面で0.7g/m2となるように2ロールサイズプレス機で、塗布後乾燥しインクジェット用紙を得た。
上記原紙上に、実施例1と同様の混合塗布液を両面で4.5g/m2となるように2ロールサイズプレス機で、塗布後乾燥しインクジェット用紙を得た。
上記原紙上に、硫酸アルミニウム30部、ポリオキシエチレンラウリルエーテル(花王製、エマルゲン106 、HLB値10.5)5部、カチオン化デンプン(王子コーンスターチ製、エースK220)64部、アニオン性スチレン-アクリル系共重合体(荒川化学工業社、ポリマロン1301S)1部の混合塗布液を両面で2.5g/m2となるように2ロールサイズプレス機で、塗布後乾燥しインクジェット用紙を得た。
上記原紙上に、ポリオキシエチレンラウリルエーテル(花王製、エマルゲン106 、HLB値10.5)5部、カチオン化デンプン(王子コーンスターチ製、エースK220)94部、スチレン-アクリル系共重合体(星光PMC社、SE2220)1部の混合塗布液を両面で2.5g/m2となるように2ロールサイズプレス機で、塗布後乾燥しインクジェット用紙を得た。
上記原紙上に、硫酸アルミニウム5部、ポリオキシエチレンラウリルエーテル(花王製、エマルゲン106 、HLB値10.5)5部、カチオン化デンプン(王子コーンスターチ製、エースK220)89部、スチレン-アクリル系共重合体(星光PMC社、SE2220)1部の混合塗布液を両面で2.5g/m2となるように2ロールサイズプレス機で、塗布後乾燥しインクジェット用紙を得た。
上記原紙上に、硫酸アルミニウム45部、ポリオキシエチレンラウリルエーテル(花王製、エマルゲン106 、HLB値10.5)5部、カチオン化デンプン(王子コーンスターチ製、エースK220)49部、スチレン-アクリル系共重合体(星光PMC社、SE2220)1部の混合塗布液を両面で2.5g/m2となるように2ロールサイズプレス機で、塗布後乾燥しインクジェット用紙を得た。
上記原紙上に、硫酸アルミニウム30部、カチオン化デンプン(王子コーンスターチ製、エースK220)69部、スチレン-アクリル系共重合体(星光PMC社、SE2220)1部の混合塗布液を両面で2.5g/m2となるように2ロールサイズプレス機で、塗布後乾燥しインクジェット用紙を得た。
上記原紙上に、硫酸アルミニウム30部、ポリオキシエチレンラウリルエーテル(花王製、エマルゲン106 、HLB値10.5)0.5部、カチオン化デンプン(王子コーンスターチ製、エースK220)68.5部、スチレン-アクリル系共重合体(星光PMC社、SE2220)1部の混合塗布液を両面で2.5g/m2となるように2ロールサイズプレス機で、塗布後乾燥しインクジェット用紙を得た。
上記原紙上に、硫酸アルミニウム30部、ポリオキシエチレンラウリルエーテル(花王製、エマルゲン106 、HLB値10.5)15部、カチオン化デンプン(王子コーンスターチ製、エースK220)54部、スチレン-アクリル系共重合体(星光PMC社、SE2220)1部の混合塗布液を両面で2.5g/m2となるように2ロールサイズプレス機で、塗布後乾燥しインクジェット用紙を得た。
上記原紙上に、硫酸アルミニウム30部、アセチレングリコール(日信化学工業製、サーフィノールSE 、HLB値6.0)5部、カチオン化デンプン(王子コーンスターチ製、エースK220)64部、スチレン-アクリル系共重合体(星光PMC社、SE2220)1部の混合塗布液を両面で2.5g/m2となるように2ロールサイズプレス機で、塗布後乾燥しインクジェット用紙を得た。
上記原紙上に、硫酸アルミニウム30部、ポリオキシエチレンオレイルエーテル(花王製
、エマルゲン420 、HLB値13.6)5部、カチオン化デンプン(王子コーンスタ
ーチ製、エースK220)64部、スチレン-アクリル系共重合体(星光PMC社、SE
2220)1部の混合塗布液を両面で2.5g/m2となるように2ロールサイズプレス
機で、塗布後乾燥しインクジェット用紙を得た。
各実施例および比較例で得たインクジェット用紙をミヤコシ製高速インクジェット プリンティングシステムMJP600で、「UCC/EAN128コード」を印刷した後、インクジェット印刷されたEAN128バーコードについて、バーコード検証機「Inspector D4000」(RJS社製)を用いてバーコードを10回走査させ評価した。
〈評価基準〉
5:バーコードリーダーの10回の走査の内、10回読み取れる。
4:バーコードリーダーの10回の走査の内、9回読み取れる。
3:バーコードリーダーの10回の走査の内、6以上9回未満読み取れる。
2:バーコードに対して複数の走査線を通過させると読み取れるレベル。
1:読み取ることが出来ないレベル。
なお、評価が2以下のものは、実用上問題がある。
各実施例および比較例で得たインクジェット用紙をミヤコシ製高速インクジェット プリンティングシステムMJP600で、黒色のブロックパターンを印刷速度150m/minにて印刷した後、インクジェット 印刷を行った部位について、インクの転写汚れについて、目視判定を行った。
〈評価基準〉
5(優)−1(劣)
なお、評価が2以下のものは、実用上問題がある。
各実施例および比較例で得たインクジェット用紙をミヤコシ製高速インクジェット プリンティングシステムMJP600で、日本規格協会発行の「カラーディジタル標準画像データ/N3」を印刷した後、インクジェット 印刷後の用紙を水道水中に30秒間浸積した後、自然乾燥した。その後、印刷画像の滲みの程度を目視で評価した。
〈評価基準〉
5(優)−1(劣)
なお、評価が2以下のものは、実用上問題がある。
各実施例および比較例で得たインクジェット用紙をミヤコシ製高速インクジェット プリンティングシステムMJP600で、「日本規格協会発行の「カラーディジタル標準画像データ/N3」を印刷した後、インクジェット印刷部をウエスで10回擦り、印刷部コスレ汚れの程度を目視で評価した。
〈評価基準〉
5(優)−1(劣)
なお、評価が2以下のものは、実用上問題がある。
各実施例および比較例で得たインクジェット用紙をミヤコシ製高速インクジェット プリンティングシステムMJP600で、日本規格協会発行の「カラーディジタル標準画像データ/N3」を印刷した後、印刷部の印刷ムラの程度を目視で評価した。
〈評価基準〉
5(優)−1(劣)
なお、評価が2以下のものは、実用上問題がある。
Claims (2)
- 顔料塗工層を有しないインクジェット記録用紙において、少なくとも片面に塗布される表面サイズプレス処理剤中に、表面サイズプレス処理剤固形分総質量100部に対し、硫酸アルミニウムを10〜40質量部、HLB値が8.0以上12.5以下である界面活性剤を1〜10質量部含有することを特徴とするインクジェット用紙であって、前記表面サイズプレス処理剤が表面サイズ剤としてスチレン-アクリル系共重合体を含有することを特徴とするインクジェット用紙。
- 前記表面サイズプレス処理剤にカチオン化ポリビニルアルコールあるいは、カチオン化デンプンを含有する事を特徴とする請求項1記載のインクジェット用紙。