JP5653555B1 - 二成分混和型イオン徐放性粘膜調整材組成物 - Google Patents
二成分混和型イオン徐放性粘膜調整材組成物 Download PDFInfo
- Publication number
- JP5653555B1 JP5653555B1 JP2014113584A JP2014113584A JP5653555B1 JP 5653555 B1 JP5653555 B1 JP 5653555B1 JP 2014113584 A JP2014113584 A JP 2014113584A JP 2014113584 A JP2014113584 A JP 2014113584A JP 5653555 B1 JP5653555 B1 JP 5653555B1
- Authority
- JP
- Japan
- Prior art keywords
- glass
- release
- ion sustained
- ion
- sustained release
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
義歯は患者の粘膜面に合わせて製作されるため、使用開始時においては患者の粘膜に良く適合し、通常であれば何ら問題なく咀嚼・嚥下・発音などの機能回復効果を発揮する。しかし長期間使用を続けると、患者の顎堤が吸収する等により、義歯床との適合が悪くなることがある。
粘膜面と義歯床の適合が悪くなった場合、義歯が局所的に強く当たることにより、口腔粘膜の発赤、及び腫脹が発生することがある。そのような症例においては、義歯床を新しく作り変える必要がある。その場合、一般的には、義歯床に粘膜調整材と呼ばれる柔らかい材料を塗布した状態で使用することにより、患者の負担を軽減したまま粘膜面の発赤、及び腫脹を回復する手法が用いられる。さらにその後、粘膜調整材を義歯床用裏装材と呼ばれる硬化性材料に置換することにより、より患者の粘膜面に適合した義歯床に作り変える、裏装または裏打ちという手法が用いられる。
このような粘膜調整材は、非架橋性(メタ)アクリレート系ポリマーを主成分とする粉材と、可塑材及びエタノール等の有機溶媒を主成分とする液材から構成される。この粉材と液材を混合し、流動性があるうちに義歯床の粘膜面に盛り上げ、流動性が低下した頃に口腔内に装着させ一定時間保持した後、義歯を口腔外に取り出し、余剰分のトリミングする方法が一般に行われている。
従来の歯科用粘膜調整材組成物は、非架橋性(メタ)アクリレート系ポリマーと可塑材が主成分であるために、粉材と液材が非常に馴染みにくく操作性が悪いばかりでなく、混合・膨潤した状態においても非常に柔らかい性状を維持しており、義歯床に対する塗布性、及び形態修正時における切削性に課題があることが知られている。例えば、粘膜調整時に形態修正をする際、切削性が悪いと研削材の回転部に歯科用粘膜調整材組成物の一部が絡みつき作業性が悪いという課題が認められる。さらに従来の粘膜調整材は、硬化性でないために粘膜面にプラーク等の汚れが付着しやすく、また細菌や真菌等が増殖することから、衛生面においても大きな課題を有していた。
以上のように、粘膜調整材はその使用方法及び口腔内の過酷な環境において多くの課題を有している。これらの課題を改善する従来技術として、粘膜調整材または粘膜調整材を含む義歯全体をコーティングする材料の改善方法が提案されている。例えば、汚れが付着しにくい成分、切削性が向上する成分、またはフッ素等のイオンを徐放する成分を粘膜調整材または前記コーティング材料に配合する等の発明がこれに該当する。
具体的には、
粉材と液材から成る二成分混和型イオン徐放性粘膜調整材組成物であって、
(a)非架橋性(メタ)アクリレート系ポリマー、
(b)イオン徐放性ガラスを含む粉材成分と
(c)可塑材、
(d)有機溶媒を含む液材成分とから構成されることを特徴とする二成分混和型イオン徐放性粘膜調整材組成物である。
また、前記二成分混和型イオン徐放性粘膜調整材組成物に粉材成分として(e)充填材を含んでいることを特徴とする二成分混和型イオン徐放性粘膜調整材組成物である。
また、(b)イオン徐放性ガラスが少なくともフッ化物イオンを徐放することを特徴とする
二成分混和型イオン徐放性粘膜調整材組成物である。
また、(b)イオン徐放性ガラスがフッ化物イオンを徐放し、さらにストロンチウムイオン、アルミニウムイオン及びホウ酸イオンの内から一種類以上のイオンを徐放するイオン徐放性ガラスであることが好ましい。さらに、少なくともフッ化物イオン、ストロンチウムイオン及びホウ酸イオンを徐放することが好ましい。
本発明の二成分混和型イオン徐放性粘膜調整材組成物は、
(a)非架橋性(メタ)アクリレート系ポリマー、
(b)イオン徐放性ガラスを含む粉材成分と
(c)可塑材、
(d)有機溶媒を含む液材成分とから構成されていることを特徴とする。
これらの非架橋性(メタ)アクリレート系ポリマーの中でもポリメチルメタクリレート、ポリエチルメタクリレート、メチルメタクリレートとエチルメタクリレートの共重合コポリマーを用いることが好ましい。
非架橋性(メタ)アクリレート系ポリマーの含有量が10重量%未満の場合は可塑材が過剰となり、弾性が維持できなくなるため、操作性及び粘膜調整能が低下する等の問題がある。一方、80重量%を越える場合は、非架橋性(メタ)アクリレート系ポリマーが過剰となり、混合・膨潤した材料が硬すぎて、操作性が低下する等の問題がある。
本発明の二成分混和型イオン徐放性粘膜調整材組成物はイオン徐放性ガラスを含み、そのガラスからガラス組成に基因したイオンが持続的に徐放することを特徴とする。
本発明に用いるイオン徐放性ガラスは非晶質構造であるが、一部結晶質構造を含んでいても何等問題はなく、さらにそれらの非晶質構造を有するガラスと結晶構造を有するガラスの混合物であっても何等問題はない。ガラス構造が非晶質であるか否かの判断はX線回折分析や透過型電子顕微鏡等の分析機器を用いて行うことができる。その中でも本発明に用いるイオン徐放性ガラスは外部環境におけるイオン濃度との平衡関係により各種イオンが徐放することから、均質な構造である非晶質構造であることが好ましい。
粉砕等によって所望の平均粒径に微粉砕されたイオン徐放性ガラスを含有する水性分散体中に、一般式(I)
また一般式(I)で表されるシラン化合物の低縮合体であることがより好ましい。例えばテトラメトキシシランおよびテトラエトキシシランを部分加水分解して縮合させた低縮合シラン化合物である。これらの化合物は単独または組み合わせて使用することができる。
熱処理後、熱処理物の解砕は剪断力または衝撃力を加えることにより容易に可能であり、解砕方法としては上記反応に用いた設備などで行うことができる。
酸性ポリマー溶液中に溶解したポリマーの重量分子量は2000〜50000の範囲であり、5000〜40000の範囲にある。2000未満の重量平均分子量を有する酸性ポリマーで処理した表面処理イオン徐放性ガラスはイオン徐放性が低くなる傾向にある。50000を超える重量平均分子量を有する酸性ポリマーは酸性ポリマー溶液の粘性が上がり、酸性ポリマー処理を行うことが困難となる。また酸性ポリマー溶液中に占める酸性ポリマー濃度は3〜25重量%の範囲が好ましく、より好ましくは8〜20重量%の範囲である。酸性ポリマー濃度3重量%未満になると上記で述べた酸性ポリマー相が脆弱になる。また酸性ポリマー濃度が25重量%を超えるとポリシロキサン層(多孔質)を拡散しにくくなる反面、イオン徐放性ガラスに接触すると酸−塩基反応が速く、反応中に硬化が始まり凝集が起こる等の問題が生じる。またポリシロキサンで被覆されたイオン徐放性ガラスに対する酸性ポリマー溶液の添加量は6〜40重量%の範囲が好ましく、より好ましくは10〜30重量%である。この添加量で換算するとポリシロキサン被覆イオン徐放性ガラスに対する酸性ポリマー量は1〜7重量%、また水量は10〜25重量%の範囲が最適値である。
以下の手法によってイオン徐放性ガラス又は他のフィラーがイオン徐放性を有しているか否かを判断することができる。
蒸留水100gに対してイオン徐放性ガラス又は他のフィラーを0.1g加え、1時間撹拌させた時の蒸留水中に徐放したイオン濃度(F1)又はイオン種に起因した元素濃度(F1)と、2時間撹拌した時の蒸留水中に徐放したイオン濃度(F1)又はイオン種に起因した元素濃度(F2)が下式(1)の関係を満足する場合をイオン徐放とみなすことができる。
F2 > F1 ・・・・式(1)
また、イオン徐放性ガラスから徐放するイオンが複数ある場合は、すべてのイオン濃度又は元素濃度が式(1)を満足する必要はなく、少なくとも一つのイオン濃度又は元素濃度が式(1)を満足した場合をイオン徐放とみなすことができる。
本発明に用いるイオン徐放性ガラスはイオン徐放の効果に基因する酸中和能を有していることが好ましい。酸中和能はpHを4.0に調整した乳酸水溶液10gに対してイオン徐放性ガラスを0.1g加え、5分間撹拌させた時のpH変化を測定することにより確認することできる。その時のpHが5.5以上、より好ましくは6.0以上、最も好ましくは6.5以上を示したとき酸中和能が発現するとみなすことができる。
これら可塑材の中でもカルボン酸エステルが好ましく、より好ましくは安息香酸ベンジル,ジブチルセバチート,ジブヂルフタレート等である。
これら有機溶媒の中でもアルコール類が好ましく、より好ましくはエタノール、イソプロピルアルコール等である。
本発明の二成分混和型イオン徐放性粘膜調整材組成物に用いることができる(e)充填材は特に限定されず、可塑材及び有機溶媒に対して膨潤しないものであれば有機成分、無機成分及びそれらの混合物または複合物でも何等制限なく使用することができる。
これらの充填材は単独だけでなく、複数を組み合わせて用いることができる。
目的:二成分混和型イオン徐放性粘膜調整材組成物の切削性を評価する。
方法:本発明の二成分混和型イオン徐放性粘膜調整材組成物を1.2g(粉材):1mL(液材)の割合で混合・膨潤させた後、混合物をステンレス製金型(20φ×2mm:円盤状)に充填した後、ナイロンフィルムを介してガラス板で圧接し、30分間放置することにより試験体を作製した。試験体を技工用カーバイドバーにより切削し、その切削性を以下の4段階で評価した。
◎・・・切削性が非常に良好であり、切削面に凹凸が認められない。
○・・・切削性が良好であり、切削面にわずかに凹凸が認められる。
△・・・粘膜調整材が研削材に絡みつき、切削しにくい。または切削面にやや凹凸が認められる。
×・・・粘膜調整材が研削材に絡みつき、切削しにくい。または切削面に凹凸が認められる。
目的:二成分混和型イオン徐放性粘膜調整材組成物からのフッ素放出特性を評価する。
方法:本発明の二成分混和型イオン徐放性粘膜調整材組成物を1.2g(粉材):1mL(液材)の割合で混合・膨潤させた後、混合物をステンレス製金型(15φ×1mm:円盤状)に充填した後、ナイロンフィルムを介してガラス板で圧接し、30分間放置することにより試験体を作製した。試験体を5mLの蒸留水が入ったプラスチック製容器に入れ、密封後37℃恒温器中に1週間放置した。1週間後容器を恒温器から取り出し、円盤状試験体から溶出したフッ素量をフッ素イオン複合電極(Model 96-09:オリオンリサーチ社製)及びイオンメーター(Model 720A:オリオンリサーチ社製)を用いて測定した。測定時にイオン強度調整剤としてTISABIII(オリオンリサーチ社製)を0.5mL添加した。また検量線の作成は0.02、0.1、1、10、50ppmの標準液を用いて行った。フッ素放出量は0.2ppm以上が好ましく、0.5ppm以上がさらに好ましい。
目的:二成分混和型イオン徐放性粘膜調整材組成物からのイオン放出特性を評価する。
方法:本発明の二成分混和型イオン徐放性粘膜調整材組成物を1.2g(粉材):1mL(液材)の割合で混合・膨潤させた後、混合物をステンレス製金型(15φ×1mm:円盤状)に充填した後、ナイロンフィルムを介してガラス板で圧接し、30分間放置することにより試験体を作製した。試験体を5mLの蒸留水が入ったプラスチック製容器に入れ、密封後37℃恒温器中に1週間放置した。1週間後容器を恒温器から取り出し、円盤状試験体から溶出したイオン量についてICP発光分析装置を用いて測定した。なお、各金属イオン量は、各イオンの標準試料(1ppm、2.5ppm、5ppm、10ppm)から求めた検量線を用いて換算した。
本発明に用いるイオン徐放性ガラスの酸中和能を以下の方法で評価した。pHを4.0に調整した乳酸水溶液10gに対してイオン徐放性ガラス及び各種フィラーを0.1g加え、5分間撹拌した後のpHをpHメーター(D-51:堀場製作所)を用いて測定することにより評価した。
目的:二成分混和型イオン徐放性粘膜調整材組成物の酸中和能を評価する。
方法:本発明の二成分混和型イオン徐放性粘膜調整材組成物を1.2g(粉材):1mL(液材)の割合で混合・膨潤させた後、混合物をステンレス製金型(15φ×1mm:円盤状)に充填した後、ナイロンフィルムを介してガラス板で圧接し、30分間放置することにより試験体を作製した。試験体を5mLの乳酸水溶液(pH4.0に調整)中に浸漬した。その後、6時間及び24時間経過後の乳酸水溶液のpHをpHメーター(D-51:堀場製作所)を用いて測定した。
PEMA50:ポリメチルメタクリレート(平均粒子径(D50):50μm、重量平均分子量:30万、形状:球状)
F1:イオン徐放性ガラス1
F2:イオン徐放性ガラス2
F3:イオン徐放性ガラス3
BB:安息香酸ベンジル
DBS:ジブチルセバチート
DBP:ジブチルフタレート
EtOH:エタノール
PMMA−C:架橋ポリメチルメタクリレート(MMA:95部及び1G5部から成るポリメチルメタクリレート、平均粒子径(D50):10μm、形状:球状)
二酸化ケイ素、酸化アルミニウム、酸化ホウ素、フッ化ナトリウム、炭酸ストロンチウムの各種原料(ガラス組成:SiO2 23.8質量%、Al2O3 16.2質量%、B2O3 10.5質量%、SrO 35.6質量%、Na2O 2.3質量%、F11.6質量%)をボールミルを用いて均一に混合し原料混合品を調製した後、その原料混合品を溶融炉中で1400℃にて溶融した。その融液を溶融炉から取り出し冷鋼板上、ロールまたは水中で冷却してガラスを生成した。4連式振動ミルのアルミナポット(内容積3.6リットル)中に直径6mmφのアルミナ玉石4kgを投入後、上記で得たガラスを500g投入して40時間粉砕を行い、イオン徐放性ガラス1を得た。このイオン徐放性ガラス1の50%平均粒子径をレーザー回折式粒度測定機(マイクロトラックSPA:日機装社製)により測定した結果、1.2μmであった。このイオン徐放性ガラス1から放出されるイオンに基因した元素量(フッ化物イオンのみイオン量)を測定し、(1)式への適合性を確認した。その結果を表1に示した。
以下に示すポリシロキサン処理及び酸性ポリマー処理を行い表面処理したイオン徐放性ガラス2を得た。
前述のイオン徐放性ガラス1を500g、シラン化合物(予めテトラメトキシシラン5g、水1000g及びエタノール100gを2時間室温で撹拌し得られたシラン化合物の低縮合物)を万能混合攪拌機に投入し、90分間撹拌混合した。その後、140℃にて熱処理を30時間施し、熱処理物を得た。この熱処理物をヘンシェルミキサーを用いて解砕し、ポリシロキサン被覆イオン徐放性ガラスを得た。このポリシロキサンで被覆されたイオン徐放性ガラス500gを撹拌しつつ、酸性ポリマー水溶液(ポリアクリル酸水溶液:ポリマー濃度13重量%、重量平均分子量20000;ナカライ社製)をヘンシェルミキサーを用いて噴霧した。その後、熱処理(100℃3時間)を施し、表面処理したイオン徐放性ガラス2を製造した。このイオン徐放性ガラス2の50%平均粒子径をレーザー回折式粒度測定機(マイクロトラックSPA:日機装社製)により測定した結果、1.3μmであった。この表面処理したイオン徐放性ガラス2から放出されるイオンに基因した元素量(フッ化物イオンのみイオン量)を測定し、(1)式への適合性を確認した。その結果を表1に示した。
二酸化ケイ素、酸化アルミニウム、酸化ホウ素、フッ化ナトリウム、炭酸ストロンチウムの各種原料を混合後、1400℃にてその混合物を溶融してガラス(ガラス組成:SiO2 19.8質量%、Al2O3 19.8質量%、B2O3 11.7質量%、SrO 35.0質量%、Na2O 2.3質量%、F11.4質量%)を得た。次に生成したガラスを振動ミルを用いて10時間粉砕し、ガラス3を得た。前述のガラス3を500g、シラン化合物(予めテトラメトキシシラン10g、水1500g、エタノール100g、メタノール70g及びイソプロパノール50gを2時間室温で撹拌し得られたシラン化合物の低縮合物)を万能混合攪拌機に投入し、90分間撹拌混合した。その後、140℃にて熱処理を30時間施し、熱処理物を得た。この熱処理物をヘンシェルミキサーを用いて解砕し、ポリシロキサンで被覆したイオン徐放性ガラスを得た。このポリシロキサンで被覆したガラス500gを撹拌しつつ、酸性ポリマー水溶液(ポリアクリル酸水溶液:ポリマー濃度13重量%、重量平均分子量20000;ナカライ社製)をヘンシェルミキサーを用いて噴霧した。その後、熱処理(100℃3時間)を施し、表面処理したイオン徐放性ガラス3を製造した。
この表面処理したイオン徐放性ガラス3の50%平均粒子径をレーザー回折式粒度測定機(マイクロトラックSPA:日機装社製)により測定した結果、3.1μmであった。この表面処理したイオン徐放性ガラス3から放出されるイオンに基因した元素量(フッ化物イオンのみイオン量)を測定し、(1)式への適合性を確認した。その結果を表1に示した。
比較例1は本発明の構成要件の中でも(b)イオン徐放性ガラスを含んでいない二成分混和型イオン徐放性粘膜調整材組成物であり、表4が示すように切削性が悪く、かつフッ素を含むイオン徐放性を有しないことが確認された。また酸中和能を有していないことが確認された。
比較例2は本発明の構成要件の中でも(c)有機溶媒を含んでいない二成分混和型イオン徐放性粘膜調整材組成物であり、表4が示すように試験体が作製不可能であることが確認された。
 
Claims (4)
- 粉材と液材から成る二成分混和型イオン徐放性粘膜調整材組成物であって
(a)非架橋性(メタ)アクリレート系ポリマー
(b)イオン徐放性ガラスを含む粉材成分と
(c)可塑材
(d)有機溶媒を含む液材成分とから構成され、
イオン徐放性ガラス (b)の組成範囲は
SiO2 15〜35質量%、
Al2O3 15〜30質量%、
B2O3 5〜20質量%、
SrO 20〜45質量%、
F 5〜15質量%、
Na2O 0〜10質量%であり、シラン化合物によりイオン徐放性ガラス表面を被覆した後に、酸性ポリマーにより表面処理されていることを特徴とする二成分混和型イオン徐放性粘膜調整材組成物。 - イオン徐放性ガラス (b)が
pHを4.0に調整した乳酸水溶液10gに対してイオン徐放性ガラスを0.1g加え、5分間撹拌させた時のpH変化を測定することにより確認することできる。その時のpHが5.5以上であることを特徴とする請求項1に記載の二成分混和型イオン徐放性義歯床用関連材料組成物。 - ポリシロキサン被覆イオン徐放性ガラスに対する酸性ポリマーの量は1〜7重量%であることを特徴とする請求項1に記載の二成分混和型イオン徐放性義歯床用関連材料組成物。
- イオン徐放性ガラス表面を被覆するシラン化合物の添加量はイオン徐放性ガラス100重量部に対して、シラン化合物のSiをSiO2に換算して0.1〜10重量部であることを特徴とする請求項1に記載の二成分混和型イオン徐放性義歯床用関連材料組成物。