JP5221843B2 - インクジェットインク用水性顔料分散体およびインクジェット記録用水性インク - Google Patents
インクジェットインク用水性顔料分散体およびインクジェット記録用水性インク Download PDFInfo
- Publication number
- JP5221843B2 JP5221843B2 JP2005170822A JP2005170822A JP5221843B2 JP 5221843 B2 JP5221843 B2 JP 5221843B2 JP 2005170822 A JP2005170822 A JP 2005170822A JP 2005170822 A JP2005170822 A JP 2005170822A JP 5221843 B2 JP5221843 B2 JP 5221843B2
- Authority
- JP
- Japan
- Prior art keywords
- meth
- pigment
- ink
- aqueous
- acrylic copolymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
また顔料粒子は、記録媒体の表面状態の影響を受けやすい欠点があった。例えば、普通紙や再生紙等の表面コーティングされていない紙のような記録媒体では、顔料粒子が該紙繊維の間に入り込んでしまい、紙表面上に残りずらく、印刷濃度が得られないといった欠点があった。また、該紙繊維の構成やサイズ剤等の処理剤の影響によりにじみや色むらが発生しやすく、にじみや色むらの程度もまちまちであるため、均一な品質を提供することが難しいといった欠点もあった。
また、写真印刷等に使用するインクジェット専用紙等の表面コーティングを有する記録媒体では、顔料粒子が繊維間に入り込まないため印刷濃度は保たれるが、最も高い要求特性である光沢性は十分でなく、印字dutyが異なる部分での光沢性に差があることがあった。
しかし該インクも、インクジェット専用紙に印字した場合、光沢感がでないといった問題があった。
即ち本発明は、(メタ)アクリル共重合体、顔料、及び塩基性物質を含有するインクジェットインク用水性顔料分散体であって、(メタ)アクリル共重合体が、ベンジル(メタ)アクリレートと(メタ)アクリル酸とを必須構成モノマーとし、該アクリル共重合体を構成する全モノマー量に対するベンジル(メタ)アクリレートと(メタ)アクリル酸との合計が85質量%以上であり、酸価40〜110mgKOH/gであるインクジェットインク用水性顔料分散体を提供する。
本発明で使用する(メタ)アクリル共重合体は、ベンジル(メタ)アクリレートと(メタ)アクリル酸とを必須構成モノマーとし、該アクリル共重合体を構成する全モノマー量に対するベンジル(メタ)アクリレートと(メタ)アクリル酸との合計が85質量%以上であり、酸価40〜110mgKOH/gである。
ベンジル(メタ)アクリレートとしては、ベンジルアクリレートとベンジルメタクリレートがあるが、ベンジルメタクリレートが、本発明の効果をより発現でき、且つ容易に入手でき安価である点で好ましい。
(メタ)アクリル酸としては、アクリル酸とメタクリル酸がある。(メタ)アクリル酸は、塩基により中和した場合の水に対する溶解度を広く制御することができ、入手がしやすく安価であるため好ましい。
使用する汎用モノマーとしては、各種(メタ)アクリル酸エステル類、スチレン、アルキルビニルエーテル、酢酸ビニルなどのビニル系単量体など、公知のビニル重合性単量体を挙げることができる。本発明の水性顔料分散体は、該(メタ)アクリル共重合体を構成する全モノマー量に対するベンジル(メタ)アクリレートと(メタ)アクリル酸との合計が85質量%以上を占めており、15%未満である汎用モノマー固有の性質はあまり発現しないので、大半の汎用モノマーを使用することができる。しかし、水酸基を有するモノマーは、酸価が比較的高い領域(100mgKOH/g前後)の組成において使用すると、得られる(メタ)アクリル共重合体の親水性が高くなりすぎてしまい、インクジェット記録用水性インク調製時に使用する水性溶媒の種類によっては、浸透性が高くなりすぎ、発色濃度、光沢等の印字特性が低下することがまれにある。これは、使用する水性溶媒の種類を適宜選択することで回避できることではあるが、(メタ)アクリル共重合体の水酸基価を少なくとも20.0mgKOH/g以下となるように設計しておくと、そのような問題を回避でき、使用する水性溶媒の種類も増え好ましい。
また、炭素原子数14以上の長鎖脂肪族炭化水素基を有するモノマーは、発色濃度や光沢値が安定しないことがまれにある。従って炭素原子数14以上の長鎖脂肪族炭化水素基を有するモノマーも、極力使用しないことが好ましい。
なお、酸価とは、(メタ)アクリル共重合体1gを中和するために必要な水酸化カリウムのmg数を意味する。
実質的には、ベンジル(メタ)アクリレート:(メタ)アクリル酸が83:17〜95:5の範囲で使用すると、該酸価の範囲となる。
本発明で使用する(メタ)アクリル共重合体は、ベンジル(メタ)アクリレートと(メタ)アクリル酸が構成成分の85%以上を占める。ベンジル(メタ)アクリレートは疎水性の成分であるが、該範囲の酸価で中和させても十分水溶性樹脂の形態となる。
ベンジル(メタ)アクリレートは、インクジェット記録用インクの顔料分散体の構成モノマーとしては公知であり、顔料分散性や、インクジェットノズルのオリフィス面に対するインク濡れ性に効果があることは知られている。
しかし、本発明のように、ベンジル(メタ)アクリレートと(メタ)アクリル酸とを必須構成モノマーとし、該アクリル共重合体を構成する全モノマー量に対するベンジル(メタ)アクリレートと(メタ)アクリル酸との合計が85質量%以上である構成を有する(メタ)アクリル共重合体を使用することで、(特に専用紙に印字したときに)印刷濃度と光沢性の両方を兼ね備えたインクジェット記録用水性インクが得られることは、今発明で初めて明らかとなったことである。これは、本発明で使用する(メタ)アクリル共重合体は、ベンジル基を多量に導入しているので、顔料インクとの親和性の高い親油性部分と、該インク媒体である水性溶媒との親和性の高い親水性部分とのバランスがとれたためと考えている。
また、光沢性は、印字物表面の平滑性を保つことで得られると考えられる。このためには、印字面定着後の顔料の空隙を埋めるような樹脂成分の存在が好ましい。
一方でインクジェットインクは印字後すぐに乾燥、即ち、水性溶媒等の液成分は浸透又は蒸発することが求められる。
本発明の水性顔料分散体の調製に用いる顔料としては、硫酸バリウム、硫酸鉛、酸化チタン、黄色鉛、ベンガラ、酸化クロム、カーボンブラック等の無機顔料、アントラキノン系顔料、ペリレン系顔料、ジスアゾ系顔料、フタロシアニン系顔料、イソインドリン系顔料、ジオキサジン系顔料、キナクリドン系顔料、ペリノン系顔料、ベンズイミダゾロン系顔料等が挙げられる。これらを単独または混合して用いることができる。
シアンの顔料としては、たとえば、C.I.ピグメント ブルー 1、C.I.ピグメント ブルー 2、C.I.ピグメント ブルー 3、C.I.ピグメント ブルー 15、C.I.ピグメント ブルー 15:1、C.I.ピグメント ブルー 15:3、C.I.ピグメント ブルー 15:34、C.I.ピグメント ブルー 16、C.I.ピグメント ブルー 22、C.I.ピグメント ブルー 60、などが挙げられる。
本発明で使用する(メタ)アクリル共重合体は、カルボキシル基の少なくとも一部を塩基性物質によってイオン化された形態とすることで、該共重合体の水性溶媒中への分散性や、顔料粒子の分散安定性を発現させる。
イオン化されたカルボキシル基の最適割合は、通常30〜100%、特に70〜100%の範囲に設定されることが好ましい。このイオン化されたカルボキシル基の含有割合は、カルボキシル基と塩基性物質のモル比を意味しているのではなく、解離平衡を考慮に入れたものである。カルボキシル基は、化学量論的に当量の強塩基性物質を用いても解離平衡によりイオン化された基(カルボキシラート基)の含有割合は100%未満であって、カルボキシラート基とカルボキシル基の混在状態である。
中でも、水酸化ナトリウムや水酸化カリウムの様なアルカリ金属水酸化物を使用すると、水性顔料分散体中の顔料粒子の分散安定性が特に良好となるので好ましい。
アンモニアや前記有機アミン等の揮発性の高い塩基性物質は、印字後の乾燥性に優れ、あるいはインクジェット記録用水性インクの調製直後の吐出安定性に優れるが、長時間放置及び/又は高温雰囲気下で揮散するため、水性顔料分散体及びインクジェット記録用水性インク中の分散粒子の分散安定性が徐々に損なわれていき、分散粒子の沈降が観察される場合がある。長期保存あるいは高温雰囲気下で使用する場合は、他の塩基性物質を選択するのが好ましい。
本発明の水性顔料分散体において、前記(メタ)アクリル共重合体は、主に顔料を分散させる役割を有するが、一部が自ら粒子となって存在していてもよい。また、顔料は、そのまま粒子として存在する他、前記(メタ)アクリル共重合体により被覆されていてもよく、存在形態に特に限定はない。
水性顔料分散体には、前記分散粒子が、平均分散粒径(メディアン径)が50〜200nmとなる様に分散していると、保存安定性や、インクの透明性に優れ好ましい。
(a)塩基性物質で中和した前記(メタ)アクリル共重合体の水溶液もしくは水性溶媒溶液に顔料を添加した後、各種の撹拌、分散装置を用いて顔料を分散させた後、必要に応じて添加剤を添加して水性顔料分散体とする方法、
などがある。
本発明のインクジェット記録用水性インクは、本発明の水性顔料分散体を前記水または水性溶媒で希釈し、これに必要に応じて乾燥抑止剤、浸透剤、あるいはその他の添加剤を添加して調製する。
乾燥抑止剤として使用できる水溶性有機溶剤としては、エチレングリコール、ジエチレングリコール、ポリエチレングリコール、グリセリン等の多価アルコール類、N−メチル−2−ピロリドン、2−ピロリドン等のピロリドン類、アミド類、ジメチルスルホキシド、イミダゾリジノン等を挙げることができる。乾燥抑止剤の使用量は、溶媒が水の場合、水100部に対して1〜150部の範囲で使用するのが好ましい。
本発明に使用される浸透剤としては、エチレングリコール、1,2,6−ヘキサントリオール、チオジグリコール、ヘキシレングリコール、ジエチレングリコールなどの多価アルコール類、ペンタンジオール、ヘキサンジオールなどのジオール類、ラウリン酸プロピレングリコールなどのグリコールエーテル類、ジエチレングリコールエチルエーテル、トリエチレングリコールモノエチルエーテル、などの多価アルコールの低級アルキルエーテル類エタノール、イソプロピルアルコール等の低級アルコール、ジエチレングリコール−N−ブチルエーテル等のグリコールエーテル、プロピレングリコール誘導体等の水溶性有機溶媒、などがあげられる。これらは単独または2種以上混合して使用することができる。2種以上を混合して使用することによって、より好ましい浸透性を得ることができる場合がある。
なお、浸透剤の選択によっては印字濃度にも影響がでることがあるので、本発明の(メタ)アクリル共重合体の構成や酸価により、該組成を調整することが好ましい。例えば、比較的酸価があり親水性の高い(メタ)アクリル共重合体を使用する場合は、疎水性が高く浸透性が小さい浸透剤を選択するのが好ましい。具体的には1,2−ヘキサンジオールや1,6−ヘキサンジオールなどのアルキルジオール類のような水溶性有機溶媒を使用すると、印字濃度を若干高くすることができる。
その他の添加剤としては、たとえば、防腐剤、防黴剤、あるいはノズル目詰まり防止用のキレート化剤などが挙げられる。
また、合成例、実施例及び比較例において、「部」及び「%」は、いずれも質量換算である。
メチルエチルケトン(以下、MEKと略記する。)100部を、窒素気流中80℃に保ち、攪拌しながらメタクリル酸ベンジル87.8部、メタクリル酸12.2部、および重合開始剤(「パーブチル(登録商標)O」〔有効成分ペルオキシ2−エチルヘキサン酸t−ブチル、日本油脂(株)製〕)6部からなる混合物を2時間かけて滴下した。滴下終了後、4時間ごとに「パーブチル(登録商標)O」0.5部を添加し、80℃で12時間攪拌した。このようにして、不揮発分52%の、カルボキシル基を有するアクリル系共重合体のMEK溶液(1−A)を得た。該樹脂の質量平均分子量は25000、酸価は80mgKOH/gであった。
メチルエチルケトン100部を用い、かつメタクリル酸ベンジル90.8部、メタクリル酸9.2部及び「パーブチル(登録商標)O」6部の混合液を用いる以外は合成例1と同様の操作を行い、酸価60mgKOH/g、不揮発分52%のアクリル系共重合体(1−B)のMEK溶液を得た。
メチルエチルケトン100部を用い、かつアクリル酸ベンジル89.8部、アクリル酸10.2部及び「パーブチル(登録商標)O」6部の混合液を用いる以外は合成例1と同様の操作を行い、酸価80mgKOH/g、不揮発分52%のアクリル系共重合体(1−C)のMEK溶液を得た。
メチルエチルケトン100部を用い、かつメタクリル酸ベンジル部82.8部、アクリル酸ブチル5部、メタクリル酸12.2部及び「パーブチル(登録商標)O」6部の混合液を用いる以外は合成例1と同様の操作を行い、酸価80mgKOH/g、不揮発分50%のアクリル系共重合体(1−D)のMEK溶液を得た。
メチルエチルケトン100部を用い、かつメタクリル酸ベンジル部80.3部、 メタクリル酸メチル7.5部、メタクリル酸12.2部及び「パーブチル(登録商標)O」6部の混合液を用いる以外は合成例1と同様の操作を行い、酸価80mgKOH/g、不揮発分52%のアクリル系共重合体(1−E)のMEK溶液を得た。
メチルエチルケトン100部を用い、かつメタクリル酸ベンジル75.8部、メタクリル酸メチル15部、メタクリル酸9.2部及び「パーブチル(登録商標)O」6部の混合液を用いる以外は合成例1と同様の操作を行い、酸価60mgKOH/g、不揮発分50%のアクリル系共重合体(1−F)のMEK溶液を得た。
メチルエチルケトン100部を用い、かつメタクリル酸ベンジル部75.8部、メタクリル酸メチル7.5部、メタクリル酸2−ヒドロキシエチル7.5部、メタクリル酸9.2部及び「パーブチル(登録商標)O」6部の混合液を用いる以外は合成例1と同様の操作を行い、酸価60mgKOH/g、水酸基価32.5mgKOH/g、不揮発分51%のアクリル系共重合体(1−G)のMEK溶液を得た。
メチルエチルケトン100部を用い、かつメタクリル酸ベンジル部79.7部、アクリル酸ブチル5部、メタクリル酸15.3部及び「パーブチル(登録商標)O」6部の混合液を用いる以外は合成例1と同様の操作を行い、酸価100mgKOH/g、不揮発分50%のアクリル系共重合体(1−H)のMEK溶液を得た。
メチルエチルケトン100部を用い、かつメタクリル酸ベンジル64.7部、メタクリル酸メチル20部、メタクリル酸15.3部及び「パーブチル(登録商標)O」6部の混合液を用いる以外は合成例1と同様の操作を行い、酸価100mgKOH/g、不揮発分52%のアクリル系共重合体(1−I)のMEK溶液を得た。
メチルエチルケトン100部を用い、かつメタクリル酸ベンジル57.8部、スチレン30部、メタクリル酸12.2部及び「パーブチル(登録商標)O」6部の混合液を用いる以外は合成例1と同様の操作を行い、酸価80mgKOH/g、不揮発分50%のスチレン−アクリル系共重合体(1−J)のMEK溶液を得た。
メチルエチルケトン100部を用い、かつメタクリル酸ベンジル69.4部、メタクリル酸30.6部及び「パーブチル(登録商標)O」6部の混合液を用いる以外は合成例1と同様の操作を行い、酸価200mgKOH/g、不揮発分52%のアクリル系共重合体(1−K)のMEK溶液を得た。
メチルエチルケトン100部を用い、かつスチレン87.8部、メタクリル酸12.2部及び「パーブチル(登録商標)O」4部の混合液を用いる以外は合成例1と同様の操作を行い、酸価80mgKOH/g、不揮発分52%のアクリル系共重合体(1−L)のMEK溶液を得た。
合成例1で得た共重合体(1−A)、5%水酸化カリウム水溶液、Fastogen(登録商標)Blue TGR(大日本インク化学工業(株)社製銅フタロシアニン系顔料)を250mLのポリビンに仕込み、混合した。ここでそれぞれの仕込量は、銅フタロシアニン系顔料が10部、樹脂は顔料に対して不揮発分で50質量%の比率となる量、5%水酸化カリウム水溶液は共重合体(B−1)の酸価が100%中和される量、水は混合液の不揮発分を30%とするのに必要な量である。
混合液をペイントコンディショナー(直径0.5mmのジルコニアビーズ使用)で2時間分散した。分散終了後、ジルコニアビーズを除いて得られた液をエバポレーターでメチルエチルケトンを留去した後、遠心分離処理(8200 G、30分間)して粗大粒子を除去したのち、純水を加えて不揮発分を調整し、不揮発分20%の水性顔料分散体(1−A)を得た。
合成例1で得た共重合体(1−A)に変えて、合成例2で得た共重合体(1−B)、及び合成例5で得た共重合体(1−D)及び(1−E)に変更した以外は同様にして、不揮発分20%の水性分散体、(1−B)、(1−D)及び(1−E)を得た。
<参考例1及び比較例9〜11>
合成例1で得た共重合体(1−A)に変えて、合成例3で得た共重合体(1−C)に変更した以外は実施例1と同様にして、不揮発分20%の水性分散体(1−C)を参考例1として得た。
また、合成例1で得た共重合体(1−A)に変えて、合成例6〜8で得た共重合体(1−F)〜(1−H)に変更した以外は実施例1と同様にして、不揮発分20%の水性分散体(1−F)〜(1−H)を比較例9〜11として得た。
合成例1で得た共重合体(1−A)に代えて、合成例5〜合成例8で得た共重合体(1−I)〜(1−L)に変更した以外は、実施例1と同様の操作を行って不揮発分20%の水性顔料分散体(1−I)〜(1−L)を得た。
ジエチレングリコールモノブチルエーテル 10.0部
ジエチレングリコール 15.0部
サーフィノール465(エアプロダクツ社製) 0.8部
水 49.2部
実施例1で得た水性顔料分散体(1−A)に変えて、実施例2で得た水性顔料分散体(1−B)、(1−D)及び(1−E)の同量を用いる以外は実施例10と同様の操作を行い、インクジェット記録用水性インク(1−B)、(1−D)及び(1−E)を調整した。
<参考例2及び比較例12〜14>
実施例1で得た水性顔料分散体(1−A)に変えて、参考例1で得た水性顔料分散体(1−C)に変更した以外は実施例10と同様にして、インクジェット記録用水性インク(1−C)を参考例2として得た。
また、実施例1で得た水性顔料分散体(1−A)に変えて、比較例6〜8で得た共重合体(1−F)〜(1−H)に変更した以外は実施例10と同様にして、インクジェット記録用水性インク1−F)〜(1−H)を比較例12〜14として得た。
実施例1で得られた水性顔料分散体(1−A)に代えて比較例1〜4で得られた水性顔料分散体(1−I)〜(1−L)の同量を用いる以外は実施例1と同様の操作を行い、インクジェット記録用水性インク(1−I)〜(1−L)を調製した。
(インクジェット記録用水性インク中の顔料粒子径判定)
試料インクに水を加えて1000倍に希釈した後、粒度分析計(リーズ・アンド・ノースラップ社製「マイクロトラックUPA150」)を使用して、試料インク中に分散している顔料の粒子径を測定し、初期粒子径とし、次の3段階の基準で判定した。
○ 粒径120nm未満。
△ 粒径120nm以上150nm未満。
× 粒径150nm以上。
水性顔料分散体を60℃で30日間静置した後、前記粒度分析計を使用して、試料中に分散している顔料の粒子径を測定した。
測定値の初期粒子径に対する変化率が10%以下のものを「○」、10%を超えるものを「×」と評価した
ピエゾ方式のインクジェットプリンタ(EM-930C、セイコーエプソン(株)製)を使用して、記録媒体上に試料インクで描画し、印字濃度試験、及び光沢値試験を行った。記録媒体としては、普通紙として、Canon(株)製「Canon PBペーパー」、あるいはXerox社製「Xerox4024」を使用し、インクジェット専用紙としてセイコーエプソン(株)製「写真用紙光沢」を使用した。
印字濃度は、専用紙について評価した。
インクジェット専用紙にベタ画像を印刷し、印字濃度測定機「GRETAG(登録商標) D196 グレタグマクベス社製」を使用し、単一サンプルの5点について着色画像濃度を測定し、それらを平均した値を印字濃度とした。数値が大きいほど印字濃度が良好であることを示しており、用紙別に次の4段階の基準で判定した。
セイコーエプソン(株)製「写真用紙光沢」
◎ 印字濃度2.7以上。
○ 印字濃度2.5以上2.7未満。
△ 印字濃度2.0以上2.5未満。
× 印字濃度2.0未満。
専用紙にベタ画像を印刷し、光沢値測定機としてヘイズグロスメーター「BYK Gardner社製」を使用し、測定角度20度で着色画像の光沢を測定した。単一サンプルの3点について測定し、それらを平均した値を光沢値とした。数値が大きいほど光沢が良好であることを示しており、次の4段階の基準で判定した。
◎ 光沢値25以上
○ 光沢値20以上。
△ 光沢値10以上20未満。
× 光沢値10未満。
上記の印字試験で得た印刷物の光沢感の度合いを目視にて次の4段階の基準で判定した。
◎ つややかで乱反射がほぼない。
○ つややかであるが乱反射が少しある。
△ つやがあるが乱反射が大きい。
× つやがなくほとんど光を反射しない。
これに対し、比較例1、比較例2はいずれも、(メタ)アクリル共重合体を構成する全モノマー量に対するベンジル(メタ)アクリレートと(メタ)アクリル酸との合計が85質量%未満である例であるが、これは印字濃度、光沢値共に低かった。比較例3は酸価が多い例であるが、比較例4はベンジル(メタ)アクリレートを含まない例であるが、これは印字濃度、及び光沢値ともに低かった。
Claims (3)
- (メタ)アクリル共重合体、顔料、及び塩基性物質を含有するインクジェットインク用水性顔料分散体であって、(メタ)アクリル共重合体が、メタクリル酸ベンジルと(メタ)アクリル酸とを必須構成モノマーとし、該(メタ)アクリル共重合体を構成する全モノマー量に対するメタクリル酸ベンジルと(メタ)アクリル酸との合計が85質量%以上であり、酸価50〜85mgKOH/gであり、水酸基価が20.0mgKOH/g以下であることを特徴とする、インクジェットインク用水性顔料分散体。
- 前記該(メタ)アクリル共重合体を構成する全モノマー量に対するベンジル(メタ)アクリレートと(メタ)アクリル酸との合計が95質量%以上である、請求項1に記載のインクジェットインク用水性顔料分散体。
- 請求項1または2に記載のインクジェットインク用水性顔料分散体を含有することを特徴とするインクジェット記録用水性インク。