JP5160763B2 - セメントモルタル組成物 - Google Patents
セメントモルタル組成物 Download PDFInfo
- Publication number
- JP5160763B2 JP5160763B2 JP2006279636A JP2006279636A JP5160763B2 JP 5160763 B2 JP5160763 B2 JP 5160763B2 JP 2006279636 A JP2006279636 A JP 2006279636A JP 2006279636 A JP2006279636 A JP 2006279636A JP 5160763 B2 JP5160763 B2 JP 5160763B2
- Authority
- JP
- Japan
- Prior art keywords
- cement
- parts
- reducing agent
- water reducing
- fine powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(1)セメント、膨張材、ポゾラン微粉末、減水剤及び細骨材を含有してなるセメントモルタル組成物において、前記膨張材が、ブレーン比表面積値2,000〜6,000cm2/gのカルシウムアルミノフェライト系膨張材で、セメント、膨張材、及びポゾラン微粉末からなる結合材100部中、1〜4部であり、前記ポゾラン微粉末が、二酸化珪素(SiO2)含有率が90%以上で水素イオン濃度が酸性領域にあるシリカ質微粉末で、セメント、膨張材、及びポゾラン微粉末からなる結合材100部中、5〜15部であり、及び前記減水剤が、ポリカルボン酸系減水剤で、セメント、膨張材、及びポゾラン微粉末からなる結合材100部に対して、0.24〜0.40部であることを特徴とするセメントモルタル組成物である。
(2)前記細骨材が、密度3.0g/cm3以上の重量骨材であることを特徴とする前記(1)のセメントモルタル組成物である。
(3)前記(1)又は(2)のセメントモルタル組成物と水とを混合してなるモルタルである。
(4)水/結合材比が20〜30%であることを特徴とする前記(3)のモルタルである。
本発明で使用する部や%は特に規定のない限り質量基準である。
CaO原料としては石灰石や消石灰等が、Al2O3原料としてはボーキサイトやアルミ残灰等が、Fe2O3原料としては銅カラミや市販の酸化鉄等が、そして、CaSO4原料としては二水石膏、半水石膏、及び無水石膏等が挙げられる。
C4AF膨張材の使用量は、セメント、膨張材、及びポゾラン微粉末からなる結合材(以下、結合材と略する)100部中1〜4部が好ましく、2〜3部がより好ましい。1部未満では良好な膨張性や保水性が得られない場合があり、4部を超えると同様に良好な膨張性が得られない場合がある。
シリカ質微粉末の製造方法は、例えば金属シリコン微粉末を火炎中で酸化させる方法や高温火炎中でシリカ質原料微粉末を溶融する方法において原料の熱処理条件を調整し、捕集温度を550℃以上にすることによって製造することができる。また、電気炉においてジルコンサンドを電融した際にサイクロンなどで捕集した後分級して製造されるものもある。
その平均粒子径は、1μm以下の超微粒子である。
発泡剤としては特に限定されるものではなく、例えば、金属粉末や過酸化物等が挙げられる。なかでもアルミニウム粉末が好ましいが、アルミニウム粉末の表面は酸化されやすく酸化皮膜で覆われると反応性が低下するため、植物油、鉱物油、又はステアリン酸等で表面処理したアルミニウム粉末が好ましい。
減水剤の使用形態は粉体、液体のいずれでも使用できるがプレミックス製品として使用する際には粉体が好ましく、セメントモルタル組成物100部に対するポリカルボン酸系減水剤の使用量は、粉体で0.05〜0.20部が好ましく、0.07〜0.15部がより好ましい。
ポリカルボン酸系減水剤が0.05部未満では高流動が得られない場合があり、0.20部を超えると泡が発生したり凝結遅延を起こす場合がある。また、本発明の効果を阻害しない範囲でメラミンスルホン酸系減水剤、リグニンスルホン酸系減水剤を併用することができる。
細骨材の使用量は、結合材100部に対して、70〜150部が好ましい。70部未満では収縮量が多くなる場合があり、150部を超えると強度や流動性が低下する場合がある。
ハンドミキサおよび高速グラウトミキサでの練り混ぜは、ペール缶等練り容器およびミキサにあらかじめ所定の水を入れ、その後ミキサを回転させながら前記結合材と重量骨材を混合したセメントモルタル組成物を投入し2分以上練り混ぜる。また、強制ミキサでの練り混ぜは、あらかじめ前記混合したセメントモルタル組成物をミキサに投入しミキサを回転させながら所定の水を投入し少なくとも2分以上練り混ぜる。練り混ぜ時間が2分未満では、練り不足のため適切なセメントモルタルの流動性が得られ難い場合がある。
また、作製したセメントモルタルを、20℃、80%RHの恒温恒湿室で、型枠に打設し、長さ変化率、及び圧縮強度を測定した。長さ変化率、圧縮強度は1日で脱型後、材齢まで20℃水中養生とした。結果を表1に併記する。
セメント :普通ポルトランドセメント、市販品
膨張材A :C4AF膨張材、ブレーン値2,900cm2/g、市販品
膨張材B :C4AF膨張材、ブレーン値1,900cm2/g
膨張材C :C4AF膨張材、ブレーン値5,830cm2/g
膨張材D :C4AF膨張材、ブレーン値6,090cm2/g
膨張剤E :CSA膨張剤、ブレーン値2,850cm2/g、市販品
ポゾラン微粉末a:シリカフューム、PH=2.90、SiO2含有率95.2%、市販品
消泡剤 :ポリオキシエチレンアルキルエーテル系、市販品
減水剤 :ポリカルボン酸系減水剤、市販品
細骨材 :フェロクロムスラグ、密度3.20g/cm3、2.0mm下品、市販品
流動性 :日本規格協会JIS R5201-1997「セメントの物理試験方法」11.フロー試験で15回の落下運動を行わない静置フローを測定。流動性の経時変化はその都度セメントモルタルを高速ハンドミキサにて10秒間練り返して測定
長さ変化率:日本規格協会JIS A 6202「コンクリート用膨張材」の附属書1「膨張材のモルタルによる膨張性試験方法」に準じて測定。材齢7日の測定値
圧縮強度 :土木学会JSCE-G505-1999「円柱供試体を用いたモルタルまたはセメントペーストの圧縮強度試験方法」に準じて測定。材齢28日の測定値
これに対して、ブレーン値が2000cm2/g未満の膨張材Bを含有したセメントモルタルは、流動性は高いが、圧縮強度が低く、長さ変化率が大きくなりすぎ(実験No.1-7)、また、ブレーン値が6000cm2/gを超えた膨張材Dを含有したセメントモルタルは、圧縮強度は高いが、流動性の保持が短くなる(実験No.1-9)から、膨張材の比表面積は、ブレーン値で2,000〜6000cm2/gが好ましい。
C4AF膨張材は、結合材100部中、1部未満では流動性、圧縮強度は得られるが、長さ変化率は小さく(実験No.1-1、No.1-10)、1部から流動性、圧縮強度にあわせて長さ変化率の効果が顕著になり、4部を超えると流動性は高くなるが、圧縮強度が低下し、長さ変化率が大きくなりすぎる(実験No.1-6)から、1〜4部が好ましい。
また、C4AF膨張材の代わりにCSA膨張材を配合したセメントモルタル(実験No.1-11〜1-12)は、流動性の保持性が悪く、また、長さ変化率はC4AF膨張材に比べ小さく膨張材混和量を多くする必要がある。したがって、本発明では、膨張材としてC4AF系膨張材を使用する。
ポゾラン微粉末b:シリカフューム、PH=6.45、SiO2含有率99.9%
ポゾラン微粉末c:シリカフューム、PH=7.73、SiO2含有率96.3%、市販品
ポゾラン微粉末d:シリカフューム、PH=9.49、SiO2含有率89.1%、市販品
これに対して、二酸化珪素(SiO2)含有率が90%以上であるが水素イオン濃度がアルカリ領域であるポゾラン微粉末c、および二酸化珪素(SiO2)含有率が90%未満で水素イオン濃度未がアルカリ領域であるポゾラン微粉末dを含有する実験No.2-7〜2-10の比較例のセメントモルタルは、ポゾラン微粉末aと同等の減水剤量では練り混ぜができず、減水剤量を増して練り混ぜても、泡が多量に発生し、優れた流動性が得にくく、また長さ変化率、圧縮強度が低下する。
したがって、二酸化珪素(SiO2)含有率が90%以上で水素イオン濃度が酸性領域にあるポゾラン微粉末を使用することにより、優れた流動性保持、適当な長さ変化率、高い圧縮強度のセメントモルタルが得られるという本発明の効果を奏することが確認された。
結合材100部中、膨張材A3部、及びポゾラン微粉末a12部、結合材100部に対し、表3に示す減水剤(ポリカルボン酸系減水剤に代えてナフタレンスルホン酸系減水剤)、消泡剤0.04部、及び細骨材100部を混合してセメントモルタル材料を調製したこと以外は実施例1と同様に行った。結果を表3に併記する。
減水剤 :ナフタレンスルホン酸系減水剤、市販品
したがって、ポリカルボン酸系減水剤を使用することにより、優れた流動性保持、適当な長さ変化率、高い圧縮強度のセメントモルタルが得られるという本発明の効果を奏すること、ポリカルボン酸系減水剤以外の減水剤を使用したのでは、このような効果は奏しないことが確認された。
これに対して水/結合材比が20%未満では、練り混ぜに大きな負荷がかかり練り混ぜが困難な場合があり、また水/結合材比が30%を超える実験No.4-3では、泡の発生が多量にみられ流動性保持は優れているが圧縮強度が低下する。
したがって、本発明におけるセメントモルタル組成物の練り混ぜに使用される水/結合材比は20〜30%が好ましい。
Claims (4)
- セメント、膨張材、ポゾラン微粉末、減水剤及び細骨材を含有してなるセメントモルタル組成物において、前記膨張材が、ブレーン比表面積値2,000〜6,000cm2/gのカルシウムアルミノフェライト系膨張材で、セメント、膨張材、及びポゾラン微粉末からなる結合材100部中、1〜4部であり、前記ポゾラン微粉末が、二酸化珪素(SiO2)含有率が90%以上で水素イオン濃度が酸性領域にあるシリカ質微粉末で、セメント、膨張材、及びポゾラン微粉末からなる結合材100部中、5〜15部であり、前記減水剤が、ポリカルボン酸系減水剤で、セメント、膨張材、及びポゾラン微粉末からなる結合材100部に対して、0.24〜0.40部であることを特徴とするセメントモルタル組成物。
- 前記細骨材が、密度3.0g/cm3以上の重量骨材であることを特徴とする請求項1に記載のセメントモルタル組成物。
- 請求項1又は2に記載のセメントモルタル組成物と水とを混合してなるモルタル。
- 水/結合材比が20〜30%であることを特徴とする請求項3に記載のモルタル。