JP5092554B2 - 高強度鉄筋用鋼材の製造方法 - Google Patents
高強度鉄筋用鋼材の製造方法 Download PDFInfo
- Publication number
- JP5092554B2 JP5092554B2 JP2007150295A JP2007150295A JP5092554B2 JP 5092554 B2 JP5092554 B2 JP 5092554B2 JP 2007150295 A JP2007150295 A JP 2007150295A JP 2007150295 A JP2007150295 A JP 2007150295A JP 5092554 B2 JP5092554 B2 JP 5092554B2
- Authority
- JP
- Japan
- Prior art keywords
- steel
- temperature
- less
- steel material
- strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
0.0100≧B(%)≧{N(%)/14−Ti(%)/27}×11+0.0005・・・(1)
第3の発明は、鋼材がさらに、質量%で、Cr:0.1〜2.0%、Mo:0.01〜1.0%、V:0.01〜1.0%、W:0.01〜1.0%、Ni:0.01〜1.0%、Cu:0.01〜1.0%、Co:0.01〜1.0%、Sb:0.0010〜0.0050%の中から選ばれる1種又は2種以上を含有することを特徴とする第1の発明または第2の発明に記載の高強度鉄筋用鋼材の製造方法。
T×logt≧1700・・・(2)
0.0100≧B(%)≧{N(%)/14−Ti(%)/27}×11+0.0005・・・(1)
尚、上記(1)式の各元素記号は質量%での各元素の含有量である。
T×logt≧1700・・・(2)
但し、Tは保持温度(K)、tは保持時間(秒)である。
10a、20a 節
Claims (4)
- 化学組成が質量%で、C:0.15〜0.30%、Si:0.05〜1%、Mn:0.2〜2.5%、P:0.03%以下、S:0.03%以下、Al:0.01〜1.0%、Nb:0.001〜0.3%、Ti:0.003%未満、N:0.0060%未満、を含有し、残部がFe及び不可避的不純物である鋼素材を、加熱温度:Ac3点〜1250℃、圧延終了温度:Ar3温度以上で丸棒、丸線材あるいは異形棒、異形線材形状への熱間圧延を行い、その後熱間圧延完了温度から500℃までの温度範囲を1.5℃/s以上の冷却速度で冷却を行い、500〜300℃までの温度範囲を1℃/s未満の冷却速度で冷却を行うことを特徴とする、降伏応力785MPa以上、全伸び8%以上、絞り35%以上の高強度鉄筋用鋼材の製造方法。
- 鋼材がさらに、Bを含有し、該Bの含有量は、質量%で、鋼中のN量、Ti量との間に下記(1)式で示される関係が成り立つことを特徴とする請求項1に記載の高強度鉄筋用鋼材の製造方法。
0.0100≧B(%)≧{N(%)/14−Ti(%)/27}×11+0.0005・・・(1) - 鋼材がさらに、質量%で、Cr:0.1〜2.0%、Mo:0.01〜1.0%、V:0.01〜1.0%、W:0.01〜1.0%、Ni:0.01〜1.0%、Cu:0.01〜1.0%、Co:0.01〜1.0%、Sb:0.0010〜0.0050%の中から選ばれる1種又は2種以上を含有することを特徴とする請求項1または請求項2に記載の高強度鉄筋用鋼材の製造方法。
- 冷却後さらに、下記(2)式を満たす保持温度T(K)、保持時間t(秒)での保持を行なうことを特徴とする請求項1ないし請求項3のいずれかに記載の高強度鉄筋用鋼材の製造方法。
T×logt≧1700・・・(2)