JP5068146B2 - 液晶パネルおよび液晶表示装置 - Google Patents
液晶パネルおよび液晶表示装置 Download PDFInfo
- Publication number
- JP5068146B2 JP5068146B2 JP2007298072A JP2007298072A JP5068146B2 JP 5068146 B2 JP5068146 B2 JP 5068146B2 JP 2007298072 A JP2007298072 A JP 2007298072A JP 2007298072 A JP2007298072 A JP 2007298072A JP 5068146 B2 JP5068146 B2 JP 5068146B2
- Authority
- JP
- Japan
- Prior art keywords
- liquid crystal
- optical compensation
- compensation layer
- film
- polarizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
Δnd(380)=Δnd(550)=Δnd(780)・・・(1)
nx>ny≧nz ・・・(2)
Rth(380)>Rth(550)>Rth(780)・・・(3)
nx=ny>nz ・・・(4)。
本明細書における用語および記号の定義は下記の通りである:
(1)「nx」は面内の屈折率が最大になる方向(すなわち、遅相軸方向)の屈折率であり、「ny」は面内で遅相軸に垂直な方向(すなわち、進相軸方向)の屈折率であり、「nz」は厚み方向の屈折率である。また、例えば「nx=ny」は、nxとnyが厳密に等しい場合のみならず、nxとnyが実質的に等しい場合も包含する。本明細書において「実質的に等しい」とは、液晶パネル(最終的には、液晶表示装置)の表示特性に実用上の影響を与えない範囲でnxとnyが異なる場合も包含する趣旨である。
(2)「面内位相差Δnd(λ)」は、23℃における波長λnmの光で測定したフィルム(層)面内の位相差値をいう。Δnd(λ)は、波長λnmにおけるフィルム(層)の遅相軸方向、進相軸方向の屈折率をそれぞれ、nx、nyとし、d(nm)をフィルム(層)の厚みとしたとき、式:Δnd(λ)=(nx−ny)×dによって求められる。なお、単にΔndと記載する場合には、Δndは波長590nmにおける面内位相差を意味する。
(3)厚み方向の位相差Rth(λ)は、23℃における波長λnmの光で測定した厚み方向の位相差値をいう。Rth(λ)は、波長λnmにおけるフィルム(層)の遅相軸方向、厚み方向の屈折率をそれぞれ、nx、nzとし、d(nm)をフィルム(層)の厚みとしたとき、式:Rth(λ)=(nx−nz)×dによって求められる。なお、単にRthと記載する場合には、Rthは波長590nmにおける厚み方向の位相差を意味する。
(4)Nz係数は、面内位相差Δndと厚み方向位相差Rthとの比であり、式:Nz=(nx−nz)/(nx−ny)によって求められる。
図1は、本発明の液晶パネルの好ましい一例を説明する概略断面図である。液晶パネル100は、第1の偏光子30と、第1の光学補償層60と、液晶セル40と、第2の光学補償層70と、第2の偏光子50と、を有する。第1の光学補償層60および第2の光学補償層70は、両方が液晶セルの一方の側(すなわち、視認側またはバックライト側)に配置されてもよく、一方が液晶セルのバックライト側に配置され一方が視認側に配置されてもよい。好ましくは、図1に示すように、第1の光学補償層60が視認側に配置され、第2の光学補償層70がバックライト側に配置される。第1の偏光子および第2の偏光子は、それぞれ、その少なくとも一方の側に保護層を有していてもよい(図示せず)。本発明の液晶パネルにおいては、第1の光学補償層60が一方の偏光子(図示例では第1の偏光子30)の液晶セル側の保護層を兼ねるので、当該位置の保護層は省略され得る。上記それぞれの光学補償層、偏光子および液晶セルは、任意の適切な粘着剤層または接着剤層を介して貼り合わせられている。
Δnd(380)=Δnd(550)=Δnd(780)・・・(1)
nx>ny≧nz ・・・(2)
Rth(380)>Rth(550)>Rth(780)・・・(3)
nx=ny>nz ・・・(4)
第1の光学補償層60は、好ましくは、その遅相軸が隣接する偏光子(図示例では第1の偏光子)の吸収軸と実質的に直交するようにして配置されている。なお、第1の光学補償層60および第2の光学補償層70の詳細については後述する。
第1の偏光子および第2の偏光子としては、目的に応じて任意の適切な偏光子が採用され得る。例えば、ポリビニルアルコール系フィルム、部分ホルマール化ポリビニルアルコール系フィルム、エチレン・酢酸ビニル共重合体系部分ケン化フィルム等の親水性高分子フィルムに、ヨウ素や二色性染料等の二色性物質を吸着させて一軸延伸したもの、ポリビニルアルコールの脱水処理物やポリ塩化ビニルの脱塩酸処理物等ポリエン系配向フィルム等が挙げられる。これらのなかでも、ポリビニルアルコール系フィルムにヨウ素などの二色性物質を吸着させて一軸延伸した偏光子が、偏光二色比が高く特に好ましい。これら偏光子の厚さは特に制限されないが、一般的に、5〜80μm程度である。
保護層は、偏光板の保護フィルムとして使用できる任意の適切なフィルムで形成される。当該フィルムの主成分となる材料の具体例としては、トリアセチルセルロース(TAC)等のセルロース系樹脂や、ポリエステル系、ポリビニルアルコール系、ポリカーボネート系、ポリアミド系、ポリイミド系、ポリエーテルスルホン系、ポリスルホン系、ポリスチレン系、ポリノルボルネン系、ポリオレフィン系、(メタ)アクリル系、アセテート系等の透明樹脂等が挙げられる。また、(メタ)アクリル系、ウレタン系、(メタ)アクリルウレタン系、エポキシ系、シリコーン系等の熱硬化型樹脂または紫外線硬化型樹脂等も挙げられる。この他にも、例えば、シロキサン系ポリマー等のガラス質系ポリマーも挙げられる。また、特開2001−343529号公報(WO01/37007)に記載のポリマーフィルムも使用できる。このフィルムの材料としては、例えば、側鎖に置換または非置換のイミド基を有する熱可塑性樹脂と、側鎖に置換または非置換のフェニル基ならびにニトリル基を有する熱可塑性樹脂を含有する樹脂組成物が使用でき、例えば、イソブテンとN−メチルマレイミドからなる交互共重合体と、アクリロニトリル・スチレン共重合体とを有する樹脂組成物が挙げられる。当該ポリマーフィルムは、例えば、上記樹脂組成物の押出成形物であり得る。それぞれの保護層は同一であってもよく、異なっていてもよい。
第1の光学補償層は、その光弾性係数の絶対値が40×10−12(m2/N)以下であり、好ましくは0.2×10−12〜35×10−12(m2/N)であり、さらに好ましくは0.2×10−12〜30×10−12(m2/N)である。光弾性係数の絶対値がこのような範囲であれば、表示ムラおよび輝度ムラを効果的に抑制することができる。
Δnd(380)=Δnd(550)=Δnd(780)・・・(1)
ここで、例えばΔnd(380)=Δnd(550)とは、Δnd(380)とΔnd(550)とが厳密に等しい場合だけでなく実質的に等しい場合も包含する。本明細書において「実質的に等しい」とは、本発明の液晶パネルの表示特性に実用上の影響を与えない範囲で、例えばΔnd(380)とΔnd(550)が異なる場合を包含する趣旨である。より具体的には、第1の光学補償層の波長380nm〜780nmにおけるΔndの最大値と最小値との差は、好ましくは10nm以下であり、さらに好ましくは8nm以下であり、特に好ましくは6nm以下である。このように、第1の光学補償層がいわゆるフラットな波長分散特性を有することにより、波長が大きくなるにしたがい厚み方向位相差が大きくなるいわゆる正分散の第2の光学補償層と組み合わせて、全方位において色つきのないニュートラルな表示の液晶パネルが得られる。
nx>ny≧nz ・・・(2)
すなわち、第1の光学補償層は、1つの実施形態においてはnx>ny=nzの屈折率分布を有し、別の実施形態においてはnx>ny>nzの屈折率分布を有する。屈折率分布がnx>ny=nzである実施形態においては、「ny=nz」は、nyとnzが厳密に等しい場合のみならず、nyとnzが実質的に等しい場合も包含する。より具体的には、この実施形態における第1の光学補償層のNz係数は、0.9を超えて1.1未満である。屈折率分布がnx>ny>nzである実施形態においては、第1の光学補償層のNz係数は、好ましくは1.1〜3.0であり、さらに好ましくは1.1〜2.0であり、特に好ましくは1.1〜1.7であり、とりわけ好ましくは1.1〜1.5であり、最も好ましくは1.1〜1.4である。このような屈折率分布(Nz係数)を有する第1の光学補償層と、後述する特定の第2の光学補償層とを組み合わせて液晶パネルに用いることにより、全方位において色つきのないニュートラルな表示が得られる液晶パネルを提供することができる。
上記のように、第1の光学補償層は、一方の偏光子(図示例では第1の偏光子)の液晶セル側の保護層として機能し得る。この場合、第1の光学補償層と第1の偏光子とは、好ましくは、粘着剤または接着剤を介して貼り合わせられている。第1の光学補償層における第1の偏光子に貼り合わされる面には、易接着処理が施されていることが好ましい。易接着処理としては、樹脂材料を塗工することが好ましい。樹脂材料としては、例えば、シリコン系樹脂、ウレタン系樹脂、アクリル系樹脂が好ましい。易接着処理されることにより、易接着層が形成される。易接着層の厚みは、好ましくは5〜100nm、より好ましくは10〜80nmである。
第2の光学補償層は、下記式(3)および(4)の関係を有する:
Rth(380)>Rth(550)>Rth(780)・・・(3)
nx=ny>nz ・・・(4)
第2の光学補償層は、単層であってもよく、2層以上の積層体であってもよい。積層体の場合には、積層体全体として上記のような光学特性を有する限り、各層を構成する材料および各層の厚みは適宜設定され得る。
このような構造を有するポリイミドを非液晶材料として用いれば、第2の光学補償層を特に薄くすることができる。なお、式(I)においてXとYの和を100とした場合に、Xは30〜70であり、Yは70〜30である。
前述の通り、本発明における第2の光学補償層は、好ましくは、基材上のコーティング層として形成され得る。基材が偏光子の保護層を兼ねる場合(例えば、基材がトリアセチルセルロースフィルムなどのセルロース系フィルムの場合)には、好ましくは、基材のコーティング層と反対の側が、一方の偏光子(図示例では、第2の偏光子)と粘着剤または接着剤を介して貼り合わせられる。基材が偏光子の保護層を兼ねない場合には、好ましくは、第2の光学補償層は第2の偏光子(代表的には、第2の偏光子の保護層)に転写され、次いで、基材が剥離される。粘着剤または接着剤についての詳細は、前述した通りである。
試料フィルムの屈折率nx、nyおよびnzを、自動複屈折測定装置(王子計測機器株式会社製,自動複屈折計KOBRA−WPR)により計測し、面内位相差Δndおよび厚み方向位相差Rthを算出した。測定温度は23℃、測定波長は590nmであった。波長分散特性に関しては、380、550および780nmで測定した。
ELDIM社製 商品名 「EZ Contrast160D」を用いて測定した。なお、斜め方向のコントラストは、極角を60°方向で方位角を0〜360°に変化させ、方位角45°、135°、225°、315°におけるコントラストを測定して、その平均値を求めた。なお、方位角および極角は図4に示す通りである。
〈カラーシフトの測定〉
ELDIM社製 商品名 「EZ Contrast160D」を用いて、方位角0〜360°に変化させて、極角を60°方向にした液晶表示装置の色調を測定し、xy色度図上にプロットした。
〈黒輝度の測定〉
ELDIM社製 商品名 「EZ Contrast160D」を用いて、極角60°方向で、方位角を−180°〜180°に変化させ、方位角と黒輝度との関係をプロットした。
〈クニック評価〉
23℃の暗室でバックライトを点灯させてから30分経過した後、黒表示をした場合の表示面を目視により観察し、輝点の有無により、クニックの有無を判断した。
A:クニックは観察されなかった。
B:クニックは観察されたが、実用上問題となるレベルではなかった。
C:クニックが観察され、実用上問題となるレベルであった。
ポリビニルアルコールフィルムを、ヨウ素を含む水溶液中で染色した後、ホウ酸を含む水溶液中で速比の異なるロール間にて6倍に一軸延伸して偏光子を作製した。
アセトアセチル基含有ポリビニルアルコール系樹脂(商品名「ゴーセファイマーZ200」、日本合成化学工業(株)製、平均重合度:1200、ケン化度:98.5モル%,アセトアセチル化度:5モル%)100重量部に対し、メチロールメラミン50重量部を30℃の温度条件下で純水に溶解し、固形分濃度3.7%に調整した水溶液を得た。この水溶液100重量部に対し、アルミナコロイド水溶液(平均粒子径15nm、固形分濃度10%、正電荷)18重量部を加えて接着剤水溶液を調製した。接着剤水溶液の粘度は9.6mPa・sであった。接着剤水溶液のpHは、4〜4.5であった。
アセトアセチル基含有ポリビニルアルコール系樹脂(商品名「ゴーセファイマーZ200」、日本合成化学工業(株)製、平均重合度:1200、ケン化度:98.5モル%,アセトアセチル化度:5モル%)100重量部に対し、メチロールメラミン50重量部を30℃の温度条件下で純水に溶解し、固形分濃度3.7%に調整した接着剤水溶液を得た。接着剤水溶液の粘度は9.6mPa・sであった。接着剤水溶液のpHは、4〜4.5であった。
ノルボルネン系樹脂フィルム(日本ゼオン社製、商品名:ゼオノア、型番:ZF14−100、厚み:100μm)を、TD方向に150℃で2.6倍に固定端一軸延伸することによって、第1の光学補償層を作製した。この第1の光学補償層の厚みは33μm、Nz=1.41(Rth=170nm、Δnd=120nm)であった。さらに、この第1の光学補償層のΔnd(380)は124nm、Δnd(550)は120nm、Δnd(780)は118nmであり、380nm〜780nmにおけるΔndの最大値と最小値との差は6nmであった。加えて、この第1の光学補償層の光弾性係数は6×10−12(m2/N)であった。
TAC基材(厚み:80μm)に、2,2´−ビス(3,4−ジカルボキシフェニル)ヘキサフルオロプロパン)および2,2´−ビス(トリフルオロメチル)−4,4´−ジアミノビフェニルから合成されたポリイミドをメチルイソブチルケトン(MIBK)に溶解した溶液(濃度:10重量%)を30μmの厚みで塗布した。その後、120℃で10分間乾燥処理することで、ポリイミド層(第2の光学補償層)の厚みが約3μmの、基材/第2の光学補償層の積層フィルムを得た。得られた第2の光学補償層の屈折率分布はnx=ny>nzであった。さらに、得られた第2の光学補償層のRth(380)は213nm、Rth(550)は180nm、Rth(780)は170nmであった。参考例1で得られた第2の偏光子と上記積層フィルムとを、積層フィルムの基材側に参考例2で得られたポリビニルアルコール系接着剤(厚み:0.1μm)を用いて貼り合わせた。さらに、第2の偏光子の第2の光学補償層とは反対の側に、トリアセチルセルロース(TAC)フィルム(厚み:80μm)を、参考例2で得られたポリビニルアルコール系接着剤(厚み:0.1μm)を用いて貼り合わせた。このようにして、偏光板一体型位相差フィルム(1B)を作製した。
液晶パネル(SONY製、BRAVIA、32インチパネル)から液晶セル(VAモード)を取り出し、アクリル系粘着剤(厚み:20μm)を用いて、上記偏光板一体型位相差フィルム(1A)と偏光板一体型位相差フィルム(1B)のそれぞれを、該液晶セルをはさんで上下に貼り合わせた。このとき、上記偏光板一体型位相差フィルム(1A)と偏光板一体型位相差フィルム(1B)のそれぞれに含まれる偏光子の吸収軸が直交するようにした。また、上記偏光板一体型位相差フィルム(1B)がバックライト側、偏光板一体型位相差フィルム(1A)が視認側となるように貼り合わせた。
得られた液晶パネル(1C)について、上記の評価方法に従ってコントラストを求め、またクニック評価を行った。結果を表1に示す。また、カラーシフトの測定結果(xy色度図)を図6に、黒輝度の測定結果を図7に示す。さらに、コニカミノルタ製CA1500を用いて、画面全体を黒表示した場合の輝度ムラを測定した。結果を図16に示す。
TAC基材(厚み:80μm)に、下記式(II)に示す構造を有するポリイミドをメチルイソブチルケトン(MIBK)に溶解した溶液(濃度:10重量%)を25μmの厚みで塗布した。その後、120℃で10分間乾燥処理することで、ポリイミド層(第2の光学補償層)の厚みが約2.5μmの、基材/第2の光学補償層の積層フィルムを得た。得られた第2の光学補償層の屈折率分布はnx=ny>nzであった。さらに、得られた第2の光学補償層のRth(380)は213nm、Rth(550)は180nm、Rth(780)は170nmであった。参考例1で得られた第2の偏光子と上記積層フィルムとを、積層フィルムの基材側に参考例2で得られたポリビニルアルコール系接着剤(厚み:0.1μm)を用いて貼り合わせた。さらに、第2の偏光子の第2の光学補償層とは反対の側に、トリアセチルセルロース(TAC)フィルム(厚み:80μm)を、参考例2で得られたポリビニルアルコール系接着剤(厚み:0.1μm)を用いて貼り合わせた。このようにして、偏光板一体型位相差フィルム(2B)を作製した。
偏光板一体型位相差フィルム(1B)に代えて偏光板一体型位相差フィルム(2B)を用いた以外は、実施例1と同様の方法で液晶パネル(2C)を作製した。
得られた液晶パネル(2C)について、上記の評価方法に従ってコントラストを求め、またクニック評価を行った。結果を表1に示す。
得られた液晶パネル(3C)について、上記の評価方法に従ってコントラストを求め、またクニック評価を行った。結果を表1に示す。
(偏光板一体型位相差フィルム(C1A)の作製)
TAC基材(厚み:80μm)に、2,2´−ビス(3,4−ジカルボキシフェニル)ヘキサフルオロプロパン)および2,2´−ビス(トリフルオロメチル)−4,4´−ジアミノビフェニルから合成されたポリイミドをメチルイソブチルケトン(MIBK)に溶解した溶液(濃度:10重量%)を30μmの厚みで塗布した。その後、120℃で10分間乾燥処理することで、ポリイミド層の厚みが約3μmの、基材/光学補償層の積層フィルムを得た。得られた積層フィルムを、150℃で1.2倍に横延伸した。延伸後の積層フィルムにおける光学補償層の屈折率分布はnx>ny>nzであり、Nz=4.9であった。また、この光学補償層は、Δnd(380)>Δnd(550)>Δnd(780)の関係を有していた。さらに、この光学補償層の光弾性係数は20×10−12(m2/N)であった。参考例1で得られた偏光子と上記積層フィルムとを、積層フィルムの基材側に参考例2で得られたポリビニルアルコール系接着剤(厚み:0.1μm)を用いて、該偏光子の吸収軸と該光学補償層の遅相軸とが直交するようにして貼り合わせた。さらに、偏光子の光学補償層とは反対の側に、トリアセチルセルロース(TAC)フィルム(厚み:80μm)を、参考例2で得られたポリビニルアルコール系接着剤(厚み:0.1μm)を用いて貼り合わせた。このようにして、偏光板一体型位相差フィルム(C1A)を作製した。
液晶パネル(SONY製、BRAVIA、32インチパネル)から液晶セル(VAモード)を取り出し、アクリル系粘着剤(厚み:20μm)を用いて、上記偏光板一体型位相差フィルム(C1A)と日東電工(株)製の偏光板(商品名:SEG1224)のそれぞれを、該液晶セルをはさんで上下に貼り合わせた。このとき、上記偏光板一体型位相差フィルム(C1A)とSEG1224のそれぞれに含まれる偏光子の吸収軸が直交するようにした。また、上記偏光板一体型位相差フィルム(C1A)がバックライト側、SEG1224が視認側となるように貼り合わせた。
得られた液晶パネル(C1C)について、上記の評価方法に従ってコントラストを求めた。結果を表1に示す。結果を上記表1に示す。また、カラーシフトの測定結果(xy色度図)を図8に、黒輝度の測定結果を図9に示す。
(液晶パネル(C2C)の作製)
上記偏光板一体型位相差フィルム(1B)が視認側、上記偏光板一体型位相差フィルム(1A)がバックライト側となるように貼り合わせた以外は、実施例1と同様の方法で液晶パネル(C2C)を作製した。
得られた液晶パネル(C2C)について、上記の評価方法に従ってコントラストを求め、またクニック評価を行った。結果を表1に示す。
ノルボルネン系樹脂フィルム(JSR社製、商品名:アートン、厚み:130μm)を、TD方向に150℃で3倍に固定端一軸延伸することによって、第1の光学補償層を作製した。この第1の光学補償層の厚みは43μm、Nz=1.34(Rth=161nm、Δnd=120nm)であった。さらに、この第1の光学補償層のΔnd(380)は124nm、Δnd(550)は120nm、Δnd(780)は119nmであり、380nm〜780nmにおけるΔndの最大値と最小値との差は5nmであった。得られた第1の光学補償層の面内位相差の波長分散特性を図10に示す。なお、図10における波長分散(Y軸)は、Δnd(λ)/Δnd(550)である。加えて、この第1の光学補償層の光弾性係数は6×10−12(m2/N)であった。
PETフィルム(厚み:50μm)に、2,2´−ビス(3,4−ジカルボキシフェニル)ヘキサフルオロプロパン)および2,2´−ビス(トリフルオロメチル)−4,4´−ジアミノビフェニルから合成されたポリイミドをシクロヘキサノンに溶解した溶液(濃度:15重量%)を30μmの厚みで塗布した。その後、100℃で10分間乾燥処理することで、PETフィルム上に厚みが約4.5μmのポリイミド層(第2の光学補償層)を得た。得られたポリイミド層(第2の光学補償層)の屈折率分布はnx=ny>nzであった。また、得られたポリイミド層(第2の光学補償層)をガラス板に粘着剤を介して転写し、ポリイミド層(第2の光学補償層)の位相差を測定したところ、Δnd=0.3nm、Rth=182nmであった。さらに、得られたポリイミド層(第2の光学補償層)のRth(380)は213nm、Rth(550)は187nm、Rth(780)は170nmであった。得られたポリイミド層(第2の光学補償層)の40°から光を入射した際の厚み方向の位相差の波長分散特性を図11に示す。なお、図11における波長分散(Y軸)は、Rth(λ)/Rth(550)である。
偏光板一体型位相差フィルム(1A)に代えて偏光板一体型位相差フィルム(2A)を用い、偏光板一体型位相差フィルム(1B)に代えて偏光板一体型位相差フィルム(3B)を用いた以外は、実施例1と同様の方法で液晶パネル(4C)を作製した。
得られた液晶パネル(4C)について、ELDIM社製 EZ Contrastを用いて、視野角特性を測定した。結果を図12に示す。また、上記の評価方法に従ってコントラストを求め、またクニック評価を行った。結果を表1に示す。
ノルボルネン系樹脂フィルムの延伸倍率を1.8倍とした以外は、実施例4と同様の方法で、ノルボルネン系樹脂フィルム偏光板一体型位相差フィルム(3A)を作製した。得られた第1の光学補償層の厚みは65μm、Nz=1.61(Rth=163nm、Δnd=101nm)であった。さらに、この第1の光学補償層のΔnd(380)は104nm、Δnd(550)は101nm、Δnd(780)は100nmであり、380nm〜780nmにおけるΔndの最大値と最小値との差は4nmであった。加えて、この第1の光学補償層の光弾性係数は6×10−12(m2/N)であった。ここで得られた第1の光学補償層の面内位相差の波長分散特性は、実施例4で得られた第1の光学補償層の面内位相差の波長分散特性と同等であった。
実施例4と同様の方法で、偏光板一体型位相差フィルム(4B)を作製した。このとき、ポリイミド層(第2の光学補償層)の厚みは約4μmであった。また、得られたポリイミド層(第2の光学補償層)の屈折率分布はnx=ny>nzであった。さらに、得られたポリイミド層をガラス板に粘着剤を介して転写し、ポリイミド層の位相差を測定したところ、Δnd=0.2nm、Rth=169nmであった。加えて、得られたポリイミド層(第2の光学補償層)のRth(380)は215nm、Rth(550)は174nm、Rth(780)は158nmであった。ここで得られた第2の光学補償層の面内位相差の波長分散特性は、実施例4で得られた第2の光学補償層の面内位相差の波長分散特性と同等であった。
偏光板一体型位相差フィルム(1A)を偏光板一体型位相差フィルム(3A)に代え、偏光板一体型位相差フィルム(1B)を偏光板一体型位相差フィルム(4B)に代えた以外は、実施例1と同様の方法で液晶パネル(5C)を得た。
得られた液晶パネル(5C)について、ELDIM社製 EZ Contrastを用いて、視野角特性を測定した。結果を図13に示す。また、上記の評価方法に従ってコントラストを求め、またクニック評価を行った。結果を表1に示す。
(偏光板一体型位相差フィルム(C1B)の作製)
トリアセチルセルロース(TAC)フィルム(富士フィルム社製、商品名:TF−TAC)をアクリル系粘着剤(厚み:20μm)を用いて3枚貼り合わせ、積層フィルムを作製した。得られた積層フィルムは、厚みが280μm、Δnd=2nm、Rth=182nmであった。また、得られた積層フィルムは、負の波長分散特性を示した。得られた積層フィルムの40°から光を入射した際の厚み方向の位相差の波長分散特性を図11に示す。
:20μm)を用いて貼り合わせ、偏光板一体型位相差フィルム(C1B)を作製した。
偏光板一体型位相差フィルム(1B)に代えて、上記偏光板一体型位相差フィルム(C1B)を用いた以外は、実施例1と同様にして液晶パネル(C3C)を作製した。
得られた液晶パネル(C3C)について、ELDIM社製 EZ Contrastを用いて、視野角特性を測定した。結果を図14に示す。また、上記の評価方法に従ってコントラストを求めた。結果を表1に示す。
(偏光板一体型位相差フィルム(C2A)の作製)
ポリカーボネートフィルム(日東電工社製、商品名:NRF、厚み:60μm)をTD方向に160℃で1.5倍に自由端一軸延伸することによって、位相差フィルムを作製した。得られた位相差フィルムはΔnd=142nm、Rth=151nmであり、光弾性係数は72×10−12(m2/N)であった。また、得られた位相差フィルムは、正の波長分散特性を示した。この位相差フィルムの面内位相差の波長分散特性を図10に示す。
偏光板一体型位相差フィルム(1A)に代えて、上記偏光板一体型位相差フィルム(C2A)を用いた以外は、実施例1と同様にして液晶パネル(C4C)を作製した。
得られた液晶パネル(C4C)について、ELDIM社製 EZ Contrastを用いて、視野角特性を測定した。結果を図15に示す。また、コニカミノルタ製CA1500を用いて、画面全体を黒表示した場合の輝度ムラを測定した。結果を図16に示す。さらに、上記の評価方法に従ってコントラストを求めた。結果を表1に示す。
40 液晶セル
50 第2の偏光子
60 第1の光学補償層
70 第2の光学補償層
100 液晶パネル
Claims (9)
- 第1の偏光子と;第1の光学補償層と;液晶セルと;第2の光学補償層と;第2の偏光子とを;視認側からこの順に備え、
該第1の光学補償層が、その光弾性係数の絶対値が40×10−12(m2/N)以下であり、その面内位相差Δndが90nm〜200nmであり、下記式(1)および(2)の関係を有し、そのNz係数が1.1〜1.41であり、ならびに、該第1の偏光子の液晶セル側の保護層として機能し、
該第2の光学補償層が、下記式(3)および(4)の関係を有する、液晶パネル:
Δnd(380)=Δnd(550)=Δnd(780)・・・(1)
nx>ny>nz ・・・(2)
Rth(380)>Rth(550)>Rth(780)・・・(3)
nx=ny>nz ・・・(4)。 - 前記第1の光学補償層の波長380nm〜780nmにおけるΔndの最大値と最小値との差が10nm以下である、請求項1に記載の液晶パネル。
- 前記第1の光学補償層が、環状オレフィン系樹脂を含有するフィルムである、請求項1または2に記載の液晶パネル。
- 前記第1の光学補償層が、固定端一軸延伸法により作製されたフィルムである、請求項3に記載の液晶パネル。
- 前記第2の光学補償層が、ポリアミド、ポリイミド、ポリエステル、ポリエーテルケトン、ポリアミドイミドおよびポリエステルイミドから選択される少なくとも1つの非液晶材料を含有する、請求項1から4のいずれかに記載の液晶パネル。
- 前記第1の光学補償層と前記第1の偏光子とが、ポリビニルアルコール系樹脂を含有する水溶性接着剤で貼り合わせられている、請求項1から5のいずれかに記載の液晶パネル。
- 前記水溶性接着剤が金属化合物コロイドを含有する、請求項6に記載の液晶パネル。
- 前記液晶セルの駆動モードが、VAモードまたはOCBモードである、請求項1から7のいずれかに記載の液晶パネル。
- 請求項1から8のいずれかに記載の液晶パネルを含む、液晶表示装置。