JP5038844B2 - 加工性の改善されたポリ(アリーレンスルフィド)組成物 - Google Patents
加工性の改善されたポリ(アリーレンスルフィド)組成物 Download PDFInfo
- Publication number
- JP5038844B2 JP5038844B2 JP2007264247A JP2007264247A JP5038844B2 JP 5038844 B2 JP5038844 B2 JP 5038844B2 JP 2007264247 A JP2007264247 A JP 2007264247A JP 2007264247 A JP2007264247 A JP 2007264247A JP 5038844 B2 JP5038844 B2 JP 5038844B2
- Authority
- JP
- Japan
- Prior art keywords
- poly
- barium
- arylene sulfide
- sulfide
- melt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
(a) ファイバー形成ポリ(アリーレンスルフィド)を紡糸口金を通して紡糸カラム内に溶融押出する工程;
(b) 得られたフィラメントを急冷ガスで冷却する工程;及び
(c) 冷却したフィラメントを紡糸カラムから回収する工程
を含むポリ(アリーレンスルフィド)ファイバーの製造方法であって、前記ポリ(アリーレンスルフィド)がバリウム含有水酸化物及び塩より成る群から選択される少なくとも1種の化合物で処理されたものである方法に関する。
上記滑剤はポリマー中に、約 0.05 から約 1.5重量%、特に好ましくは約 0.1から約 0.5重量%の量で存在する。典型的には、この滑剤をポリ(アリーレンスルフィド)樹脂に直接接触させるようないずれかの手段によって本発明の組成物中に加える。必要ならば、対象組成物の滑剤成分はバリウム化合物と共に押し出すか、又は1以上の独立した配合工程で加えてもよい。
本発明のポリ(アリーレンスルフィド)("PAS") 成分は式:
上記プレポリマーを製造するための出発原料はアルカリ金属スルフィド、ジハロ芳香族化合物及び重合溶媒を含む。アルカリ金属スルフィドには、硫化リチウム、硫化ナトリウム、硫化カリウム、硫化ルビジウム、硫化セシウム及びそれらの混合物が含まれる。これらのアルカリ金属スルフィドは水和物若しくは水性混合液として、又は無水形態で使用することができる。これらのアルカリ金属スルフィドのうち、硫化ナトリウムが最も安価で商業的に好ましい。アルカリ金属スルフィド中に微量に存在することがありうる酸性塩(例えば、アルカリ金属ジスルフィド及びアルカリ金属重炭酸塩)を中和するために、それと組み合わせて少量のアルカリ金属水酸化物を使用することもできる。
予備重合は好ましくは 160ないし 260℃、特に好ましくは 180ないし 235℃の範囲の温度で行う。160℃よりも低い温度では、反応速度が非常に遅くなるが、260℃以上の温度では、形成された PASが分解されて非常に低い溶融粘度の PASだけが製造されがちである。
予備重合から二相分離重合への転換点では、上記PAS の溶融粘度は好ましくは(310℃及び剪断速度 200 sec-1で)0.5 ないし 30 Pa.sec. の範囲である。高重合度のPAS を得るには 1 Pa.sec.から 20 Pa.sec. の範囲がより適している。0.5 Pa.sec. よりも低い粘度では二相分離の形成が不十分であり、それによって重合系の分解又は反応速度の低下が容易に起こりうる。30 Pa.sec.よりも高い粘度では、ポリマー開裂を促進するであろう有害物質がより多量に蓄積されることになり、そのため望ましくないことにポリマー収量の低下及びポリマー系の分解が起きることになる。
本発明の組成物は多様な成形品及び押出品の製造に有用であり、ファイバー及びモノフィラメントに用いるのに特に適している。溶融体中で相対的に高い延性度を示す組成物はフィルム、シート、ファイバー及びモノフィラメントの製造に有用である。さらに、本発明の組成物は封入剤又は被膜として使用することもできる。
PPSI - ヘキスト・セラニーズ・コーポレーションから入手できるポリアリーレンスルフィドで、温度 310℃及び剪断速度 1200 sec -1における平均溶融粘度が 140 Pa.sec.と報告されているもの。
PPSII - ヘキスト・セラニーズ・コーポレーションから入手できるポリアリーレンスルフィドで、1200 sec-1における平均溶融粘度が 55 Pa.sec. と報告されているもの。
AXEL INT 38H - アクセル・プラスチックス・リサーチ・ラボ社から入手できる、架橋ポリエチレンワックス及び脂肪酸の混合物。
PETS - ペンタエリスリトールテトラステアレート。
Weston 618 - ジェネラル・エレクトリック社から入手できるジステアリルペンタエリスリトールジホスファイト。
Acrawax C - ロンザ社の N,N- エチレンビスステアラミド。
PE Wax - アライド−シグナル社から AC629A の商標名で販売されているポリエチレンワックス。
以下の実施例に報告するように、重ね剪断粘着力を以下の手順で測定した:
22.86 cm× 22.86 cm × 0.95 cmの合わせ雄雌溝付き成形型を硬質アルミニウムで作り、中に幅 2.54 cm×深さ 0.25 cm×長さ 22.86 cm の溝を平行に5本付けた。3個の熱電対穴を一方の端からプレートの中心まであけ、熱の均一性をモニターした。試験からこれは±2℃以内であることが示された。次いで、プレートを強烈に陽極酸化して耐磨耗性を持たせた。
1,100,000 ダインの力を保持できるグリップを備えた手動ジョー;
ゲージの長さ - 12.70 cm ;
クロスヘッド速度 - 0.127 cm/min ;及び
サンプル幅 - 2.54 cm。
他に断らない限り、所定の組成物について 25 回ずつ試験を繰り返し、試験標本についての最大荷重の平均値を最大荷重として報告した。接合面において接着性(金属とプラスチック表面)又は凝集性(プラスチック内)の両方の不良が起こりうることに注意すべきである。不良の様式は試験の後に接合表面を調べることにより明らかにすることできる。
成分を記載の比率で混合して得られた混合物を表示のように Haakeコニカル二軸スクリュー押出機(System90)又は 30 mm ZSK二軸スクリュー押出機のいずれかで溶融ブレンドすることにより表1に示す組成物を配合して押出物を製造し、冷却及びペレット化した。混合する前に、ポリ(フェニレンスルフィド)及び他の成分は 110℃の温度で一晩乾燥させた。押出条件は以下の通りであった:
Haake 押出機:
溶融温度:300 ないし 330℃;
押出ダイ温度:310 ないし 330℃;及び
スクリュー速度:50-300 rpm
減圧:なし
ZSK 押出機:
溶融温度:310 ないし 335℃;
押出ダイ温度:310 ないし 330℃;及び
スクリュー速度:150 rpm
減圧:約 635 mmHg
組成物の溶融粘度を Kayeness Rheometer を用いて 310℃及び 1200sec-1で測定した。種々の組成物の重ね剪断粘着力を以下に記載する手順を用いて測定し、表1に報告する。
99.30 重量%の PPSII、0.35重量%の水酸化バリウム8水和物及び0.35重量%の表示の滑剤を含有する組成物を用いて、実施例1に特定した条件下で Haake二軸スクリュー押出機で表2に記載の組成物を配合した。
表3に記載の組成物を 70 mm ZSK条件を用いて実施例1に記載したように配合した。ペレット化した PPS押出物を通常の溶融紡糸法を用いて連続ベースで溶融紡糸した。使用した紡糸口金は孔の直径が 0.23 mmの 1000 環状孔紡糸口金であった。溶融温度は約 300℃で、孔当たりの押出量は 0.559 g/min/孔であった。フィラメントは 35℃、湿度 70%の急冷エアで冷却した。紡糸仕上げを施し、フィラメントを 777 m/minの巻取速度で巻き取った。得られた糸は 6400 デニールであった。
上記紡績糸に延伸滑剤の希釈分散水溶液(85℃に加熱)を注ぎ、ステープルファイバー延伸枠による2段階延伸法で 2.9倍、次いで 1.04 倍に延伸した。延伸した糸を冷却して縮れさせ、この加工糸を乾燥させて 180℃でヒートセットした。
より条件の厳しい実験を、実施例3に記載のものと同様の手段であるが、全体直径が 0.508 mm で葉の長さが 0.214 mm 、葉の幅が 0.102 mm の三葉式のY形紡糸口金孔を有する紡糸口金を使用して行った。孔当たりの押出量は 0.233 g/min、急冷エアは 28℃、そして巻取速度は 899 m/minであった。フィラメントのトータルの厚みは実施例3の 6400 デニールに対して 4550 デニールであった。これらの条件下における慣用的なPPS の加工は著しく不良であった。
押出レオメーター・ストランド中におけるゲル形成を調べるために試験法を開発した。この試験で、表5に記載のPPS配合物を通常のレオメーター中で 350℃で溶融して保持した。ストランドを押出し、5分間隔で回収した。次いで各ストランドをゲルについて調べた。これにより、最初にゲルが形成されたおよその時間が測定できた。これらの実験についてのデータを表5に表す。データから、バリウム処理したポリマーをゲル化の兆候を示す前に溶融体中に保持することができる時間が滑剤を加えることにより延長されることがわかる。このことは重要である。というのは、ゲル形成が正常な加工を中断させかねないからである。
Claims (3)
- 溶融紡糸操作におけるポリ(アリーレンスルフィド)の加工性を改善するための方法であって、
溶融紡糸する前に該ポリ(アリーレンスルフィド)をイオン性バリウムの供給源及び滑剤で処理することを含み、
該ポリ(アリーレンスルフィド)がバリウム含有水酸化物及びその塩よりなる群から選択される少なくとも1種のバリウム含有化合物で処理され、
該バリウム含有化合物が、酢酸バリウム、硝酸バリウム、亜硝酸バリウム、硫酸バリウム、クエン酸バリウム又はそれらの組み合わせである、前記方法。 - 請求項1に記載の方法であって、バリウム含有化合物での処理によってポリ(アリーレンスルフィド)に0.05 から2.0重量%のバリウムが供給される方法。
- 請求項2に記載の方法であって、ポリ(アリーレンスルフィド)がポリフェニレンスルフィドである方法。