JP4756628B2 - 水系itoインク - Google Patents
水系itoインク Download PDFInfo
- Publication number
- JP4756628B2 JP4756628B2 JP2004348535A JP2004348535A JP4756628B2 JP 4756628 B2 JP4756628 B2 JP 4756628B2 JP 2004348535 A JP2004348535 A JP 2004348535A JP 2004348535 A JP2004348535 A JP 2004348535A JP 4756628 B2 JP4756628 B2 JP 4756628B2
- Authority
- JP
- Japan
- Prior art keywords
- water
- ito
- ink
- weight
- solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
容量1Lの容器中でITO粉(三井金属鉱業社製、一次粒子の平均粒径20nm)180gと溶媒としての純水378gを混合し、さらに表面張力調整剤として2−n−ブトキシエタノール42gを添加したものを、湿式メディアミル(メデイア:φ0.8mmジルコニアビーズ)により、湿式解砕処理を行いスラリーを得た。
前記ITOインクAについて、市販のインクジェットプリンター(セイコー・エプソン社製PM−G700)を用い、無アルカリガラス基板OA−10(日本電気硝子社製)へ配線パターン(ライン&スペース100μm、長さ2cm)の作製を行ったところ、ITOインクAはインクジェットノズルに目詰まりすること無く印刷可能であった。連続50回の印刷後、ノズルの目詰まりを確認するため、ノズルチェックパターン印刷を実施したところ、ノズル詰まりは確認されなかった。また、得られた配線パターンを光学顕微鏡で観察したところ、配線パターンに断線やインクの飛散は観察されず、良好な配線パターンであった。
ITOインクAを、10cm角の無アルカリガラス基板OA−10(日本電気硝子社製)上に、スピンコーターを用い回転数800rpmの条件で塗膜した。次に、塗膜したガラス基板を、250℃×30分の条件によりホットプレート上で大気焼成を行った後、水素含有量が1容量%の水素−窒素混合雰囲気で、250℃×30分の条件で還元焼成を行い、ガラス基板上にITO電極膜を形成した。電極厚みをSEM観察により測定したところ、約1μmであった。ITO電極膜の比抵抗を四探針抵抗測定機ロレスタGP(三菱化学社製)にて測定し、また、ガラス基板との密着性をJIS K 5600 パラグラフ5−6に準じ、クロスカット法により評価した。比抵抗は1.8×10−1Ω・cmであり、密着性の評価は、分類0であり、良好な密着性が得られている。
容量1Lの容器中にITO粉72gと溶媒としての純水442gを混合し、さらに表面張力調整剤として2−n−ブトキシエタノール56gとエチレングリコール56gを添加し、湿式メディアミル(メデイア:φ0.65mmジルコニアビーズ)により、湿式解砕処理を行いスラリーを得た。
Claims (4)
- 溶媒としての水、ITO粉、表面張力調整剤、密着性向上剤を含む水系ITOインクであって、
当該水系ITOインク重量を100重量%としたとき、当該溶媒としての水を30重量%以上含有し、前記密着性向上剤としてチタンカップリング剤、ジルコニアカップリング剤からなる群より選択される1種又は2種以上を0.3重量%〜20重量%含有する組成を備えることを特徴とする水系ITOインク。 - 前記表面張力調整剤はアルコール類、グリコール類からなる群より選択される1種または2種以上を組み合わせたものである請求項1に記載の水系ITOインク。
- 前記溶媒としての水は、イオン交換水又は蒸留水であることを特徴とする請求項1又は請求項2に記載の水系ITOインク。
- 前記ITO粉は、当該粉粒の一次粒子径が100nm以下である請求項1〜請求項3のいずれかに記載の水系ITOインク。