JP4756575B2 - 栽培培地収容具 - Google Patents
栽培培地収容具 Download PDFInfo
- Publication number
- JP4756575B2 JP4756575B2 JP2005054691A JP2005054691A JP4756575B2 JP 4756575 B2 JP4756575 B2 JP 4756575B2 JP 2005054691 A JP2005054691 A JP 2005054691A JP 2005054691 A JP2005054691 A JP 2005054691A JP 4756575 B2 JP4756575 B2 JP 4756575B2
- Authority
- JP
- Japan
- Prior art keywords
- titanium
- titanium oxide
- carbon
- layer
- oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
実施例1〜3
アセチレンの燃焼炎を用い、厚さ0.3mmのチタン板をその表面温度が約1100℃となるように加熱処理することにより、表面層として炭素がTi−C結合の状態でドープされた炭素ドープ酸化チタン層を有するチタン板を形成した。1100℃での加熱処理時間をそれぞれ5秒(実施例1)、3秒(実施例2)、1秒(実施例3)に調整することにより炭素ドープ量及び炭素ドープ酸化チタン層の厚さが異なる炭素ドープ酸化チタン層を有するチタン板を形成した。
市販されている酸化チタンゾル(石原産業製STS−01)を厚さ0.3mmのチタン板にスピンコートした後、加熱して密着性を高めた酸化チタン皮膜を有するチタン板を形成した。
SUS板上に酸化チタンがスプレーコートされている市販品を比較例2の酸化チタン皮膜を有する基体とした。
実施例1で得られた炭素がTi−C結合の状態でドープされた炭素ドープ酸化チタン層及び比較例1の酸化チタン皮膜について、ナノハードネステスター(NHT)(スイスのCSM Instruments製)により、圧子:ベルコビッチタイプ、試験荷重:2mN、負荷除荷速度:4mN/minの条件下で皮膜硬度を測定したところ、実施例1の炭素がTi−C結合の状態でドープされた炭素ドープ酸化チタン層はビッカース硬度が1340と高い値であった。一方、比較例1の酸化チタン皮膜のビッカース硬度は160であった。
実施例1の炭素がTi−C結合の状態でドープされた炭素ドープ酸化チタン層及び比較例1の酸化チタン皮膜について、マイクロスクラッチテスター(MST)(スイスのCSM Instruments製)により、圧子:ロックウェル(ダイヤモンド)、先端半径200μm、初期荷重:0N、最終荷重:30N、負荷速度:50N/min、スクラッチ長:6mm、ステージ速度:10.5mm/minの条件下で耐スクラッチ性試験を実施した。スクラッチ痕内に小さな膜の剥離が起こる「剥離開始」荷重及びスクラッチ痕全体に膜の剥離が起こる「全面剥離」荷重を求めた。その結果は第1表に示す通りであった。
実施例1の炭素がTi−C結合の状態でドープされた炭素ドープ酸化チタン層及び比較例1の酸化チタン皮膜について、高温トライボメーター(HT−TRM)(スイスのCSM Instruments製)により、試験温度:室温及び470℃、ボール:直径12.4mmのSiC球、荷重:1N、摺動速度:20mm/sec、回転半径:1mm、試験回転数:1000回転の条件下で摩耗試験を実施した。
実施例1の炭素がTi−C結合の状態でドープされた炭素ドープ酸化チタン層を有するチタン板を1M硫酸水溶液及び1M水酸化ナトリウム水溶液にそれぞれ室温で1週間浸漬した後、上記の皮膜硬度、耐摩耗性、及び後記する光電流密度を測定したところ、浸漬の前後で、結果に有意な差は認められなかった。即ち、実施例1の炭素がTi−C結合の状態でドープされた炭素ドープ酸化チタン層は高い耐薬品性を有することが認められた。
実施例1の炭素がTi−C結合の状態でドープされた酸化チタン層について、X線光電子分光分析装置(XPS)で、加速電圧:10kV、ターゲット:Alとし、2700秒間Arイオンスパッタリングを行い、分析を開始した。このスパッタ速度がSiO2膜相当の0.64Å/sとすると、深度は約173nmとなる。そのXPS分析の結果を図2に示す。結合エネルギーが284.6eVである時に最も高いピークが現れる。これはCls分析に一般的に見られるC−H(C)結合であると判断される。次に高いピークが結合エネルギー281.7eVである時に見られる。Ti−C結合の結合エネルギーが281.6eVであるので、実施例1の炭素ドープ酸化チタン層中ではCがTi−C結合としてドープされていると判断される。なお、炭素ドープ酸化チタン層の深さ方向の異なる位置の11点でXPS分析を行った結果、全ての点で281.6eV近傍に同様なピークが現れた。
実施例1〜3の炭素がTi−C結合の状態でドープされた炭素ドープ酸化チタン層及び比較例1、2の酸化チタン皮膜の波長応答性をOriel社のモノクロメーターを用いて測定した。具体的には、それぞれの層、皮膜に対し、0.05M硫酸ナトリウム水溶液中で対極との間に電圧を0.3V印加し、光電流密度を測定した。
実施例1〜3の炭素がTi−C結合の状態でドープされた炭素ドープ酸化チタン層及び比較例1、2の酸化チタン皮膜について、式
η=jp(Ews−Eapp)/I
で定義される光エネルギー変換効率ηを求めた。ここで、Ewsは水の理論分解電圧(=1.23V)、Eappは印加電圧(=0.3V)、Iは照射光強度である。この結果を図4に示す。図4は光エネルギー変換効率ηを照射光波長に対して示してある。
実施例1及び2の炭素がTi−C結合の状態でドープされた炭素ドープ酸化チタン層及び比較例1の酸化チタン皮膜について、消臭試験を実施した。具体的には、消臭試験に一般的に用いられるアセトアルデヒドを炭素ドープ酸化チタン層を有する基体と共に1000mlのガラス容器に封入し、初期の吸着による濃度減少の影響が無視できるようになってから、UVカットフィルタ付き蛍光灯にて可視光を照射し、所定の照射時間毎にアセトアルデヒド濃度をガスクロマトグラフィーで測定した。なお、各皮膜の表面積は8.0cm2とした。
実施例1の炭素ドープ酸化チタン層及び比較例1の酸化チタン皮膜について、防汚試験を実施した。各皮膜を(財)電力中央研究所内の喫煙室内に設置し、145日後の表面の汚れを観察した。なお、この喫煙室内には太陽光の直接の入射はない。
実施例1〜3と同様にアセチレンの燃焼炎を用い、厚さ0.3mmのチタン板を、第2表に示す表面温度で第2表に示す時間の間加熱処理することにより、表面層として炭素ドープ酸化チタン層を有するチタン板を形成した。
天然ガスの燃焼炎を用い、厚さ0.3mmのチタン板を、第2表に示す表面温度で第2表に示す時間の間加熱処理した。
実施例4〜7の炭素ドープ酸化チタン層及び比較例3の皮膜について、上記の試験例1と同様にしてビッカース硬度(HV)を測定した。それらの結果を第2表に示す。また、実施例4〜7で形成された炭素ドープ酸化チタン層は、水滴との接触角が2°程度の超親水性であった。
実施例4〜7の炭素ドープ酸化チタン層及び比較例1及び3の酸化チタン皮膜について、試験例6と同様に、0.05M硫酸ナトリウム水溶液中で対極との間に電圧を0.3V印加し、300nm〜520nmの光を照射して光電流密度を測定した。その結果を図7に示す。図7には、得られた光電流密度jpを電位ECP(Vvs. SSE)に対して示してある。
アセチレンの燃焼炎を用い、厚さ0.3mmのTi−6Al−4V合金板をその表面温度が約1100℃となるように加熱処理することにより、表面層が炭素ドープ酸化チタンを含有するチタン合金からなる合金板を形成した。1100℃での加熱処理時間を60秒とした。このようにして形成された炭素ドープ酸化チタンを含有する層は水滴との接触角が2°程度の超親水性であり、また実施例4で得られた炭素ドープ酸化チタン層と同様な光触媒活性を示した。
厚さ0.3mmのステンレス鋼板(SUS316)の表面にスパッタリングによって膜厚が約500nmのチタン薄膜を形成した。アセチレンの燃焼炎を用い、その表面温度が約900℃となるように加熱処理することにより、表面層として炭素ドープ酸化チタン層を有するステンレス鋼板を形成した。900℃での加熱処理時間を15秒とした。このようにして形成された炭素ドープ酸化チタン層は水滴との接触角が2°程度の超親水性であり、また、実施例4で得られた炭素ドープ酸化チタン層と同様な光触媒活性を示した。
粒径20μmの酸化チタン粉末をアセチレンの燃焼炎中に供給し、燃焼炎中に所定時間滞留させてその表面温度が約1000℃となるように加熱処理することにより、表面層として炭素ドープ酸化チタン層を有するチタン粉末を形成した。1000℃での加熱処理時間を4秒とした。このようにして形成された炭素ドープ酸化チタン層を有するチタン粉末、実施例4で得られた炭素ドープ酸化チタン層と同様な光触媒活性を示した。
厚さ1mmのガラス板(パイレックス(登録商標))の表面にスパッタリングによって膜厚が約100nmのチタン薄膜を形成した。アセチレンの燃焼炎を用い、その表面温度が1100℃(実施例11)、又は1500℃(実施例12)となるように加熱処理することにより、表面層として炭素ドープ酸化チタン層を有するガラス板を形成した。1100℃、又は1500℃での加熱処理時間を10秒とした。このようにして形成された炭素ドープ酸化チタン層は表面温度が1100℃の場合には図8(a)に写真で示すように透明であったが、表面温度が1500℃の場合には図9に示すように海に浮かぶ多数の小島状の起伏が表面に生じており、図8(b)に示すように半透明となった。
厚さ0.3mmのチタン板の表面を、アセチレンの燃焼炎により、第3表に示す表面層温度で第3表に示す時間加熱処理した。その後その燃焼炎を当てた表面を厚さ30mmのステンレスブロックの平らな面と接触させて冷却すると、チタン板表面の大部分に白色の酸化チタンからなる微細柱が林立している層が露出している部材と、薄膜上に白色の酸化チタンからなる多数の連続した狭幅突起部及び該突起部上に林立している微細柱が露出している小片部材とに分離した。即ち、加熱処理で表面層内部に形成された酸化チタンからなる微細柱が林立している層がその後の冷却で該微細柱が林立している層が該表面層に沿う方向で切断された。このようにして実施例13〜16の多機能材を得た。
厚さ0.3mmのTi−6Al−4V合金板の表面を、アセチレンの燃焼炎により、第3表に示す表面層温度で第3表に示す時間加熱処理した。その後その燃焼炎を当てた表面を厚さ30mmのステンレスブロックの平らな面と接触させて冷却すると、チタン合金板表面の大部分にチタン合金酸化物からなる微細柱が林立している層が露出している部材と、薄膜上にチタン合金酸化物からなる多数の連続した狭幅突起部及び該突起部上に林立している微細柱が露出している小片部材とに分離した。
厚さ0.3mmのステンレス鋼板(SUS316)の表面に電子ビーム蒸着によって膜厚が約3μmのチタン薄膜を形成した。その薄膜表面を、アセチレンの燃焼炎により、第3表に示す表面層温度で第3表に示す時間加熱処理した。その後その燃焼炎を当てた表面を厚さ30mmのステンレスブロックの平らな面と接触させて冷却すると、ステンレス鋼板表面の大部分に白色の酸化チタンからなる微細柱が林立している層が露出している部材と、薄膜上に白色の酸化チタンからなる多数の連続した狭幅突起部及び該突起部上に林立している微細柱が露出している小片部材とに分離した。
実施例13〜18得られた基板表面に微細柱が林立している層が露出している部材の微細柱側表面について、JIS K 5600−5−4(1999)に基づき、三菱鉛筆株式会社製ユニ1H〜9H鉛筆を用いて鉛筆引っかき硬度試験を実施した。その結果は第3表に示す通りであった。即ち、全ての試験片について9Hの鉛筆を用いた場合にも損傷は認められなかった。
実施例13〜18で得られた基板表面に微細柱が林立している層が露出している部材を1M硫酸水溶液及び1M水酸化ナトリウム水溶液にそれぞれ室温で1週間浸漬し、水洗し、乾燥させた後、上記の引っかき硬度試験:鉛筆法を実施した。その結果は第3表に示す通りであった。即ち、全ての試験片について9Hの鉛筆を用いた場合にも損傷は認められず、高い耐薬品性を有することが認められた。
実施例13〜18で得られた基板表面に微細柱が林立している層が露出している部材を管状炉内に入れ、大気雰囲気下で室温から1時間かけて500℃まで昇温させ、500℃の恒温で2時間保持し、更に1時間かけて室温まで静置冷却した後、上記の引っかき硬度試験:鉛筆法を実施した。その結果は第3表に示す通りであった。即ち、全ての試験片について9Hの鉛筆を用いた場合にも損傷は認められず、高い耐熱性をを有することが認められた。
試料として、実施例16で得られた基板表面に微細柱が林立している層が露出している表面積8cm2の部材及び比較例1で得られた酸化チタン皮膜を有する表面積8cm2のチタン板を用いて消臭試験を実施した。具体的には、それらの試料をそれぞれ、約10μmol/Lの濃度に調整したメチレンブルー水溶液80mL中に浸漬し、初期の吸着による濃度減少の影響が無視できるようになってから、松下電器産業株式会社製のUVカットフィルター付き蛍光灯により可視光を照射し、所定の照射時間毎に波長660nmにおけるメチレンブルー水溶液の吸光度をHACH社製水質検査装置DR/2400で測定した。その結果は図14に示す通りであった。
実施例15で得られた基板表面に微細柱が林立している層が露出している部材の微細柱から得た試料についてX線回折(XRD)を行った結果、ルチル型の結晶構造を有することが判明した。
Claims (10)
- 炭素がTi−C結合の状態でドープされた酸化チタン又はチタン合金酸化物からなる多機能皮膜と、心材とで構成されており、該心材がチタン、チタン合金、チタン合金酸化物又は酸化チタンであることを特徴とする栽培培地収容具。
- 多機能皮膜のビッカース硬度が300以上であることを特徴とする請求項1記載の栽培培地収容具。
- 表面の少なくとも一部に、炭素がドープされている酸化チタン又はチタン合金酸化物からなる多機能皮膜と、心材とで構成されており、該心材がチタン、チタン合金、チタン合金酸化物又は酸化チタンであり、該多機能皮膜の表面に、炭素がドープされている酸化チタン又はチタン合金酸化物からなる微細柱が林立していることを特徴とする栽培培地収容具。
- 炭素がTi−C結合の状態でドープされていることを特徴とする請求項3記載の栽培培地収容具。
- 多機能皮膜が炭素を0.3〜15at%含有していることを特徴とする請求項1〜4の何れかに記載の栽培培地収容具。
- 栽培培地収容具が表面層の多機能皮膜と中間層と心材とで構成されており、該中間層がチタン、チタン合金、チタン合金酸化物又は酸化チタンであり、該心材がチタン、チタン合金及び酸化チタン以外の材質で構成されていることを特徴とする請求項1〜4の何れかに記載の栽培培地収容具。
- 表面層の多機能皮膜がTi−C結合を介してその下層のチタン、チタン合金、チタン合金酸化物又は酸化チタンに結合されていることを特徴とする請求項6記載の栽培培地収容具。
- 多機能皮膜が可視光応答型光触媒として機能することを特徴とする請求項1〜7の何れかに記載の栽培培地収容具。
- チタン合金がTi−6Al−4V、Ti−6Al−6V−2Sn、Ti−6Al−2Sn−4Zr−6Mo、Ti−10V−2Fe−3Al、Ti−7Al−4Mo、Ti−5Al−2.5Sn、Ti−6Al−5Zr−0.5Mo−0.2Si、Ti−5.5Al−3.5Sn−3Zr−0.3Mo−1Nb−0.3Si、Ti−8Al−1Mo−1V、Ti−6Al−2Sn−4Zr−2Mo、Ti−5Al−2Sn−2Zr−4Mo−4Cr、Ti−11.5Mo−6Zr−4.5Sn、Ti−15V−3Cr−3Al−3Sn、Ti−15Mo−5Zr−3Al、Ti−15Mo−5Zr、又はTi−13V−11Cr−3Alである請求項1〜8の何れかに記載の栽培培地収容具。
- 栽培培地収容具が種苗用箱、苗床箱、水耕栽培用養液収容装置、プランター又は植木鉢であることを特徴とする請求項1〜9の何れかに記載の栽培培地収容具。