JP4319158B2 - 塗膜密着性と耐塗装下腐食性に優れた高クロム鋼 - Google Patents
塗膜密着性と耐塗装下腐食性に優れた高クロム鋼 Download PDFInfo
- Publication number
- JP4319158B2 JP4319158B2 JP2005065207A JP2005065207A JP4319158B2 JP 4319158 B2 JP4319158 B2 JP 4319158B2 JP 2005065207 A JP2005065207 A JP 2005065207A JP 2005065207 A JP2005065207 A JP 2005065207A JP 4319158 B2 JP4319158 B2 JP 4319158B2
- Authority
- JP
- Japan
- Prior art keywords
- coating
- steel
- corrosion resistance
- adhesion
- coating film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(1)質量%にて、
C:0.001〜0.030%、
Si:1.0%以下、
Mn:1.0%以下、
P:0.040%以下、
S:0.030%以下、
Cr:7.0〜14.0%、
N:0.025%以下
を含有し、残部はFeおよび不可避不純物からなる鋼であって、表面酸化皮膜内にSiおよびCrの濃化層を有し、その濃化の最も大きい部分の濃度が、C、OおよびNを除いたカチオンのみの割合で、Siについては8%以上、Crについては18%以上35%以下であることを特徴とする塗膜密着性と耐塗装下腐食性に優れた高クロム鋼。
(2)上記(1)の基材組成に、さらに、質量%で、
Ti:0.08〜2%、
Nb:0.08〜2%、
Al:0.01〜1%
の内1種以上を含み、表面酸化皮膜内に付加元素の濃化層を有し、これら元素の濃化の最も大きい部分の濃度の合計が、C、OおよびNを除いたカチオンのみの割合で、1%以上であることを特徴とする塗膜密着性と耐塗装下腐食性に優れた高クロム鋼。
(3)上記(1)あるいは(2)の基材組成に、さらに、質量%で、
Ni:0.08〜2%、
Cu:0.08〜2%、
Mo:0.08〜2%、
W:0.08〜2%
の内1種以上を含むことを特徴とする塗膜密着性と耐塗装下腐食性に優れた高クロム鋼。
(4)上記(1)乃至3のいずれか記載の塗膜密着性と耐塗装下腐食性に優れた高クロム鋼であって、熱延板又は冷延板を焼鈍後、硫酸又は硝酸を含む溶液を用いて酸洗されてなることを特徴とする塗膜密着性と耐塗装下腐食性に優れた高クロム鋼。
Cは、鋼材の強度を向上させるために有効な元素である。構造物の強度部材として必要な機械特性を確保するため0.001%以上添加することとしたが、0.030%を越えて添加すると逆に靱性を低下させる。このため、0.001%以上、0.030%以下に限定した。
表面酸化皮膜内のSiは、塗膜密着性を向上させると共に、塗膜下腐食を抑制する作用を有する。表面酸化皮膜内において、C、OおよびNを除いたカチオンのみの割合で、その濃化の最も大きい部分の濃度を5%以上とすることで、密着性向上と塗膜下腐食防止に顕著な効果が現れる。Siは皮膜に濃縮するほど改善効果が現れるため、腐食環境が厳しいなど特に必要な際には、皮膜内での濃化層のSi濃度を9%以上にすることが望ましい。
本発明鋼は、所定成分のステンレス鋼を通常の方法で溶解圧延し、焼鈍酸洗を組み合わせた製造工程では、安定して製造することはできない。そこで、以下に製造方法について詳細に記載する。しかし、本願の発明鋼は、ここに記載された方法で製造されたものに限定されるものではない。
本願は塗膜を構成する樹脂組成物の種類を限定するものではない。これは、SiやCrなどの表面濃化により、密着性と耐塗膜下腐食性が向上する機構が、特定の樹脂との特異作用によるものではなく、鋼材と有機物との静電的、電気化学的な相互作用によりものであり、有機物を主成分とする組成物からなる塗膜であれば、程度に差異はあるものの、優れた効果を発揮するものと考えられるためである。
Claims (4)
- 質量%にて、
C:0.001〜0.030%、
Si:1.0%以下、
Mn:1.0%以下、
P:0.040%以下、
S:0.030%以下、
Cr:7.0〜14.0%、
N:0.025%以下
を含有し、残部はFeおよび不可避不純物からなる鋼であって、表面酸化皮膜内にSiおよびCrの濃化層を有し、その濃化の最も大きい部分の濃度が、C、OおよびNを除いたカチオンのみの割合で、Siについては8%以上、Crについては18%以上35%以下であることを特徴とする塗膜密着性と耐塗装下腐食性に優れた高クロム鋼。 - 請求項1の基材組成に、さらに、質量%で、
Ti:0.08〜2%、
Nb:0.08〜2%、
Al:0.01〜1%
の内1種以上を含み、表面酸化皮膜内に付加元素の濃化層を有し、これら元素の濃化の最も大きい部分の濃度の合計が、C、OおよびNを除いたカチオンのみの割合で、1%以上であることを特徴とする塗膜密着性と耐塗装下腐食性に優れた高クロム鋼。 - 請求項1あるいは2の基材組成に、さらに、質量%で、
Ni:0.08〜2%、
Cu:0.08〜2%、
Mo:0.08〜2%、
W:0.08〜2%
の内1種以上を含むことを特徴とする塗膜密着性と耐塗装下腐食性に優れた高クロム鋼。 - 請求項1乃至3のいずれかに記載の塗膜密着性と耐塗装下腐食性に優れた高クロム鋼であって、熱延板又は冷延板を焼鈍後、硫酸又は硝酸を含む溶液を用いて酸洗されてなることを特徴とする塗膜密着性と耐塗装下腐食性に優れた高クロム鋼。